CN110330310A - A kind of preparation method of high intensity crackle household china - Google Patents

A kind of preparation method of high intensity crackle household china Download PDF

Info

Publication number
CN110330310A
CN110330310A CN201910437610.0A CN201910437610A CN110330310A CN 110330310 A CN110330310 A CN 110330310A CN 201910437610 A CN201910437610 A CN 201910437610A CN 110330310 A CN110330310 A CN 110330310A
Authority
CN
China
Prior art keywords
parts
glaze
crackle
preparation
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201910437610.0A
Other languages
Chinese (zh)
Other versions
CN110330310B (en
Inventor
苏康福
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FUJIAN QUANZHOU LONGPENG GROUP Co Ltd
Original Assignee
FUJIAN QUANZHOU LONGPENG GROUP Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FUJIAN QUANZHOU LONGPENG GROUP Co Ltd filed Critical FUJIAN QUANZHOU LONGPENG GROUP Co Ltd
Priority to CN201910437610.0A priority Critical patent/CN110330310B/en
Publication of CN110330310A publication Critical patent/CN110330310A/en
Application granted granted Critical
Publication of CN110330310B publication Critical patent/CN110330310B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

A kind of preparation method of high intensity crackle household china, the high intensity crackle household china includes green body and glaze, green body includes following raw material: albite, cullet, clay, sepiolite, wollastonite, limestone, tourmaline, sericite, silicon powder, calcium oxide, lanthana, strontium carbonate, tin oxide, pass through principal component albite, cullet, clay, sepiolite, wollastonite, limestone, sericite and auxiliary element tourmaline, silicon powder, calcium oxide, tin oxide, it cooperates between lanthana and strontium carbonate, sepiolite and tourmaline cooperate, reduce the firing temperature of ceramics, sericite, wollastonite, limestone and silicon powder cooperation, the anti-folding and compressive property of green body can be increased.

Description

A kind of preparation method of high intensity crackle household china
Technical field
The invention belongs to porcelain preparation fields, and in particular to a kind of preparation method of high intensity crackle household china.
Background technique
With social progress and development, to environmental protection and use safe consciousness also more more and more intense, crockery is compared Have many advantages, such as that wearability is good in plastic dinner, be readily cleaned, durable.The firing of crockery and applying has long-drawn-out in China Long history, various shapes, colorful, refrigerant fine and smooth, the easy washing of feel, deep to be liked by compatriots, the meal of existing top grade Tool generallys use Bone China, and Bone China is made of raw materials such as bone meal, kaolin, quartz, feldspars, and firing temperature is in 1300- Between 1350 DEG C, cost of material is high, firing temperature is high, and the brittleness of crockery is big, and impact resistance ability is low, frangible.
Cracked glaze is a kind of decorative art of porcelain, and porcelain glaze is covered with many crackles, and having to dredge has close, is coarse and fine, Have with short, has Qu Youzhi, the lines of likeness in form cracking, crab claw or ice crack, glaze cracking original is one of firing defect, but is worked as The glaze cracking of certain products is very special, and lines is uniform, clearly, is covered with device face, gives a kind of special aesthetic feeling of people, and then people are just It is therefrom inspired, so that summing up experience, removes the crackle for causing this glaze consciously, thus gradually createed and opened Piece glaze, cracked glaze Producing reason are exactly that the thermal expansion coefficient of glaze is greater than the thermal expansion coefficient of green body, are being burnt into simple terms In the process, glaze generates biggish tensile stress, so that glaze be made to form many crackles, in the prior art, the decoration of household china is imitated Fruit is common, and aesthetic feeling is insufficient, is further improved.
Summary of the invention
The purpose of the present invention is overcoming the prior art, a kind of preparation method of high-intensitive crackle household china is provided.
