CN109694944A - 一种封头热处理工艺 - Google Patents

一种封头热处理工艺 Download PDF

Info

Publication number
CN109694944A
CN109694944A CN201710992719.1A CN201710992719A CN109694944A CN 109694944 A CN109694944 A CN 109694944A CN 201710992719 A CN201710992719 A CN 201710992719A CN 109694944 A CN109694944 A CN 109694944A
Authority
CN
China
Prior art keywords
heat treatment
thermal chamber
seal head
end socket
treatment technology
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710992719.1A
Other languages
English (en)
Inventor
王立新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YIXING LIANFENG CHEMICAL MACHINERY CO Ltd
Original Assignee
YIXING LIANFENG CHEMICAL MACHINERY CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YIXING LIANFENG CHEMICAL MACHINERY CO Ltd filed Critical YIXING LIANFENG CHEMICAL MACHINERY CO Ltd
Priority to CN201710992719.1A priority Critical patent/CN109694944A/zh
Publication of CN109694944A publication Critical patent/CN109694944A/zh
Pending legal-status Critical Current

Abstract

一种封头热处理工艺，包括以下步骤：（1）先将热处理室内温度加热至330~370℃，保持7~10min；（2）将封头放入加热后的热处理室，先逐步加热到450~485℃之间，保持125~160min，后移出热处理室；（3）将热处理室移出的封头吊住浸入水中进行冷却，然后吊出放置自然风干。

Description

一种封头热处理工艺
技术领域
本发明属于封头生产相关领域，具体涉及一种封头热处理工艺。
背景技术
目前，大部分封头厂都采用去应力退火进行热处理。但在实际工作中发现，对于成形时变形量较大的封头，虽然采取了退应力退火处理，但在压力容器的使用过程中还是出现了裂纹，甚至在封头与筒体焊接过程中也出现过裂纹。同时对于封头的热处理，没有精确可控的方法，整体热处理效果不佳，产品质量不高，不符合实际使用要求。
发明内容
发明目的：本发明的目的是为了克服现有技术中的不足，提供控制精确，有效提高产品质量的封头热处理工艺。
技术方案：为了解决上述技术问题，采用以下技术方案：一种封头热处理工艺，包括以下步骤：
（1）先将热处理室内温度加热至330~370℃，保持7~10min；
（2）将封头放入加热后的热处理室，先逐步加热到450~485℃之间，保持125~160min，后移出热处理室；
（3）将热处理室移出的封头吊住浸入水中进行冷却，然后吊出放置自然风干。
有益效果：本发明中的封头热处理工艺，能较好的恢复材料的性能，其温度控制精确，既满足标准要求，又达到良好的使用效果，有效提高产品质量，符合实际使用要求。
具体实施方式
实施例：一种封头热处理工艺，包括以下步骤：（1）先将热处理室内温度加热至330~370℃，保持7~10min；（2）将封头放入加热后的热处理室，先逐步加热到450~485℃之间，保持125~160min，后移出热处理室；（3）将热处理室移出的封头吊住浸入水中进行冷却，然后吊出放置自然风干。

Claims (1)

1.一种封头热处理工艺，其特征在于，包括以下步骤：
（1）先将热处理室内温度加热至330~370℃，保持7~10min；
（2）将封头放入加热后的热处理室，先逐步加热到450~485℃之间，保持125~160min，后移出热处理室；
（3）将热处理室移出的封头吊住浸入水中进行冷却，然后吊出放置自然风干。
CN201710992719.1A 2017-10-23 2017-10-23 一种封头热处理工艺 Pending CN109694944A (zh)