CN107524015A - 一种耐磨无纺布及其制备方法 - Google Patents

一种耐磨无纺布及其制备方法 Download PDF

Info

Publication number
CN107524015A
CN107524015A CN201710769126.9A CN201710769126A CN107524015A CN 107524015 A CN107524015 A CN 107524015A CN 201710769126 A CN201710769126 A CN 201710769126A CN 107524015 A CN107524015 A CN 107524015A
Authority
CN
China
Prior art keywords
wear
dispersion liquid
parts
woven fabric
woven fabrics
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201710769126.9A
Other languages
English (en)
Other versions
CN107524015B (zh
Inventor
叶小平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongtai Yusen Technology Co ltd
Original Assignee
Yancheng Hengtian Nonwoven Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yancheng Hengtian Nonwoven Technology Co Ltd filed Critical Yancheng Hengtian Nonwoven Technology Co Ltd
Priority to CN201710769126.9A priority Critical patent/CN107524015B/zh
Publication of CN107524015A publication Critical patent/CN107524015A/zh
Application granted granted Critical
Publication of CN107524015B publication Critical patent/CN107524015B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种耐磨无纺布，包括一层无纺布和涂附于无纺布两侧面的耐磨涂层；所述的耐磨涂层包括石膏晶须、丙烯酸树脂、高锰合金、碳化硅、六方氮化硼，通过将无纺布浸没于涂层分散液中，再进行晾干后得到本发明的耐磨无纺布，本发明的无纺布耐磨性好，制备工艺简单，涂层和无纺布本体的附着度强。

