CN109881299A - 一种耐磨无纺布及其制备方法 - Google Patents
一种耐磨无纺布及其制备方法 Download PDFInfo
- Publication number
- CN109881299A CN109881299A CN201910154250.3A CN201910154250A CN109881299A CN 109881299 A CN109881299 A CN 109881299A CN 201910154250 A CN201910154250 A CN 201910154250A CN 109881299 A CN109881299 A CN 109881299A
- Authority
- CN
- China
- Prior art keywords
- wear
- parts
- agent
- woven fabric
- zine oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及无纺布加工领域，具体涉及一种耐磨无纺布及其制备方法，其成分按重量份计：聚对羟基苯甲酸脂、聚酰胺、玻璃纤维、纳米氧化银、纳米氧化锌、丙烯酸聚氨酯、聚氨酯脱模剂、纳米硫酸钠、无硫化钼、消泡剂、交联剂和适量的水，本发明所制备的无纺布无纺布防磨的效果、延伸率高，同时无纺布本身的柔软好；本发明制备的无纺布中通过纳米氧化锌、丙烯酸聚氨酯、聚氨酯脱模剂、纳米硫酸钠、无硫化钼和水制备的耐磨剂，使得无纺布表面光滑度得到显著提高，摩擦系数降低，使得防磨性能得到明显改善；此外，本发明的制备方法简单，便于大面积推广。
Description
技术领域
本发明涉及无纺布加工领域，具体涉及一种耐磨无纺布及其制备方法。
背景技术
无纺布(英文名：Non Woven Fabric或者Nonwoven cloth)又称不织布，是由定向的或随机的纤维而构成。因具有布的外观和某些性能而称其为布。
无纺布具有防潮、透气、柔韧、质轻、不助燃、容易分解、无毒无刺激性、色彩丰富、价格低廉、可循环再用等特点。如多采用聚丙烯(pp材质)粒料为原料，经高温熔融、喷丝、铺纲、热压卷取连续一步法生产而成。
无纺布制品色彩丰富、鲜艳明丽、时尚环保、用途广泛、美观大方，图案和款式都多样，且质轻、环保、可循环再用，被国际公认为保护地球生态的环保产品。适用于农用薄膜、制鞋、制革、床垫、子母被、装饰、化工、印刷、汽车、建材，家具等行业，及服装衬布，医疗卫生一次性手术衣，口罩，帽，床单，酒店一次性台布，美容，桑拿乃至当今时尚的礼品袋，精品袋，购物袋，广告袋等等。
现有无纺布的耐磨改性方法，通常是在无纺布的两个表面贴附上防磨胶，甚至是硬质防磨胶层，虽然起到了防磨的效果，但也失去了无纺布本身的柔软特定，得不到消费者的认可。
基于此，本发明提供了一种耐磨无纺布及其制备方法。
发明内容
针对现有技术的不足，本发明提供了一种用于地铁盾构管片防腐防水无纺布，制备的无纺布防磨的效果，同时无纺布本身的柔软好。
为实现以上目的，本发明通过以下技术方案予以实现：
一种耐磨无纺布，其成分按重量份计：聚对羟基苯甲酸脂65-85份、聚酰胺25-35份、玻璃纤维10-16份、纳米氧化银3.2-4.8份、纳米氧化锌8.6-12.5份、丙烯酸聚氨酯5.6-7.3份、聚氨酯脱模剂3.2-4.3份、纳米硫酸钠7.2-8.5份、无硫化钼3.5-4.5份、消泡剂12.3-16.6份、交联剂18-23份和适量的水。
优选的，一种耐磨无纺布，其制备方法包括以下步骤：
a、制备耐磨剂：将纳米氧化锌、丙烯酸聚氨酯、聚氨酯脱模剂、纳米硫酸钠、无硫化钼和水置于熔融炉中，水用量为纳米氧化锌分量的5倍，将熔融炉抽至真空，将熔融炉内的温度升至180-210℃，然后进行搅拌，搅拌至恒重，恒温储存，得到耐磨剂，备用；
b、制备杀菌剂：将纳米氧化锌和纳米氧化锌置于搅拌机中进行充分搅拌，得到杀菌剂；
