CN1098229C

CN1098229C - Process for preparing crystal-like relief brick

Info

Publication number: CN1098229C
Application number: CN00109796A
Authority: CN
Inventors: 吴锦强
Original assignee: Individual
Current assignee: Individual
Priority date: 2000-07-10
Filing date: 2000-07-10
Publication date: 2003-01-08
Anticipated expiration: 2020-07-10
Also published as: CN1276357A

Abstract

The present invention relates to a production technique of a relief crystal brick. The relief crystal brick is directly stacked on a wall and floor tile semifinished product adobe printed with different patterns and flower colours with the conventional production method of a wall and floor tile through the cooperation of a conventional dry glazing technology and a colourless transparent fusion cake or a coloured transparent fusion cake or an opaque fusion cake and granules thereof mutually combined, enters a kiln and is burnt once, so a sparkling bright beautiful unique artistic effect with strong stereo perception is formed. The method has the advantages of simple manufacture technique, practicality, continuous mechanized production, high production efficiency, etc.

Description

A kind of production technique of crystal-like relief brick

The present invention relates to ceramic wall and floor bricks decoration technology technical field, particularly the production technique of once-firing crystal-like relief brick after heap on the wall floor tile is filled out the frit particle.

Existing crystal-like relief brick production method, be with clear frit particle or milkiness frit particle or milkiness fancy glaze on wall floor tile work in-process, adopt manual heap to fill out solid pattern, and under 800～1100 ℃ of temperature secondary or repeatedly heavily burn, form floating brilliant pattern.Therefore this method can not give birth to mechanize continuous production on the tight line owing to be that manual heap is filled out, and makes that production technique becomes complicated, labour intensity is big, and productivity is low, cost is high, and can not once-firing.

The object of the present invention is to provide the mechanize of a kind of energy continous way to produce the production technique of crystal-like relief brick, and can go into the kiln once-firing.

The object of the present invention is achieved like this: a kind of production technique of crystal-like relief brick, adopt conventional wall floor tile production method, cooperate conventional dry glazing technology, the direct heap of particle with water white transparency frit or colored transparent frit or milkiness frit and combination mutually thereof fills in the wall floor tile work in-process adobe that is printed on different pattern, pattern, go into the kiln once-firing, its method steps is: (1) carries out granulation respectively with water white transparency frit, colored transparent frit, milkiness frit, its macrobead scope is 20～60 orders, and the small-particle scope is 50～80 orders; (2), be that 20～60 purpose water white transparency frit grains or colored transparent frit grain or milkiness frit grain directly use separately with the granularity of 100% (weight percent) according to the design effect requirements; Or above-mentioned three kinds of frit grains are used in combination, its macrobead amount ranges is respectively 95～100% (weight percents), and the small-particle amount ranges is respectively 0～5% (weight percent), by the design effect requirement, choose suitable cooperation ratio, form frit grain group and use; (3) with water white transparency frit, colored transparent frit and milkiness frit respectively fine powder be broken to by 110 mesh sieves, and with above-mentioned three kinds of frit powders and organic binder bond be 100: 50～70 proportioning mixing in proportion respectively, make the frit printing glaze respectively; (4) according to the layout requirement of wall floor tile, on the brilliant adobe position of decorating of needs heap with the colored net of 20～40 orders frit printing glaze of biting; (5) utilize conventional dry glazing technology, above-mentioned single frit grain or the frit grain group of working good heap are filled out on the frit printing glaze; (6) the roller kiln once-firing is sent in the adobe of wall floor tile work in-process, firing range is 1050～1200 ℃, and the firing time cycle is 20～60 minutes.Behind the finished product, can produce sparkling and crystal-clear, beautiful, rich color, color and luster is soft, stereoscopic sensation is strong artistic effect at the brilliant position of heap.When filling out, obtain the floating brilliant pattern of pure transparent vitreous body with water white transparency frit grain heap; When the large and small particle of water white transparency frit and colored transparent frit is used in combination, can obtain the floating brilliant pattern glittering and translucent, that rich color is natural; Use milkiness frit particle directly to pile when filling out, can obtain the floating brilliant pattern of spotless white solid.

Compare with existing crystal-like relief brick production technology, the present invention has the following advantages:

(1) adopt conventional wall floor tile production method, cooperate conventional dry glazing technology, that the product color of producing enriches is changeable, color and luster is soft, floating brilliant stereoeffect is good;

(2) product once-firing;

(3) can continous way mechanize produce on production line, equipment is simple, and technology is simple and easy, and labour intensity is low, the productivity height.

In sum as seen, compare with existing crystal-like relief brick production method, outstanding technical characterstic and obvious effects that the present invention had are conspicuous.

By following embodiment the present invention is further elaborated.

Embodiment 1:

Water white transparency frit powder that will be by 110 mesh sieves and organic binder bond are mixed into the frit printing glaze in 100: 60 ratio, and need pile on the brilliant position with the 20 orders flowers net wall brick and ground brick body of biting, with conventional dry glazing technology 20～50 order water white transparency frit grains heap is filled out on the frit printing glaze, go into the kiln once-firing, firing temperature is 1200 ℃, firing period 20 minutes, floating brilliant pattern glittering and translucent, that color and luster is soft, anaglyph is outstanding appears in the brilliant position of visible heap behind the finished product.

