CN109748593A - A kind of silica refractory - Google Patents
A kind of silica refractory Download PDFInfo
- Publication number
- CN109748593A CN109748593A CN201711055419.7A CN201711055419A CN109748593A CN 109748593 A CN109748593 A CN 109748593A CN 201711055419 A CN201711055419 A CN 201711055419A CN 109748593 A CN109748593 A CN 109748593A
- Authority
- CN
- China
- Prior art keywords
- parts
- quartz sand
- silica refractory
- refractory
- magnesia
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to pipeline high temperature resistant technical fields, it is related to the manufacture of silica refractory, more particularly to a kind of silica refractory, feature include: that silica refractory includes following components: quartz sand, boric acid, phenolic resin, zirconium oxide, magnesium silicate, sodium metasilicate, magnesia and calcium oxide.
Description
Technical field
The invention belongs to pipeline high temperature resistant technical fields, are related to a kind of manufacture of silica refractory, more particularly to quartz
Refractory material.
Background technique
Refractoriness is not less than 1599 DEG C of a kind of inorganic non-metallic material.Refractoriness refers to that refractory material bullet sample exists
In the case of not having loading, high temperature action is resisted without softening molten Celsius temperature.But it only cannot be complete to define with refractoriness
Face describes refractory material, and 1599 DEG C are not absolute.Now being defined as all physicochemical properties allows it under high temperature environment
The material used is known as refractory material.Refractory material is widely used in metallurgy, chemical industry, petroleum, machine-building, silicate, power etc.
Industrial circle, dosage is maximum in metallurgical industry, accounts for the 69%~60% of total output.
Application to refractory in steel, non-ferrous metal, glass, cement, ceramics, petrochemical industry, machinery, boiler, light industry, electric power,
The every field of the national economy such as military project is to guarantee that above-mentioned industry production run and technology develop essential basic material,
Irreplaceable important function is played in hot industry production development.
In the art, also seldom for the refractory material under alkaline border, the refractory material under existing alkalinity is basic
Upper service life is not grown.
Summary of the invention
In order to solve the problems in the prior art, the present invention provides silica refractories.
Silica refractory, feature include: that silica refractory includes following components: quartz sand, boric acid, phenolic aldehyde tree
Rouge, zirconium oxide, magnesium silicate, sodium metasilicate, magnesia and calcium oxide.
The silica refractory, its main feature is that: quartz sand refractory material contains following components, the parts by weight of each component
Are as follows:
125-159 parts of quartz sand
15-25 parts of boric acid
20-35 parts of phenolic resin
50-75 parts of zirconium oxide
15-29 parts of magnesium silicate
25-35 parts of sodium metasilicate
55-110 parts of magnesia
55-110 parts of calcium oxide.
The silica refractory, its main feature is that: quartz sand refractory material contains following components, the parts by weight of each component
Are as follows:
159 parts of quartz sand
25 parts of boric acid
35 parts of phenolic resin
75 parts of zirconium oxide
29 parts of magnesium silicate
35 parts of sodium metasilicate
110 parts of magnesia
110 parts of calcium oxide.
The silica refractory, its main feature is that: quartz sand refractory material contains following components, the parts by weight of each component
Are as follows:
125 parts of quartz sand
15 parts of boric acid
20 parts of phenolic resin
50 parts of zirconium oxide
15 parts of magnesium silicate
25 parts of sodium metasilicate
55 parts of magnesia
55 parts of calcium oxide.
Specific embodiment
Embodiment 1
Silica refractory, feature include: that silica refractory includes following components: quartz sand, boric acid, phenolic resin, oxygen
Change zirconium, magnesium silicate, sodium metasilicate, magnesia and calcium oxide.
The silica refractory, its main feature is that: quartz sand refractory material contains following components, the parts by weight of each component
Are as follows:
125-159 parts of quartz sand
15-25 parts of boric acid
20-35 parts of phenolic resin
50-75 parts of zirconium oxide
15-29 parts of magnesium silicate
25-35 parts of sodium metasilicate
55-110 parts of magnesia
Embodiment 2
The silica refractory, its main feature is that: quartz sand refractory material contains following components, the parts by weight of each component are as follows:
159 parts of quartz sand
25 parts of boric acid
35 parts of phenolic resin
75 parts of zirconium oxide
29 parts of magnesium silicate
35 parts of sodium metasilicate
110 parts of magnesia
110 parts of calcium oxide.
Embodiment 3
The silica refractory, its main feature is that: quartz sand refractory material contains following components, the parts by weight of each component are as follows:
125 parts of quartz sand
15 parts of boric acid
20 parts of phenolic resin
50 parts of zirconium oxide
15 parts of magnesium silicate
25 parts of sodium metasilicate
55 parts of magnesia
55 parts of calcium oxide.
Claims (4)
1. silica refractory, feature includes: that silica refractory includes following components: quartz sand, boric acid, phenolic resin,
Zirconium oxide, magnesium silicate, sodium metasilicate, magnesia and calcium oxide.
2. silica refractory according to claim 1, its main feature is that: quartz sand refractory material contains following components, respectively
The parts by weight of component are as follows:
125-159 parts of quartz sand
15-25 parts of boric acid
20-35 parts of phenolic resin
50-75 parts of zirconium oxide
15-29 parts of magnesium silicate
25-35 parts of sodium metasilicate
55-110 parts of magnesia
55-110 parts of calcium oxide.
3. silica refractory according to claim 1, its main feature is that: quartz sand refractory material contains following components, respectively
The parts by weight of component are as follows:
159 parts of quartz sand
25 parts of boric acid
35 parts of phenolic resin
75 parts of zirconium oxide
29 parts of magnesium silicate
35 parts of sodium metasilicate
110 parts of magnesia
110 parts of calcium oxide.
4. silica refractory according to claim 1, its main feature is that: quartz sand refractory material contains following components, respectively
The parts by weight of component are as follows:
125 parts of quartz sand
15 parts of boric acid
20 parts of phenolic resin
50 parts of zirconium oxide
15 parts of magnesium silicate
25 parts of sodium metasilicate
55 parts of magnesia
55 parts of calcium oxide.