CN109928716A - 一种中温高档锂质瓷的制备方法 - Google Patents

一种中温高档锂质瓷的制备方法 Download PDF

Info

Publication number
CN109928716A
CN109928716A CN201711355854.1A CN201711355854A CN109928716A CN 109928716 A CN109928716 A CN 109928716A CN 201711355854 A CN201711355854 A CN 201711355854A CN 109928716 A CN109928716 A CN 109928716A
Authority
CN
China
Prior art keywords
glaze
preparation
blank
medium temperature
follows
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711355854.1A
Other languages
English (en)
Inventor
黄帅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201711355854.1A priority Critical patent/CN109928716A/zh
Publication of CN109928716A publication Critical patent/CN109928716A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种中温高档锂质瓷的制备方法，其坯料和釉料配方的重量百分比组成为：坯料：滑石30～45%、锂长石20～35%、钾长石5～15%、高岭土10～18%、膨润土3～5%、石英0～15%；釉料：锂长石20～40%、方解石5～15%、高岭土4～8%、石英0～15%、ZnO 3～5%、BaCO3 0～5%、玻璃料20～35%；经过坯料和釉料制备、成型、干燥、坯体素烧、施釉、干燥、中温釉烧获得制品，其中坯体素烧温度范围为：1140～1160℃，保温时间为30min，中温釉烧温度为1100℃、保温时间为30min，获得具有釉面质量好、光泽度高制品，因此具有广阔的应用前景。

Description

一种中温高档锂质瓷的制备方法
技术领域
本发明属无机非金属材料（陶瓷）领域，具体涉及一种中温高档锂质瓷的制备方法。
背景技术
目前国内中温锂质瓷制备方法大都采用一次烧成工艺，但由于锂质瓷烧成温度范围狭窄，在烧成过程中温度不易控制，当温度过高或保温时间过长时易产生变形缺陷，当温度过低或保温时间短时易产生炸裂缺陷，因此目前中温锂质瓷生产过程中为扩宽烧成范围，往往加入30％左右的滑石，然而由于采用一次性烧成工艺，其在烧成过程中随滑石的分解釉面会产生较多的针孔缺陷，另外因锂质瓷坯体的膨胀系数较大，釉的膨胀系数为了要与之匹配，一次烧成后釉面光泽度差且易产生针孔缺陷，因此目前中温锂质瓷的制备方法已经不能满足消费者的需求，严重阻碍了中锂镁质日用陶瓷品质的提升。
发明内容
本发明要解决的技术问题是提供一种釉面质量好、光泽度高、原料成本低廉、生产工艺简单的中温锂质瓷的制备方法。
本发明通过以下技术方案予以实现：一种中温高档锂质瓷的制备方法，采用矿物原料及化工原料, 其坯料和釉料配方的重量百分比组成为：
坯料：滑石30～45%、锂长石20～35%、钾长石5～15%、高岭土10～18%、膨润土3～5%、石英0～15%；
釉料：锂长石20～40%、方解石5～15%、高岭土4～8%、石英0～15%、ZnO 3～5%、BaCO3 0～5%、玻璃料20～35%；
经过坯料和釉料制备、成型、干燥、坯体素烧、施釉、干燥、中温釉烧获得制品，其中坯体素烧温度范围为：1140～1160℃，保温时间为30min，中温釉烧温度为1100℃、保温时间为30min。
所述坯料的制备工艺为：按坯料配方称量原料混合均匀，然后装入球磨设备内球磨，出磨泥料细度为0.008％万孔筛余。
所述釉料的制备工艺为：按釉料配方称量原料合均匀，然后装入球磨设备内球磨，出磨釉料细度为0.03％万孔筛余。
本发明采用天然矿物原料和工业纯原料，通过两次烧成工艺制备了一种釉面质量好、光泽度高的中温锂质瓷，高温素烧既有利于有机物的排除和滑石的晶型转化及消除残余应力，又通过反应中生产的液相克服了坯体变形，有效的消除了釉面针孔，提高了釉面亮度，因此具有广阔的市场前景。
具体实施方式
为更进一步阐述本发明、为达成预定发明目的所采取的技术手段及功效，以下结合较佳实施例，对本发明进行详细说明：
实施列一：
一种中温高档锂质瓷的制备方法，按质量百分比称取坯料：滑石32%、锂长石26%、钾长石10%、高岭土15%、膨润土4%、石英13%，经混合球磨，控制出磨泥料细度为0.008％万孔筛余，泥浆陈腐后，注浆成形获得坯体，该坯体预先经过素烧，素烧温度为1150℃、保温时间为30min；
按质量百分比称取釉料：锂长石24%、方解石14%、高岭土6%、石英14%、ZnO 3%、BaCO3 4%、玻璃料35%，经混合球磨，控制出磨泥料细度为0.03％万孔筛余，然后在素烧过的素胎内外表面上釉、干燥，在1100℃烧成，保温时间为30min。
将制备好的试样进行光泽度性能测试，光泽度为85。
实施列二：
一种中温高档锂质瓷的制备方法，按质量百分比称取坯料：滑石40%、锂长石22%、钾长石8%、高岭土11%、膨润土5%、石英14%，经混合球磨，控制出磨泥料细度为0.008％万孔筛余，泥浆陈腐后，注浆成形获得坯体，该坯体预先经过素烧，素烧温度为1160℃、保温时间为30min；
按质量百分比称取釉料：锂长石34%、方解石11%、高岭土8%、石英12%、ZnO 5%、BaCO3 5%、玻璃料25%，经混合球磨，控制出磨泥料细度为0.03％万孔筛余，然后在素烧过的素胎内外表面上釉、干燥，在1100℃烧成，保温时间为30min。
将制备好的试样进行光泽度性能测试，光泽度为86。

Claims (3)

1.一种中温高档锂质瓷的制备方法，采用矿物原料及化工原料, 其坯料和釉料配方的重量百分比组成为：
坯料：滑石30～45%、锂长石20～35%、钾长石5～15%、高岭土10～18%、膨润土3～5%、石英0～15%；
釉料：锂长石20～40%、方解石5～15%、高岭土4～8%、石英0～15%、ZnO 3～5%、BaCO3 0～5%、玻璃料20～35%；
经过坯料和釉料制备、成型、干燥、坯体素烧、施釉、干燥、中温釉烧获得制品，其中坯体素烧温度范围为：1140～1160℃，保温时间为30min，中温釉烧温度为1100℃、保温时间为30min。
2.根据权利要求1所述的制备方法，其特征在于：所述坯料的制备工艺为：按坯料配方称量原料混合均匀，然后装入球磨设备内球磨，出磨泥料细度为0.008％万孔筛余。
3.根据权利要求1所述的制备方法，其特征在于：所述釉料的制备工艺为：按釉料配方称量原料合均匀，然后装入球磨设备内球磨，出磨釉料细度为0.03％万孔筛余。
CN201711355854.1A 2017-12-16 2017-12-16 一种中温高档锂质瓷的制备方法 Pending CN109928716A (zh)