CN105130477A - Alkaline quartz fireproof material - Google Patents
Alkaline quartz fireproof material Download PDFInfo
- Publication number
- CN105130477A CN105130477A CN201510630529.6A CN201510630529A CN105130477A CN 105130477 A CN105130477 A CN 105130477A CN 201510630529 A CN201510630529 A CN 201510630529A CN 105130477 A CN105130477 A CN 105130477A
- Authority
- CN
- China
- Prior art keywords
- parts
- quartz sand
- refractory
- alkaline
- boric acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of pipeline resistance to high temperature, relating to alkaline quartz fireproof material manufacturing, in particular to an alkaline quartz fireproof material which is characterized by being prepared from the following components: quartz sand, boric acid, phenolic resin, zirconia, magnesium silicate and magnesium oxide.
Description
Technical field
The invention belongs to the high temperature resistant technical field of pipeline, relate to a kind of manufacture of alkaline silica refractory, particularly relate to a kind of alkaline silica refractory.
Background technology
Refractoriness is not less than a class ceramic of 1599 DEG C.Refractoriness refers to that refractory materials cone-shaped body sample is not having in loading situation, resists high temperature action and does not soften molten centigradetemperature.But only define with refractoriness and can not describe refractory materials, 1599 DEG C is not absolute comprehensively.Now be defined as the material that all physicochemical property allow it to use in high temperature environments and be called refractory materials.Refractory materials is widely used in the industrial circles such as metallurgy, chemical industry, oil, machinofacture, silicate, power, and in metallurgical industry, consumption is maximum, accounts for 69% ~ 60% of ultimate production.
Application to refractory is in the every field of the national economy such as iron and steel, non-ferrous metal, glass, cement, pottery, petrochemical industry, machinery, boiler, light industry, electric power, military project, be ensure above-mentioned industry production run and the requisite basic material of technical development, in hot industry production development, play irreplaceable vital role.
In the art, also little for the refractory materials under alkaline border, the refractory materials under existing alkalescence substantially work-ing life not long.
Summary of the invention
In order to solve the problems of the prior art, the invention provides a kind of alkaline silica refractory.
A kind of alkaline silica refractory, its feature comprises following component: quartz sand, boric acid, resol, zirconium white, Magnesium Silicate q-agent and magnesium oxide.
Described one alkalescence silica refractory, be characterized in: quartz sand refractory materials contains following component, the weight part of each component is:
Quartz sand 280-350 part
Boric acid 5-10 part
Resol 15-20 part
Zirconium white 5-10 part
Magnesium Silicate q-agent 15-29 part
Magnesium oxide 110-220 part.
Described one alkalescence silica refractory, be characterized in: quartz sand refractory materials contains following component, the weight part of each component is:
Quartz sand 350 parts
Boric acid 10 parts
20 parts, resol
Zirconium white 10 parts
Magnesium Silicate q-agent 29 parts
220 parts, magnesium oxide.
Described one alkalescence silica refractory, be characterized in: quartz sand refractory materials contains following component, the weight part of each component is:
Quartz sand 280 parts
Boric acid 5 parts
15 parts, resol
Zirconium white 5 parts
Magnesium Silicate q-agent 15 parts
110 parts, magnesium oxide.
Embodiment
embodiment 1
A kind of alkaline silica refractory, its feature comprises: silica refractory comprises following component: quartz sand, boric acid, resol, zirconium white, Magnesium Silicate q-agent and magnesium oxide.
Described one alkalescence silica refractory, be characterized in: quartz sand refractory materials contains following component, the weight part of each component is:
Quartz sand 280-350 part
Boric acid 5-10 part
Resol 15-20 part
Zirconium white 5-10 part
Magnesium Silicate q-agent 15-29 part
Magnesium oxide 110-220 part.
embodiment 2
Described one alkalescence silica refractory, be characterized in: quartz sand refractory materials contains following component, the weight part of each component is:
Quartz sand 350 parts
Boric acid 10 parts
20 parts, resol
Zirconium white 10 parts
Magnesium Silicate q-agent 29 parts
220 parts, magnesium oxide.
embodiment 3
Described one alkalescence silica refractory, be characterized in: quartz sand refractory materials contains following component, the weight part of each component is:
Quartz sand 280 parts
Boric acid 5 parts
15 parts, resol
Zirconium white 5 parts
Magnesium Silicate q-agent 15 parts
110 parts, magnesium oxide.
Claims (4)
1. an alkaline silica refractory, its feature comprises: silica refractory comprises following component: quartz sand, boric acid, resol, zirconium white, Magnesium Silicate q-agent and magnesium oxide.
2. the alkaline silica refractory of one according to claim 1, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 280-350 part
Boric acid 5-10 part
Resol 15-20 part
Zirconium white 5-10 part
Magnesium Silicate q-agent 15-29 part
Magnesium oxide 110-220 part.
3. the alkaline silica refractory of one according to claim 1, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 350 parts
Boric acid 10 parts
20 parts, resol
Zirconium white 10 parts
Magnesium Silicate q-agent 29 parts
220 parts, magnesium oxide.
4. the alkaline silica refractory of one according to claim 1, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 280 parts
Boric acid 5 parts
15 parts, resol
Zirconium white 5 parts
Magnesium Silicate q-agent 15 parts
110 parts, magnesium oxide.