CN109424135A - The technique that the putty of metope in building is coated - Google Patents
The technique that the putty of metope in building is coated Download PDFInfo
- Publication number
- CN109424135A CN109424135A CN201710788981.4A CN201710788981A CN109424135A CN 109424135 A CN109424135 A CN 109424135A CN 201710788981 A CN201710788981 A CN 201710788981A CN 109424135 A CN109424135 A CN 109424135A
- Authority
- CN
- China
- Prior art keywords
- putty
- coating
- metope
- smooth
- brush
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses the techniques that the putty of metope in a kind of pair of building is coated, comprising the following steps: base treatment repairs, scrapes first pass putty and polish, scrape second time putty and polish, under-coating varnish, mend putty again, polish, second coating, polish, third road coating.The step of technique, is simple, shortens construction period, has standardized operation, it can be improved the flatness of metope, resource has been saved, has solved existing putty coating processes low efficiency, has been constructed according to the experience of worker oneself, the experience of each worker is different, it causes quality different, so that the flatness of metope is affected, causes to do over again, waste of resource, the problem of extending the duration.
Description
Technical field
The present invention relates to a kind of technique, the technique coated more particularly, to the putty of metope in a kind of pair of building.
Background technique
Powder of lacquer putty for use on is one kind of building decoration materials, and main component is talcum powder and glue.The rough house table just purchased
One layer of white --- the putty in face, the whiteness of usual putty is in 90 or more fineness 330 or more.Putty is looked for for wall-surface patching
A kind of flat substrate is laid a good foundation for decoration in next step (brush paint wallpaper).Putty is divided into interior wall and two kinds of exterior wall,
Exterior wall putty to resist exposing to the weather so colloidality is big, intensity is high, and environmentally friendly index is slightly lower.Inner wall putty composite index is preferable, is good for
Kang Huanbao, so interior wall not external application, exterior wall is not interior to be used.Usual putty is gypsum or cement base, and such rough surface compares
It is secured to be easy bonding.But a bed boundary Ji Lai sealing base is still brushed in base when construction while improving wall
Putty can be preferably bonded on basal plane for the adhesive force in face.Putty (fillering) is a kind of decoration type of smooth surface of wall
Material is a kind of thick slurry coating material, is essential a kind of product before coating paints.Painting is imposed on priming paint or is directly applied and imposes on
On object, to remove rugged defect on coated article surface.Using a small amount of Qi Ji, auxiliary agent, mass filler and suitable
Coloring pigment is formulated, and pigment used is mainly iron oxide red, carbon black, chrome yellow etc..Filler is mainly calcium bicarbonate, talcum powder etc..
The working surface that there is recess in part can be filled up, can also be struck off in all surfaces, usually after prime coat parches, be applied over priming paint
Layer surface.It is required that adhesion is good, does not crack in baking process.Existing putty coating processes low efficiency is all according to work
The experience of people oneself is constructed, and the experience of each worker is different, causes quality different, so that the flatness of metope is by shadow
It rings, causes to do over again, waste of resource extends the duration.
Summary of the invention
It is all the experience according to worker oneself it is an object of the invention to overcome above-mentioned existing putty coating processes low efficiency
It constructs, the experience of each worker is different, and it causes quality different, so that the flatness of metope is affected, causes to do over again, wave
The problem of taking resource, extending the duration technique that the putty of metope in a kind of pair of building is coated is devised, the technique
Step is simple, shortens construction period, has standardized operation, can be improved the flatness of metope, has saved resource, solves existing
Putty coating processes low efficiency is constructed according to the experience of worker oneself, and the experience of each worker is different, causes quality
The problem of difference causes to do over again so that the flatness of metope is affected, waste of resource, extends the duration.
