CN110003896A - 一种抗氧化铈掺杂碳量子点及其制备方法与应用 - Google Patents
一种抗氧化铈掺杂碳量子点及其制备方法与应用 Download PDFInfo
- Publication number
- CN110003896A CN110003896A CN201910179616.2A CN201910179616A CN110003896A CN 110003896 A CN110003896 A CN 110003896A CN 201910179616 A CN201910179616 A CN 201910179616A CN 110003896 A CN110003896 A CN 110003896A
- Authority
- CN
- China
- Prior art keywords
- quantum dot
- carbon quantum
- cerium
- cerium dopping
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明属于纳米材料与医学工程领域，涉及一种抗氧化铈掺杂碳量子点及其制备方法与应用。本发明以甘氨酸为表面钝化剂，柠檬酸为碳源材料，硝酸铈提供铈元素通过一步水热碳化法，经透析和冷冻干燥除去残余物和水分，获得铈掺杂碳量子点。所制备的铈掺杂碳量子点具有较强的荧光性能、较好的抗氧化效果以及良好的生物相容性等优异特性，且成功应用于体外活细胞抗氧化实验，在生物医学领域具有广阔的应用前景。本发明提供的制备方法具有工艺简单、成本低廉、易于大规模生产的特点。
Description
技术领域
本发明属于纳米材料与医学工程领域，涉及一种抗氧化铈掺杂碳量子点及其制备方法与应用。
背景技术
铈（Ce）是稀土元素在周期表中的一种元素，由于其电子结构缺少来自Ce3+中4f轨道的单电子，Ce通常存在于四价和更稳定的状态。尽管如此，CeO2在纳米尺度上表现出更典型的特性。由于萤石结构具有许多立方空间，所以铈离子具有可逆地在三价和四价之间转换的能力。近年来，由于CeO2纳米材料的再生性能和抗氧化性能，被认为是理想的抗氧化材料，在纳米医学中有着广泛的应用前景。正是因为Ce3+／Ce4+较低的还原势能，CeO2可以清除氧自由基，而且Ce3+和Ce4+之间可以相互转换，使得氧化铈纳米材料抗氧化性能可再生。当形成表面氧的缺陷时，Ce4+离子恢复到Ce3+状态，以弥补氧化铈形成过程中的空位，形成了具有可重现性的稳定结构。利用CeO2 可再生的抗氧化性能，目前已应用于生物工程和医学领域的研究。除了可减少活性氧簇（ROS）的产生以外，CeO2可模拟超氧化物歧化酶的活性、模拟过氧化氢酶的活性以及清除NO、羟基等作用,并逐渐应用于生物学及医学。
近年来，荧光碳量子点（CQDs）作为一种新型碳纳米材料受到广泛关注，碳量子点由于具有良好的生物相容性、化学稳定性和优异的荧光性能，在生物成像、基因传递和生物传感等领域有着广泛的应用。已经开发了广泛的获得杂原子掺杂CQDs（如硫和氮掺杂的CQD）的方法。尽管氧化铈通过其清除自由基的功能可以在一系列生物过程中发挥作用，但迄今为止，现还缺少关于铈掺杂碳量子点制备及其应用方面的研究报道。
发明内容
为了解决上述现有技术存在的问题，本发明的目的在于提供一种抗氧化铈掺杂碳量子点及其制备方法与应用。本发明采用一步水热碳化法，碳量子点的成型、铈掺杂与表面钝化可同时完成，通过本发明所述方法制备的铈掺杂碳量子点的生物相容性良好、具有较高荧光性能和抗氧化作用。