Description

一种耐磨无纺布及其制备方法
技术领域
本发明涉及一种耐磨无纺布及其制备方法。
背景技术
无纺布是一种非织造布，它是直接利用高聚物切片、短纤维或长丝将纤维通过气流或机械成网，然后经过水刺，针刺，或热轧加固，最后经过后整理形成的无编织的布料。具有柔软、透气和平面结构的新型纤维制品，优点是不产生纤维屑，强韧、耐用、丝般柔软，也是增强材料的一种，而且还有棉质的感觉，和棉织品相比，无纺布的袋子容易成形，而且造价便宜。目前，在一些领域需要无纺布具备高耐磨性能，但是现有技术中的无纺布无法满足该要求，所以需要开发一种耐磨的无纺布。
发明内容
针对上述现有技术的不足之处，本发明解决的问题为：提供一种耐磨的无纺布及其制备方法。
为解决上述问题，本发明采取的技术方案如下：
一种耐磨无纺布，包括一层无纺布和涂附于无纺布两侧面的耐磨涂层；所述的耐磨涂层包括石膏晶须、丙烯酸树脂、高锰合金、碳化硅、六方氮化硼；所述的石膏晶须、丙烯酸树脂、高锰合金、碳化硅、六方氮化硼的重量份分别为：10～20份、100份、10～15份、10～15份、20～40份。
进一步，所述的石膏晶须、丙烯酸树脂、高锰合金、碳化硅、六方氮化硼的重量份分别为：15份、100份、12份、13份、30份。
进一步，所述的石膏晶须和六方氮化硼的重量比为1：2。
进一步，所述的无纺布为涤纶或者丙纶无纺布。
一种耐磨无纺布的制备方法，步骤如下：
a、将丙烯酸树脂溶于热水中进行搅拌，得到丙烯酸树脂分散液；
b、将石膏晶须、高锰合金、碳化硅、六方氮化硼按照比例投入水中进行充分搅拌，得到改性分散液；
c、将改性分散液投入到丙烯酸树脂分散液中，进行充分搅拌，得到涂层分散液，同时对涂层分散液进行加热保温；
d、对无纺布表面进行绒面处理，通过刷子在无纺布的两侧进行挂刷，使得无纺布表面的纹理遭到破坏，形成绒面；
e、将d中经过绒面处理的无纺布直接投入到c中的涂层分散液中浸泡，同时对涂层分散液进行加热；
f、将无纺布从涂层分散液中取出，自然晾干即可。
进一步，所述步骤a中的热水温度为40至50℃，搅拌时间为40至50min。
进一步，所述步骤b中的搅拌时间为20至30min。
进一步，所述步骤c中的搅拌时间为70至80min，涂层分散液的温度控制在50至55℃。
进一步，所述步骤e中无纺布在涂层分散液中浸泡时间为20至30min，控制涂层分散液温度为55至60℃。
进一步，所述步骤f中晾干时间为10至12小时。
本发明的有益效果
本发明在无纺布的两侧面设置涂层，涂层包括石膏晶须、丙烯酸树脂、高锰合金、碳化硅、六方氮化硼，调节各个配比的重量份，达到满足本发明无纺布的耐磨效果；同时在制备过程中，对无纺布表面进行绒面处理以及浸泡的方式进行附着涂层，最后通过晾干的方式达到涂层附着的目的，本发明制备方法涂层附着在无纺布上十分的牢固，提高了无纺布的耐磨性能。
具体实施方式
下面对本发明内容作进一步详细说明。
实施例1
一种耐磨无纺布，包括一层无纺布和涂附于无纺布两侧面的耐磨涂层；所述的耐磨涂层包括石膏晶须、丙烯酸树脂、高锰合金、碳化硅、六方氮化硼；所述的石膏晶须、丙烯酸树脂、高锰合金、碳化硅、六方氮化硼的重量份分别为：10份、100份、10份、10份、20份。所述的无纺布可为涤纶或者丙纶无纺布。
一种耐磨无纺布的制备方法，步骤如下：
a、将丙烯酸树脂溶于热水中进行搅拌，得到丙烯酸树脂分散液；热水温度为40℃，搅拌时间为40 min；
b、将石膏晶须、高锰合金、碳化硅、六方氮化硼按照比例投入水中进行充分搅拌，得到改性分散液；搅拌时间为20 min；
c、将改性分散液投入到丙烯酸树脂分散液中，进行充分搅拌，得到涂层分散液，同时对涂层分散液进行加热保温；搅拌时间为70 min，涂层分散液的温度控制在50℃；
d、对无纺布表面进行绒面处理，通过刷子在无纺布的两侧进行挂刷，使得无纺布表面的纹理遭到破坏，形成绒面；
e、将d中经过绒面处理的无纺布直接投入到c中的涂层分散液中浸泡，同时对涂层分散液进行加热；无纺布在涂层分散液中浸泡时间为20 min，控制涂层分散液温度为55℃；
f、将无纺布从涂层分散液中取出，自然晾干即可；晾干时间为10小时。
实施例2
一种耐磨无纺布，包括一层无纺布和涂附于无纺布两侧面的耐磨涂层；所述的耐磨涂层包括石膏晶须、丙烯酸树脂、高锰合金、碳化硅、六方氮化硼；所述的石膏晶须、丙烯酸树脂、高锰合金、碳化硅、六方氮化硼的重量份分别为：15份、100份、12份、13份、30份。所述的无纺布可为涤纶或者丙纶无纺布。
一种耐磨无纺布的制备方法，步骤如下：
a、将丙烯酸树脂溶于热水中进行搅拌，得到丙烯酸树脂分散液；热水温度为45℃，搅拌时间为45min；
b、将石膏晶须、高锰合金、碳化硅、六方氮化硼按照比例投入水中进行充分搅拌，得到改性分散液；搅拌时间为25min；
c、将改性分散液投入到丙烯酸树脂分散液中，进行充分搅拌，得到涂层分散液，同时对涂层分散液进行加热保温；搅拌时间为75min，涂层分散液的温度控制在52℃；
d、对无纺布表面进行绒面处理，通过刷子在无纺布的两侧进行挂刷，使得无纺布表面的纹理遭到破坏，形成绒面；
e、将d中经过绒面处理的无纺布直接投入到c中的涂层分散液中浸泡，同时对涂层分散液进行加热；无纺布在涂层分散液中浸泡时间为24min，控制涂层分散液温度为56℃；
f、将无纺布从涂层分散液中取出，自然晾干即可；晾干时间为11小时。
实施例3
一种耐磨无纺布，包括一层无纺布和涂附于无纺布两侧面的耐磨涂层；所述的耐磨涂层包括石膏晶须、丙烯酸树脂、高锰合金、碳化硅、六方氮化硼；所述的石膏晶须、丙烯酸树脂、高锰合金、碳化硅、六方氮化硼的重量份分别为： 20份、100份、15份、15份、40份。所述的无纺布可为涤纶或者丙纶无纺布。
一种耐磨无纺布的制备方法，步骤如下：
a、将丙烯酸树脂溶于热水中进行搅拌，得到丙烯酸树脂分散液；热水温度为50℃，搅拌时间为50min；
b、将石膏晶须、高锰合金、碳化硅、六方氮化硼按照比例投入水中进行充分搅拌，得到改性分散液；搅拌时间为30min；
c、将改性分散液投入到丙烯酸树脂分散液中，进行充分搅拌，得到涂层分散液，同时对涂层分散液进行加热保温；搅拌时间为80min，涂层分散液的温度控制在55℃；
d、对无纺布表面进行绒面处理，通过刷子在无纺布的两侧进行挂刷，使得无纺布表面的纹理遭到破坏，形成绒面；
e、将d中经过绒面处理的无纺布直接投入到c中的涂层分散液中浸泡，同时对涂层分散液进行加热；无纺布在涂层分散液中浸泡时间为30min，控制涂层分散液温度为60℃；
f、将无纺布从涂层分散液中取出，自然晾干即可；晾干时间为12小时。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (10)

