CN109440245A - 一种抗菌复合纱线及其制备方法 - Google Patents
一种抗菌复合纱线及其制备方法 Download PDFInfo
- Publication number
- CN109440245A CN109440245A CN201910022298.9A CN201910022298A CN109440245A CN 109440245 A CN109440245 A CN 109440245A CN 201910022298 A CN201910022298 A CN 201910022298A CN 109440245 A CN109440245 A CN 109440245A
- Authority
- CN
- China
- Prior art keywords
- fiber
- scribbled
- composite yarns
- silver
- antimicrobial composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗菌复合纱线,所述复合纱线由混纺纱线与金属铜丝合股而成,其中混纺纱线由镀银纤维与纺纱纤维混纺而成,该抗菌复合纱线制备方法为先将纤维基材经化学镀银或真空镀银形成镀银纤维,以及将镀银纤维与纺纱纤维混纺制成混纺纱线;再将纯铜或者含铜合金经拉丝制成金属铜丝;最后将将混纺纱线与一个根金属铜丝合股制成复合纱线。该复合纱线自始至终保持高效的抗菌效果,此外,抗菌复合纱线还具有导电性以及非常优异的抗静电性能和防辐射性能。
Description
技术领域
本发明涉及生活用品领域,更具体地说,它涉及一种抗菌复合纱线及其制备方法。
背景技术
纺织品纤维是一个细菌的良好寄宿地。在使用或穿着过程中,特别是那些贴身穿的内衣裤,袜子等,由于其特定的温度和湿度特别容易滋生细菌,这不仅会产生不愉快的气味,而且还可能引起皮肤瘙痒,严重的情况下还可能通过接触转播疾病或者是引起交叉感染。随着生活水平的提高,人们对健康和清洁问题越来越关心,对于纺织品的要求也不再仅仅局限于原有的功能,这表现在对卫生清洁保健等功能的需求不断提高。由此可以预测抗菌纺织品的应用和需求会越来越多。
抗菌纺织品既可以由成品或半成品直接经过抗菌整理而制得、也可以由抗菌纱线通过织造而制得。整理工艺相对来说操作简单、成本低廉,但通过整理得到的产品的抗菌效果普遍具有持久性差的缺点,往往会随着洗涤次数的增加而显著下降、最终失去原用的抗菌效果。因此要想得到持久高效的抗菌产品,必须先制得持久高效的抗菌纱线。
抗菌剂是抗菌产品中必不可少的核心成分。抗菌剂的种类以及数量虽然繁多,但最常用的,目前最流行的是银离子和铜离子抗菌剂,主要是因为,相对于其他类型的抗菌剂,银离子、铜离子抗菌剂具有高效、广谱和安全的特点。不过,基于银离子的抗菌效果远远高于铜离子的抗菌效果这样一个事实,这也就说明了为什么即使银比铜贵很多,但人们还是热衷于银离子抗菌剂的原因所在。此外,抗菌剂的种类和添加方法决定了产品是否具有持久抗菌效果。例如,含银沸石或者氧化铜的熔融纺丝,镀银纤维等,由于抗菌剂跟基材纤维溶合为一体,因此具有持久效果。
中国专利CN205711179U公开了一种功能抗菌面料的制造方法。其中涉及到一种含镀银纤维和/或含铜纤维与其它纤维的混纺纱线,其中所述的含镀银纤维和含铜纤维是在基纤维的表层通过物理喷射而制得的短纤维。但无论是通过化学或者物理的方法,例如化学镀或者真空溅射,包覆在基层纤维表面上的铜层很容易被氧化,且氧化后的产物在水分的作用下转变为铜盐。一般情况下,镀铜层非常薄,不超过1微米,因此整个铜层都可能迅速被氧化变成铜盐,而铜盐本身的强度就很低,加上跟底层基材纤维的表面不具有牢固的结合,因此极容易从纤维表面上剥落下来,最终导致抗菌效果的下降。
发明内容
针对现有技术存在的不足,本发明提供了一种具有持久高效的抗菌复合纱线。
一种抗菌复合纱线,所述复合纱线由混纺纱线与金属铜丝合股而成,其中混纺纱线由镀银纤维与纺纱纤维混纺而成。
本发明进一步设置:所述镀银纤维由纤维基材经化学镀银或真空镀银形成,纤维基材为锦纶纤维、涤纶纤维、丙纶纤维或腈纶纤维的一种或多种。
本发明进一步设置:所述纺纱纤维为棉、麻、再生纤维素纤维、竹纤维、莫代尔、锦纶、涤纶、腈纶、丙纶、维纶或羊毛的一种或多种。
本发明进一步设置:该金属铜丝是由纯铜或者含铜合金经拉丝制成,其直径为1~60微米。
本发明进一步设置:其中含铜合金中的铜含量不低于50%重量。
本发明还提供一种抗菌复合纱线的制备方法,包括以下步骤:
1)、将纤维基材经化学镀银或真空镀银形成镀银纤维;
2)、将镀银纤维与纺纱纤维混纺制成混纺纱线;
3)、将纯铜或者含铜合金经拉丝制成金属铜丝;
4)、将混纺纱线与一个根金属铜丝合股制成复合纱线。
本发明进一步设置:所述混纺纱线中镀银纤维和纺纱纤维重量比:镀银纤维为1~5%,纺纱纤维95~99%。
本发明进一步设置:其中步骤4中的混纺纱线支数为30~60。