为达到以上目的，本发明采用如下技术方案：
一种铈掺杂碳量子点，所述的铈掺杂碳量子点为球形，具有非晶格和晶格的混合相结构，铈以两种成键方式存在于铈掺杂碳量子点中，粒径约为1.4~3.7nm，在360 nm激发光下有最大的发射波长440 nm。
本发明还提供了上述铈掺杂碳量子点的制备方法，包括如下步骤：
（1）将甘氨酸、柠檬酸和六水硝酸铈溶解于双蒸水，室温条件下磁力搅拌充分分散，获得均匀的透明溶液；
（2）将步骤（1）中制备的透明溶液放入反应釜中封闭，放入真空干燥箱中高温加热处理，待冷却到室温后把反应釜取出，获得量子点溶液，离心去除大颗粒沉淀，收集上清液；
（3）将步骤（2）收集的上清液装入透析袋内进行透析，将透析后的溶液冷冻干燥至粉末状，即获得铈掺杂碳量子点（Ce-doped CQDs）。
更优的，所述步骤（1）为将柠檬酸和六水硝酸铈溶解在双蒸水中螯和后加入甘氨酸，室温条件下磁力搅拌充分分散，获得均匀的透明溶液。
进一步地，本发明步骤（1）中所述的柠檬酸、六水硝酸铈、双蒸水和甘氨酸的用量比均为0.6~1.5g：0.84~1.68 g：0.1~0.8 g：20mL。
本发明步骤（2）中所述的高温加热为160~200℃。
本发明步骤（3）中所述的透析袋是分子截留量为1000~5000 Da的亲水性纤维素透析袋。
本发明还提供了上述铈掺杂碳量子点在制备抗氧化产品方面的用途，其具有良好的生物相容性和可忽略的细胞毒性，这些性质为进一步的生物医学应用提供参考，进一步地，所述抗氧化产品为用于治疗由自由基引起的疾病的药物。
与现有技术相比，本发明的有益效果是：
本发明以甘氨酸为表面钝化剂，柠檬酸为碳源，硝酸铈提供铈元素通过一步水热碳化法，经透析和冷冻干燥除去残余物和水分，获得铈掺杂碳量子点；本发明提供的制备方法中所用甘氨酸为具有优异的生物亲和性的天然小分子伯氨基化合物，其成本低廉、生物毒性小并且环境友好；甘氨酸作为助色基团显著提高碳量子点的荧光量子产率，同时加速脱水碳化形成碳纳米结晶。本发明制备过程简单，对设备需求低，操作简便，产物不需要进一步纯化，适合大规模工业生产。
本发明提供的铈掺杂碳量子点具有荧光和抗氧化双重功；不仅具有优异的光学特性，而且具有超氧化物歧化酶特征，可以缓解H2O2引起的氧化损伤，对细胞有一定保护作用。具有良好的生物相容性和可忽略的细胞毒性，这些性质为进一步的生物医学应用提供参考，铈掺杂碳量子点在制备抗氧化产品方面具有广阔的应用前景。
附图说明
图1是 实施例9中制备的Ce-doped CQDs物理形貌特征的表征图；其中，A是 Ce-doped CQDs的透射电镜图；B.是Ce-doped CQDs的粒径分布图；
图2是实施例9中制备的Ce-doped CQDs光学性质的表征图；其中，A是Ce-doped CQDs的紫外吸收光谱，A中右上插图为Ce-doped CQDs水溶液在紫外灯照射下的荧光图片；B是 Ce-doped CQDs在波长为300nm到4000nm的荧光光谱图；
图3是实施例9中制备的Ce-doped CQDs化学结构表征图，其中，A是.光电子能谱图；B是铈元素分峰谱图；
图4是实施例11中 Ce-doped CQDs的生物安全性实验；其中，A是MEF 细胞；B是3T3 细胞；
图5是实施例12中 Ce-doped CQDs的体外抗氧化实验；其中，A是MEF 细胞；B是3T3 细胞；
图6是实施例12中不同浓度Ce-doped CQDs孵育3T3细胞2小时后在H2O2诱导的氧化应激下通过活死细胞染色3T3细胞的荧光图像。
