CN107044196A - A kind of concrete is plastered face emulsion paint brushing technique - Google Patents
A kind of concrete is plastered face emulsion paint brushing technique Download PDFInfo
- Publication number
- CN107044196A CN107044196A CN201710432201.2A CN201710432201A CN107044196A CN 107044196 A CN107044196 A CN 107044196A CN 201710432201 A CN201710432201 A CN 201710432201A CN 107044196 A CN107044196 A CN 107044196A
- Authority
- CN
- China
- Prior art keywords
- emulsion
- metope
- putty
- cleaned
- face
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Plastered face emulsion paint brushing technique the invention discloses a kind of concrete, belong to the realm of building construction, its technical scheme is as follows, comprises the following steps：Material preparation, base treatment, repairing putty, Puttying, repairing polishing, the application of first pass emulsion, second time emulsion application, the 3rd time emulsion application, maintenance, the entirety with lifting emulsion paint coat effect, reduction later stage bulge, the advantage of obscission.
Description
Technical field
The present invention relates to the realm of building construction, more particularly to a kind of concrete is plastered face emulsion paint brushing technique.
Background technology
Emulsion paint is one kind of organic coating, is that pigment, filler and various auxiliary agents are added by base-material of synthetic resin emulsion
The class water paint being formulated.
Covered when concrete wall surface basal layer is constructed, it is necessary to carry out base putty layer and scrape, cover emulsion paint scraping, improve wall
Decorative effect.
But to brushing processing not enough in place during the coating construction of existing emulsion paint, cause actual service life compared with
Short, the debris in multilayer latex enamelled coating easily produces influence to the later stage, and debris causes the connection effect between enamelled coating to substantially reduce,
Bulge is easily produced, causes the large area of later stage enamelled coating to come off.
The content of the invention
Plastered face emulsion paint brushing technique it is an object of the invention to provide a kind of concrete, it has the whole of lifting emulsion paint
Body coats effect, reduces later stage bulge, the advantage of obscission.
The present invention above-mentioned technical purpose technical scheme is that：A kind of concrete is plastered face latex
Brushing technique is painted, is comprised the following steps：
Step one：Material prepares：Prepare coating, inserts, pigment；
Step 2：Base treatment：Chipping is removed into peeling, loosening and bulge etc. in the basic units such as metope；
Step 3：Repairing putty：It is with water gypsum that the punishment time such as recessed, gap in hole collided with the basic units such as metope is levelling, after drying
It will be polished with No. 1 sand paper at protrusion, and floating dust etc. is swept only；
Step 4：Puttying：First pass is laterally completely scraped with rubber scraper plate, and an a scraper plate and then scraper plate, joint must not stay raft,
Ground after drying with No. 1 sand paper, floating putty and mottling are polished into polishing, then metope is cleaned up；
Vertically completely scraped with rubber scraper plate for second time, material therefor and method are polished with first pass putty after drying with No. 1 sand paper
And clean up；
With rubber scraper plate spot putting, with the full Puttying of steel disc scraper plate, the basic units such as metope are struck off into light, used after drying for 3rd time
Fine sandpaper polishes polishing；
Step 5：Repairing polishing：Polished again by sand paper overall；
Step 6：First pass emulsion is applied：Emulsion thin coat is diluted with water using preceding stirring, and application order is that first brush is pushed up
Whitewashed a wall after plate face, whitewash a wall face when should be first up and then down；First metope is cleaned up, then cleaned metope dust with cloth；Emulsion scumbling
Material spread pen brushing, putty is mended after drying again, and coated abrasive working is used after multiple benefit putty is dried, and is cleaned up, and carries out 20-30 degree
Blowing hot-air air-dry；
Step 7：Second time emulsion is applied：Emulsion thin coat is diluted with water using preceding stirring, and application order is that first brush is pushed up
Whitewashed a wall after plate face, whitewash a wall face when should be first up and then down；First metope is cleaned up, then cleaned metope dust with cloth；Emulsion scumbling
Material spread pen brushing, emulsion thin coat is diluted with water using preceding stirring, and is mended again after putty, drying varniss after drying, with thin
Sand paper polishes off metope goose pimples and spread pen hair, is cleaned up after ground smooth, and the blowing hot-air for carrying out 25-30 degree is air-dried；
Step 8：3rd time emulsion is applied：Emulsion thin coat is diluted with water using preceding stirring, and application order is that first brush is pushed up
Whitewashed a wall after plate face, whitewash a wall face when should be first up and then down；First metope is cleaned up, then cleaned metope dust with cloth；Emulsion scumbling
Material spread pen brushing, is operated continuously, during brushing since one, is gradually brushed to other end, is overlapped up and down along brush,
Latter spread pen immediately previous spread pen.
