CN110095829A - 一种太阳能聚热发电镜子生产工艺 - Google Patents
一种太阳能聚热发电镜子生产工艺 Download PDFInfo
- Publication number
- CN110095829A CN110095829A CN201910366774.9A CN201910366774A CN110095829A CN 110095829 A CN110095829 A CN 110095829A CN 201910366774 A CN201910366774 A CN 201910366774A CN 110095829 A CN110095829 A CN 110095829A
- Authority
- CN
- China
- Prior art keywords
- solar energy
- energy heat
- heat build
- mirror
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种太阳能聚热发电镜子生产工艺，采用以下原料：氯化氢、乙烯、苯甲酸酯、月桂酸钠、硫酸氢钠、涤纶树脂材料、高分子基材、纳米陶瓷材料、成膜剂、固化剂、太阳能聚热镜，通过在太阳能聚热发电镜子上进行镀膜处理，分别通过保护膜与抗晒膜起到了表面防刮，表面防护，抗老化的作用，在不影响热能吸收的前提下进行太阳能聚热发电镜子的保护。
Description
技术领域
本发明涉及太阳能聚热发电领域，尤其是涉及一种太阳能聚热发电镜子生产工艺。
背景技术
太阳能集热器是一种将太阳的辐射能转换为热能的设备，而太阳能集热器中需要用到大量的太阳能聚热发电镜子，为了吸收太阳能散发的能量，太阳能聚热发电镜子需要常年在太阳下进行暴晒，久而久之太阳能聚热发电镜子就会发生老化，影响使用。
发明内容
本发明为克服上述情况不足，旨在提供一种能解决上述问题的技术方案。
一种太阳能聚热发电镜子生产工艺，一种太阳能聚热发电镜子生产工艺，采用以下原料：氯化氢、乙烯、苯甲酸酯、月桂酸钠、硫酸氢钠、涤纶树脂材料、高分子基材、纳米陶瓷材料、成膜剂、固化剂、太阳能聚热镜，包括以下步骤：
步骤一：制备太阳能聚热镜，根据不同的实用方式生产不同规格的太阳能聚热镜；
步骤二：将高分子基材、涤纶树脂材料进行溶解混合，得到原料混合溶液；
步骤三：将氯化氢、乙烯、苯甲酸酯、月桂酸钠、硫酸氢钠、加入到原料混合溶液中，进行搅拌混合，混合完成后进行降温处理；
步骤四：将成膜剂、固化剂、加入到原料混合溶液中进行混合，得到保护膜原液，混合完成后将原料混合溶液加入到镀膜设备中；
步骤五：将太阳能聚热镜送入到镀膜设备中，通过镀膜设备将保护膜原液通过镀膜工艺镀在太阳能聚热镜的表面，使得太阳能聚热镜表面形成一层保护膜；
步骤六：将纳米陶瓷材料进行溶液，而后加入成膜剂、固化剂，进行混合，得出防晒膜原液，将抗晒膜原液加入到镀膜设备中；
步骤七：将带有保护膜的太阳能聚热镜送入到镀膜设备中，通过镀膜设备将防晒膜原液通过镀膜工艺镀在太阳能聚热镜上保护膜的表面，使得太阳能聚热镜的保护膜上多一层抗晒膜。
作为本发明进一步的方案：所述太阳能聚热镜为线性菲涅尔聚光透镜。
作为本发明进一步的方案：所述保护膜的原料配比为：氯化氢2-3份、乙烯3-5份、苯甲酸酯2-3份、月桂酸钠4-6份、硫酸氢钠2-3份、涤纶树脂材料20-25份、高分子基材10-15份、成膜剂5-8份、固化剂3-5份。
作为本发明进一步的方案：所述保护膜的原料配比为：纳米陶瓷材料20-25份、成膜剂3-5份、固化剂1-3份。
与现有技术相比，本发明的有益效果是：通过在太阳能聚热发电镜子上进行镀膜处理，分别通过保护膜与抗晒膜起到了表面防刮，表面防护，抗老化的作用，在不影响热能吸收的前提下进行太阳能聚热发电镜子的保护。