具体实施方式
以下结合实施例对本发明做进一步描述说明，下面描述的实施例是示例性的，仅用于解释本发明，而不能理解为对本发明的限制。
实施例 1：
在该实施例中，通过下列步骤制备铈掺杂碳量子点：
将0.60 g甘氨酸、0.84 g柠檬酸和0.10 g六水硝酸铈溶解在20 mL双蒸水中，室温条件下磁力搅拌，使其充分溶解获得均匀透明的溶液。将上述溶液加入到反应釜中封闭，放入电热恒温真空干燥箱160℃加热4h，冷却至室温，得到量子点溶液，经2000 rpm离心15分钟去除大颗粒沉淀。收集上清液注入到分子截留量为1000Da的透析袋内进行透析，透析时间为72 h，每间隔12 h 换一次水。将透析产物进行在-80℃冻干机中进行冷冻干燥至粉末状，获得铈掺杂碳量子点。
实施例 2：
将0.75 g甘氨酸、0.84 g柠檬酸和0.10 g六水硝酸铈溶解在20 mL双蒸水中，室温条件下磁力搅拌，使其充分溶解获得均匀透明的溶液。将上述溶液加入到反应釜中封闭，放入电热恒温真空干燥箱200℃加热3h，冷却至室温，得到量子点溶液，经2000 rpm离心15分钟去除大颗粒沉淀。收集上清液注入到分子截留量为2000 Da的透析袋内进行透析，透析时间为72 h，每间隔12 h 换一次水。将透析产物进行在-80 ℃冻干机中进行冷冻干燥至粉末状，获得铈掺杂碳量子点。
实施例 3：
将0.90 g甘氨酸、0.84g柠檬酸和0.10 g六水硝酸铈溶解在20 mL双蒸水中，室温条件下磁力搅拌，使其充分溶解获得均匀透明的溶液。将上述溶液加入到反应釜中封闭，放入电热恒温真空干燥箱200℃加热7h，冷却至室温，得到量子点溶液，经2000 rpm离心15分钟去除大颗粒沉淀。收集上清液注入到分子截留量为2000 Da的透析袋内进行透析，透析时间为72 h，每间隔12 h 换一次水。将透析产物进行在-80 ℃冻干机中进行冷冻干燥至粉末状，获得铈掺杂碳量子点。
实施例 4：
将0.75 g甘氨酸、0.84 g柠檬酸和0.20 g六水硝酸铈溶解在20 mL双蒸水中，室温条件下磁力搅拌，使其充分溶解获得均匀透明的溶液。将上述溶液加入到反应釜中封闭，放入电热恒温真空干燥箱180℃加热4 h，冷却至室温，得到量子点溶液，经2000 rpm离心15分钟去除大颗粒沉淀。收集上清液注入到分子截留量为4000 Da的透析袋内进行透析，透析时间为72 h，每间隔12 h 换一次水。将透析产物进行在-80 ℃冻干机中进行冷冻干燥至粉末状，获得铈掺杂碳量子点。
实施例 5：
将0.75 g甘氨酸、0.84 g柠檬酸和0.40 g六水硝酸铈溶解在20 mL双蒸水中，室温条件下磁力搅拌，使其充分溶解获得均匀透明的溶液。将上述溶液加入到反应釜中封闭，放入电热恒温真空干燥箱200℃加热4h，冷却至室温，得到量子点溶液，经2000 rpm离心15分钟去除大颗粒沉淀。收集上清液注入到分子截留量为5000 Da的透析袋内进行透析，透析时间为72 h，每间隔12 h 换一次水。将透析产物进行在-80 ℃冻干机中进行冷冻干燥至粉末状，获得铈掺杂碳量子点。
实施例 6：
将0.75g甘氨酸、0.84g柠檬酸和0.80 g六水硝酸铈溶解在20 mL双蒸水中，室温条件下磁力搅拌，使其充分溶解获得均匀透明的溶液。将上述溶液加入到反应釜中封闭，放入电热恒温真空干燥箱加热4h，冷却至室温，得到量子点溶液，经3000 rpm离心15分钟去除大颗粒沉淀。收集上清液注入到分子截留量为2000 Da的透析袋内进行透析，透析时间为72 h，每间隔12 h 换一次水。将透析产物进行在-80℃冻干机中进行冷冻干燥至粉末状，获得铈掺杂碳量子点。
