CN105272277A - Alkaline ceramic fiber refractory material - Google Patents
Alkaline ceramic fiber refractory material Download PDFInfo
- Publication number
- CN105272277A CN105272277A CN201510630420.2A CN201510630420A CN105272277A CN 105272277 A CN105272277 A CN 105272277A CN 201510630420 A CN201510630420 A CN 201510630420A CN 105272277 A CN105272277 A CN 105272277A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic fiber
- silicon carbide
- boric acid
- alkaline ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of high temperature resistance of pipelines, relates to preparation of alkaline refractory materials, and especially relates to an alkaline ceramic fiber refractory material. The above quartz refractory material comprises alumina, boric acid, phenolic resin, zirconia, sodium silicate and silicon carbide.
Description
Technical field
The invention belongs to the high temperature resistant technical field of pipeline, relate to the manufacture of basic refractory, particularly relate to a kind of alkaline ceramic fiber fireproof material.
Background technology
Refractoriness is not less than a class ceramic of 1599 DEG C.Refractoriness refers to that refractory materials cone-shaped body sample is not having in loading situation, resists high temperature action and does not soften molten centigradetemperature.But only define with refractoriness and can not describe refractory materials, 1599 DEG C is not absolute comprehensively.Now be defined as the material that all physicochemical property allow it to use in high temperature environments and be called refractory materials.Refractory materials is widely used in the industrial circles such as metallurgy, chemical industry, oil, machinofacture, silicate, power, and in metallurgical industry, consumption is maximum, accounts for 69% ~ 60% of ultimate production.
Application to refractory is in the every field of the national economy such as iron and steel, non-ferrous metal, glass, cement, pottery, petrochemical industry, machinery, boiler, light industry, electric power, military project, be ensure above-mentioned industry production run and the requisite basic material of technical development, in hot industry production development, play irreplaceable vital role.
In the art, also little for the refractory materials under alkaline border, the refractory materials under existing alkalescence substantially work-ing life not long.
Summary of the invention
In order to solve the problems of the prior art, the invention provides a kind of alkaline ceramic fiber fireproof material.
A kind of alkaline ceramic fiber fireproof material, its feature comprises: silica refractory comprises following component: aluminum oxide, boric acid, resol, zirconium white, water glass and silicon carbide.
Described a kind of alkaline ceramic fiber fireproof material, is characterized in: alumina refractory contains following component, and the weight part of each component is:
Aluminum oxide 350-450 part
Boric acid 5-10 part
Resol 15-20 part
Zirconium white 5-10 part
Water glass 15-20 part
Silicon carbide 5-10 part.
Described a kind of alkaline ceramic fiber fireproof material, is characterized in: alumina refractory contains following component, and the weight part of each component is:
450 parts, aluminum oxide
Boric acid 10 parts
20 parts, resol
Zirconium white 10 parts
Water glass 20 parts
10 parts, silicon carbide.
Described a kind of alkaline ceramic fiber fireproof material, is characterized in: alumina refractory contains following component, and the weight part of each component is:
350 parts, aluminum oxide
Boric acid 5 parts
15 parts, resol
Zirconium white 5 parts
Water glass 15 parts
5 parts, silicon carbide.
Embodiment
embodiment 1
A kind of alkaline ceramic fiber fireproof material, its feature comprises: silica refractory comprises following component: aluminum oxide, boric acid, resol, zirconium white, water glass, silicon carbide and magnesium oxide.
Described a kind of alkaline ceramic fiber fireproof material, is characterized in: alumina refractory contains following component, and the weight part of each component is:
Aluminum oxide 350-450 part
Boric acid 5-10 part
Resol 15-20 part
Zirconium white 5-10 part
Water glass 15-20 part
Silicon carbide 5-10 part.
embodiment 2
Described a kind of alkaline ceramic fiber fireproof material, is characterized in: alumina refractory contains following component, and the weight part of each component is:
450 parts, aluminum oxide
Boric acid 10 parts
20 parts, resol
Zirconium white 10 parts
Water glass 20 parts
10 parts, silicon carbide.
embodiment 3
Described a kind of alkaline ceramic fiber fireproof material, is characterized in: alumina refractory contains following component, and the weight part of each component is:
350 parts, aluminum oxide
Boric acid 5 parts
15 parts, resol
Zirconium white 5 parts
Water glass 15 parts
5 parts, silicon carbide.
Claims (4)
1. an alkaline ceramic fiber fireproof material, its feature comprises: silica refractory comprises following component: aluminum oxide, boric acid, resol, zirconium white, water glass and silicon carbide.
2. a kind of alkaline ceramic fiber fireproof material according to claim 1, is characterized in: alumina refractory contains following component, and the weight part of each component is:
Aluminum oxide 350-450 part
Boric acid 5-10 part
Resol 15-20 part
Zirconium white 5-10 part
Water glass 15-20 part
Silicon carbide 5-10 part.
3. a kind of alkaline ceramic fiber fireproof material according to claim 1, is characterized in: alumina refractory contains following component, and the weight part of each component is:
450 parts, aluminum oxide
Boric acid 10 parts
20 parts, resol
Zirconium white 10 parts
Water glass 20 parts
10 parts, silicon carbide.
4. a kind of alkaline ceramic fiber fireproof material according to claim 1, is characterized in: alumina refractory contains following component, and the weight part of each component is:
350 parts, aluminum oxide
Boric acid 5 parts
15 parts, resol
Zirconium white 5 parts
Water glass 15 parts
5 parts, silicon carbide.