c、制备耐磨无纺布：将步骤a中的耐磨剂、步骤b中的杀菌剂、聚对羟基苯甲酸脂、聚酰胺、玻璃纤维、消泡剂、交联剂和适量的水添加到螺杆挤压机进行熔融，再经纺丝、牵伸、成网、热轧后制得耐磨无纺布；
优选的，所述消泡剂选用改性乳化硅油。
优选的，所述步骤a中的恒温储存温度为50℃。
优选的，所述增稠剂由聚氧化乙烯和羧甲基纤维素钠按照质量比1∶1混合而成。
优选的，所述步骤a和b中的纳米氧化银分量一样多。
有益效果：
本发明以聚对羟基苯甲酸脂、聚酰胺、玻璃纤维、纳米氧化银、纳米氧化锌、丙烯酸聚氨酯、聚氨酯脱模剂、纳米硫酸钠、无硫化钼、消泡剂、交联剂和适量的水作为制备无纺布的原料，所制备的无纺布无纺布防磨的效果、延伸率高，同时无纺布本身的柔软好。本发明制备的无纺布中通过纳米氧化锌、丙烯酸聚氨酯、聚氨酯脱模剂、纳米硫酸钠、无硫化钼和水制备的耐磨剂，使得无纺布表面光滑度得到显著提高，摩擦系数降低，使得防磨性能得到明显改善。此外，本发明的制备方法简单，便于大面积推广。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1：
一种耐磨无纺布，其成分按重量份计：聚对羟基苯甲酸脂65份、聚酰胺32份、玻璃纤维10份、纳米氧化银3.2份、纳米氧化锌8.6份、丙烯酸聚氨酯5.6份、聚氨酯脱模剂3.2份、纳米硫酸钠7.2份、无硫化钼3.5份、消泡剂16.6份、交联剂23份和适量的水。
一种耐磨无纺布，其制备方法包括以下步骤：
a、制备耐磨剂：将纳米氧化锌、丙烯酸聚氨酯、聚氨酯脱模剂、纳米硫酸钠、无硫化钼和水置于熔融炉中，水用量为纳米氧化锌分量的5倍，将熔融炉抽至真空，将熔融炉内的温度升至180℃，然后进行搅拌，搅拌至恒重，恒温储存，得到耐磨剂，备用；
b、制备杀菌剂：将纳米氧化锌和纳米氧化锌置于搅拌机中进行充分搅拌，得到杀菌剂；
c、制备耐磨无纺布：将步骤a中的耐磨剂、步骤b中的杀菌剂、聚对羟基苯甲酸脂、聚酰胺、玻璃纤维、消泡剂、交联剂和适量的水添加到螺杆挤压机进行熔融，再经纺丝、牵伸、成网、热轧后制得耐磨无纺布；
消泡剂选用改性乳化硅油。
步骤a中的恒温储存温度为50℃。
增稠剂由聚氧化乙烯和羧甲基纤维素钠按照质量比1∶1混合而成。
步骤a和b中的纳米氧化银分量一样多。
实施例2：
一种耐磨无纺布，其成分按重量份计：聚对羟基苯甲酸脂72份、聚酰胺28份、玻璃纤维12份、纳米氧化银4.8份、纳米氧化锌9.7份、丙烯酸聚氨酯7.3份、聚氨酯脱模剂3.6份、纳米硫酸钠8.5份、无硫化钼3.8份、消泡剂12.3份、交联剂18份和适量的水。
一种耐磨无纺布，其制备方法包括以下步骤：
a、制备耐磨剂：将纳米氧化锌、丙烯酸聚氨酯、聚氨酯脱模剂、纳米硫酸钠、无硫化钼和水置于熔融炉中，水用量为纳米氧化锌分量的5倍，将熔融炉抽至真空，将熔融炉内的温度升至190℃，然后进行搅拌，搅拌至恒重，恒温储存，得到耐磨剂，备用；
b、制备杀菌剂：将纳米氧化锌和纳米氧化锌置于搅拌机中进行充分搅拌，得到杀菌剂；
c、制备耐磨无纺布：将步骤a中的耐磨剂、步骤b中的杀菌剂、聚对羟基苯甲酸脂、聚酰胺、玻璃纤维、消泡剂、交联剂和适量的水添加到螺杆挤压机进行熔融，再经纺丝、牵伸、成网、热轧后制得耐磨无纺布；
消泡剂选用改性乳化硅油。
步骤a中的恒温储存温度为50℃。
增稠剂由聚氧化乙烯和羧甲基纤维素钠按照质量比1∶1混合而成。
步骤a和b中的纳米氧化银分量一样多。
实施例3：
一种耐磨无纺布，其成分按重量份计：聚对羟基苯甲酸脂78份、聚酰胺25份、玻璃纤维14份、纳米氧化银3.7份、纳米氧化锌11.1份、丙烯酸聚氨酯6.2份、聚氨酯脱模剂3.9份、纳米硫酸钠7.6份、无硫化钼4.2份、消泡剂13.9份、交联剂20份和适量的水。
一种耐磨无纺布，其制备方法包括以下步骤：
a、制备耐磨剂：将纳米氧化锌、丙烯酸聚氨酯、聚氨酯脱模剂、纳米硫酸钠、无硫化钼和水置于熔融炉中，水用量为纳米氧化锌分量的5倍，将熔融炉抽至真空，将熔融炉内的温度升至200℃，然后进行搅拌，搅拌至恒重，恒温储存，得到耐磨剂，备用；
