CN109734874A - 餐厨废弃油改性酚醛树脂的制备方法 - Google Patents
餐厨废弃油改性酚醛树脂的制备方法 Download PDFInfo
- Publication number
- CN109734874A CN109734874A CN201910041050.7A CN201910041050A CN109734874A CN 109734874 A CN109734874 A CN 109734874A CN 201910041050 A CN201910041050 A CN 201910041050A CN 109734874 A CN109734874 A CN 109734874A
- Authority
- CN
- China
- Prior art keywords
- phenolic resin
- kitchen
- parts
- modified phenolic
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种餐厨废弃油改性酚醛树脂的制备方法，属于聚氨酯发泡领域；由以下原料制备而成：餐厨废弃油50‑500份，聚醚多元醇100‑1000份，TDI 10‑300份，酚醛树脂100‑1000份，硅烷偶联剂5‑15份，扩链剂10‑50份。本发明中的餐厨废弃油改性酚醛树脂的制备方法，能够大大提高了餐厨废弃油的再利用率，避免餐厨废弃油再次流入人们的餐桌。本发明制备的餐厨废弃油改性酚醛树脂，利用餐厨废弃油来改性酚醛树脂，提高酚醛树脂的韧性，很大程度上提高了产品的性能。
Description
技术领域
本发明涉及一种餐厨废弃油改性酚醛树脂的制备方法，属于聚氨酯发泡领域。
背景技术
酚醛树脂是酚类化合物和醛类化合物进行缩聚反应而值得的合成树脂的统称，具有良好的耐热性，阻燃性，刚性，耐磨耐腐蚀性，电绝缘性等特点，但酚醛树脂的脆性大，韧性差，损伤容限低，不易用作结构材料，大大制约了其使用范围。
餐厨废弃油泛指在生活中产生的各种劣质油，其主要成分为甘油三酯，我国每年会产生大量的餐厨废弃油，其流入餐桌会对人体造成很大的危害，本发明提供了一种餐厨废弃油的再利用方法，利用餐厨废弃油来改性酚醛树脂，提高酚醛树脂的韧性。大大提高了餐厨废弃油的再利用率。
发明内容
根据现有技术的不足，本发明要解决的技术问题是：提供一种餐厨废弃油改性酚醛树脂的制备方法，利用餐厨废弃油来改性酚醛树脂，提高酚醛树脂的韧性，技能节约资源，同时又能提高产品性能。
本发明解决其技术问题所采用的技术方案是：提供一种餐厨废弃油改性酚醛树脂的制备方法，由以下原料制备而成：
餐厨废弃油50-500份，
聚醚多元醇100-1000份，
TDI 10-300份，
酚醛树脂100-1000份，
硅烷偶联剂5-15份，
扩链剂10-50份。
所述的聚醚多元醇的官能度为2-3，分子量为1000-10000。
所述的硅烷偶联剂为乙烯基三乙氧基硅烷、乙烯基三甲氧基硅烷或乙烯基三(β-甲氧乙氧基)硅烷。
所述的扩链剂为多元醇类扩链剂、醇胺类扩链剂或二元胺类扩链剂；
所述的多元醇类扩链剂为1，4-丁二醇、丙二醇、乙二醇、一缩二乙二醇、丙三醇或三羟甲基丙烷；
所述的醇胺类扩链剂为乙醇胺、二乙醇胺或三乙醇胺；
所述的二元胺类扩链剂为MOCA。
所述的酚醛树脂为聚乙烯醇缩醛改性酚醛树脂、二甲苯改性酚醛树脂、环氧改性酚醛树脂、有机硅改性酚醛树脂或硼改性酚醛树。
所述的餐厨废弃油改性酚醛树脂的制备方法，制备步骤如下：
将聚醚多元醇倒入三口烧瓶中升温110℃脱水至水分小于0.02％，降温80-100℃，滴入计量的TDI与之反应2-5小时，再滴入计量的餐厨废弃油和扩链剂搅拌反应2-5小时，升温至 120-150度加入酚醛树脂反应3-5小时，脱单体1-3小时，降温至80-100度加入硅烷偶联剂搅拌反应3-5小时，得到改性酚醛树脂。
其中餐厨废弃油和聚醚多元醇的质量一般来说m餐厨废弃油/m聚醚多元醇为1/2-1/10。
本发明的有益效果是：
1、本发明中的餐厨废弃油改性酚醛树脂的制备方法，能够大大提高了餐厨废弃油的再利用率，避免餐厨废弃油再次流入人们的餐桌；
2、本发明制备的餐厨废弃油改性酚醛树脂，利用餐厨废弃油来改性酚醛树脂，提高酚醛树脂的韧性，很大程度上提高了产品的性能；
