CN105130476A - Quartz fireproofing material - Google Patents
Quartz fireproofing material Download PDFInfo
- Publication number
- CN105130476A CN105130476A CN201510630479.1A CN201510630479A CN105130476A CN 105130476 A CN105130476 A CN 105130476A CN 201510630479 A CN201510630479 A CN 201510630479A CN 105130476 A CN105130476 A CN 105130476A
- Authority
- CN
- China
- Prior art keywords
- parts
- quartz sand
- refractory
- quartz
- boric acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of high temperature resistance of pipelines, and relates to preparation of a quartz fireproofing material, in particular to a quartz fireproofing material. The quartz fireproofing material is characterized by being prepared from the following components: quartz sand, boric acid, phenolic resin, magnesium silicate, sodium silicate and calcium oxide.
Description
Technical field
The invention belongs to the high temperature resistant technical field of pipeline, relate to the manufacture of silica refractory, particularly relate to a kind of silica refractory.
Background technology
Refractoriness is not less than a class ceramic of 1599 DEG C.Refractoriness refers to that refractory materials cone-shaped body sample is not having in loading situation, resists high temperature action and does not soften molten centigradetemperature.But only define with refractoriness and can not describe refractory materials, 1599 DEG C is not absolute comprehensively.Now be defined as the material that all physicochemical property allow it to use in high temperature environments and be called refractory materials.Refractory materials is widely used in the industrial circles such as metallurgy, chemical industry, oil, machinofacture, silicate, power, and in metallurgical industry, consumption is maximum, accounts for 69% ~ 60% of ultimate production.
Application to refractory is in the every field of the national economy such as iron and steel, non-ferrous metal, glass, cement, pottery, petrochemical industry, machinery, boiler, light industry, electric power, military project, be ensure above-mentioned industry production run and the requisite basic material of technical development, in hot industry production development, play irreplaceable vital role.
In the art, also little for the refractory materials under alkaline border, the refractory materials under existing alkalescence substantially work-ing life not long.
Summary of the invention
In order to solve the problems of the prior art, the invention provides a kind of silica refractory.
A kind of silica refractory, its feature comprises: a kind of silica refractory comprises following component: quartz sand, boric acid, resol, Magnesium Silicate q-agent, water glass and calcium oxide.
Described a kind of silica refractory, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 180-350 part
Boric acid 5-10 part
Resol 40-60 part
Magnesium Silicate q-agent 35-40 part
Water glass 25-35 part
Calcium oxide 110-150 part.
Described a kind of silica refractory, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 350 parts
Boric acid 10 parts
60 parts, resol
Magnesium Silicate q-agent 40 parts
Water glass 35 parts
150 parts, calcium oxide.
Described a kind of silica refractory, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 180 parts
Boric acid 5 parts
40 parts, resol
Magnesium Silicate q-agent 35 parts
Water glass 25 parts
110 parts, calcium oxide.
Embodiment
embodiment 1
A kind of silica refractory, its feature comprises: a kind of silica refractory comprises following component: quartz sand, boric acid, resol, Magnesium Silicate q-agent, water glass and calcium oxide.
Described a kind of silica refractory, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 180-350 part
Boric acid 5-10 part
Resol 40-60 part
Magnesium Silicate q-agent 35-40 part
Water glass 25-35 part
Calcium oxide 110-150 part.
embodiment 2
Described a kind of silica refractory, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 350 parts
Boric acid 10 parts
60 parts, resol
Magnesium Silicate q-agent 40 parts
Water glass 35 parts
150 parts, calcium oxide.
embodiment 3
Described a kind of silica refractory, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 180 parts
Boric acid 5 parts
40 parts, resol
Magnesium Silicate q-agent 35 parts
Water glass 25 parts
110 parts, calcium oxide.
Claims (4)
1. a silica refractory, its feature comprises: a kind of silica refractory comprises following component: quartz sand, boric acid, resol, Magnesium Silicate q-agent, water glass and calcium oxide.
2. a kind of silica refractory according to claim 1, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 180-350 part
Boric acid 5-10 part
Resol 40-60 part
Magnesium Silicate q-agent 35-40 part
Water glass 25-35 part
Calcium oxide 110-150 part.
3. a kind of silica refractory according to claim 1, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 350 parts
Boric acid 10 parts
60 parts, resol
Magnesium Silicate q-agent 40 parts
Water glass 35 parts
150 parts, calcium oxide.
4. a kind of silica refractory according to claim 1, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 180 parts
Boric acid 5 parts
40 parts, resol
Magnesium Silicate q-agent 35 parts
Water glass 25 parts
110 parts, calcium oxide.