CN109851934A - 一种可反复塑性的口腔印模托盘及其制造、使用方法 - Google Patents
一种可反复塑性的口腔印模托盘及其制造、使用方法 Download PDFInfo
- Publication number
- CN109851934A CN109851934A CN201811565841.1A CN201811565841A CN109851934A CN 109851934 A CN109851934 A CN 109851934A CN 201811565841 A CN201811565841 A CN 201811565841A CN 109851934 A CN109851934 A CN 109851934A
- Authority
- CN
- China
- Prior art keywords
- tray
- parts
- buccal impression
- weight
- plasticity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了可反复塑性的口腔印模托盘及其制造、使用方法,该口腔印模托盘由85‑99重量份记忆高分子材料、0.05‑1重量份抗菌剂、0.05‑1重量份色素组成。其采用记忆高分子材料通过注塑而成,印模托盘可以根据患者口腔组织大小而调整大小,提高了患者印模过程的舒适度;托盘形变量大、记忆效应显著、感应温度低,适合反复使用;其内掺杂抗菌剂,可自行消毒,省去了消毒过程,为医院节约了资源。
Description
技术领域
本发明口腔印模托盘领域,具体涉及一种可反复塑性的口腔印模托盘及其制造、使用方法。
背景技术
口腔印模托盘主要用于放置印模材料,是制取口腔内组织形态模型的重要工具。市场上现有的印模托盘主要有不锈钢托盘和塑料托盘。这两种托盘都是不可塑形,针对口腔内组织大小不同的患者不能做到精确适应口腔。同时,由于托盘不是一次性耗材,需在不同的患者口腔中使用,为避免交叉感染,每次使用之前都需要毒。
发明内容
本发明为了解决上述技术问题提供一种可反复塑性的口腔印模托盘及其制造、使用方法。
本发明通过下述技术方案实现:
一种可反复塑性的口腔印模托盘,该托盘由85-99重量份记忆高分子材料、0.05-1重量份抗菌剂、0.05-1重量份色素组成。
作为优选,所述记忆高分子材料包括聚苯乙烯-丁二烯、聚苯乙烯-乙烯-丁烯、交联聚乙烯、聚乙烯-醋酸乙烯、聚丙烯酸十八酯-丙烯酸、聚己内酯、聚己内酯二醇、聚羟基丁酸酯、羟基丁酸已酸共聚酯中的一种或多种组合物。
作为优选,所述抗菌剂包括载银磷酸锆、载银沸石中的一种或两种组合物。
作为优选,所述色素包括为钛黄、氧化铁黄、钴蓝、铁红中的一种或多种组合物。
一种口腔印模托盘的制造方法,包括以下步骤:
A1、在20℃至30℃温度下真空干燥记忆高分子材料8小时至12小时;
B1、获取并混合口腔印模托盘的材料,该材料由85-99重量份记忆高分子材料、0.05-1重量份抗菌剂、0.05-1重量份色素组成;
C1、将材料放入注塑机内注塑,注塑温度为160℃-220℃;
D1、注塑保压冷却10分钟至20分钟后脱模。
一种口腔印模托盘的使用方法,包括以下步骤:
A2、根据患者口腔组织形态的大小,将采用上述方法制得的口腔印模托盘在50℃至70℃水浴中塑性;
B2、将塑性后的口腔印模托盘取出并冷却至常温后填入印模材料中取模;
C2、使用后进行清洗,放置于50℃至70℃水浴中恢复形状。
本发明与现有技术相比,具有如下的优点和有益效果:
1、本发明的口腔印模托盘采用记忆高分子材料通过注塑而成,印模托盘可以根据患者口腔组织大小而调整大小,提高了患者印模过程的舒适度;托盘形变量大、记忆效应显著、感应温度低,适合反复使用。
