CN105272279A - Novel alkaline refractory material - Google Patents
Novel alkaline refractory material Download PDFInfo
- Publication number
- CN105272279A CN105272279A CN201510630582.6A CN201510630582A CN105272279A CN 105272279 A CN105272279 A CN 105272279A CN 201510630582 A CN201510630582 A CN 201510630582A CN 105272279 A CN105272279 A CN 105272279A
- Authority
- CN
- China
- Prior art keywords
- parts
- refractory materials
- novel alkaline
- alkaline refractory
- quartz sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of pipeline high temperature resistance, relates to preparation of novel alkaline refractory materials, and especially relates to a novel alkaline refractory material. The novel alkaline refractory material comprises quartz sand, phenolic resin, magnesium silicate, sodium silicate, magnesium oxide and calcium oxide.
Description
Technical field
The invention belongs to the high temperature resistant technical field of pipeline, relate to the manufacture of novel alkaline refractory materials, particularly relate to a kind of novel alkaline refractory materials.
Background technology
Refractoriness is not less than a class ceramic of 1599 DEG C.Refractoriness refers to that refractory materials cone-shaped body sample is not having in loading situation, resists high temperature action and does not soften molten centigradetemperature.But only define with refractoriness and can not describe refractory materials, 1599 DEG C is not absolute comprehensively.Now be defined as the material that all physicochemical property allow it to use in high temperature environments and be called refractory materials.Refractory materials is widely used in the industrial circles such as metallurgy, chemical industry, oil, machinofacture, silicate, power, and in metallurgical industry, consumption is maximum, accounts for 69% ~ 60% of ultimate production.
Application to refractory is in the every field of the national economy such as iron and steel, non-ferrous metal, glass, cement, pottery, petrochemical industry, machinery, boiler, light industry, electric power, military project, be ensure above-mentioned industry production run and the requisite basic material of technical development, in hot industry production development, play irreplaceable vital role.
In the art, also little for the refractory materials under alkaline border, the refractory materials under existing alkalescence substantially work-ing life not long.
Summary of the invention
In order to solve the problems of the prior art, the invention provides a kind of novel alkaline refractory materials.
A kind of novel alkaline refractory materials, is characterized in that comprising following component: quartz sand, resol, Magnesium Silicate q-agent, water glass, magnesium oxide and calcium oxide.
Described a kind of novel alkaline refractory materials, is characterized in: a kind of novel alkaline refractory materials contains following component, and the weight part of each component is:
Quartz sand 350-550 part
Resol 30-50 part
Magnesium Silicate q-agent 75-95 part
Water glass 60-80 part
Magnesium oxide 110-150 part
Calcium oxide 110-150 part.
Described a kind of novel alkaline refractory materials, is characterized in: a kind of novel alkaline refractory materials contains following component, and the weight part of each component is:
Quartz sand 350 parts
30 parts, resol
Magnesium Silicate q-agent 75 parts
Water glass 60 parts
110 parts, magnesium oxide
110 parts, calcium oxide.
Described a kind of novel alkaline refractory materials, is characterized in: a kind of novel alkaline refractory materials contains following component, and the weight part of each component is:
Quartz sand 550 parts
50 parts, resol
Magnesium Silicate q-agent 95 parts
Water glass 80 parts
150 parts, magnesium oxide
150 parts, calcium oxide.
Embodiment
embodiment 1
A kind of novel alkaline refractory materials, is characterized in that comprising following component: quartz sand, resol, Magnesium Silicate q-agent, water glass, magnesium oxide and calcium oxide.
Described a kind of novel alkaline refractory materials, is characterized in: a kind of novel alkaline refractory materials contains following component, and the weight part of each component is:
Quartz sand 350-550 part
Resol 30-50 part
Magnesium Silicate q-agent 75-95 part
Water glass 60-80 part
Magnesium oxide 110-150 part
Calcium oxide 110-150 part.
embodiment 2
Described a kind of novel alkaline refractory materials, is characterized in: a kind of novel alkaline refractory materials contains following component, and the weight part of each component is:
Quartz sand 350 parts
30 parts, resol
Magnesium Silicate q-agent 75 parts
Water glass 60 parts
110 parts, magnesium oxide
110 parts, calcium oxide.
embodiment 3
A kind of novel alkaline refractory materials stated, is characterized in: a kind of novel alkaline refractory materials contains following component, and the weight part of each component is:
Quartz sand 550 parts
50 parts, resol
Magnesium Silicate q-agent 95 parts
Water glass 80 parts
150 parts, magnesium oxide
150 parts, calcium oxide.
Claims (4)
1. a novel alkaline refractory materials, is characterized in that comprising following component: quartz sand, resol, Magnesium Silicate q-agent, water glass, magnesium oxide and calcium oxide.
2. a kind of novel alkaline refractory materials according to claim 1, be characterized in: a kind of novel alkaline refractory materials contains following component, the weight part of each component is:
Quartz sand 350-550 part
Resol 30-50 part
Magnesium Silicate q-agent 75-95 part
Water glass 60-80 part
Magnesium oxide 110-150 part
Calcium oxide 110-150 part.
3. a kind of novel alkaline refractory materials according to claim 1, be characterized in: a kind of novel alkaline refractory materials contains following component, the weight part of each component is:
Quartz sand 350 parts
30 parts, resol
Magnesium Silicate q-agent 75 parts
Water glass 60 parts
110 parts, magnesium oxide
110 parts, calcium oxide.
4. a kind of novel alkaline refractory materials according to claim 1, be characterized in: a kind of novel alkaline refractory materials contains following component, the weight part of each component is:
Quartz sand 550 parts
50 parts, resol
Magnesium Silicate q-agent 95 parts
Water glass 80 parts
150 parts, magnesium oxide
150 parts, calcium oxide.