1.一种耐磨无纺布，其特征在于，包括一层无纺布和涂附于无纺布两侧面的耐磨涂层；所述的耐磨涂层包括石膏晶须、丙烯酸树脂、高锰合金、碳化硅、六方氮化硼；所述的石膏晶须、丙烯酸树脂、高锰合金、碳化硅、六方氮化硼的重量份分别为：10～20份、100份、10～15份、10～15份、20～40份。
2.根据权利要求1所述的耐磨无纺布，其特征在于，所述的石膏晶须、丙烯酸树脂、高锰合金、碳化硅、六方氮化硼的重量份分别为：15份、100份、12份、13份、30份。
3.根据权利要求2所述的耐磨无纺布，其特征在于，所述的石膏晶须和六方氮化硼的重量比为1：2。
4.根据权利要求1所述的耐磨无纺布，其特征在于，所述的无纺布为涤纶或者丙纶无纺布。
5.一种耐磨无纺布的制备方法，其特征在于，步骤如下：
a、将丙烯酸树脂溶于热水中进行搅拌，得到丙烯酸树脂分散液；
b、将石膏晶须、高锰合金、碳化硅、六方氮化硼按照比例投入水中进行充分搅拌，得到改性分散液；
c、将改性分散液投入到丙烯酸树脂分散液中，进行充分搅拌，得到涂层分散液，同时对涂层分散液进行加热保温；
d、对无纺布表面进行绒面处理，通过刷子在无纺布的两侧进行挂刷，使得无纺布表面的纹理遭到破坏，形成绒面；
e、将d中经过绒面处理的无纺布直接投入到c中的涂层分散液中浸泡，同时对涂层分散液进行加热；
f、将无纺布从涂层分散液中取出，自然晾干即可。
6.根据权利要求5所述的耐磨无纺布的制备方法，其特征在于，所述步骤a中的热水温度为40至50℃，搅拌时间为40至50min。
7.根据权利要求5所述的耐磨无纺布的制备方法，其特征在于，所述步骤b中的搅拌时间为20至30min。
8.根据权利要求5所述的耐磨无纺布的制备方法，其特征在于，所述步骤c中的搅拌时间为70至80min，涂层分散液的温度控制在50至55℃。
9.根据权利要求5所述的耐磨无纺布的制备方法，其特征在于，所述步骤e中无纺布在涂层分散液中浸泡时间为20至30min，控制涂层分散液温度为55至60℃。
10.根据权利要求5所述的耐磨无纺布的制备方法，其特征在于，所述步骤f中晾干时间为10至12小时。
CN201710769126.9A 2017-08-31 2017-08-31 一种耐磨无纺布及其制备方法 Active CN107524015B (zh)