The purpose of the invention is achieved by the following technical solution: the technique coated to the putty of metope in building,
The following steps are included:
(1) base treatment: chipping is removed at peeling, loosening and bulge position in wall basic level, by the dust in base, dirt
The sundries such as dirt, splash and mortar current mark clean up, and the iron wire steel bar end of surface of wall is polished, the processing of outside brush antirust paint；
(2) repair: with water gypsum, by the hole collided in the bases such as metope, recessed, gap etc. is levelling respectively, with No. 1 after drying
Sand paper polishes protrusion, and will drift along etc. and to clean out；
(3) it scrapes first pass putty and polishes: after the biggish gap of coating surface fills up smooth, completely scraping cream using batch embedding tool
Glue putty one time, all small sand holes and contraction fissure are both needed to completely scrape, with the neat degree of being of closely knit, smooth, line angle seamed edge, meanwhile,
It answers one to scrape down one to scrape along metope is horizontal with scraping, scrapes thin thickness 1-2mm as far as possible, must not leak and scrape, connector must not stay raft, be careful not to flaw
Dirty door and window and other object planes after putty parches, wrap up in smooth small plank with No. 1 sand paper, and putty slag and the place of being uneven are polished
It is smooth, pay attention to firmly uniform, protection corner angle, is criticized clearly with palm broom completely after mill, first pass is laterally completely scraped with scraper plate, and a scraper plate connects
One scraper plate, connector must not stay raft, and each scraper plate wants agile when finally receiving head；
(4) scrape second time putty and polish: second time full putty method requires this all over putty with before to head time putty
To smear direction orthogonal all over scraping, i.e., should scrape along metope is perpendicular, metope is further scraped it is full and polish flat it is smooth, smooth until,
It is vertically completely scraped with scraper plate for second time, a scraper plate connects a scraper plate, and connector must not stay raft, and each scraper plate wants agile when finally receiving head；
(5) under-coating varnish: must clean up substrate surface before first pass coating application, clean floating ash, brush appropriate to the occasion use
Spread pen, brushing sequence are usually from top to bottom, from left to right, to erect after first horizontal, first sideline, corner angle, facet, rear big face, at inner corner trim
Must not have residual coating, rib must not be wrapped up at external corner, as wall once brush cannot from it is upper on earth when, should at many levels up and down simultaneously operation,
Work in coordination cooperation, avoid connecing raft, brush overlapping phenomenon, independent face it is every all over application with a collection of coating, and once complete；
(6) mend putty again: after first pass coating parches, answering general inspection one time, such as it is defective should locally answer coating material it is greasy
Son one time, and scraped and smeared with ox horn, in order to avoid damage coating paint film；
(7) polish: mended after putty parches again, coated surface polished using fine sandpaper smooth, pays attention to exerting oneself to answer it is light and even, and
Must not worn out paint film, surface is cleaned up after mill；
(8) second coating: must clean up substrate surface before first pass coating application, clean floating ash, when brushing
Spread pen is preferably used, brushing sequence is usually from top to bottom, from left to right, to erect after first horizontal, first sideline, corner angle, facet, rear big face, yin
Must not have residual coating at angle, rib must not be wrapped up at external corner, as wall once brush cannot from it is upper on earth when, should make simultaneously up and down at many levels
Industry, cooperation of working in coordination avoid connecing raft, brush overlapping phenomenon, and independent face is every all over the same a collection of coating of application, and once completes；
(9) polish: mended after putty parches again, coated surface polished using fine sandpaper smooth, pays attention to exerting oneself to answer it is light and even, and
Must not worn out paint film, surface is cleaned up after mill；
(10) third road coating: for third all over coating using spraying, spray gun uses No. 1 spray gun, and spray gun pressure adjusts 0.3-
0.5N/mm2At an angle of 90 degrees, distance is advisable for 40-50cm for nozzle and facing, and when spraying answers specking uniform, and moving distance is all suitable
In, when spraying generally since inconspicuous one, gradually moved in proper order to other end, it, must not until unobtrusively brush is received at place
Appearance connects raft, after, whole surface is bright and clean consistent, round and smooth exquisiteness, no stream pendant film color phenomenon, when spraying, by metope it is all its
Its facing all covered with newspaper it is tight, in order to avoid pollute, before swabbing should by substrate surface dust, dirt, splash and smear
Clean, the coating of extemporaneous preparation is removed with mortar current mark, it is necessary to bonding agent is mixed, coating thickness is uniform, and it is flat and smooth, it does not flow
It hangs, bottom drain, third time do not scrape spot putting after metope strikes off light drying with scraper plate and polish polishing with fine sandpaper, be careful not to
Leakage mill or putty is worn out, brush emulsion paint three times.
In conclusion shortening construction period, having standardized behaviour the beneficial effects of the present invention are: the step of technique is simple
Make, can be improved the flatness of metope, saved resource, solve existing putty coating processes low efficiency, be all according to worker
The experience of oneself is constructed, and the experience of each worker is different, and it is different to cause quality, so that the flatness of metope is affected,
It causes to do over again, waste of resource, the problem of extending the duration.
Specific embodiment
Below with reference to embodiment, the present invention is described in further detail, but embodiments of the present invention are not limited only to
This.