By using above-mentioned technical proposal, putty is covered by scraping of constantly repeating for three times, it is effective to ensure the flat of putty layer
Whole degree, is polished after reducing the position of debris adhesion, and per pass coating, effectively ensures surfacing, is removed putty and is coagulated
Gu the exudate on rear surface, reduces the influence to the later stage, pass through three application emulsions, it is effective to improve the entirety after emulsion is molded
Intensity, and polished per preceding twice after coating, it is ensured that the flatness on surface, the emulsion coated after enabling is uniformly connected
Effect, reduces later stage generation and comes off, and the effect air-dried of being blown by hot blast, effectively blows away debris, and improve emulsion table
The temperature in face, keeps two layers of temperature to approach, reduces temperature difference during being coated in the later stage, it is to avoid produced in the later stage different
Temperature change causes to produce space, it is to avoid produce the bulge phenomenon after coating, improves overall connection effect.
Further, step 2：The debris such as the dust remained in substrate surface, dirt, splash and mortar current mark is clear
It is net except sweeping.
By using above-mentioned technical proposal, the effective flatness for ensureing basic unit, bonding strength when improving Puttying is protected
Hold uniform, decrease scrape cover during putty produce and come off and influence construction, improve the efficiency of construction in later stage.
Further, step 4：Indoor putty, its match ratio is：Polyvinyl acetate emulsion：Talcum powder or chalk powder：2%
Cmc soln=1：5：3.5.
By using above-mentioned technical proposal, overall viscosity is improved, is easy to construction.
Further, step 4：Exterior wall, kitchen, lavatory, the moistureproof putty in bathroom, its match ratio is：Poly vinyl acetate emulsion
Liquid：Cement：Water=1：5：1.
By using above-mentioned technical proposal, with good moisture effect, the adaptation life-span in later stage is improved.
Further, step 9：Maintenance：After coating has been applied, room air keeps circulation.
By using above-mentioned technical proposal, it is ensured that the drying effect of paint film, surface is unglazed or gloss after prevention drying varniss
It is not enough.
In summary, the invention has the advantages that：
1st, yield material is effectively cleared up in work progress；
2nd, the overall coating effect of lifting emulsion paint；
3rd, later stage bulge, obscission are reduced.
Brief description of the drawings
Fig. 1 is the process chart of the present embodiment.
Embodiment
The present invention is described in further detail below in conjunction with accompanying drawing.
A kind of concrete is plastered face emulsion paint brushing technique, is comprised the following steps：
Step one：Material prepares：Prepare coating, inserts, pigment；
Coating：Ethanoic acid ethene latex lacquer, acrylic latex coating；
Inserts：It is chalk powder, land plaster, talcum powder, carboxymethyl cellulose, polyvinyl acetate emulsion, floor Huang, red oxide, black
Soot, lithopone etc.；
Pigment：Colors have alkali resistance, sunproof organic or inorganic pigment.
Step 2：Base treatment：Metope keeps drying, and basic unit's moisture content is not more than 10%；
Plastered work has been fully completed, and is crossed wall coil road, hole, negative and positive angle etc. and is answered advanced processing to finish, it is ensured that metope is dried, various
Hole through walls is plastered polishing in advance；
Door glass is installed in advance；
Ground construction is finished, and pipe-line equipment is installed, and examination water pressure testing has been finished；
Before large-area construction, model room is first carried out, after check up and appraisal is qualified, tissue teams and groups carry out large-area construction.