本发明的附加方面和优点将在下面的描述中部分给出，部分将从下面的描述中变得明显，或通过本发明的实践了解到。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明实施例中，一种太阳能聚热发电镜子生产工艺，采用以下原料：氯化氢、乙烯、苯甲酸酯、月桂酸钠、硫酸氢钠、涤纶树脂材料、高分子基材、纳米陶瓷材料、成膜剂、固化剂、太阳能聚热镜，包括以下步骤：
步骤一：制备太阳能聚热镜，根据不同的实用方式生产不同规格的太阳能聚热镜；
步骤二：将高分子基材、涤纶树脂材料进行溶解混合，得到原料混合溶液；
步骤三：将氯化氢、乙烯、苯甲酸酯、月桂酸钠、硫酸氢钠、加入到原料混合溶液中，进行搅拌混合，混合完成后进行降温处理；
步骤四：将成膜剂、固化剂、加入到原料混合溶液中进行混合，得到保护膜原液，混合完成后将原料混合溶液加入到镀膜设备中；
步骤五：将太阳能聚热镜送入到镀膜设备中，通过镀膜设备将保护膜原液通过镀膜工艺镀在太阳能聚热镜的表面，使得太阳能聚热镜表面形成一层保护膜；
步骤六：将纳米陶瓷材料进行溶液，而后加入成膜剂、固化剂，进行混合，得出防晒膜原液，将抗晒膜原液加入到镀膜设备中；
步骤七：将带有保护膜的太阳能聚热镜送入到镀膜设备中，通过镀膜设备将防晒膜原液通过镀膜工艺镀在太阳能聚热镜上保护膜的表面，使得太阳能聚热镜的保护膜上多一层抗晒膜。
所述太阳能聚热镜为线性菲涅尔聚光透镜。
所述保护膜的原料配比为：氯化氢2-3份、乙烯3-5份、苯甲酸酯2-3份、月桂酸钠4-6份、硫酸氢钠2-3份、涤纶树脂材料20-25份、高分子基材10-15份、成膜剂5-8份、固化剂3-5份。
所述保护膜的原料配比为：纳米陶瓷材料20-25份、成膜剂3-5份、固化剂1-3份。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
Claims (4)
1.一种太阳能聚热发电镜子生产工艺，其特征在于，采用以下原料：氯化氢、乙烯、苯甲酸酯、月桂酸钠、硫酸氢钠、涤纶树脂材料、高分子基材、纳米陶瓷材料、成膜剂、固化剂、太阳能聚热镜，包括以下步骤：
步骤一：制备太阳能聚热镜，根据不同的实用方式生产不同规格的太阳能聚热镜；
步骤二：将高分子基材、涤纶树脂材料进行溶解混合，得到原料混合溶液；
步骤三：将氯化氢、乙烯、苯甲酸酯、月桂酸钠、硫酸氢钠、加入到原料混合溶液中，进行搅拌混合，混合完成后进行降温处理；
步骤四：将成膜剂、固化剂、加入到原料混合溶液中进行混合，得到保护膜原液，混合完成后将原料混合溶液加入到镀膜设备中；
步骤五：将太阳能聚热镜送入到镀膜设备中，通过镀膜设备将保护膜原液通过镀膜工艺镀在太阳能聚热镜的表面，使得太阳能聚热镜表面形成一层保护膜；
步骤六：将纳米陶瓷材料进行溶液，而后加入成膜剂、固化剂，进行混合，得出防晒膜原液，将抗晒膜原液加入到镀膜设备中；
步骤七：将带有保护膜的太阳能聚热镜送入到镀膜设备中，通过镀膜设备将防晒膜原液通过镀膜工艺镀在太阳能聚热镜上保护膜的表面，使得太阳能聚热镜的保护膜上多一层抗晒膜。
2.根据权利要求1所述的一种太阳能聚热发电镜子生产工艺，其特征在于，所述太阳能聚热镜为线性菲涅尔聚光透镜。
3.根据权利要求1所述的一种太阳能聚热发电镜子生产工艺，其特征在于，所述保护膜的原料配比为：氯化氢2-3份、乙烯3-5份、苯甲酸酯2-3份、月桂酸钠4-6份、硫酸氢钠2-3份、涤纶树脂材料20-25份、高分子基材10-15份、成膜剂5-8份、固化剂3-5份。
4.根据权利要求1所述的一种太阳能聚热发电镜子生产工艺，其特征在于，所述保护膜的原料配比为：纳米陶瓷材料20-25份、成膜剂3-5份、固化剂1-3份。