Embodiment:
The technique that the putty of metope in building is coated, comprising the following steps:
(1) base treatment: chipping is removed at peeling, loosening and bulge position in wall basic level, by the dust in base, dirt
The sundries such as dirt, splash and mortar current mark clean up, and the iron wire steel bar end of surface of wall is polished, the processing of outside brush antirust paint；
(2) repair: with water gypsum, by the hole collided in the bases such as metope, recessed, gap etc. is levelling respectively, with No. 1 after drying
Sand paper polishes protrusion, and will drift along etc. and to clean out；
(3) it scrapes first pass putty and polishes: after the biggish gap of coating surface fills up smooth, completely scraping cream using batch embedding tool
Glue putty one time, all small sand holes and contraction fissure are both needed to completely scrape, with the neat degree of being of closely knit, smooth, line angle seamed edge, meanwhile,
It answers one to scrape down one to scrape along metope is horizontal with scraping, scrapes thin thickness 1-2mm as far as possible, must not leak and scrape, connector must not stay raft, be careful not to flaw
Dirty door and window and other object planes after putty parches, wrap up in smooth small plank with No. 1 sand paper, and putty slag and the place of being uneven are polished
It is smooth, pay attention to firmly uniform, protection corner angle, is criticized clearly with palm broom completely after mill, first pass is laterally completely scraped with scraper plate, and a scraper plate connects
One scraper plate, connector must not stay raft, and each scraper plate wants agile when finally receiving head；
(4) scrape second time putty and polish: second time full putty method requires this all over putty with before to head time putty
To smear direction orthogonal all over scraping, i.e., should scrape along metope is perpendicular, metope is further scraped it is full and polish flat it is smooth, smooth until,
It is vertically completely scraped with scraper plate for second time, a scraper plate connects a scraper plate, and connector must not stay raft, and each scraper plate wants agile when finally receiving head；
(5) under-coating varnish: must clean up substrate surface before first pass coating application, clean floating ash, brush appropriate to the occasion use
Spread pen, brushing sequence are usually from top to bottom, from left to right, to erect after first horizontal, first sideline, corner angle, facet, rear big face, at inner corner trim
Must not have residual coating, rib must not be wrapped up at external corner, as wall once brush cannot from it is upper on earth when, should at many levels up and down simultaneously operation,
Work in coordination cooperation, avoid connecing raft, brush overlapping phenomenon, independent face it is every all over application with a collection of coating, and once complete；
(6) mend putty again: after first pass coating parches, answering general inspection one time, such as it is defective should locally answer coating material it is greasy
Son one time, and scraped and smeared with ox horn, in order to avoid damage coating paint film；
(7) polish: mended after putty parches again, coated surface polished using fine sandpaper smooth, pays attention to exerting oneself to answer it is light and even, and
Must not worn out paint film, surface is cleaned up after mill；
(8) second coating: must clean up substrate surface before first pass coating application, clean floating ash, when brushing
Spread pen is preferably used, brushing sequence is usually from top to bottom, from left to right, to erect after first horizontal, first sideline, corner angle, facet, rear big face, yin
Must not have residual coating at angle, rib must not be wrapped up at external corner, as wall once brush cannot from it is upper on earth when, should make simultaneously up and down at many levels
Industry, cooperation of working in coordination avoid connecing raft, brush overlapping phenomenon, and independent face is every all over the same a collection of coating of application, and once completes；
(9) polish: mended after putty parches again, coated surface polished using fine sandpaper smooth, pays attention to exerting oneself to answer it is light and even, and
Must not worn out paint film, surface is cleaned up after mill；
(10) third road coating: for third all over coating using spraying, spray gun uses No. 1 spray gun, and spray gun pressure adjusts 0.3-
0.5N/mm2At an angle of 90 degrees, distance is advisable for 40-50cm for nozzle and facing, and when spraying answers specking uniform, and moving distance is all suitable
In, when spraying generally since inconspicuous one, gradually moved in proper order to other end, it, must not until unobtrusively brush is received at place
Appearance connects raft, after, whole surface is bright and clean consistent, round and smooth exquisiteness, no stream pendant film color phenomenon, when spraying, by metope it is all its
Its facing all covered with newspaper it is tight, in order to avoid pollute, before swabbing should by substrate surface dust, dirt, splash and smear
Clean, the coating of extemporaneous preparation is removed with mortar current mark, it is necessary to bonding agent is mixed, coating thickness is uniform, and it is flat and smooth, it does not flow
It hangs, bottom drain, third time do not scrape spot putting after metope strikes off light drying with scraper plate and polish polishing with fine sandpaper, be careful not to
Leakage mill or putty is worn out, brush emulsion paint three times.
The step of technique, is simple, shortens construction period, has standardized operation, can be improved the flatness of metope, saves
Resource, solves existing putty coating processes low efficiency, is constructed according to the experience of worker oneself, each worker's
Experience is different, causes quality different, so that the flatness of metope is affected, causes to do over again, waste of resource extends the duration
Problem.
The above is only presently preferred embodiments of the present invention, not does limitation in any form to the present invention, it is all according to
According to technology of the invention, method any simple modification substantially to the above embodiments, equivalent variations, the present invention is each fallen within
Protection scope within.