b、制备杀菌剂：将纳米氧化锌和纳米氧化锌置于搅拌机中进行充分搅拌，得到杀菌剂；
c、制备耐磨无纺布：将步骤a中的耐磨剂、步骤b中的杀菌剂、聚对羟基苯甲酸脂、聚酰胺、玻璃纤维、消泡剂、交联剂和适量的水添加到螺杆挤压机进行熔融，再经纺丝、牵伸、成网、热轧后制得耐磨无纺布；
消泡剂选用改性乳化硅油。
步骤a中的恒温储存温度为50℃。
增稠剂由聚氧化乙烯和羧甲基纤维素钠按照质量比1∶1混合而成。
步骤a和b中的纳米氧化银分量一样多。
实施例4：
一种耐磨无纺布，其成分按重量份计：聚对羟基苯甲酸脂85份、聚酰胺35份、玻璃纤维16份、纳米氧化银4.2份、纳米氧化锌12.5份、丙烯酸聚氨酯6.7份、聚氨酯脱模剂4.3份、纳米硫酸钠8.1份、无硫化钼4.5份、消泡剂15.3份、交联剂21份和适量的水。
一种耐磨无纺布，其制备方法包括以下步骤：
a、制备耐磨剂：将纳米氧化锌、丙烯酸聚氨酯、聚氨酯脱模剂、纳米硫酸钠、无硫化钼和水置于熔融炉中，水用量为纳米氧化锌分量的5倍，将熔融炉抽至真空，将熔融炉内的温度升至210℃，然后进行搅拌，搅拌至恒重，恒温储存，得到耐磨剂，备用；
b、制备杀菌剂：将纳米氧化锌和纳米氧化锌置于搅拌机中进行充分搅拌，得到杀菌剂；
c、制备耐磨无纺布：将步骤a中的耐磨剂、步骤b中的杀菌剂、聚对羟基苯甲酸脂、聚酰胺、玻璃纤维、消泡剂、交联剂和适量的水添加到螺杆挤压机进行熔融，再经纺丝、牵伸、成网、热轧后制得耐磨无纺布；
消泡剂选用改性乳化硅油。
步骤a中的恒温储存温度为50℃。
增稠剂由聚氧化乙烯和羧甲基纤维素钠按照质量比1∶1混合而成。
步骤a和b中的纳米氧化银分量一样多。
需要说明的是，在本文中，诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。在没有更多限制的情况下，由语句“包括一个......’限定的要素，并不排除在包括所述要素的过程、方法、物品或者设备中还存在另外的相同要素。
以上实施例仅用以说明本发明的技术方案，而非对其限制；尽管参照前述实施例对本发明进行了详细的说明，本领域的普通技术人员应当理解：其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换；而这些修改或者替换，并不使相应技术方案的本质脱离本发明各实施例技术方案的精神和范围。
Claims (6)
1.一种耐磨无纺布，其特征在于，其成分按重量份计：聚对羟基苯甲酸脂65-85份、聚酰胺25-35份、玻璃纤维10-16份、纳米氧化银3.2-4.8份、纳米氧化锌8.6-12.5份、丙烯酸聚氨酯5.6-7.3份、聚氨酯脱模剂3.2-4.3份、纳米硫酸钠7.2-8.5份、无硫化钼3.5-4.5份、消泡剂12.3-16.6份、交联剂18-23份和适量的水。
2.根据权利要求1所述的一种耐磨无纺布，其特征在于，其制备方法包括以下步骤：
a、制备耐磨剂：将纳米氧化锌、丙烯酸聚氨酯、聚氨酯脱模剂、纳米硫酸钠、无硫化钼和水置于熔融炉中，水用量为纳米氧化锌分量的5倍，将熔融炉抽至真空，将熔融炉内的温度升至180-210℃，然后进行搅拌，搅拌至恒重，恒温储存，得到耐磨剂，备用；
b、制备杀菌剂：将纳米氧化锌和纳米氧化锌置于搅拌机中进行充分搅拌，得到杀菌剂；
c、制备耐磨无纺布：将步骤a中的耐磨剂、步骤b中的杀菌剂、聚对羟基苯甲酸脂、聚酰胺、玻璃纤维、消泡剂、交联剂和适量的水添加到螺杆挤压机进行熔融，再经纺丝、牵伸、成网、热轧后制得耐磨无纺布。
3.据权利要求1所述的一种耐磨无纺布，其特征在于：所述消泡剂选用改性乳化硅油。
4.根据权利要求1所述的一种耐磨无纺布，其特征在于：所述交联剂选用乙丙橡胶、各种氟橡胶、CPE中的任意一种。
5.根据权利要求2所述的一种耐磨无纺布的制备方法，其特征在于：所述步骤a中的恒温储存温度为50℃。
6.根据权利要求1所述的一种耐磨无纺布，其特征在于：所述步骤a和b中的纳米氧化银分量一样多。