Chipping is removed into peeling, loosening and bulge etc. in the basic units such as metope, by the dust remained in substrate surface, dirt
The eliminating impurities such as dirt, splash and mortar current mark are swept only, the effective flatness for ensureing basic unit, improve bonding strength during Puttying
Keep uniform, decrease scrape cover during putty produce and come off and influence construction, improve the efficiency of construction in later stage.
Step 3：Repairing putty：It is with water gypsum that the punishment time such as recessed, gap in hole collided with the basic units such as metope is levelling, do
It will be polished after dry with No. 1 sand paper at protrusion, and floating dust etc. swept only.
Step 4：Puttying：Indoor putty, its match ratio is：Polyvinyl acetate emulsion：Talcum powder or chalk powder：2% carboxylic
Methocel solution=1：5：3.5；Overall viscosity is improved, is easy to construction.
Exterior wall, kitchen, lavatory, the moistureproof putty in bathroom, its match ratio is：Polyvinyl acetate emulsion：Cement：Water=1：5：
1；With good moisture effect, the adaptation life-span in later stage is improved.
First pass is laterally completely scraped with rubber scraper plate, and an a scraper plate and then scraper plate, joint must not stay raft, with No. 1 after drying
Sand paper is ground, and floating putty and mottling is polished into polishing, then metope is cleaned up.
Vertically completely scraped with rubber scraper plate for second time, material therefor and method are with first pass putty, with No. 1 sand paper after drying
Polish and clean up.
With rubber scraper plate spot putting, with the full Puttying of steel disc scraper plate, the basic units such as metope are struck off into light, dried for 3rd time
Polishing is polished with fine sandpaper afterwards；
Scrape by what is constantly repeated for three times and cover putty, the effective flatness for ensureing putty layer reduces the position of debris adhesion, and
Polished after per pass coating, effectively ensure surfacing, removed the exudate on surface after putty solidification, reduce to the later stage
Influence.
Step 5：Repairing polishing：Polished again by sand paper overall.
Step 6：First pass emulsion is applied：Surrounding environment, and humidifying air have been cleared up before applying first, dust suction is carried out, prevented
Only stir up a cloud of dust, influence coating quality；
Emulsion thin coat is diluted with water using preceding stirring, and application order is face of first whitewashing a wall after brush top plate, whitewash a wall face when should be first
Under after upper；First metope is cleaned up, then cleaned metope dust with cloth；The spread pen brushing of emulsion thin coat, is mended again after drying
Putty, coated abrasive working is used after multiple benefit putty is dried, and is cleaned up, and the blowing hot-air for carrying out 20-30 degree is air-dried.
Step 7：Second time emulsion is applied：Emulsion thin coat is diluted with water using preceding stirring, and application order is first
Whitewashed a wall after brush top plate face, whitewash a wall face when should be first up and then down；First metope is cleaned up, then cleaned metope dust with cloth；Emulsion
Thin coat spread pen brushing, emulsion thin coat is diluted with water using preceding stirring, and is mended again after putty, drying varniss after drying,
Metope goose pimples and spread pen hair are polished off with fine sandpaper, cleaned up after ground smooth, the blowing hot-air for carrying out 25-30 degree is air-dried.
Step 8：3rd time emulsion is applied：Emulsion thin coat is diluted with water using preceding stirring, and application order is first
Whitewashed a wall after brush top plate face, whitewash a wall face when should be first up and then down；First metope is cleaned up, then cleaned metope dust with cloth；Emulsion
Thin coat spread pen brushing, is operated continuously, during brushing since one, is gradually brushed to other end, mutual along brush up and down
Linking, latter spread pen immediately previous spread pen.
By three application emulsions, the effective bulk strength improved after emulsion shaping, and carried out per preceding twice after coating
Polishing, it is ensured that the flatness on surface, the emulsion coated after enabling is reduced later stage generation and come off by uniform connection function, and
By the air-dried effect of hot blast air blowing, effectively debris is blown away, and improves the temperature on emulsion surface, the process coated in the later stage
The middle temperature for being kept for two layers is approached, and reduces temperature difference, it is to avoid different temperature changes are produced in the later stage to be caused to produce space, it is to avoid
The bulge phenomenon after coating is produced, overall connection effect is improved.