Claims (1)
1. the technique that the putty of metope is coated in pair building, which comprises the following steps:
(1) base treatment: removing chipping for peeling in wall basic level, loosening and bulge position, by base dust, dirt,
The sundries such as splash and mortar current mark clean up, and the iron wire steel bar end of surface of wall is polished, the processing of outside brush antirust paint；
(2) repair: with water gypsum, by the hole collided in the bases such as metope, recessed, gap etc. is levelling respectively, with No. 1 sand paper after drying
Protrusion is polished, and will be drifted along etc. and cleaned out；
(3) it scrapes first pass putty and polishes: after the biggish gap of coating surface fills up smooth, it is greasy completely to scrape latex using batch embedding tool
Son one time, all small sand holes and contraction fissure are both needed to completely scrape, with the neat degree of being of closely knit, smooth, line angle seamed edge, meanwhile, Ying Yi
It scrapes down one to scrape along metope is horizontal with scraping, scrapes thin thickness 1-2mm as far as possible, must not leak and scrape, connector must not stay raft, be careful not to stain door
Window and other object planes after putty parches, wrap up in smooth small plank with No. 1 sand paper, putty slag and the place of being uneven are polished flat,
Pay attention to firmly uniform, protection corner angle, is criticized clearly with palm broom completely after mill, first pass is laterally completely scraped with scraper plate, and a scraper plate connects one and scrapes
Plate, connector must not stay raft, and each scraper plate wants agile when finally receiving head；
(4) scrape second time putty and polish: second time full putty method requires this to scrape all over putty with preceding time to head time putty
It is orthogonal to smear direction, i.e., should be scraped along metope is perpendicular, metope is further scraped it is full and polish flat it is smooth, smooth until, second
All over vertically completely being scraped with scraper plate, a scraper plate connects a scraper plate, and connector must not stay raft, and each scraper plate wants agile when finally receiving head；
(5) under-coating varnish: must clean up substrate surface before first pass coating application, clean floating ash, brush appropriate to the occasion spread pen,
Brushing sequence is usually from top to bottom, from left to right, to erect after first horizontal, first sideline, corner angle, facet, rear big face, must not have at inner corner trim
Residual coating must not wrap up in rib at external corner, as wall once brush cannot from it is upper on earth when, should operation simultaneously up and down at many levels, mutually match
Cooperation is closed, avoids connecing raft, brush overlapping phenomenon, every time application of independent face is once completed with a collection of coating；
(6) putty is mended again: after first pass coating parches, being answered general inspection one time, should locally mend paint render one again Ru defective
Time, and scraped and smeared with ox horn, in order to avoid damage coating paint film；
(7) polish: mended after putty parches again, coated surface polished using fine sandpaper smooth, pays attention to exerting oneself to answer it is light and even, and must not
Worn out paint film cleans up surface after mill；
(8) second coating: must clean up substrate surface before first pass coating application, clean floating ash, brush appropriate to the occasion use
Spread pen, brushing sequence are usually from top to bottom, from left to right, to erect after first horizontal, first sideline, corner angle, facet, rear big face, at inner corner trim
Must not have residual coating, rib must not be wrapped up at external corner, as wall once brush cannot from it is upper on earth when, should at many levels up and down simultaneously operation,
Work in coordination cooperation, avoid connecing raft, brush overlapping phenomenon, independent face it is every all over application with a collection of coating, and once complete；
(9) polish: mended after putty parches again, coated surface polished using fine sandpaper smooth, pays attention to exerting oneself to answer it is light and even, and must not
Worn out paint film cleans up surface after mill；
(10) third road coating: for third all over coating using spraying, spray gun uses No. 1 spray gun, and spray gun pressure adjusts 0.3-0.5N/mm2
At an angle of 90 degrees, distance is advisable for 40-50cm for nozzle and facing, and when spraying answers specking uniform, and moving distance is all moderate, when spraying
Generally since inconspicuous one, gradually moved in proper order to other end, until unobtrusively brush is received at place, there is not allowed that raft is connect,
After, whole surface is bright and clean consistent, round and smooth exquisiteness, no stream pendant film color phenomenon, when spraying, all other facing of metope is complete
Portion's newspaper cover it is tight, in order to avoid pollute, before swabbing should by substrate surface dust, dirt, splash and smear and mortar current mark
Remove clean, the coating of extemporaneous preparation, it is necessary to bonding agent is mixed, coating thickness is uniform, flat and smooth, not sagging, non-bottom drain, the
Scrape spot putting with scraper plate three times, metope strike off light it is dry after, polish polishing with fine sandpaper, be careful not to leakage and grind or by putty
It is worn out, brush emulsion paint three times.