CN110028291A - 一种装配式混凝土建筑快速化灌浆施工方法 - Google Patents
一种装配式混凝土建筑快速化灌浆施工方法 Download PDFInfo
- Publication number
- CN110028291A CN110028291A CN201910403241.3A CN201910403241A CN110028291A CN 110028291 A CN110028291 A CN 110028291A CN 201910403241 A CN201910403241 A CN 201910403241A CN 110028291 A CN110028291 A CN 110028291A
- Authority
- CN
- China
- Prior art keywords
- grouting
- early
- reinforcing bar
- construction method
- bar sleeve
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种装配式混凝土建筑快速化灌浆施工方法，包括下列步骤：步骤一：通过组装式封边装置对灌浆腔封边；步骤二：拌制均匀的早强型钢筋连接用套筒灌浆料浆体；步骤三：将步骤二的早强型钢筋连接用套筒灌浆料浆体通过灌浆机注入步骤一中的灌浆腔内；使用多通道转换器将拌制均匀的早强型钢筋连接用套筒灌浆料浆体同时注入多个灌浆腔内，灌浆材料抗压强度2h即可达到35MPa的技术要求。本发明可广泛应用于装配式混凝土建筑快速化灌浆施工，具有材料获取范围广、施工简便高效、封边材料可循环利用、节能环保等优点。
Description
技术领域
本发明涉及装配式建筑施工技术领域，具体涉及一种装配式混凝土建筑快速化灌浆施工方法。
背景技术
近几年以来，装配整体式混凝土结构因其在工程质量、能源节约、环境保护、社会效益等方面具有显著优势，在建筑领域得到了广泛推广和实施，钢筋套筒灌浆连接技术作为一种主要的预制构件连接技术，实现了装配整体式混凝土结构受力钢筋的有效连接。
通常，钢筋套筒灌浆连接施工流程主要是在施工现场完成预制构件安装固定后，再进行灌浆腔密封处理，然后使用套筒灌浆料拌合物进行套筒灌浆。密封材料一般使用水泥基砂浆，凝结时间较长，且容易出现密封不牢靠而漏浆的情况，而套筒灌浆料凝结时间也较长，24h才能达到预定强度要求。这种工艺形式导致施工周期延长，制约了装配式建筑快速化施工理念的发展。
因此，开发一种装配式混凝土建筑快速化灌浆施工的方法，改善现有灌浆施工周期较长的现状，对于推进和加快装配式建筑发展具有重大意义。
发明内容
有鉴于此，本发明的目的是克服现有技术中的缺陷，提供一种装配式混凝土建筑快速化灌浆施工方法，改善现有灌浆施工周期较长的现状，对于推进和加快装配式建筑发展具有重大意义。
本发明的一种装配式混凝土建筑快速化灌浆施工方法，包括下列步骤：
步骤一：通过组装式封边装置对灌浆腔封边；
步骤二：拌制均匀的早强型钢筋连接用套筒灌浆料浆体；
步骤三：将步骤二的早强型钢筋连接用套筒灌浆料浆体通过灌浆机注入步骤一中的灌浆腔内。
进一步，在步骤二中，所述早强型钢筋连接用套筒灌浆料浆体由早强型钢筋连接用套筒灌浆料干粉料与水按重量比1：(0.12～0.14)机械拌和而成。
进一步，所述早强型钢筋连接用套筒灌浆料干粉料包括以下重量百分比的组分：水泥5～15％、沸石粉12～17.5％、氢氧化钙16～20％、石膏2～3％、活性三氧化二铝2.5～3.5％、氧化镁1～2％、界面增强剂0.1～0.5％、诱导剂3～6％、减水剂0.3～0.5％、细骨料40～45％，各组分的重量百分比之和为100％；所述水泥强度等级不低于42.5。
进一步，所述的沸石粉比表面积≥400m2/kg，沸石粉包括以下重量百分比的组分：1～2.5％的CaO、1.5～2％的MgO、0.5～2％的Fe2O3、10～15％的Al2O3、55～68％的SiO2、0.5～0.75％的TiO2，烧失量为10～12％；。
