CN103183903A - 一种阻燃的环氧树脂改性的酚醛树脂成型材料 - Google Patents

一种阻燃的环氧树脂改性的酚醛树脂成型材料 Download PDF

Info

Publication number
CN103183903A
CN103183903A CN2011104429224A CN201110442922A CN103183903A CN 103183903 A CN103183903 A CN 103183903A CN 2011104429224 A CN2011104429224 A CN 2011104429224A CN 201110442922 A CN201110442922 A CN 201110442922A CN 103183903 A CN103183903 A CN 103183903A
Authority
CN
China
Prior art keywords
epoxy resin
parts
fire
resol
formed material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011104429224A
Other languages
English (en)
Inventor
金蒙娜
金惠良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU YAMEI MANNEQUINS Co Ltd
Original Assignee
CHANGSHU YAMEI MANNEQUINS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU YAMEI MANNEQUINS Co Ltd filed Critical CHANGSHU YAMEI MANNEQUINS Co Ltd
Priority to CN2011104429224A priority Critical patent/CN103183903A/zh
Publication of CN103183903A publication Critical patent/CN103183903A/zh
Pending legal-status Critical Current

Abstract

一种阻燃的环氧树脂改性的酚醛树脂成型材料，属于热固性模塑料技术领域。其特征在于其包含以下组份：酚醛树脂40~44份；固化剂3.6~7.5份；固化促进剂0.6~1.2份；环氧树脂4~7份；脱模剂1.2~2.0份；矿物填料38~44份；增强纤维23~25份；阻燃剂4～8份。具有耐热性能好、强度好、成型方便的特点。

Description

一种阻燃的环氧树脂改性的酚醛树脂成型材料
技术领域
本发明属于热固性模塑料技术领域，具体涉及一种阻燃的环氧树脂改性的酚醛树脂成型材料。
背景技术
酚醛模塑料具有较好的强度和耐候性，而环氧树脂具有很好的黏结性，但是，由于酚醛树脂和环氧树脂的阻燃性能均较为逊色，因此，工业上应用受到限制。
发明内容
本发明的任务是要提供一种兼有良好的阻燃性与粘结性的阻燃的环氧树脂改性的酚醛树脂成型材料。
本发明的任务是这样来完成的，一种阻燃的环氧树脂改性的酚醛树脂成型材料，其包含以下组份：
Figure BDA0000125236720000011
本发明的一个实施例中，所述的酚醛树脂为酸法生产的酚醛树脂。
本发明的另一个实施例中，所述的固化剂为六次亚甲基四胺。
本发明的又一个实施例中，所述的固化促进剂为氧化镁。
本发明的再一个实施例中，所述的环氧树脂为双酚A型环氧树脂。
本发明的还有一个实施例中，所述的脱模剂为硬脂酸锂。
本发明的更而一个实施例中，所述的矿物填料为氢氧化铝。
本发明的进而一个实施例中，所述的增强纤维为玻璃纤维。
本发明的又更而一个实施例中，所述的阻燃剂为四溴双酚A或八溴二苯乙烷。
本发明提供的阻燃的环氧树脂改性的酚醛树脂成型材料具有耐热性能好、强度好、成型方便的特点。经过测试，弯曲强度88MPa，热变形温度240℃，阻燃性达到V-0等级(UL-94-V-0 1.6mm)。
具体实施方式
实施例1
Figure BDA0000125236720000021
具体实施时，首先依次准确称量上述原料，然后混合均匀，转移至开炼机上热混合6分钟，接着拉片、冷却、粉碎，即得本色的阻燃的环氧树脂改性的酚醛树脂成型材料。
实施例2
Figure BDA0000125236720000022
具体实施时，首先依次准确称量上述原料，然后混合均匀，转移至开炼机上热混合6分钟，接着拉片、冷却、粉碎，即得黑色的阻燃的环氧树脂改性的酚醛树脂成型材料。
实施例3
Figure BDA0000125236720000023
Figure BDA0000125236720000031
具体实施时，首先依次准确称量上述原料，然后混合均匀，转移至开炼机上热混合6分钟，接着拉片、冷却、粉碎，即得红色的阻燃的环氧树脂改性的酚醛树脂成型材料。
实施例4
Figure BDA0000125236720000032
具体实施时，首先依次准确称量上述原料，然后混合均匀，转移至开炼机上热混合6分钟，接着拉片、冷却、粉碎，即得黄色的阻燃的环氧树脂改性的酚醛树脂成型材料。
经过测试，上述阻燃的环氧树脂改性的酚醛树脂成型材料具有如下性能：
Figure BDA0000125236720000033

Claims (9)

1.一种阻燃的环氧树脂改性的酚醛树脂成型材料，其特征在于其包含以下组份：
酚醛树脂      40~44份；
固化剂        3.6~7.5份；
固化促进剂    0.6~1.2份；
环氧树脂      4~7份；
脱模剂        1.2~2.0份；
矿物填料      38~44份；
增强纤维      23~25份；
阻燃剂        4～8份。
2.根据权利要求1所述的一种阻燃的环氧树脂改性的酚醛树脂成型材料，其特征在于所述的酚醛树脂为酸法生产的酚醛树脂。
3.根据权利要求1所述的一种阻燃的环氧树脂改性的酚醛树脂成型材料，其特征在于所述的固化剂为六次亚甲基四胺。
4.根据权利要求1所述的一种阻燃的环氧树脂改性的酚醛树脂成型材料，其特征在于所述的固化促进剂为氧化镁。
5.根据权利要求1所述的一种阻燃的环氧树脂改性的酚醛树脂成型材料，其特征在于所述的环氧树脂为双酚A型环氧树脂。
6.根据权利要求1所述的一种阻燃的环氧树脂改性的酚醛树脂成型材料，其特征在于所述的脱模剂为硬脂酸锂。
7.根据权利要求1所述的一种阻燃的环氧树脂改性的酚醛树脂成型材料，其特征在于所述的矿物填料为氢氧化铝。
8.根据权利要求1所述的一种阻燃的环氧树脂改性的酚醛树脂成型材料，其特征在于所述的增强纤维为玻璃纤维。
9.根据权利要求1所述的一种阻燃的环氧树脂改性的酚醛树脂成型材料，其特征在于所述的阻燃剂为四溴双酚A或八溴二苯乙烷。
CN2011104429224A 2011-12-27 2011-12-27 一种阻燃的环氧树脂改性的酚醛树脂成型材料 Pending CN103183903A (zh)