The present invention adopts the following technical scheme:
A kind of preparation method of high intensity crackle household china, the high intensity crackle household china includes green body and glaze, institute State the raw material that green body includes following parts by weight: 20-25 parts of albite, 35-40 parts of cullet, 25-30 parts of clay, sepiolite 15- 18 parts, 10-12 parts of wollastonite, 8-10 parts of limestone, 5-8 parts of tourmaline, 8-12 parts of sericite, 5-8 parts of silicon powder, calcium oxide 2- 5 parts, 1-3 parts of lanthana, 1-2 parts of strontium carbonate, 0.5-0.8 parts of tin oxide；The glaze includes the raw material of following parts by weight: thoroughly long 15-22 parts of stone, 10-12 parts of mica powder, 5-8 parts of light burnt powder, 6-8 parts of andalusite, 10-12 parts of calcite, becomes 20-25 parts of quartz 2-3 parts of matter rock powder, 1-3 parts of zirconium silicate, 2-6 parts of zinc oxide, 6-8 parts of magnesia, 0.8-1 parts of cerium oxide, calgon 1-2 Part, preparation method includes the following steps:
(1) green body and glaze composition of raw materials weighing and burden are pressed, raw material crushes respectively, mix, wet ball grinding, be made base starch with Glaze slip；
(2) base slurry is made in step (1) and ceramic body is made；
(4) glaze slip made from step (1) is applied into ceramic body surface after the drying；
(4) it after the glaze slip on ceramic body surface is dry, is sent into kiln, is warming up to 980-1050 under oxidizing atmosphere DEG C, 6-8h is fired in heat preservation, is then converted into reducing atmosphere, is warming up to 1150-1180 DEG C, and 4-5h is fired in heat preservation, is finally cooled to 850-880 DEG C, 1-2h is fired in heat preservation, and the high-intensitive crackle household china is made.
Further, the shrinking percentage of the glaze is greater than the shrinking percentage of the green body.
Further, the shrinking percentage of the glaze is 16-18%, and the shrinking percentage of the green body is 8-12%.
Further, it raw material wet grinding 40-48 hours in the ball mill, is ground when glaze slip wet ball mill in the step (1) Grinding media is water, raw material: ball: water=1:1.5-1.8:1.2-1.5.
Further, it when base starches wet ball mill in the step (1), raw material wet grinding 25-30 hours in the ball mill, grinds Grinding media is water, raw material: ball: water=1:1.2-1.5:1-1.2.
Further, the moulding process of ceramic body is roll forming in the step (2).
Further, in the step (3), the glazing mode of glaze slip is leaching glaze or leaching glaze.
Further, the glaze with a thickness of 0.4-0.6mm.
By the above-mentioned description of this invention it is found that compared with prior art, the beneficial effects of the present invention are: green body passes through master Ingredient albite, cullet, clay, sepiolite, wollastonite, limestone, sericite and auxiliary element tourmaline, silicon powder, oxygen To change and cooperates between calcium, tin oxide, lanthana and strontium carbonate, sepiolite and tourmaline cooperate, the firing temperature of ceramics is reduced, Sericite, wollastonite, limestone and silicon powder cooperation, can increase the anti-folding and compressive property of green body, while reducing the receipts of green body Shrinkage, glaze by principal component glassy feldspar, quartz, mica powder, light burnt powder, andalusite, calcite and auxiliary element go bad rock powder, It cooperates between zirconium silicate, aluminium oxide, magnesia and cerium oxide, the glaze for firing formation is bright, and its shrinking percentage is greater than base The shrinking percentage of body, forming household china surface made of finally firing, there are many crackles, increase the beauty of household china；
The present invention is cooperated by green body and glaze, using single firing process, first undergoes oxidizing atmosphere, in experience also Primordial Qi Atmosphere is fired, and forms household china surface obtained there are many crackle, quality are hard, High anti bending strength, chemical stability is good, and day It drops to cement plate from 1 meter of height with tableware not rupture, acid and alkali-resistance can use in micro-wave oven, not damaged in automatic dish-washing machine.
Specific embodiment
Below by way of specific embodiment, the invention will be further described.
A kind of high intensity crackle household china, including green body and glaze.
Green body includes the raw material of following parts by weight: 20-25 parts of albite, 35-40 parts of cullet, 25-30 parts of clay, Hai Pao 15-18 parts of stone, 10-12 parts of wollastonite, 8-10 parts of limestone, 5-8 parts of tourmaline, 8-12 parts of sericite, 5-8 parts of silicon powder, oxygen Change calcium 2-5 parts, 1-3 parts of lanthana, 1-2 parts of strontium carbonate, 0.5-0.8 parts of tin oxide.
Glaze includes the raw material of following parts by weight: 15-22 parts of glassy feldspar, 20-25 parts of quartz, 10-12 parts of mica powder, light-burned 5-8 parts of powder, 6-8 parts of andalusite, 10-12 parts of calcite, rock powder 2-3 parts rotten, 1-3 parts of zirconium silicate, 2-6 parts of zinc oxide, oxidation 6-8 parts of magnesium, 0.8-1 parts of cerium oxide, 1-2 parts of calgon.
Specifically, the shrinking percentage of glaze is greater than the shrinking percentage of the green body, further, the shrinking percentage of glaze is 16- 18%, the shrinking percentage of the green body is 8-12%.
