CN109880241A - 一种汽车天窗密封发泡胶条及其制备方法 - Google Patents
一种汽车天窗密封发泡胶条及其制备方法 Download PDFInfo
- Publication number
- CN109880241A CN109880241A CN201910170894.1A CN201910170894A CN109880241A CN 109880241 A CN109880241 A CN 109880241A CN 201910170894 A CN201910170894 A CN 201910170894A CN 109880241 A CN109880241 A CN 109880241A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- adhesive tape
- vulcanization
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种汽车天窗密封发泡胶条及其制备方法,其原料包括三元乙丙橡胶5527型、炭黑N550型、石蜡油、碳酸钙、氧化锌、硬脂酸、防老剂MB、促进剂PZ、促进剂M‑75、促进剂CZ、促进剂TMTD、硫化剂DTDM、硫磺粉、发泡剂R‑380。制备方法为配料、密炼、开炼、挤出、硫化、裁截。本发明的配方和生产工艺简单、硫化时间短、密封性能良好,生产效率高、可以长时间的使用且有效的防止漏水现象的发生。
Description
技术领域
本发明涉及橡胶材料密封技术领域,尤其涉及一种汽车天窗密封发泡胶条及其制备方法。
背景技术
现代工业领域中,密封技术起着举足轻重的作用,密封失效不仅会大幅增加后续维修成本,还可能导致致命的灾难。材料性能是密封制品性能好坏的决定性因素。在汽车领域,汽车密封胶条是汽车的重要零部件之一,广泛用于车门、车窗、车身、座椅、天窗、发动机箱和后备箱等部位,具有防水、密封、隔音、防尘、防冻、减震、保暖及节能的重要作用。
近年来,随着汽车工业的快速发展以及人们需求的多元化、环保化、高性能化和美观化等要求,汽车门窗密封条的研究和开发日益受到人们的关注,尤其是其密封性、耐高温和低温性能、耐腐蚀性以及环保性能等研究具有重要的意义。
目前,汽车门窗密封条所用材料多数都以橡胶为主,如三元乙丙橡胶、丁腈橡胶、氯丁橡胶、天然橡胶等。其中,三元乙丙橡胶的应用日趋广泛。三元乙丙橡胶的主链是不含双键的完全饱和的直链型结构,其侧链上有二烯泾,密度较低,可大量充油和加入填充剂,因而可降低橡胶制品的成本。三元乙丙橡胶具有优良的耐老化性,耐臭氧性,耐候性,耐热性(可在120℃环境中长期使用),耐化学性(如醇,酸,强碱,氧化剂),但不耐脂肪族和芳香族类溶剂侵蚀。此外,三元乙丙橡胶有突出的耐蒸汽性能。三元乙丙橡胶已广泛用于洗衣机,电视机中的配件和门窗密封制品,或多种复合体剖面的胶条生产中。
现在,市场上的天窗密封仍然存在着许多问题,如天窗的密封条耐老化性不强,时间长了容易老化漏水。
发明内容
本发明的目的是提供一种汽车天窗密封发泡胶条及其制备方法,解决密封、原料复杂、老化漏水的问题。
为了解决上述问题,本发明采用如下技术方案:
一种汽车天窗密封发泡胶条包括以下重量份的原料,三元乙丙橡胶5527型50~150份,炭黑N550型50~150份,石蜡油20~90份,碳酸钙1~30份,氧化锌0.1~15份,硬脂酸0.1~1.5份,防老剂MB:0.5~3份,促进剂PZ:0.1~2.0份,促进剂M-75:0.1~2.0份,促进剂CZ:0.5~1.5份,促进剂TMTD:0.1~1.5份,硫化剂DTDM:0.1~0.8份,硫磺粉0.1~2.0份、发泡剂R-380:1~5份。
优选的,包括以下重量份的原料,三元乙丙橡胶5527型100份,炭黑N550型90~110份,石蜡油50~60份,碳酸钙10~20份,氧化锌5~8份,硬脂酸0.5~1.3份,防老剂MB:1.5~2.0份,促进剂PZ:1.0~1.5份,促进剂M-75:1.0~1.5份,促进剂CZ:0.8~1.2份,促进剂TMTD0:.5~0.8份,硫化剂DTDM:0.4~0.6份,硫磺粉1.0~1.5份,发泡R-380:3~4份。
一种汽车天窗密封发泡胶条的制备方法:(1)称取相应重量份的原料;(2)密炼;(3)开炼;(4)挤出;(5)硫化;(6)裁剪。
优选的,所述密炼设置条件为:温度140~145℃;时间13~19分钟。
优选的,所述开炼设置条件为:温度70~90℃;薄通2~4次。
优选的,所述挤出设置条件为:温度50~60℃;转速为10~18转/分钟。
优选的,所述硫化设置条件为:温度175~185℃;时间12~18分钟
与现有技术相比,本发明的有益技术效果:本发明采用三元乙丙橡胶5527型与为主,加入炭黑N550型,炭黑是补强填充体系中重要的补强填充剂,对橡胶材料的物理机械性能和加工工艺都有重要的作用。在本申请中还加入四种促进剂PZ、M-75、CZ和TMTD,四种促进剂协同作用可将硫化时间缩短,进而极大地提高了生产效率,氧化锌和硬脂酸作为硫化活性剂,能够充分提高复合促进剂的活性,进而加速硫化反应进行并缩短硫化时间,同时提高三元乙丙橡胶的热稳定性,提高交联密度。本发明中除了硫化剂DTDM外,还加入了硫磺,硫磺搭配硫化剂的使用可以在硫化过程中形成单、双硫键,赋予橡胶优良的耐热老化性能;碳酸钙的存在则可降低生产成本;防老剂的加入可以使胶条使用时间更长。本申请的配方和生产工艺简单,生产效率高,硫化时间短,密封性能良好,同时可以长时间的使用且有效的防止漏水现象的发生。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更容易被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界点。