3、本发明配方合理，节约资源，同时相对于现有技术来说更加环保。
4、耐高温、耐酸碱性好、耐腐蚀、低烟低毒。高温下残碳率高，高温下结构性能好
5、原料易得，生产成本低。合理利用资源，绿色环保。
具体实施方式
下面对本发明的实施例做进一步描述：
实施例1
一种餐厨废弃油改性酚醛树脂的制备方法，将100份DL-1000D(官能度2，分子量1000) 倒入三口烧瓶中，氮气置换保护下升温110度脱水至水分小于0.02％，降温80度滴入10份 TDI，搅拌反应2小时，滴入10份1，4-丁二醇，50份餐厨废弃油，搅拌反应2小时，升温至120度加入100份二甲苯改性酚醛树脂反应3小时，脱单体2小时，降温至80度，加入5 份乙烯基三乙氧基硅烷，搅拌反应3小时得到产品。
实施例2
一种餐厨废弃油改性酚醛树脂的制备方法，将1000份DMD-6000(官能度3，分子量6000) 倒入三口烧瓶中，氮气置换保护下升温110度脱水至水分小于0.02％，降温90度滴入300份 TDI，搅拌反应2.5小时，滴入35份二乙醇，500份餐厨废弃油，搅拌反应3小时，升温130 度加入1000份环氧改性酚醛树脂反应4小时，脱单体1小时，降温90度加入10份乙烯基三甲氧基硅烷，搅拌反应4小时得到产品。
实施例3
一种餐厨废弃油改性酚醛树脂的制备方法，将500份DL-4000D(官能度2，分子量4000) 倒入三口烧瓶中，氮气置换保护下升温110度脱水至水分小于0.02％，降温100度滴入66份 TDI，搅拌反应3小时，滴入50份MOCA，200份餐厨废弃油，搅拌反应5小时，升温至150度加入500份聚乙烯醇缩醛改性酚醛树脂反应5小时，脱单体3小时，降温至100度加入15 份乙烯基三(β-甲氧乙氧基)硅烷，搅拌反应5小时得到产品。
对实施例1-3和对比例1-2的产品进行性能测试，测试方法如下：
(1)压缩试验，拉伸试验及三点弯曲试验使用IN-STRON 1185万能力学试验机进行。拉伸试验按照GB/T 1040.3-2006进行，拉伸试验速度为2mm/min，夹距30mm。压缩试验按照GB/T 1041-2008进行，压缩速度为1mm/min，三点弯曲试验按照 GB/T 9341-2008进行，跨距64mm，速度为1mm/min，冲击强度试验按照GB/T 1043.1-2008进行，使用高低温摆锤冲击试验机，跨距64mm，摆锤5J。
(2)将固化后的样品切割打磨成各种尺寸用于力学性能测试，压缩试验所需尺寸10mm×10mm×10mm。拉伸试验所需尺寸80mm×4mm×3mm。三点弯曲试验，冲击强度试验所需尺寸80mm×10mm×4mm。其中冲击强度试验需在样品中部做 A型缺口，深度2mm。
Claims (6)
1.一种餐厨废弃油改性酚醛树脂的制备方法，其特征在于由以下原料制备而成：
餐厨废弃油50-500份，
聚醚多元醇100-1000份，
TDI 10-300份，
酚醛树脂100-1000份，
硅烷偶联剂5-15份，
扩链剂10-50份。
2.根据权利要求1所述的餐厨废弃油改性酚醛树脂的制备方法，其特征在于所述的聚醚多元醇的官能度为2-3，分子量为1000-10000。
3.根据权利要求1所述的餐厨废弃油改性酚醛树脂的制备方法，其特征在于所述的硅烷偶联剂为乙烯基三乙氧基硅烷、乙烯基三甲氧基硅烷或乙烯基三(β-甲氧乙氧基)硅烷。
4.根据权利要求1所述的餐厨废弃油改性酚醛树脂的制备方法，其特征在于所述的扩链剂为多元醇类扩链剂、醇胺类扩链剂或二元胺类扩链剂；
所述的多元醇类扩链剂为1，4-丁二醇、丙二醇、乙二醇、一缩二乙二醇、丙三醇或三羟甲基丙烷；
所述的醇胺类扩链剂为乙醇胺、二乙醇胺或三乙醇胺；
所述的二元胺类扩链剂为MOCA。
5.根据权利要求1所述的餐厨废弃油改性酚醛树脂的制备方法，其特征在于所述的酚醛树脂为聚乙烯醇缩醛改性酚醛树脂、二甲苯改性酚醛树脂、环氧改性酚醛树脂、有机硅改性酚醛树脂或硼改性酚醛树脂。
6.根据权利要求1所述的餐厨废弃油改性酚醛树脂的制备方法，其特征在于制备步骤如下：
将聚醚多元醇倒入三口烧瓶中升温110℃脱水至水分小于0.02％，降温80-100℃，滴入计量的TDI与之反应2-5小时，再滴入计量的餐厨废弃油和扩链剂搅拌反应2-5小时，升温至120-150度加入酚醛树脂反应3-5小时，脱单体1-3小时，降温至80-100度加入硅烷偶联剂搅拌反应3-5小时，得到改性酚醛树脂。