A kind of preparation method of high intensity crackle household china, includes the following steps:
(1) green body and glaze composition of raw materials weighing and burden are pressed, raw material crushes respectively, mix, wet ball grinding, be made base starch with Glaze slip；
(2) base slurry is made in step (1) and ceramic body is made；
(3) glaze slip made from step (1) is applied into ceramic body surface after the drying；
(4) it after the glaze slip on ceramic body surface is dry, is sent into kiln, is warming up to 980-1050 under oxidizing atmosphere DEG C, 6-8h is fired in heat preservation, is then converted into reducing atmosphere, is warming up to 1150-1180 DEG C, and 4-5h is fired in heat preservation, is finally cooled to 850-880 DEG C, 1-2h is fired in heat preservation, and the high-intensitive crackle household china is made.
Specifically, in step (1) when glaze slip wet ball mill, raw material wet grinding 40-48 hours in the ball mill, abrasive media For water, raw material: ball: water=1:1.5-1.8:1.2-1.5；When base starches wet ball mill, wet grinding 25-30 is small in the ball mill for raw material When, abrasive media is water, raw material: ball: water=1:1.2-1.5:1-1.2.
Moulding process into ceramic body is roll forming.
The glazing mode of glaze slip is leaching glaze or leaching glaze.
Glaze with a thickness of 0.4-0.6mm.
Embodiment 1
A kind of high intensity crackle household china, including green body and glaze.
Green body includes the raw material of following parts by weight: 20 parts of albite, 40 parts of cullet, 25 parts of clay, 15 parts of sepiolite, silicon 12 parts of lime stone, 8 parts of limestone, 8 parts of tourmaline, 12 parts of sericite, 5 parts of silicon powder, 5 parts of calcium oxide, 1 part of lanthana, strontium carbonate 2 Part, 0.5 part of tin oxide.
Glaze includes the raw material of following parts by weight: 22 parts of glassy feldspar, 20 parts of quartz, 10 parts of mica powder, 8 parts of light burnt powder, red 6 parts of pillar, 12 parts of calcite, rotten 2 parts of rock powder, 3 parts of zirconium silicate, 6 parts of zinc oxide, 6 parts of magnesia, 1 part of cerium oxide, six inclined phosphorus 2 parts of sour sodium.
Specifically, the shrinking percentage of glaze is greater than the shrinking percentage of the green body, further, the shrinking percentage of glaze is 16%, The shrinking percentage of the green body is 8%.
A kind of preparation method of high intensity crackle household china, includes the following steps:
(1) green body and glaze composition of raw materials weighing and burden are pressed, raw material crushes respectively, mix, wet ball grinding, be made base starch with Glaze slip；
(2) base slurry is made in step (1) and ceramic body is made；
(3) glaze slip made from step (1) is applied into ceramic body surface after the drying；
(4) it after the glaze slip on ceramic body surface is dry, is sent into kiln, 980 DEG C is warming up under oxidizing atmosphere, heat preservation 8h to be fired, reducing atmosphere is then converted into, is warming up to 1150 DEG C, 5h is fired in heat preservation, is finally cooled to 880 DEG C, and 1h is fired in heat preservation, The high-intensitive crackle household china is made.
Specifically, wet grinding 40 hours, abrasive media are raw material in the ball mill in step (1) when glaze slip wet ball mill Water, raw material: ball: water=1:1.5:1.5；When base starches wet ball mill, wet grinding 30 hours, abrasive media are raw material in the ball mill Water, raw material: ball: water=1:1.2:1.
Moulding process into ceramic body is roll forming.
The glazing mode of glaze slip is leaching glaze.
Glaze with a thickness of 0.6mm.
Embodiment 2
A kind of high intensity crackle household china, including green body and glaze.
Green body includes the raw material of following parts by weight: 25 parts of albite, 35 parts of cullet, 30 parts of clay, 18 parts of sepiolite, silicon 10 parts of lime stone, 10 parts of limestone, 5 parts of tourmaline, 8 parts of sericite, 8 parts of silicon powder, 2 parts of calcium oxide, 3 parts of lanthana, strontium carbonate 1 Part, 0.8 part of tin oxide.
Glaze includes the raw material of following parts by weight: 15 parts of glassy feldspar, 25 parts of quartz, 12 parts of mica powder, 5 parts of light burnt powder, red 8 parts of pillar, 10 parts of calcite, rotten 3 parts of rock powder, 1 part of zirconium silicate, 2 parts of zinc oxide, 8 parts of magnesia, 0.8 part of cerium oxide, six are partially 1 part of sodium phosphate.