实施例1
称取三元乙丙橡胶5527型50份,炭黑N550型50份,石蜡油20份,碳酸钙1份,氧化锌0.1份,硬脂酸0.1份,防老剂MB:0.5份,促进剂PZ:0.1份,促进剂M-75:0.1份,促进剂CZ:0.5份,促进剂TMTD:0.1份,硫化剂DTDM:0.1份,硫磺粉0.1份,发泡剂R-380:1份;进行密炼,密炼温度为140℃,时间为13分钟;之后进行开炼,开炼温度为70℃,薄通2次;开炼结束后将产品放入挤出机中挤出,温度设置为50℃,转速设置为12转/分钟;然后放入硫化箱中硫化,设置温度为175℃,硫化时间为12分钟;硫化结束后取出样品,按照客户要求裁剪即可。
实施例2
三元乙丙橡胶5527型100份,炭黑N550型100份,石蜡油50份,碳酸钙15份,氧化锌7份,硬脂酸1.0份,防老剂MB:2份,促进剂PZ:1.2份,促进剂M-75:1.2份,促进剂CZ:1.0份,促进剂TMTD:1.0份,硫化剂DTDM:0.5份,硫磺粉1.0份、发泡剂R-380:3份;进行密炼,密炼温度为142℃,时间为16分钟;之后进行开炼,开炼温度为80℃,薄通3次;开炼结束后将产品放入挤出机中挤出,温度设置为55℃,转速设置为14转/分钟;然后放入硫化箱中硫化,设置温度为180℃,硫化时间为15分钟;硫化结束后取出样品,按照客户要求裁剪即可。
实施例3
三元乙丙橡胶5527型150份,炭黑N550型150份,石蜡油90份,碳酸钙30份,氧化锌15份,硬脂酸1.5份,防老剂MB:3份,促进剂PZ:2.0份,促进剂M-75:2.0份,促进剂CZ:1.5份,促进剂TMTD:1.5份,硫化剂DTDM:0.8份,硫磺粉2.0份、发泡剂R-380:5份;进行密炼,密炼温度为145℃,时间为19分钟;之后进行开炼,开炼温度为90℃,薄通4次;开炼结束后将产品放入挤出机中挤出,温度设置为60℃,转速设置为18转/分钟;然后放入硫化箱中硫化,设置温度为185℃,硫化时间为18分钟;硫化结束后取出样品,按照客户要求裁剪即可。
实施例4
准备两条拉伸强度相同的胶条,一条为实施例3中所得到的汽车天窗密封发泡胶条作为实验组,一条为普通的汽车天窗密封胶条作为对照组,其他条件相同,两条胶条经过一段时间使用后对其拉伸强度进行测试。实验结果为:实验组的拉伸强度为之前的85%,而对照组的拉伸强度为之前的60%,说明本申请的胶条防老化效果更好。
实施例5
将实施例2原料中的四种促进剂PZ、M-75、CZ和TMTD改为使用三种促进剂PZ、CZ和TMTD,其他原料相同作为对照组,实施例2作为实验组对二者的硫化时间进行测试。实验结果表明,对照组所用硫化时间为22min,实验组的硫化时间为15min,说明四种促进剂的联合使用会减少硫化时间。
以上所述的实施例仅是对本发明的优选方式进行描述,并非对本发明的范围进行限定,在不脱离本发明设计精神的前提下,本领域普通技术人员对本发明的技术方案做出的各种变形和改进,均应落入本发明权利要求书确定的保护范围内。
Claims (7)
1.一种汽车天窗密封发泡胶条,其特征在于,包括以下重量份的原料:三元乙丙橡胶5527型50~150份,炭黑N550型50~150份,石蜡油20~90份,碳酸钙1~30份,氧化锌0.1~15份,硬脂酸0.1~1.5份,防老剂MB:0.5~3份,促进剂PZ:0.1~2.0份,促进剂M-75:0.1~2.0份,促进剂CZ:0.5~1.5份,促进剂TMTD:0.1~1.5份,硫化剂DTDM:0.1~0.8份,硫磺粉0.1~2.0份,发泡剂R-380:1~5份。
2.根据权利要求1所述的发泡胶条,其特征在于,包扩以下重量份的原料:三元乙丙橡胶5527型100份,炭黑N550型90~110份,石蜡油50~60份,碳酸钙10~20份,氧化锌5~8份,硬脂酸0.5~1.3份,防老剂MB:1.5~2.0份,促进剂PZ:1.0~1.5份,促进剂M-75:1.0~1.5份,促进剂CZ:0.8~1.2份,促进剂TMTD:0.5~0.8份,硫化剂DTDM0:.4~0.6份,硫磺粉1.0~1.5份,发泡R-380:3~4份。
3.一种汽车天窗密封发泡胶条的制备方法,其特征在于,包括以下步骤:(1)称取相应重量份的原料;(2)密炼;(3)开炼;(4)挤出;(5)硫化;(6)裁剪。
4.根据权利要求3所述的制备方法,其特征在于,所述密炼设置条件为:温度140~145℃;时间13~19分钟。
5.根据权利要求3所述的制备方法,其特征在于,所述开炼设置条件为:温度70~90℃;薄通2~4次。
6.根据权利要求3所述的制备方法,其特征在于,所述挤出设置条件为:温度50~60℃;转速为10~18转/分钟。
7.根据权利要求3所述的制备方法,其特征在于,所述硫化设置条件为:温度175~185℃;时间12~18分钟。