CN105503214A - Refractory material for pipelines - Google Patents

Refractory material for pipelines Download PDF

Info

Publication number
CN105503214A
CN105503214A CN201510978093.XA CN201510978093A CN105503214A CN 105503214 A CN105503214 A CN 105503214A CN 201510978093 A CN201510978093 A CN 201510978093A CN 105503214 A CN105503214 A CN 105503214A
Authority
CN
China
Prior art keywords
parts
refractory materials
quartz sand
pipeline
silicon carbide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510978093.XA
Other languages
Chinese (zh)
Inventor
唐刚全
张丰琼
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SICHUAN QUANFENG NEW MATERIALS TECHNOLOGY Co Ltd
Original Assignee
SICHUAN QUANFENG NEW MATERIALS TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SICHUAN QUANFENG NEW MATERIALS TECHNOLOGY Co Ltd filed Critical SICHUAN QUANFENG NEW MATERIALS TECHNOLOGY Co Ltd
Priority to CN201510978093.XA priority Critical patent/CN105503214A/en
Publication of CN105503214A publication Critical patent/CN105503214A/en
Pending legal-status Critical Current

Abstract

The invention belongs to the technical field of high temperature resistance of pipelines and relates to manufacturing of a refractory material for pipelines, in particular to a refractory material for pipelines. The refractory material is characterized in that a quartz refractory material comprises components as follows: quartz sand, boric acid, phenolic resin, zirconium oxide, magnesium silicate, sodium silicate, silicon carbide, magnesium oxide and calcium oxide.

Description

A kind of pipeline refractory materials
Technical field
The invention belongs to the high temperature resistant technical field of pipeline, relate to a kind of manufacture of pipeline refractory materials, particularly relate to a kind of pipeline refractory materials.
Background technology
Refractoriness is not less than a class ceramic of 1599 DEG C.Refractoriness refers to that refractory materials cone-shaped body sample is not having in loading situation, resists high temperature action and does not soften molten centigradetemperature.But only define with refractoriness and can not describe refractory materials, 1599 DEG C is not absolute comprehensively.Now be defined as the material that all physicochemical property allow it to use in high temperature environments and be called refractory materials.Refractory materials is widely used in the industrial circles such as metallurgy, chemical industry, oil, machinofacture, silicate, power, and in metallurgical industry, consumption is maximum, accounts for 69% ~ 60% of ultimate production.
Application to refractory is in the every field of the national economy such as iron and steel, non-ferrous metal, glass, cement, pottery, petrochemical industry, machinery, boiler, light industry, electric power, military project, be ensure above-mentioned industry production run and the requisite basic material of technical development, in hot industry production development, play irreplaceable vital role.
At the outside surface of novel material pipeline, the usual way that one deck refractory materials is this area pipeline is set, but due to technical limitation, this refractory materials intensity does not reach standard in the art, and work-ing life is not very long, is difficult to reach the requirement that this area pipeline needs to reach.
Summary of the invention
In order to solve the problems of the prior art, the invention provides a kind of pipeline refractory materials.
A kind of pipeline refractory materials, its feature comprises: silica refractory comprises following component: quartz sand, boric acid, resol, zirconium white, Magnesium Silicate q-agent, water glass, silicon carbide, magnesium oxide and calcium oxide.
Described a kind of pipeline refractory materials, is characterized by: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 750-950 part
Boric acid 25-45 part
Resol 125-180 part
Zirconium white 10-25 part
Magnesium Silicate q-agent 15-45 part
Water glass 25-35 part
Silicon carbide 10-45 part
Magnesium oxide 125-220 part
Calcium oxide 125-220 part.
Described a kind of pipeline refractory materials, is characterized by: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 750 parts
Boric acid 25 parts
125 parts, resol
Zirconium white 10 parts
Magnesium Silicate q-agent 15 parts
Water glass 25 parts
10 parts, silicon carbide
125 parts, magnesium oxide
125 parts, calcium oxide.
Described a kind of pipeline refractory materials, is characterized by: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 950 parts
Boric acid 45 parts
180 parts, resol
Zirconium white 25 parts
Magnesium Silicate q-agent 45 parts
Water glass 35 parts
45 parts, silicon carbide
220 parts, magnesium oxide
220 parts, calcium oxide.
Embodiment
Embodiment 1
A kind of pipeline refractory materials, its feature comprises: silica refractory comprises following component: quartz sand, boric acid, resol, zirconium white, Magnesium Silicate q-agent, water glass, silicon carbide, magnesium oxide and calcium oxide.
Described a kind of pipeline refractory materials, is characterized by: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 750-950 part
Boric acid 25-45 part
Resol 125-180 part
Zirconium white 10-25 part
Magnesium Silicate q-agent 15-45 part
Water glass 25-35 part
Silicon carbide 10-45 part
Magnesium oxide 125-220 part
Calcium oxide 125-220 part.
Embodiment 2
Described a kind of pipeline refractory materials, is characterized by: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 750 parts
Boric acid 25 parts
125 parts, resol
Zirconium white 10 parts
Magnesium Silicate q-agent 15 parts
Water glass 25 parts
10 parts, silicon carbide
125 parts, magnesium oxide
125 parts, calcium oxide.
Embodiment 3
Described a kind of pipeline refractory materials, is characterized by: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 950 parts
Boric acid 45 parts
180 parts, resol
Zirconium white 25 parts
Magnesium Silicate q-agent 45 parts
Water glass 35 parts
45 parts, silicon carbide
220 parts, magnesium oxide
220 parts, calcium oxide.

Claims (4)

1. a pipeline refractory materials, its feature comprises: silica refractory comprises following component: quartz sand, boric acid, resol, zirconium white, Magnesium Silicate q-agent, water glass, silicon carbide, magnesium oxide and calcium oxide.
2. a kind of pipeline refractory materials according to claim 1, is characterized by: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 750-950 part
Boric acid 25-45 part
Resol 125-180 part
Zirconium white 10-25 part
Magnesium Silicate q-agent 15-45 part
Water glass 25-35 part
Silicon carbide 10-45 part
Magnesium oxide 125-220 part
Calcium oxide 125-220 part.
3. a kind of pipeline refractory materials according to claim 1, is characterized by: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 750 parts
Boric acid 25 parts
125 parts, resol
Zirconium white 10 parts
Magnesium Silicate q-agent 15 parts
Water glass 25 parts
10 parts, silicon carbide
125 parts, magnesium oxide
125 parts, calcium oxide.
4. a kind of pipeline refractory materials according to claim 1, is characterized by: quartz sand refractory materials contains following component, each quartz sand 950 parts
Boric acid 45 parts
180 parts, resol
Zirconium white 25 parts
Magnesium Silicate q-agent 45 parts
Water glass 35 parts
45 parts, silicon carbide
220 parts, magnesium oxide
220 parts, calcium oxide.
CN201510978093.XA 2015-12-23 2015-12-23 Refractory material for pipelines Pending CN105503214A (en)