CN103160073A - 改性的酚醛玻璃钢复合材料 - Google Patents

改性的酚醛玻璃钢复合材料 Download PDF

Info

Publication number
CN103160073A
CN103160073A CN2011104223838A CN201110422383A CN103160073A CN 103160073 A CN103160073 A CN 103160073A CN 2011104223838 A CN2011104223838 A CN 2011104223838A CN 201110422383 A CN201110422383 A CN 201110422383A CN 103160073 A CN103160073 A CN 103160073A
Authority
CN
China
Prior art keywords
parts
reinforced plastics
matrix material
fiberglass reinforced
plastics matrix
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011104223838A
Other languages
English (en)
Inventor
叶法冬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU CITY FADONG PLASTIC INDUSTRY Co Ltd
Original Assignee
CHANGSHU CITY FADONG PLASTIC INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU CITY FADONG PLASTIC INDUSTRY Co Ltd filed Critical CHANGSHU CITY FADONG PLASTIC INDUSTRY Co Ltd
Priority to CN2011104223838A priority Critical patent/CN103160073A/zh
Publication of CN103160073A publication Critical patent/CN103160073A/zh
Pending legal-status Critical Current

Abstract

一种改性的酚醛玻璃钢复合材料，属于高分子材料技术领域。其是由以下重量份数的原料构成：酚醛树脂 43~47 份；固化剂 3~5.5 份；固化促进剂 1.1~1.8 份；冲击改性剂 6 ～ 8 份；脱模剂 1.5~2.0 份；矿物填料 40~44 份；增强纤维 18~22 份。本发明提供的改性的酚醛玻璃钢复合材料具有耐热性能好、强度高、成型方便的特点。

Description

改性的酚醛玻璃钢复合材料
技术领域
本发明属于高分子材料技术领域，具体涉及一种改性的酚醛玻璃钢复合材料。
背景技术
酚醛玻璃钢材料具有优良的刚性，但是缺乏很好的韧性。在很多冲击的场合，由于酚醛玻璃钢材料的冲击强度低而导致材料不适用。
发明内容
本发明的任务是要提供一种具有优异的耐冲击效果而藉以适应冲击的场合的改性的酚醛玻璃钢复合材料。
本发明的任务是这样来完成的，一种改性的酚醛玻璃钢复合材料，其是由以下重量份数的原料构成：
酚醛树脂    43～47份；
固化剂      3～5.5份；
固化促进剂  1.1～1.8份；
冲击改性剂  6～8份；
脱模剂      1.5～2.0份；
矿物填料    40～44份；
增强纤维    18～22份。
本发明的一个实施例中，所述的酚醛树脂是指酸法生产的酚醛树脂。
本发明的另一个实施例中，所述的固化剂是指六次亚甲基四胺。
本发明的又一个实施例中，所述的固化促进剂是氧化镁。
本发明的再一个实施例中，所述的冲击改性剂是抗冲苯乙烯。
本发明的还一个实施例中，所述的脱模剂是硬脂酸钙。
本发明的更而一个实施例中，所述的矿物填料是指滑石粉。
本发明的进而一个实施例中，所述的增强纤维是玻璃纤维。
本发明提供的改性的酚醛玻璃钢复合材料具有耐热性能好、强度高、成型方便的特点。经过测试，弯曲强度85MPa，热变形温度240℃，冲击强度(缺口)大于2.8kj/m2。
具体实施方式
实施例1
酚醛树脂            43份；
六次亚甲基四胺      3份；
氧化镁              1.1份；
抗冲聚苯乙烯        6.1份；
硬脂酸钙            1.5份；
滑石粉              40份；
玻璃纤维            18份。
具体实施时，首先依次准确称量上述原料，然后混合均匀，转移至开炼机上热混合6分钟，接着拉片、冷却、粉碎，即得本色的耐冲击改性的酚醛玻璃钢复合材料。
实施例2
酚醛树脂            45份；
六次亚甲基四胺      3.8份；
氧化镁              1.3份；
抗冲聚苯乙烯        6.7份；
硬脂酸钙            1.8份；
滑石粉              41份；
玻璃纤维            19份；
碳黑                1份。
具体实施时，首先依次准确称量上述原料，然后混合均匀，转移至开炼机上热混合6分钟，接着拉片、冷却、粉碎，即得黑色的耐冲击改性的酚醛玻璃钢复合材料。
实施例3
酚醛树脂              46份；
六次亚甲基四胺        4.7份；
氧化镁                1.6份；
抗冲聚苯乙烯          7.3份；
硬脂酸钙              1.9份；
滑石粉                43份；
玻璃纤维              21份；
酞氰蓝                2份。
具体实施时，首先依次准确称量上述原料，然后混合均匀，转移至开炼机上热混合6分钟，接着拉片、冷却、粉碎，即得蓝色的耐冲击改性的酚醛玻璃钢复合材料。
实施例4
酚醛树脂              47份；
六次亚甲基四胺        5.3份；
氧化镁                1.8份；
抗冲聚苯乙烯          7.9份；
硬脂酸钙              2.0份；
滑石粉                44份；
玻璃纤维              22份；
酞氰绿                2份.
具体实施时，首先依次准确称量上述原料，然后混合均匀，转移至开炼机上热混合6分钟，接着拉片、冷却、粉碎，即得绿色的耐冲击改性的酚醛玻璃钢复合材料。
经过测试，上述耐冲击改性的酚醛玻璃钢复合材料具有如下性能：
Figure BDA0000121082140000031

Claims (8)

1.一种改性的酚醛玻璃钢复合材料，其特征在于其是由以下重量份数的原料构成：
酚醛树脂      43~47份；
固化剂        3~5.5份；
固化促进剂    1.1~1.8份；
冲击改性剂    6～8份；
脱模剂        1.5~2.0份；
矿物填料      40~44份；
增强纤维      18~22份。
2.根据权利要求1所述的改性的酚醛玻璃钢复合材料，其特征在于所述的酚醛树脂是指酸法生产的酚醛树脂。
3.根据权利要求1所述的改性的酚醛玻璃钢复合材料，其特征在于所述的固化剂是指六次亚甲基四胺。
4.根据权利要求1所述的改性的酚醛玻璃钢复合材料，其特征在于所述的固化促进剂是氧化镁。
5.根据权利要求1所述的改性的酚醛玻璃钢复合材料，其特征在于所述的冲击改性剂是抗冲苯乙烯。
6.根据权利要求1所述的改性的酚醛玻璃钢复合材料，其特征在于所述的脱模剂是硬脂酸钙。
7.根据权利要求1所述的改性的酚醛玻璃钢复合材料，其特征在于所述的矿物填料是指滑石粉。
8.根据权利要求1所述的改性的酚醛玻璃钢复合材料，其特征在于所述的增强纤维是玻璃纤维。
CN2011104223838A 2011-12-16 2011-12-16 改性的酚醛玻璃钢复合材料 Pending CN103160073A (zh)