进一步，所述的活性三氧化二铝的制备方法为：将200目和/或以上的三氧化二铝粉末于350℃下恒温6h，再降温至100℃后加入三氧化二铝粉末重量百分比0.5％的常温纯净水并混合均匀，降温至常温后制得活性三氧化二铝。
进一步，所述的氢氧化钙为工业级和/或以上品质，比表面积≥300m2/kg；石膏含水率≤0.5％，比表面积≥300m2/kg；氧化镁活性30～70s，比表面积≥350m2/kg；界面增强剂为粉末状氧化石墨烯，比表面积≥80000m2/kg，单层比≥99％，含氧量25～35％；诱导剂由硅酸钠和/或硅酸钾组成，模数≥2.0；减水剂为粉剂型聚羧酸高效减水剂；细骨料为20～100目天然砂、石英砂、金刚砂中的一种或多种。
进一步，在步骤一中，所述组装式封边装置包括覆盖于灌浆腔边部开口外侧的橡胶条、覆盖于橡胶条外侧的挡板和固定于预制混凝土构件并压紧固定挡板的固定角钢。
进一步，在步骤三中，所述灌浆机通过一多通道转换器将拌制均匀的早强型钢筋连接用套筒灌浆料浆体同时注入多个灌浆腔内。
本发明的有益效果是：与现有施工工艺相比，本发明的有益之处在于：
1、本发明提供的灌浆腔密封方法无需使用水泥基砂浆，器材可重复利用，降低了施工成本，并且相比于水泥基砂浆存在水泥水化一段时间后才能达到预定强度的弊端，可在密封后直接进行灌浆，极大地提高了密封施工效率，解决了水泥基砂浆因强度不满足要求而出现开裂漏浆的问题；
2、本发明提供的早强型钢筋连接用套筒灌浆料，主要使用硅铝聚合物胶凝材料，极大地减少了水泥用量，可有效缓解能源消耗，降低碳排放，促进建筑行业向生态环保方面的转型升级。同时，充分利用硅铝聚合物胶凝材料凝结时间快的特性，实现套筒灌浆料的早强性能，在2h即可达到抗压强度35MPa的性能要求，大幅度提高了灌浆施工效率；
3、本发明提供的灌浆施工方法，使用多通道转换器，可一次性向多个灌浆腔进行灌浆，实现了灌浆作业的高效化，进一步加快了灌浆施工作业速度。
附图说明
下面结合附图和实施例对本发明作进一步描述：
图1为本发明的结构示意图；
图2为本发明中灌浆机连接结构示意图。
具体实施方式
图1为本发明的结构示意图，图2为本发明中灌浆机连接结构示意图，如图所示，本实施例一中的一种装配式混凝土建筑快速化灌浆施工方法，包括下列步骤：
步骤一：通过组装式封边装置对灌浆腔封边；
步骤二：拌制均匀的早强型钢筋连接用套筒灌浆料浆体；
步骤三：将步骤二的早强型钢筋连接用套筒灌浆料浆体通过灌浆机注入步骤一中的灌浆腔内。
在预制墙柱吊装固定完毕后，将橡胶条1固定于挡板一侧形成灌浆腔2密封板3(即挡板)，再将灌浆腔密封板贴合于灌浆腔外侧，然后使用固定角钢4将灌浆腔密封板固定于灌浆腔外侧，并通过螺钉5将灌浆腔密封板进行加强固定，完成灌浆腔封边工序后，使用灌浆机6将拌制均匀的早强型钢筋连接用套筒灌浆料浆体经由多通道转换器与注浆管注入灌浆腔内。所述灌浆机通过一多通道转换器7其中一个出口与灌浆机相连，其余出口与一根和/或多根注浆管相连，所述的每根注浆管近出浆口处设有止通阀8。
以下实施例、比较例制备的早强型钢筋连接用套筒灌浆料中
所用水泥为强度等级52.5的普通硅酸盐水泥；所述沸石粉组分为1.34％的CaO、1.75％的MgO、0.74％的Fe2O3、11.75％的Al2O3、59.26％的SiO2、0.62％的TiO2、烧失量11.33％；所述细骨料为天然砂；
所述活性三氧化二铝的制备方法为：将200目和/或以上的三氧化二铝粉末于350℃下恒温6h，再降温至100℃后加入三氧化二铝粉末重量百分比0.5％的常温纯净水并混合均匀，降温至常温后制得活性三氧化二铝。
以下实施例、比较例制备的早强型钢筋连接用套筒灌浆料，其制备方法为：称取石膏、活性三氧化二铝、氧化镁、界面增强剂、诱导剂、减水剂，混匀；再边搅拌边加入水泥、沸石粉、氢氧化钙、细骨料，混匀；按照0.13的水料比加水，混匀得所述早强型钢筋连接用套筒灌浆料成品。