Specifically, the shrinking percentage of glaze is greater than the shrinking percentage of the green body, further, the shrinking percentage of glaze is 18%, The shrinking percentage of the green body is 12%.
A kind of preparation method of high intensity crackle household china, includes the following steps:
(1) green body and glaze composition of raw materials weighing and burden are pressed, raw material crushes respectively, mix, wet ball grinding, be made base starch with Glaze slip；
(2) base slurry is made in step (1) and ceramic body is made；
(3) glaze slip made from step (1) is applied into ceramic body surface after the drying；
(4) it after the glaze slip on ceramic body surface is dry, is sent into kiln, 1050 DEG C is warming up under oxidizing atmosphere, protect Temperature fires 6h, is then converted into reducing atmosphere, is warming up to 1180 DEG C, and 4h is fired in heat preservation, is finally cooled to 850 DEG C, heat preservation is fired The high-intensitive crackle household china is made in 2h.
Specifically, wet grinding 48 hours, abrasive media are raw material in the ball mill in step (1) when glaze slip wet ball mill Water, raw material: ball: water=1:1.8:1.2；When base starches wet ball mill, wet grinding 25 hours, abrasive media are raw material in the ball mill Water, raw material: ball: water=1:1.5:1.2.
Moulding process into ceramic body is roll forming.
The glazing mode of glaze slip is leaching glaze.
Glaze with a thickness of 0.4mm.
Embodiment 3
A kind of high intensity crackle household china, including green body and glaze.
Green body includes the raw material of following parts by weight: 22 parts of albite, 38 parts of cullet, 28 parts of clay, 16 parts of sepiolite, silicon 11 parts of lime stone, 9 parts of limestone, 6 parts of tourmaline, 10 parts of sericite, 6 parts of silicon powder, 4 parts of calcium oxide, 2 parts of lanthana, strontium carbonate 1.5 parts, 0.6 part of tin oxide.
Glaze includes the raw material of following parts by weight: 18 parts of glassy feldspar, 23 parts of quartz, 11 parts of mica powder, 6 parts of light burnt powder, red 7 parts of pillar, 11 parts of calcite, rotten 2.5 parts of rock powder, 2 parts of zirconium silicate, 4 parts of zinc oxide, 7 parts of magnesia, 0.9 part of cerium oxide, six 1.5 parts of sodium metaphosphate.
Specifically, the shrinking percentage of glaze is greater than the shrinking percentage of the green body, further, the shrinking percentage of glaze is 17%, The shrinking percentage of the green body is 10%.
A kind of preparation method of high intensity crackle household china, includes the following steps:
(1) green body and glaze composition of raw materials weighing and burden are pressed, raw material crushes respectively, mix, wet ball grinding, be made base starch with Glaze slip；
(2) base slurry is made in step (1) and ceramic body is made；
(3) glaze slip made from step (1) is applied into ceramic body surface after the drying；
(4) it after the glaze slip on ceramic body surface is dry, is sent into kiln, 1020 DEG C is warming up under oxidizing atmosphere, protect Temperature fires 7h, is then converted into reducing atmosphere, is warming up to 1165 DEG C, and 4.5h is fired in heat preservation, is finally cooled to 860 DEG C, heat preservation is burnt The high-intensitive crackle household china is made in 1.5h processed.
Specifically, wet grinding 44 hours, abrasive media are raw material in the ball mill in step (1) when glaze slip wet ball mill Water, raw material: ball: water=1:1.6:1.4；When base starches wet ball mill, wet grinding 28 hours, abrasive media are raw material in the ball mill Water, raw material: ball: water=1:1.4:1.1.
Moulding process into ceramic body is roll forming.
The glazing mode of glaze slip is leaching glaze.
Glaze with a thickness of 0.5mm.