Step 9：Maintenance：After coating has been applied, room air keeps circulation, it is ensured that the drying effect of paint film, prevents paint film
Surface is unglazed after drying or gloss is not enough.
This specific embodiment is only explanation of the invention, and it is not limitation of the present invention, people in the art
Member can make the modification without creative contribution to the present embodiment as needed after this specification is read, but as long as at this
All protected in the right of invention by Patent Law.
Claims (5)
- The face emulsion paint brushing technique 1. a kind of concrete is plastered, it is characterized in that：Comprise the following steps：Step one：Material prepares：Prepare coating, inserts, pigment；Step 2：Base treatment：Chipping is removed into peeling, loosening and bulge etc. in the basic units such as metope；Step 3：Repairing putty：It is with water gypsum that the punishment time such as recessed, gap in hole collided with the basic units such as metope is levelling, after drying It will be polished with No. 1 sand paper at protrusion, and floating dust etc. is swept only；Step 4：Puttying：First pass is laterally completely scraped with rubber scraper plate, and an a scraper plate and then scraper plate, joint must not stay raft, Ground after drying with No. 1 sand paper, floating putty and mottling are polished into polishing, then metope is cleaned up；Vertically completely scraped with rubber scraper plate for second time, material therefor and method are polished with first pass putty after drying with No. 1 sand paper And clean up；With rubber scraper plate spot putting, with the full Puttying of steel disc scraper plate, the basic units such as metope are struck off into light, used after drying for 3rd time Fine sandpaper polishes polishing；Step 5：Repairing polishing：Polished again by sand paper overall；Step 6：First pass emulsion is applied：Emulsion thin coat is diluted with water using preceding stirring, and application order is that first brush is pushed up Whitewashed a wall after plate face, whitewash a wall face when should be first up and then down；First metope is cleaned up, then cleaned metope dust with cloth；Emulsion scumbling Material spread pen brushing, putty is mended after drying again, and coated abrasive working is used after multiple benefit putty is dried, and is cleaned up, and carries out 20-30 degree Blowing hot-air air-dry；Step 7：Second time emulsion is applied：Emulsion thin coat is diluted with water using preceding stirring, and application order is that first brush is pushed up Whitewashed a wall after plate face, whitewash a wall face when should be first up and then down；First metope is cleaned up, then cleaned metope dust with cloth；Emulsion scumbling Material spread pen brushing, emulsion thin coat is diluted with water using preceding stirring, and is mended again after putty, drying varniss after drying, with thin Sand paper polishes off metope goose pimples and spread pen hair, is cleaned up after ground smooth, and the blowing hot-air for carrying out 25-30 degree is air-dried；Step 8：3rd time emulsion is applied：Emulsion thin coat is diluted with water using preceding stirring, and application order is that first brush is pushed up Whitewashed a wall after plate face, whitewash a wall face when should be first up and then down；First metope is cleaned up, then cleaned metope dust with cloth；Emulsion scumbling Material spread pen brushing, is operated continuously, during brushing since one, is gradually brushed to other end, is overlapped up and down along brush, Latter spread pen immediately previous spread pen.
- The face emulsion paint brushing technique 2. a kind of concrete according to claim 1 is plastered, it is characterized in that：Step 2：Will be residual The eliminating impurities such as the dust, dirt, splash and the mortar current mark that stay in substrate surface are swept only.
- The face emulsion paint brushing technique 3. a kind of concrete according to claim 2 is plastered, it is characterized in that：Step 4：It is indoor Putty, its match ratio is：Polyvinyl acetate emulsion：Talcum powder or chalk powder：2% cmc soln=1：5：3.5.
- The face emulsion paint brushing technique 4. a kind of concrete according to claim 3 is plastered, it is characterized in that：Step 4：Exterior wall, Kitchen, lavatory, the moistureproof putty in bathroom, its match ratio is：Polyvinyl acetate emulsion：Cement：Water=1：5：1.
- The face emulsion paint brushing technique 5. a kind of concrete according to claim 4 is plastered, it is characterized in that：Step 9：Maintenance： After coating has been applied, room air keeps circulation.