实施例 7：
将0.84 g柠檬酸和0.80 g六水硝酸铈溶解在20 mL双蒸水中螯和1小时，加入0.75 g甘氨酸，室温条件下磁力搅拌，使其充分溶解获得均匀透明的溶液。将上述溶液加入到反应釜中封闭，放入电热恒温真空干燥箱加热4 h，冷却至室温，得到量子点溶液，经2000 rpm离心15分钟去除大颗粒沉淀。收集上清液注入到分子截留量为2000 Da的透析袋内进行透析，透析时间为72 h，每间隔12 h 换一次水。将透析产物进行在-80 ℃冻干机中进行冷冻干燥至粉末状，获得铈掺杂碳量子点。通过柠檬酸与六水硝酸铈先行螯和，提高了量子点碳化效果。
实施例 8：
将0.84 g柠檬酸和0.80 g六水硝酸铈溶解在20 mL双蒸水中螯和1小时，加入0.75g甘氨酸，室温条件下磁力搅拌，使其充分溶解获得均匀透明的溶液。将上述溶液加入到反应釜中封闭，放入电热恒温真空干燥箱200℃加热6h，冷却至室温，得到量子点溶液，经2000rpm离心15分钟去除大颗粒沉淀。收集上清液注入到分子截留量为2000 Da的透析袋内进行透析，透析时间为72 h，每间隔12 h 换一次水。将透析产物进行在-80 ℃冻干机中进行冷冻干燥至粉末状，获得铈掺杂碳量子点。经比较，4h加热时间下，碳量子点的碳化效果最优
实施例 9：
将1.68 g柠檬酸和0.80 g六水硝酸铈溶解在20 mL双蒸水中螯和1小时，加入1.50g甘氨酸，室温条件下磁力搅拌，使其充分溶解获得均匀透明的溶液。将上述溶液加入到反应釜中封闭，放入电热恒温真空干燥箱加热4 h，冷却至室温，得到量子点溶液，经2000 rpm离心15分钟去除大颗粒沉淀。收集上清液注入到分子截留量为2000 Da的透析袋内进行透析，透析时间为72 h，每间隔12 h 换一次水。将透析产物进行在-80 ℃冻干机中进行冷冻干燥至粉末状，获得铈掺杂碳量子点。通过等比例增加甘氨酸和柠檬酸的量，量子点碳化效果进一步提高。
实施例10：Ce-doped CQDs的形貌特性及荧光性能
（1）Ce-doped CQDs的形貌表征。
利用HRTEM方法对实施例9中制备的Ce-doped CQDs的物理形貌进行分析表征；其中，A是 Ce-doped CQDs的透射电镜图；B.是Ce-doped CQDs的粒径分布图；如图1所示制备的Ce-doped CQDs颗粒具有较好分散性，粒径均一分布。通过ImageJ统计量子点粒径大小，其粒径为1.4~3.7 nm。
（2）Ce-doped CQDs的光学性能的表征。
利用荧光分光光度计和紫外吸收光度计对实施例9中制备的Ce-doped CQDs的光学特征进行表征，其中，A是Ce-doped CQDs的紫外吸收光谱，A中右上插图为Ce-doped CQDs水溶液在紫外灯照射下的荧光图片；B是 Ce-doped CQDs在波长为300nm到400nm的荧光光谱图； 如图2所示，Ce-doped CQDs水溶液在可见光-紫外区域没有明显的吸收峰；右上插图中Ce-doped CQDs水溶液在紫外灯照射下的荧光图片表明，Ce-doped CQDs水溶液在自然光下呈浅棕色，在紫外灯照射下发出蓝色荧光；荧光发射光谱示其具有较宽的发射光谱，与传统的CQDs发射波长随激发波长变化而变化的特性一致，Ce-doped CQDs发射峰强度随着激发波长（300-400 nm）的变化先增大后下降，但无明显红移，在360 nm激发光下有最大的发射波长440nm。由此说明制备的Ce-doped CQDs具有较好的分散性和荧光特性。