Embodiment 2:

With 67% (weight percent) granularity is warm frit in 20～60 purpose water white transparencies, 30% (weight percent) granularity is a warm frit in 20～40 the green transparent, 3% (weight percent) granularity is a warm frit in 60～80 purposes white milkiness, mixing; To make the frit printing glaze in 100: 70 ratio mixing by the water white transparency frit powder and the organic binder bond of 110 mesh sieves, and spend net to bite with 40 orders and need pile on the brilliant position in adobe, heap is filled out the frit group grain of getting ready, goes into the kiln once-firing.Firing temperature is 1130 ℃, firing period 33 minutes.As seen heap brilliant position color fusion is natural, soft behind the finished product, and the white small-particle that floating intracrystalline is suspending is given the pleasing sense of people like waving up and down.

Embodiment 3:

With the granularity of 100% (weight percent) is that the yellow low-temperature transparent frit of 20～60 purposes is standby; To be to make the frit printing glaze with organic binder bond in 100: 50 ratio mixings after yellow low-temperature transparent frit was pulverized 110 mesh sieves more equally.Utilize 30 orders flower net that above-mentioned frit printing glaze is bitten and to pile on the brilliant position, standby frit grain heap is filled out on the frit printing glaze, go into the kiln once-firing with conventional dry glazing technology in the work in-process adobe.Firing temperature is 1050 ℃, firing period 60 minutes.The brilliant position of visible heap yellow is soft, clear behind the finished product, pattern stereoscopic impression is good.

Embodiment 4:

Middle temperature milkiness frit with 100% (weight percent) is a granulated into 20～50 orders, and the middle temperature milkiness frit that again other is equipped with is in small, broken bits makes the frit printing glaze after sieving by 110.Utilize 20 orders flowers net that the frit printing glaze is bitten in the work in-process adobe, with the dry glazing technology frit grain is piled and filled out on the frit printing glaze, go into the kiln once-firing.1130 ℃ of firing temperatures, firing period 48 minutes.Visible floating brilliant pattern is sparkling and crystal-clear, pure white behind the finished product, stereoscopic sensation is good.

Embodiment 5:

With 20～50 order water white transparency frit grains, 95% (weight percent), other gets 50～80 order milkiness frit grains of 5% (weight percent), and both mixings are standby; To make the frit printing glaze by 110 purpose water white transparency frit powders.Other technology is with embodiment 1.Visible embossment position is sparkling and crystal-clear bright, full of moving sense behind the finished product.

Embodiment 6:

With 20～50 order water white transparency frits 55% (weight percent), the blue clear frit 30% (weight percent) of 20～50 orders, 20～50 order milkiness frit grains, 15% (weight percent); To make the frit printing glaze by the water white transparency frit powder of 110 mesh sieves.Other technology is with embodiment 2.The beautiful brilliant flower of blue and white appears in visible floating brilliant position behind the finished product.

Embodiment 7:

With 20～50 order water white transparency frit grains, 70% (weight percent), 20～50 order milkiness frit grains, 30% (weight percent) is with both mixings; The water white transparency frit powder that other is equipped with is by 110 mesh sieves and make the frit printing glaze.Other technology is with embodiment 2.The brilliant flower of visible beautiful white flies on the floating crystalline substance behind the finished product.

Claims

1, a kind of production technique of crystal-like relief brick, it is characterized in that: adopt conventional wall floor tile production method to cooperate the dry glazing technology, the direct heap of particle with water white transparency frit or colored transparent frit or milkiness frit and combination mutually thereof fills in the wall floor tile work in-process adobe that is printed on different pattern, pattern, go into the kiln once-firing, its method steps is:

(1) water white transparency frit, colored transparent clinker and milkiness frit are carried out granulation respectively, its macrobead scope is 20～60 orders, and the small-particle scope is 50～80 orders;

(2), be that 20～60 purpose water white transparency clinker grains or colored transparent frit grain or milkiness frit grain directly use separately with the granularity of 100% (weight percent) according to the design effect requirement; Or above-mentioned three kinds of frit grains are used in combination, its macrobead amount ranges is respectively 95～100% (weight percents), the small-particle amount ranges is 0～5% (weight percent), three kinds of frit grains in above-mentioned amount ranges, by the design effect requirement, choose suitable cooperation ratio, form frit grain group and use;

(3) with water white transparency frit, colored transparent frit and milkiness frit respectively fine powder be broken to by 110 mesh sieves, and will to state three kinds of frit powders and organic binder bond respectively be 100: 50～70 proportioning mixing in proportion, makes the frit printing glaze respectively;

(4) according to the layout requirement of wall floor tile, pile the frit printing glaze of biting required with 20-40 order flower net on the brilliant adobe position of decorating at needs;

(5) utilize conventional dry glazing technology, above-mentioned single frit grain or the frit grain group of working good heap are filled out on the frit printing glaze;

(6) the roller kiln once-firing is sent in the adobe of wall floor tile work in-process, firing range is 1050～1200 ℃, and the firing time cycle is 20～60 minutes.