实施例
一种早强型钢筋连接用套筒灌浆料，包括以下重量百分比的组份：水泥10％、沸石粉15％、氢氧化钙18％、石膏2.8％、活性三氧化二铝3％、氧化镁1.5％、界面增强剂0.25％、诱导剂4％、减水剂0.45％、细骨料45％。
比较例
一种早强型钢筋连接用套筒灌浆料，包括以下重量百分比的组份：水泥13％、沸石粉15％、氢氧化钙18％、石膏2.8％、氧化镁1.5％、界面增强剂0.25％、诱导剂4％、减水剂0.45％、细骨料45％。
按实施例、比较例制成的灌浆料物理性能如下表所示：
由上表可知，实施例制备的早强型钢筋连接用套筒灌浆料经过养护后的物理性能更出众。通过对比实施例和比较例可知，在灌浆料加入本发明的方法制备的活性三氧化二铝，能够使早强型钢筋连接用套筒灌浆料的物理性能显著提升。
最后说明的是，以上实施例仅用以说明本发明的技术方案而非限制，尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的宗旨和范围，其均应涵盖在本发明的权利要求范围当中。
Claims (8)
1.一种装配式混凝土建筑快速化灌浆施工方法，其特征在于：包括下列步骤：
步骤一：通过组装式封边装置对灌浆腔封边；
步骤二：拌制均匀的早强型钢筋连接用套筒灌浆料浆体；
步骤三：将步骤二的早强型钢筋连接用套筒灌浆料浆体通过灌浆机注入步骤一中的灌浆腔内。
2.根据权利要求1所述的一种装配式混凝土建筑快速化灌浆施工方法，其特征在于：在步骤二中，所述早强型钢筋连接用套筒灌浆料浆体由早强型钢筋连接用套筒灌浆料干粉料与水按重量比1：(0.12～0.14)机械拌和而成。
3.根据权利要求2所述的一种装配式混凝土建筑快速化灌浆施工方法，其特征在于：所述早强型钢筋连接用套筒灌浆料干粉料包括以下重量百分比的组分：水泥5～15％、沸石粉12～17.5％、氢氧化钙16～20％、石膏2～3％、活性三氧化二铝2.5～3.5％、氧化镁1～2％、界面增强剂0.1～0.5％、诱导剂3～6％、减水剂0.3～0.5％、细骨料40～45％，各组分的重量百分比之和为100％；所述水泥强度等级不低于42.5。
4.根据权利要求3所述的一种装配式混凝土建筑快速化灌浆施工方法，其特征在于：所述的沸石粉比表面积≥400m2/kg，沸石粉包括以下重量百分比的组分：1～2.5％的CaO、1.5～2％的MgO、0.5～2％的Fe2O3、10～15％的Al2O3、55～68％的SiO2、0.5～0.75％的TiO2，烧失量为10～12％；。
5.根据权利要求3所述的一种装配式混凝土建筑快速化灌浆施工方法，其特征在于：所述的活性三氧化二铝的制备方法为：将200目和/或以上的三氧化二铝粉末于350℃下恒温6h，再降温至100℃后加入三氧化二铝粉末重量百分比0.5％的常温纯净水并混合均匀，降温至常温后制得活性三氧化二铝。
6.根据权利要求3所述的一种装配式混凝土建筑快速化灌浆施工方法，其特征在于：所述的氢氧化钙为工业级和/或以上品质，比表面积≥300m2/kg；石膏含水率≤0.5％，比表面积≥300m2/kg；氧化镁活性30～70s，比表面积≥350m2/kg；界面增强剂为粉末状氧化石墨烯，比表面积≥80000m2/kg，单层比≥99％，含氧量25～35％；诱导剂由硅酸钠和/或硅酸钾组成，模数≥2.0；减水剂为粉剂型聚羧酸高效减水剂；细骨料为20～100目天然砂、石英砂、金刚砂中的一种或多种。
7.根据权利要求1所述的一种装配式混凝土建筑快速化灌浆施工方法，其特征在于：在步骤一中，所述组装式封边装置包括覆盖于灌浆腔边部开口外侧的橡胶条、覆盖于橡胶条外侧的挡板和固定于预制混凝土构件并压紧固定挡板的固定角钢。
8.根据权利要求1所述的一种装配式混凝土建筑快速化灌浆施工方法，其特征在于：在步骤三中，所述灌浆机通过一多通道转换器将拌制均匀的早强型钢筋连接用套筒灌浆料浆体同时注入多个灌浆腔内。