（3）Ce-doped CQDs的化学结构的表征。
利用X射线光电子能谱分析（XPS）对实施例9中制备的Ce-doped CQDs的化学结构进行表征。图3是化学结构表征图，其中，A是光电子能谱图；B是铈元素分峰谱图；如图3所示，Ce-doped CQDs主要由有碳，氮，氧和铈四种元素组成，表明铈元素已成功掺杂入碳量子点颗粒；图B显示掺杂的铈元素在885.0和903.5eV处存在两个强峰（由32eV的自旋轨道分裂产生），这与Ce3+的标准光谱一致，而888.1,898.0,900.9,906.4和916.4eV的峰值是Ce4+存在的指标，以上结果表明铈元素主要以2种成键方式存在碳量子点颗粒中。由XPS结果我们还可以计算制备的Ce-doped CQDs具有优良的Ce3+和Ce4+的原子比例（25%：75%），已知Ce3+通过模拟超氧化物歧化酶（SOD）活性去除·OH，而Ce4+通过模拟过氧化氢酶（CAT）活性分解H2O2。
实施例11：Ce-doped CQDs的生物安全性
通过CCK-8测定Ce-doped CQDs的生物安全性。将MEF细胞和3T3细胞（购自中科院上海细胞研究所）以每孔1.0×10 4个细胞的密度接种到96孔板中，每组3个副孔。在37 ℃和5％CO2孵化24小时后，细胞密度达到80％汇合，用含有不同浓度（0、50、100、200、400和800μg /mL）的Ce-doped CQDs新鲜培养基孵育24小时；然后用PBS缓冲液洗涤细胞，向每个孔中加入10μLCCK-8溶液和90μL新鲜DMEM培养基，将96孔板在37℃和5％ CO2下再孵育2小时，使用酶标仪在450nm的发射波长处检测每个孔的吸光度；细胞活力（%）=[A(Ce-doped CQDs)-A(空白)]/[A(0)-A(空白)]*100 %，实验独立重复三次。
图4是 Ce-doped CQDs的生物安全性实验图；其中，A是MEF 细胞；B是3T3 细胞；如图4所示，在不同浓度的Ce-doped CQDs处理24小时暴露时间后，细胞活力没有显示出显著变化，即使在800 μg/mL的最高剂量下，所有实验组的细胞活力仍为90％左右，表明Ce-doped CQDs对细胞具有非常轻微的细胞毒性。
实施例12：Ce-doped CQDs的抗氧化能力
使用（CCK-8）测定来测试Ce-doped CQDs在H2O2的刺激下的抗氧化作用。以与实施例10中同样的方式，将MEF细胞和3T3细胞接种在96孔板中并培养。第二天，细胞用不同浓度（0、50、100、200和400 μg/mL）的Ce-doped CQDs预处理约24小时，并暴露于新鲜制剂30％H2O2中，每孔适当浓度。同时设置空白组，不含30％ H2O2，每个都设立了3个副孔。用H2O2处理2小时后，PBS缓冲液洗涤细胞，加入CCK-8试剂孵育2小时，使用酶标仪在450nm的发射波长处检测每个孔的吸光度。
图5是Ce-doped CQDs的体外抗氧化实验图；其中，A是MEF 细胞；B是3T3 细胞；如图5所示，MEF细胞和3T3细胞的细胞活力随着相同氧化应激下Ce-doped CQDs浓度的增加而逐渐提高。可见，Ce-doped CQDs通过有效的自由基清除能力表现出较优异的抗氧化作用。