Above three embodiments and existing tableware for daily use porcelain obtain following performance parameter through test:
The performance parameter table of each embodiment of table 1
Green body of the present invention by principal component albite, cullet, clay, sepiolite, wollastonite, limestone, sericite with It cooperates between auxiliary element tourmaline, silicon powder, calcium oxide, tin oxide, lanthana and strontium carbonate, sepiolite and tourmaline Cooperation, reduces the firing temperature of ceramics, and sericite, wollastonite, limestone and silicon powder cooperation can increase the anti-folding of green body and resist Performance is pressed, while reducing the shrinking percentage of green body, glaze passes through principal component glassy feldspar, quartz, mica powder, light burnt powder, andalusite, side Xie Shiyu auxiliary element goes bad to cooperate between rock powder, zirconium silicate, aluminium oxide, magnesia and cerium oxide, fires the glaze of formation Face is bright, and its shrinking percentage is greater than the shrinking percentage of green body, forms household china surface made of finally firing there are many crackle, increases Add the beauty of household china；Cooperated by green body and glaze, using single firing process, first undergo oxidizing atmosphere, restored in experience Atmosphere is fired, and forms household china surface obtained there are many crackle, quality are hard, and High anti bending strength, chemical stability is good, and Tableware for daily use drops to cement plate from 1 meter of height and does not rupture, and acid and alkali-resistance can use in micro-wave oven, not damaged in automatic dish-washing machine.
The foregoing is only a preferred embodiment of the present invention, therefore cannot be limited the scope of implementation of the present invention with this, i.e., According to equivalent changes and modifications made by scope of the present invention patent and description, it should still belong to what the invention patent covered In range.

Claims (8)

1. a kind of preparation method of high intensity crackle household china, it is characterised in that: the high intensity crackle household china includes green body And glaze, the green body include the raw material of following parts by weight: 20-25 parts of albite, 35-40 parts of cullet, 25-30 parts of clay, 15-18 parts of sepiolite, 10-12 parts of wollastonite, 8-10 parts of limestone, 5-8 parts of tourmaline, 8-12 parts of sericite, silicon powder 5-8 Part, 2-5 parts of calcium oxide, 1-3 parts of lanthana, 1-2 parts of strontium carbonate, 0.5-0.8 parts of tin oxide；The glaze includes following parts by weight Raw material: 15-22 parts of glassy feldspar, 20-25 parts of quartz, 10-12 parts of mica powder, 5-8 parts of light burnt powder, 6-8 parts of andalusite, calcite 10-12 parts, it is rock powder 2-3 part rotten, 1-3 parts of zirconium silicate, 2-6 parts of zinc oxide, 6-8 parts of magnesia, 0.8-1 parts of cerium oxide, six inclined 1-2 parts of sodium phosphate, preparation method includes the following steps:
(1) green body and glaze composition of raw materials weighing and burden are pressed, raw material crushes respectively, mix, wet ball grinding, and obtained base is starched and glaze Slurry；
(2) base slurry is made in step (1) and ceramic body is made；
(3) glaze slip made from step (1) is applied into ceramic body surface after the drying；
(4) it after the glaze slip on ceramic body surface is dry, is sent into kiln, 980-1050 DEG C is warming up under oxidizing atmosphere, protect Temperature fires 6-8h, is then converted into reducing atmosphere, is warming up to 1150-1180 DEG C, and 4-5h is fired in heat preservation, is finally cooled to 850- 880 DEG C, 1-2h is fired in heat preservation, and the high-intensitive crackle household china is made.
2. a kind of preparation method of high-intensitive crackle household china according to claim 1, it is characterised in that: the glaze Shrinking percentage is greater than the shrinking percentage of the green body.
3. a kind of preparation method of high-intensitive crackle household china according to claim 2, it is characterised in that: the glaze Shrinking percentage is 16-18%, and the shrinking percentage of the green body is 8-12%.
4. a kind of preparation method of high-intensitive crackle household china according to claim 1 or 2 or 3, it is characterised in that: described In step (1) when glaze slip wet ball mill, raw material wet grinding 40-48 hours in the ball mill, abrasive media was water, raw material: ball: water =1:1.5-1.8:1.2-1.5.
5. a kind of preparation method of high-intensitive crackle household china according to claim 1 or 2 or 3, it is characterised in that: described When base starches wet ball mill in step (1), raw material wet grinding 25-30 hours in the ball mill, abrasive media was water, raw material: ball: water =1:1.2-1.5:1-1.2.
6. a kind of preparation method of high-intensitive crackle household china according to claim 1 or 2 or 3, it is characterised in that: described The moulding process of ceramic body is roll forming in step (2).
7. a kind of preparation method of high-intensitive crackle household china according to claim 1 or 2 or 3, it is characterised in that: described In step (3), the glazing mode of glaze slip is leaching glaze or leaching glaze.
8. a kind of preparation method of high-intensitive crackle household china according to claim 1 or 2 or 3, it is characterised in that: described Glaze with a thickness of 0.4-0.6mm.
CN201910437610.0A 2019-05-24 2019-05-24 Preparation method of high-strength crack household porcelain Active CN110330310B (en)