CN102875959B - 玻璃微珠填充的酚醛高分子复合材料的制备方法 - Google Patents

玻璃微珠填充的酚醛高分子复合材料的制备方法 Download PDF

Info

Publication number
CN102875959B
CN102875959B CN2012103505329A CN201210350532A CN102875959B CN 102875959 B CN102875959 B CN 102875959B CN 2012103505329 A CN2012103505329 A CN 2012103505329A CN 201210350532 A CN201210350532 A CN 201210350532A CN 102875959 B CN102875959 B CN 102875959B
Authority
CN
China
Prior art keywords
parts
phenolic aldehyde
preparation
filled
polymer composite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2012103505329A
Other languages
English (en)
Other versions
CN102875959A (zh
Inventor
方云祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU YONGXIANG ELECTROMECHANICAL Co Ltd
Original Assignee
CHANGSHU YONGXIANG ELECTROMECHANICAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU YONGXIANG ELECTROMECHANICAL Co Ltd filed Critical CHANGSHU YONGXIANG ELECTROMECHANICAL Co Ltd
Priority to CN2012103505329A priority Critical patent/CN102875959B/zh
Publication of CN102875959A publication Critical patent/CN102875959A/zh
Application granted granted Critical
Publication of CN102875959B publication Critical patent/CN102875959B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种玻璃微珠填充的酚醛高分子复合材料的制备方法，属于热固性模塑料制备技术领域。其是先称取金属氧化物 0.8~1.5 份、增强纤维 14~18 份和表面相容剂 0.4~0.8 份投入容器中混合均匀，再依次投入按重量份数称取的酚醛树脂 30~33 份、甲阶酚醛树脂 6~9 份、固化剂 2.5~4.2 份、玻璃微珠 11~12 份、复合脱模剂 1.3~1.8 份、矿物填料 14~19 份、氮化硅 3~6 份和阻燃剂 6 ～ 9 份，继续混合 8-10min ，而后转移至开炼机开炼 5-6min ，最后经拉片、冷却和粉碎，得到玻璃微珠填充的酚醛高分子复合材料。优点：具有强度高，加工方便的特点。经过测试，弯曲强度 86MPa, 热变形温度 240 ℃ , 阻燃性达到 V-0 等级。

Description

玻璃微珠填充的酚醛高分子复合材料的制备方法
技术领域
本发明属于热固性模塑料制备技术领域，具体涉及一种玻璃微珠填充的酚醛高分子复合材料的制备方法。
背景技术
酚醛高分子材料以其优异的性能而被广泛的应用于电子领域，但是在耐热阻燃指标方面仍有待于提高。玻璃微珠是一种耐温好，比重轻的填料，可以改善材料的耐热性能。因此制备具有良好的耐热效果的玻璃微珠填充的酚醛高分子复合材料具有积极意义。
发明内容
本发明的任务是要提供一种玻璃微珠填充的酚醛高分子复合材料的制备方法，该方法获得的酚醛高分子复合材料具有优异的阻燃、耐热和电气绝缘性能。
本发明的目的是这样来达到的，一种玻璃微珠填充的酚醛高分子复合材料的制备方法，其是先将按重量份数称取的金属氧化物0.8~1.5份、增强纤维14~18份和表面相容剂0.4~0.8份投入容器中混合均匀，再依次投入按重量份数称取的酚醛树脂30~33份、甲阶酚醛树脂6~9份、固化剂2.5~4.2份、玻璃微珠11~12份、复合脱模剂1.3~1.8份、矿物填料14~19份、氮化硅3~6份和阻燃剂6～9份，继续混合8-10min，而后转移至开炼机开炼5-6min，最后经拉片、冷却和粉碎，得到玻璃微珠填充的酚醛高分子复合材料。
在本发明的一个具体的实施例中，所述的酚醛树脂为草酸法生产的酚醛树脂；所述的甲阶酚醛树脂为碱催化合成的酚醛树脂。
在本发明的另一个具体的实施例中，所述的固化剂为六次亚甲基四胺；所述的金属氧化物是指氧化锌。
在本发明的又一个具体的实施例中，所述的玻璃微珠为空心玻璃微珠。
在本发明的再一个具体的实施例中，所述的复合脱模剂由重量百分比为20%的硬脂酸钙和重量百分比为80%的硬脂酸锌组成。
在本发明的还有一个具体的实施例中，所述的矿物填料为氢氧化铝。
在本发明的更而一个具体的实施例中，所述的氮化硅为长径比200～250的氮化硅晶须。
在本发明的进而一个具体的实施例中，所述的增强纤维为长度为3mm的玻璃纤维。
在本发明的又更而一个具体的实施例中，所述的表面相容剂为乙烯基三甲氧基硅烷。
在本发明的又进而一个具体的实施例中，所述的阻燃剂为十溴二苯乙烷。
本发明方法得到的玻璃微珠填充的酚醛高分子复合材料具有强度高，加工方便的特点。经过测试，弯曲强度86MPa,热变形温度240℃, 阻燃性达到V-0等级（UL-94-V-0 1.6mm）。
具体实施方式
实施例1：
先将按重量份数称取的氧化锌0.8份、长度为3mm的玻璃纤维16份和乙烯基三甲氧基硅烷0.4份投入容器中混合均匀，再依次投入按重量份数称取的草酸法生产的酚醛树脂33份、碱催化合成的酚醛树脂6份、六次亚甲基四胺3份、空心玻璃微珠11份、由质量百分比为20%的硬脂酸钙和质量百分比为80%的硬脂酸锌组成的复合脱模剂 1.5份、氢氧化铝14份、长径比为200～250的氮化硅晶须6份和十溴二苯乙烷6份，继续混合8-10min，而后转移至开炼机开炼5-6min，最后经拉片、冷却和粉碎，得到玻璃微珠填充的酚醛高分子复合材料。
实施例2：
先将按重量份数称取的氧化锌1.5份、长度为3mm的玻璃纤维14份和乙烯基三甲氧基硅烷0.5份投入容器中混合均匀，再依次投入按重量份数称取的草酸法生产的酚醛树脂30份、碱催化合成的酚醛树脂9份、六次亚甲基四胺2.5份、空心玻璃微珠11.5份、由质量百分比为20%的硬脂酸钙和质量百分比为80%的硬脂酸锌组成的复合脱模剂 1.3份、氢氧化铝19份、长径比为200～250的氮化硅晶须3份和十溴二苯乙烷9份，继续混合8-10min，而后转移至开炼机开炼5-6min，最后经拉片、冷却和粉碎，得到玻璃微珠填充的酚醛高分子复合材料。
实施例3：
先将按重量份数称取的氧化锌1份、长度为3mm的玻璃纤维18份和乙烯基三甲氧基硅烷0.6份投入容器中混合均匀，再依次投入按重量份数称取的草酸法生产的酚醛树脂31份、碱催化合成的酚醛树脂8份、六次亚甲基四胺4.2份、空心玻璃微珠12份、由质量百分比为20%的硬脂酸钙和质量百分比为80%的硬脂酸锌组成的复合脱模剂 1.8份、氢氧化铝16份、长径比为200～250的氮化硅晶须4份和十溴二苯乙烷7份，继续混合8-10min，而后转移至开炼机开炼5-6min，最后经拉片、冷却和粉碎，得到玻璃微珠填充的酚醛高分子复合材料。
实施例4：
先将按重量份数称取的氧化锌1.3份、长度为3mm的玻璃纤维17份和乙烯基三甲氧基硅烷0.8份投入容器中混合均匀，再依次投入按重量份数称取的草酸法生产的酚醛树脂32份、碱催化合成的酚醛树脂7份、六次亚甲基四胺3.5份、空心玻璃微珠11.7份、由质量百分比为20%的硬脂酸钙和质量百分比为80%的硬脂酸锌组成的复合脱模剂 1.6份、氢氧化铝18份、长径比为200～250的氮化硅晶须5份和十溴二苯乙烷8份，继续混合8-10min，而后转移至开炼机开炼5-6min，最后经拉片、冷却和粉碎，得到玻璃微珠填充的酚醛高分子复合材料。
由实施例1至4得到的玻璃微珠填充的酚醛高分子复合材料具有下表所述的技术指标：