2、本方案的口腔印模托盘内掺杂抗菌剂,可自行消毒,省去了消毒过程,为医院节约了资源。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚明白,下面结合实施例,对本发明作进一步的详细说明,本发明的示意性实施方式及其说明仅用于解释本发明,并不作为对本发明的限定。
实施例1
一种可反复塑性的口腔印模托盘,该托盘由85-99重量份记忆高分子材料、0.05-1重量份抗菌剂、0.05-1重量份色素组成。
其中,记忆高分子材料包括聚苯乙烯-丁二烯、聚苯乙烯-乙烯-丁烯、交联聚乙烯、聚乙烯-醋酸乙烯、聚丙烯酸十八酯-丙烯酸、聚己内酯、聚己内酯二醇、聚羟基丁酸酯、羟基丁酸已酸共聚酯中的一种或多种组合物。
抗菌剂包括载银磷酸锆、载银沸石中的一种或两种组合物。
色素包括为钛黄、氧化铁黄、钴蓝、铁红中的一种或多种组合物。
实施例2
基于上述实施例,本实施例公开一具体试试方式。
口腔印模托盘,由99重量份聚苯乙烯-丁二烯、0.05重量份载银磷酸锆、0.05重量份钛黄组成。
实施例3
基于上述实施例,本实施例公开一具体试试方式。
口腔印模托盘,由99重量份聚己内酯二醇、0. 5重量份载银磷酸锆、1重量份钛黄组成。
实施例4
一种口腔印模托盘的制造方法,包括以下步骤:
A1、在20℃至30℃温度下真空干燥记忆高分子材料8小时至12小时;
B1、获取并混合口腔印模托盘的材料,该材料由85-99重量份记忆高分子材料、0.05-1重量份抗菌剂、0.05-1重量份色素组成;
C1、将材料放入注塑机内注塑,注塑温度为160℃-220℃;
D1、注塑保压冷却10分钟至20分钟后脱模。
发明使用的原料易得、生产工艺简单,因此同现有产品相比,降低了生产成本。本发明无大型的设备或昂贵的设备费用,制作简单生产方便,因此可适用于大规模生产。
实施例5
一种口腔印模托盘的使用方法,包括以下步骤:
A2、根据患者口腔组织形态的大小,将实施例4的方法制得的口腔印模托盘在50℃至70℃水浴中塑性;
B2、将塑性后的口腔印模托盘取出并冷却至常温后填入印模材料中取模;
C2、使用后进行清洗,放置于50℃至70℃水浴中恢复形状。
以上所述的具体实施方式,对本发明的目的、技术方案和有益效果进行了进一步详细说明,所应理解的是,以上所述仅为本发明的具体实施方式而已,并不用于限定本发明的保护范围,凡在本发明的精神和原则之内,所做的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (6)
1.一种可反复塑性的口腔印模托盘,其特征在于,该托盘由85-99重量份记忆高分子材料、0.05-1重量份抗菌剂、0.05-1重量份色素组成。
2.根据权利要求1所述的一种可反复塑性的口腔印模托盘,其特征在于,所述记忆高分子材料包括聚苯乙烯-丁二烯、聚苯乙烯-乙烯-丁烯、交联聚乙烯、聚乙烯-醋酸乙烯、聚丙烯酸十八酯-丙烯酸、聚己内酯、聚己内酯二醇、聚羟基丁酸酯、羟基丁酸已酸共聚酯中的一种或多种组合物。
3.根据权利要求1所述的一种可反复塑性的口腔印模托盘,其特征在于,所述抗菌剂包括载银磷酸锆、载银沸石中的一种或两种组合物。
4.根据权利要求1所述的一种可反复塑性的口腔印模托盘,其特征在于,所述色素包括为钛黄、氧化铁黄、钴蓝、铁红中的一种或多种组合物。
5.一种口腔印模托盘的制造方法,其特征在于,包括以下步骤:
A1、在20℃至30℃温度下真空干燥记忆高分子材料8小时至12小时;
B1、获取并混合口腔印模托盘的材料,该材料由85-99重量份记忆高分子材料、0.05-1重量份抗菌剂、0.05-1重量份色素组成;
C1、将材料放入注塑机内注塑,注塑温度为160℃-220℃;
D1、注塑保压冷却10分钟至20分钟后脱模。
6.一种口腔印模托盘的使用方法,其特征在于,包括以下步骤:
A2、根据患者口腔组织形态的大小,将根据权利要求5的方法制得的口腔印模托盘在50℃至70℃水浴中塑性;
B2、将塑性后的口腔印模托盘取出并冷却至常温后填入印模材料中取模;
C2、使用后进行清洗,放置于50℃至70℃水浴中恢复形状。