CN104926337A - Fireproofing material - Google Patents
Fireproofing material Download PDFInfo
- Publication number
- CN104926337A CN104926337A CN201510392922.6A CN201510392922A CN104926337A CN 104926337 A CN104926337 A CN 104926337A CN 201510392922 A CN201510392922 A CN 201510392922A CN 104926337 A CN104926337 A CN 104926337A
- Authority
- CN
- China
- Prior art keywords
- parts
- refractory materials
- quartz sand
- silicon carbide
- boric acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of pipeline high temperature resistance, and relates to manufacturing of a fireproofing material, in particular to the fireproofing material. The fireproofing material is characterized in that the quartz fireproofing material comprises quartz sand, boric acid, phenolic resin, zirconia, magnesium silicate, sodium silicate, silicon carbide, magnesium oxide and calcium oxide.
Description
Technical field
The invention belongs to the high temperature resistant technical field of pipeline, relate to a kind of manufacture of refractory materials, particularly relate to a kind of refractory materials.
Background technology
Refractoriness is not less than a class ceramic of 1599 DEG C.Refractoriness refers to that refractory materials cone-shaped body sample is not having in loading situation, resists high temperature action and does not soften molten centigradetemperature.But only define with refractoriness and can not describe refractory materials, 1599 DEG C is not absolute comprehensively.Now be defined as the material that all physicochemical property allow it to use in high temperature environments and be called refractory materials.Refractory materials is widely used in the industrial circles such as metallurgy, chemical industry, oil, machinofacture, silicate, power, and in metallurgical industry, consumption is maximum, accounts for 69% ~ 60% of ultimate production.
Application to refractory is in the every field of the national economy such as iron and steel, non-ferrous metal, glass, cement, pottery, petrochemical industry, machinery, boiler, light industry, electric power, military project, be ensure above-mentioned industry production run and the requisite basic material of technical development, in hot industry production development, play irreplaceable vital role.
In the art, also little for the refractory materials under alkaline border, the refractory materials under existing alkalescence substantially work-ing life not long.
Summary of the invention
In order to solve the problems of the prior art, the invention provides a kind of refractory materials.
A kind of refractory materials, its feature comprises: silica refractory comprises following component: quartz sand, boric acid, resol, zirconium white, Magnesium Silicate q-agent, water glass, silicon carbide, magnesium oxide and calcium oxide.
Described a kind of refractory materials, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 125-159 part
Boric acid 5-10 part
Resol 20-35 part
Zirconium white 5-10 part
Magnesium Silicate q-agent 15-29 part
Water glass 25-35 part
Silicon carbide 5-10 part
Magnesium oxide 55-110 part
Calcium oxide 55-110 part.
Described a kind of refractory materials, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 159 parts
Boric acid 10 parts
35 parts, resol
Zirconium white 10 parts
Magnesium Silicate q-agent 29 parts
Water glass 35 parts
10 parts, silicon carbide
110 parts, magnesium oxide
110 parts, calcium oxide.
Described a kind of refractory materials, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 125 parts
Boric acid 5 parts
20 parts, resol
Zirconium white 5 parts
Magnesium Silicate q-agent 15 parts
Water glass 25 parts
5 parts, silicon carbide
55 parts, magnesium oxide
55 parts, calcium oxide.
Embodiment
embodiment 1
A kind of refractory materials, its feature comprises: silica refractory comprises following component: quartz sand, boric acid, resol, zirconium white, Magnesium Silicate q-agent, water glass, silicon carbide, magnesium oxide and calcium oxide.
Described a kind of refractory materials, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 125-159 part
Boric acid 5-10 part
Resol 20-35 part
Zirconium white 5-10 part
Magnesium Silicate q-agent 15-29 part
Water glass 25-35 part
Silicon carbide 5-10 part
Magnesium oxide 55-110 part
Calcium oxide 55-110 part.
embodiment 2
Described a kind of refractory materials, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 159 parts
Boric acid 10 parts
35 parts, resol
Zirconium white 10 parts
Magnesium Silicate q-agent 29 parts
Water glass 35 parts
10 parts, silicon carbide
110 parts, magnesium oxide
110 parts, calcium oxide.
embodiment 3
Described a kind of refractory materials, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 125 parts
Boric acid 5 parts
20 parts, resol
Zirconium white 5 parts
Magnesium Silicate q-agent 15 parts
Water glass 25 parts
5 parts, silicon carbide
55 parts, magnesium oxide
55 parts, calcium oxide.
Claims (4)
1. a refractory materials, its feature comprises: silica refractory comprises following component: quartz sand, boric acid, resol, zirconium white, Magnesium Silicate q-agent, water glass, silicon carbide, magnesium oxide and calcium oxide.
2. a kind of refractory materials according to claim 1, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 125-159 part
Boric acid 5-10 part
Resol 20-35 part
Zirconium white 5-10 part
Magnesium Silicate q-agent 15-29 part
Water glass 25-35 part
Silicon carbide 5-10 part
Magnesium oxide 55-110 part
Calcium oxide 55-110 part.
3. a kind of refractory materials according to claim 1, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 159 parts
Boric acid 10 parts
35 parts, resol
Zirconium white 10 parts
Magnesium Silicate q-agent 29 parts
Water glass 35 parts
10 parts, silicon carbide
110 parts, magnesium oxide
110 parts, calcium oxide.
4. a kind of refractory materials according to claim 1, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 125 parts
Boric acid 5 parts
20 parts, resol
Zirconium white 5 parts
Magnesium Silicate q-agent 15 parts
Water glass 25 parts
5 parts, silicon carbide
55 parts, magnesium oxide
55 parts, calcium oxide.