Claims (7)

1.一种玻璃微珠填充的酚醛高分子复合材料的制备方法，其特征在于其是先将按重量份数称取的金属氧化物0.8~1.5份、增强纤维14~18份和表面相容剂0.4~0.8份投入容器中混合均匀，再依次投入按重量份数称取的酚醛树脂30~33份、甲阶酚醛树脂6~9份、固化剂2.5~4.2份、玻璃微珠11~12份、复合脱模剂1.3~1.8份、矿物填料14~19份、氮化硅3~6份和阻燃剂6～9份，继续混合8-10min，而后转移至开炼机开炼5-6min，最后经拉片、冷却和粉碎，得到玻璃微珠填充的酚醛高分子复合材料，所述的酚醛树脂为草酸法生产的酚醛树脂；所述的甲阶酚醛树脂为碱催化合成的酚醛树脂，所述的固化剂为六次亚甲基四胺；所述的金属氧化物是指氧化锌，所述的矿物填料为氢氧化铝。
2.根据权利要求1所述的玻璃微珠填充的酚醛高分子复合材料的制备方法，其特征在于所述的玻璃微珠为空心玻璃微珠。
3.根据权利要求1所述的玻璃微珠填充的酚醛高分子复合材料的制备方法，其特征在于所述的复合脱模剂由重量百分比为20%的硬脂酸钙和重量百分比为80%的硬脂酸锌组成。
4.根据权利要求1所述的玻璃微珠填充的酚醛高分子复合材料的制备方法，其特征在于所述的氮化硅为长径比200～250的氮化硅晶须。
5.根据权利要求1所述的玻璃微珠填充的酚醛高分子复合材料的制备方法，其特征在于所述的增强纤维为长度为3mm的玻璃纤维。
6.根据权利要求1所述的玻璃微珠填充的酚醛高分子复合材料的制备方法，其特征在于所述的表面相容剂为乙烯基三甲氧基硅烷。
7.根据权利要求1所述的玻璃微珠填充的酚醛高分子复合材料的制备方法，其特征在于所述的阻燃剂为十溴二苯乙烷。
CN2012103505329A 2012-09-20 2012-09-20 玻璃微珠填充的酚醛高分子复合材料的制备方法 Expired - Fee Related CN102875959B (zh)