CN105272280A - Novel alkaline ceramic fiber quartz refractory material - Google Patents
Novel alkaline ceramic fiber quartz refractory material Download PDFInfo
- Publication number
- CN105272280A CN105272280A CN201510630611.9A CN201510630611A CN105272280A CN 105272280 A CN105272280 A CN 105272280A CN 201510630611 A CN201510630611 A CN 201510630611A CN 105272280 A CN105272280 A CN 105272280A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic fiber
- quartz sand
- novel alkaline
- alkaline ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of pipeline high temperature resistance, relates to preparation of novel alkaline ceramic fiber quartz refractory materials, and especially relates to a novel alkaline ceramic fiber quartz refractory material. The novel alkaline ceramic fiber quartz refractory material comprises quartz sand, boric acid, phenolic resin, zirconia, magnesium silicate, sodium silicate and alumina.
Description
Technical field
The invention belongs to the high temperature resistant technical field of pipeline, relate to a kind of manufacture of novel alkaline ceramic fiber silica refractory, particularly relate to a kind of novel alkaline ceramic fiber silica refractory.
Background technology
Refractoriness is not less than a class ceramic of 1599 DEG C.Refractoriness refers to that refractory materials cone-shaped body sample is not having in loading situation, resists high temperature action and does not soften molten centigradetemperature.But only define with refractoriness and can not describe refractory materials, 1599 DEG C is not absolute comprehensively.Now be defined as the material that all physicochemical property allow it to use in high temperature environments and be called refractory materials.Refractory materials is widely used in the industrial circles such as metallurgy, chemical industry, oil, machinofacture, silicate, power, and in metallurgical industry, consumption is maximum, accounts for 69% ~ 60% of ultimate production.
Application to refractory is in the every field of the national economy such as iron and steel, non-ferrous metal, glass, cement, pottery, petrochemical industry, machinery, boiler, light industry, electric power, military project, be ensure above-mentioned industry production run and the requisite basic material of technical development, in hot industry production development, play irreplaceable vital role.
In the art, also little for the refractory materials under alkaline border, the refractory materials under existing alkalescence substantially work-ing life not long.
Summary of the invention
In order to solve the problems of the prior art, the invention provides a kind of novel alkaline ceramic fiber silica refractory.
A kind of novel alkaline ceramic fiber silica refractory, its feature comprises: silica refractory comprises following component: quartz sand, boric acid, resol, zirconium white, Magnesium Silicate q-agent, water glass and aluminum oxide.
Described a kind of novel alkaline ceramic fiber silica refractory, be characterized in: quartz sand refractory materials contains following component, the weight part of each component is:
Quartz sand 120-150 part
Boric acid 5-10 part
Resol 20-35 part
Magnesium Silicate q-agent 15-45 part
Water glass 45-55 part
Aluminum oxide 250-450 part.
Described a kind of novel alkaline ceramic fiber silica refractory, be characterized in: quartz sand refractory materials contains following component, the weight part of each component is:
Quartz sand 150 parts
Boric acid 10 parts
35 parts, resol
Magnesium Silicate q-agent 45 parts
Water glass 55 parts
450 parts, aluminum oxide.
Described a kind of novel alkaline ceramic fiber silica refractory, be characterized in: quartz sand refractory materials contains following component, the weight part of each component is:
Quartz sand 120 parts
Boric acid 5 parts
20 parts, resol
Magnesium Silicate q-agent 15 parts
Water glass 45 parts
250 parts, aluminum oxide.
Embodiment
embodiment 1
A kind of novel alkaline ceramic fiber silica refractory, its feature comprises: silica refractory comprises following component: quartz sand, boric acid, resol, zirconium white, Magnesium Silicate q-agent, water glass and aluminum oxide.
Quartz sand 120-150 part
Boric acid 5-10 part
Resol 20-35 part
Magnesium Silicate q-agent 15-45 part
Water glass 45-55 part
Aluminum oxide 250-450 part.
embodiment 2
Described a kind of silica refractory, is characterized in: quartz sand refractory materials contains following component, and the weight part of each component is:
Quartz sand 150 parts
Boric acid 10 parts
35 parts, resol
Magnesium Silicate q-agent 45 parts
Water glass 55 parts
450 parts, aluminum oxide.
embodiment 3
Described a kind of novel alkaline ceramic fiber silica refractory, be characterized in: quartz sand refractory materials contains following component, the weight part of each component is:
Quartz sand 120 parts
Boric acid 5 parts
20 parts, resol
Magnesium Silicate q-agent 15 parts
Water glass 45 parts
250 parts, aluminum oxide.
Claims (4)
1. a novel alkaline ceramic fiber silica refractory, its feature comprises: silica refractory comprises following component: quartz sand, boric acid, resol, zirconium white, Magnesium Silicate q-agent, water glass and aluminum oxide.
2. a kind of novel alkaline ceramic fiber silica refractory according to claim 1, be characterized in: quartz sand refractory materials contains following component, the weight part of each component is:
Quartz sand 120-150 part
Boric acid 5-10 part
Resol 20-35 part
Magnesium Silicate q-agent 15-45 part
Water glass 45-55 part
Aluminum oxide 250-450 part.
3. a kind of novel alkaline ceramic fiber silica refractory according to claim 1, be characterized in: quartz sand refractory materials contains following component, the weight part of each component is:
Quartz sand 150 parts
Boric acid 10 parts
35 parts, resol
Magnesium Silicate q-agent 45 parts
Water glass 55 parts
450 parts, aluminum oxide.
4. a kind of novel alkaline ceramic fiber silica refractory according to claim 1, be characterized in: quartz sand refractory materials contains following component, the weight part of each component is:
Quartz sand 120 parts
Boric acid 5 parts
20 parts, resol
Magnesium Silicate q-agent 15 parts
Water glass 45 parts
250 parts, aluminum oxide.