本发明有益效果:镀银纤维和铜丝均具抗菌效果,将银和铜均匀混进纱线中,通过银铜的协同作用,其总体的抗菌效果有飞跃性的提高。
其中镀银纤维在潮湿的环境下具有超强的抗菌效果,但在干燥的环境下却没有,铜虽然在潮湿的环境下有抗菌效果,但效果远远不及银,不过,在干燥的环境下铜通过一种被称之为接触杀菌的特殊机制,对很多种病原体微生物,细菌,酵母和病毒都有很好的抑制效果,对某些细菌而言,接触时间数秒、数十秒就可达到灭菌的效果。
两者同时使用可以互相弥补各自的短处,让纱线以至于织物无论是处在干燥或者潮湿的环境下都具有卓越的抗菌效果,这是银或者铜单独使用时不具有的特征。此外,使用金属铜丝可以彻底防止因为氧化引起的镀层剥落而最终导致的抗菌效果的下降,自始至终保持高效的抗菌效果。即使经过100次水洗后对常见的几种细菌,例如,大肠杆菌、金色葡萄球菌、白色念珠菌的抑菌率仍然高达99.9%。此外,抗菌复合纱线还具有导电性以及非常优异的抗静电性能和防辐射性能。
具体实施方式
下面以具体的实例对本发明做进一步阐述,其中举例说明,仅用于说明,并不限制发明的范围。实施例中未注明具体技术和条件者,按照本领域内的文献所描述的技术或条件或者按产品说明进行。所用试剂或设备,均为可以通过市购获得的常规产品。
一种抗菌复合纱线,所述复合纱线由混纺纱线与金属铜丝合股而成,其中混纺纱线由镀银纤维与纺纱纤维混纺而成。
其中所述镀银纤维由纤维基材经化学镀银或真空镀银形成,纤维基材为锦纶纤维、涤纶纤维、丙纶纤维或腈纶纤维的一种或多种。
其中所述纺纱纤维为棉、麻、再生纤维素纤维、竹纤维、莫代尔、锦纶、涤纶、腈纶、丙纶、维纶或羊毛的一种或多种。
其中该金属铜丝是由纯铜或者含铜合金经拉丝制成,其直径为1~60微米。
本发明还提供一种如何该抗菌复合纱线的制备方法,具体描述如下:一种抗菌复合纱线的制备方法,包括以下步骤:
1)、将纤维基材经化学镀银或真空镀银形成镀银纤维;
2)、将镀银纤维与纺纱纤维混纺制成混纺纱线;
3)、将纯铜或者含铜合金经拉丝制成金属铜丝;
4)、将混纺纱线与一个根金属铜丝合股制成复合纱线。
其中所述混纺纱线中镀银纤维和纺纱纤维重量比:镀银纤维为1~5%,纺纱纤维95~99%,其中步骤4中的混纺纱线支数为30~60。
为了进一步说明制备方法,还提供两种具体实施方案:
实施了1:将重量比1%的镀银纤维为和99%的棉纤维混合开松后经紧密赛络纺纺纱工艺制成混纺纱线,其中所述混纺纱线支数为50S。将上述混纺纱线与一根直径为30微米的纯铜丝经合股制成复合纱线。按照国家标准《FZ/T73023-2006(震荡法)附录C水洗50次》进行检查,对大肠杆菌、金色葡萄球菌和白色念珠菌的抑菌率均大于99.9%。该复合纱线保留了棉纱的特性,手感柔软,可在多种纺织品中得到应用。
实施例2:将重量比2%的镀银纤维、49%的棉纤维,49%的涤纶纤维混合开松后经紧密赛络纺纺纱工艺制成混纺纱线,其中所述混纺纱线支数为32S。将上述混纺纱线与一根直径为30微米的合金铜丝经合股制成复合纱线。按照国家标准《FZ/T73023-2006(震荡法)附录C水洗50次》进行检查,对大肠杆菌、金色葡萄球菌和白色念珠菌的抑菌率均大于99.9%。所得复合纱线保留了涤棉纱的特性,手感柔软,可在多种纺织品中得到应用。
以上所述仅是本发明的优选实施方式,本发明的保护范围并不仅局限于上述实施例,凡属于本发明思路下的技术方案均属于本发明的保护范围。应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理前提下的若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (8)
1.一种抗菌复合纱线,其特征是:所述复合纱线由混纺纱线与金属铜丝合股而成,其中混纺纱线由镀银纤维与纺纱纤维混纺而成。
2.根据权利要求1所述的一种抗菌复合纱线,其特征是:所述镀银纤维由纤维基材经化学镀银或真空镀银形成,纤维基材为锦纶纤维、涤纶纤维、丙纶纤维或腈纶纤维的一种或多种。
3.根据权利要求1所述的一种抗菌复合纱线,其特征是:所述纺纱纤维为棉、麻、再生纤维素纤维、竹纤维、莫代尔、锦纶、涤纶、腈纶、丙纶、维纶或羊毛的一种或多种。
4.根据权利要求1所述的一种抗菌复合纱线,其特征是:该金属铜丝是由纯铜或者含铜合金经拉丝制成,其直径为1~60微米。
5.根据权利要求4所述的一种抗菌复合纱线,其特征是:其中含铜合金中的铜含量不低于50%重量。
6.一种抗菌复合纱线的制备方法,其特征是:包括以下步骤:
1)、将纤维基材经化学镀银或真空镀银形成镀银纤维;
2)、将镀银纤维与纺纱纤维混纺制成混纺纱线;
3)、将纯铜或者含铜合金经拉丝制成金属铜丝;
4)、将混纺纱线与一个根金属铜丝合股制成复合纱线。
7.根据权利要求6所述的一种抗菌复合纱线的制备方法,其特征是:所述混纺纱线中镀银纤维和纺纱纤维重量比:镀银纤维为1~5%,纺纱纤维95~99%。
8.根据权利要求6所述的一种抗菌复合纱线的制备方法,其特征是:其中步骤4中的混纺纱线支数为30~60。