进一步的，为了评估Ce-doped CQDs的抗氧化作用，对其进行活死亡细胞染色测定；将3T3细胞以2.0×10 4个细胞/孔的密度接种在24孔板中，培养24小时。然后，设置六组试验组分别同时进行对比，试验组分别为：对照组、H2O2组、H2O2 + 50μg / mL CeO2、H2O2 +100 μg/mL CeO2、H2O2 + 200 μg/mL CeO2、H2O2 + 400 μg/mL CeO2。每组细胞增长到80％，对照组暴露于正常生长条件，没有任何H2O2和Ce-doped CQDs；H2O2组只用选择浓度的H2O2无Ce-doped CQDs孵育2h，即没有处理；其他试验组用不同浓度的Ce-doped CQDs（50、100、200和400μg / mL）并指示H2O2分别孵育4小时，加入二乙酸荧光素（FDA）和碘化丙啶（PI）工作缓冲液进行细胞染色，在荧光显微镜下观察染色细胞的荧光，活细胞呈绿色，死细胞呈现红色。
图6是不同浓度Ce-doped CQDs孵育3T3细胞2小时后在H2O2诱导的氧化应激下通过活死细胞染色3T3细胞的荧光图像。如图6所示，在用单一Ce-doped CQDs处理的3T3细胞中观察到几乎没有红色荧光，但是在600 μM的H2O2处理中可以看到大量的红色荧光，这表明H2O2可引起显着的细胞凋亡。但是，随着Ce-doped CQDs浓度的增加，H2O2诱导的细胞凋亡逐渐减轻。特别是在H2O2诱导的氧化应激诱导氧化应激后，400 μg/mL Ce-doped CQDs处理后，只能看到少量的红色荧光。结合活体染色结果可知，Ce-doped CQDs对氧化应激诱导的细胞凋亡具有良好的抗氧化作用。
尽管上面已经示出和描述了本发明的实施例，可以理解的是，上述实施例是示例性的，不能理解为对本发明的限制，在不相互矛盾的情况下，本领域的技术人员可以将本说明书中描述的不同实施例或示例以及不同实施例或示例的特征进行结合和组合。
Claims (8)
1.一种铈掺杂碳量子点，其特征在于，所述的铈掺杂碳量子点为球形，具有非晶格和晶格的混合相结构，铈以两种成键方式存在于铈掺杂碳量子点中。
2.如权利要求1所述的铈掺杂碳量子点的制备方法，其特征在于：包括如下步骤：
（1）将甘氨酸、柠檬酸和六水硝酸铈溶解于双蒸水，室温条件下磁力搅拌充分分散，获得均匀的透明溶液；
（2）将步骤（1）中制备的透明溶液放入反应釜中封闭，放入真空干燥箱中高温加热处理，待冷却到室温后把反应釜取出，获得量子点溶液，离心去除大颗粒沉淀，收集上清液；
（3）将步骤（2）收集的上清液装入透析袋内进行透析，将透析后的溶液冷冻干燥至粉末状，即获得铈掺杂碳量子点。
3.根据权利要求2所述的铈掺杂碳量子点的制备方法，其特征在于，所述步骤（1）为将柠檬酸和六水硝酸铈溶解在双蒸水中螯和后加入甘氨酸，室温条件下磁力搅拌充分分散，获得均匀的透明溶液。
4.根据权利要求2或3任一项所述的铈掺杂碳量子点的制备方法，其特征在于，步骤（1）中所述的柠檬酸、六水硝酸铈、双蒸水和甘氨酸的用量比均为0.6~1.5g：0.84~1.68g：0.1~0.8g：20mL。
5.根据权利要求2或3任一项所述的铈掺杂碳量子点的制备方法，其特征在于，步骤（2）中所述的高温加热为160~200℃，3~7h。
6.根据权利要求2或3任一项所述的铈掺杂碳量子点的制备方法，其特征在于，步骤（3）中所述的透析袋是分子截留量为1000~5000 Da的亲水性纤维素透析袋。
7.如权利要求1所述的铈掺杂碳量子点在制备抗氧化产品方面的用途。
8.根据权利要求7所述的用途，其特征在于，所述的抗氧化产品为用于治疗由自由基引起的疾病的药物。