CN109369112A - A kind of grass planting concrete construction and preparation method thereof based on draft root system configuration - Google Patents

A kind of grass planting concrete construction and preparation method thereof based on draft root system configuration Download PDF

Info

Publication number
CN109369112A
CN109369112A CN201811529421.8A CN201811529421A CN109369112A CN 109369112 A CN109369112 A CN 109369112A CN 201811529421 A CN201811529421 A CN 201811529421A CN 109369112 A CN109369112 A CN 109369112A
Authority
CN
China
Prior art keywords
grass planting
planting concrete
parts
concrete
draft
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201811529421.8A
Other languages
Chinese (zh)
Other versions
CN109369112B (en
Inventor
江辉
刘瑶
程洪
甘建军
胡盛明
孙笑
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanchang Institute of Technology
Original Assignee
Nanchang Institute of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanchang Institute of Technology filed Critical Nanchang Institute of Technology
Priority to CN201811529421.8A priority Critical patent/CN109369112B/en
Publication of CN109369112A publication Critical patent/CN109369112A/en
Application granted granted Critical
Publication of CN109369112B publication Critical patent/CN109369112B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of grass planting concrete construction and preparation method thereof based on draft root system configuration, grass planting concrete is by grass planting concrete multi-level structure composition, according to the natural growth rhythm of root density and root diameter, it is divided into layer 2-4, overall thickness is 10~15cm, and the porosity of grass planting concrete is in 10~35% ranges.Grass planting concrete is prepared by the raw material of following parts by weight: 113--313 parts of cement, 1421--1568 parts of coarse aggregate, 113--313 parts of fine aggregate, 2--10 parts of hardening agent, and 0.23-0.63 part of water-reducing agent, 29--95 parts of water.Preparation method of the invention comprehensively considers from microscopical structure feature and vegetation physiological growth characteristic parameter angle, help to provide the good growing space of science and growth conditions for plant root growth, improve growth vigor and coverage rate of the herbaceous plant in concrete, tension, anti-folding, bending resistance and the anti-filter performance for promoting concrete, form " draft-concrete-soil " complex for adapting to plant nature growth rhythm.

Description

A kind of grass planting concrete construction and preparation method thereof based on draft root system configuration
Technical field
The present invention relates to ecological engineering technologies, are based on grass more particularly, to the one kind for following draft root system nature growth rhythm Grass planting concrete construction of this root system configuration and preparation method thereof.
Background technique
Under the extremely arduous background of current China's ecological construction task, ecology is carried out to engineering measure using biological control measure It protects more more and more urgent, therefore promotes and applies the ecological technique that combines with herbaceous plant of concrete and product has and greatly answers With prospect, space and market.
Since the 90's of 20th century, Japanese concrete engineering association proposes the concept of eco-concrete, learns at present Persons mainly conduct a research in the Macroscopic physical of grass planting concrete, mechanics and the raw aspect of performance of plant.So-called grass planting concrete is one Class special concrete material injects nutrient soil in the hole of concrete, draft using random macroporosity concrete as skeleton Root system is grown in concrete pore, and plant is combined together with concrete, forms the environment with some strength and vegetative coverage The eco-concrete of friendly.
Yearning with the development and people of Social Ecology civilization construction to good life, grass planting concrete is in water conservancy, friendship Ying Ersheng is transported in the river slope protection works in fields such as logical, ground mine, territory and municipal administration.However, being given birth to naturally under soil environment Long draft is compared, and grass planting concrete has special random pore structure, this has certain restriction effect to the growth of draft. The mechanical strength and structure hole of grass planting concrete be it is conflicting, pursue partial size it is big, hole is big when, though be conducive to plant Growth, but resistance to compression and flexural strength will reduce;Partial size is small, and hole is small, and intensity increases but do not adapt to plant root growth Demand so that draft survival rate and growth vigor reduce, the overall performance of " draft-concrete-soil complex " weakens.
Summary of the invention
The first purpose of the invention is to provide one kind to follow draft root system nature growth rhythm, can satisfy engineering strength It is required that, greening require and Ecological regulation services and effect, structure easily be layered, resistance to compression, anti-folding and anti-bending strength by force, easy construction, The grass planting concrete construction based on draft root system configuration of high-efficiency environment friendly.
A second object of the present invention is to provide a kind of preparation sides of grass planting concrete construction based on draft root system configuration Method.
The first purpose of this invention is achieved in that
A kind of grass planting concrete construction based on draft root system configuration, is characterized in: grass planting concrete is by the random hole construction of multilayer Composition, the coarse aggregate size from upper layer to lower layer is gradually reduced, while the porosity of grass planting concrete is reduced to 10% by 35%, shape At the multilayered structure grass planting concrete for adapting to herbaceous plant nature growth rhythm.
According to the natural growth rhythm of root density and root diameter, the overall thickness of grass planting concrete is 10~15cm, by grass planting Concrete is divided into 2-4 level from longitudinal cross-section: when dividing 2 layers, the thickness ratio of upper layer and lower layer is 1:2-1:1;When dividing 3 layers, The thickness ratio on upper layer, middle layer and lower layer is 1.5:2:1;At points 4 layers, upper layer, at the middle and upper levels, the thickness ratio of middle lower layer and lower layer be 2.5: 2: 2: 1;The porosity of grass planting concrete is 10-35%.
According to the herbaceous plant nature growth rhythm of root diameter size, the partial size of coarse aggregate is matched from large to small along depth direction System, the porosity of grass planting concrete is according to the draft natural law, and the partial size of upper layer coarse aggregate is larger, and more concentrates, using big The coarse aggregate of partial size prepares celluar concrete, and the porosity of the grass planting concrete on upper layer is controlled in 30-35%, middle layer or lower layer's root According to the size of the variation adjustment coarse aggregate size of root quantity, the porosity of the grass planting concrete in middle layer is 15~30%, lower layer The porosity of grass planting concrete is 10%~15%.
The herbaceous plant nature growth rhythm gradually subtracts to meet the density of Herb Root with the increase of depth Few, root diameter size is gradually reduced with the increase of depth, and root system intensity is different, the most root of draft of generally shorter root system System concentrates within the 10-15cm of top, and the most root system of the draft of longer root system concentrates within the 30-60cm of top.
Grass planting concrete is prepared by following raw material in parts by weight: 113--313 parts of cement, coarse aggregate 1421-- 1568 parts, 113--313 parts of fine aggregate, 2--10 parts of hardening agent, 0.23-0.63 part of water-reducing agent, 29--95 parts of water.
The cement is R42.5 ordinary portland cement.
The coarse aggregate is artificial rubble and natural pebble, and partial size is 10~40mm, and large-sized coarse aggregate is 30mm ~40mm.
The fine aggregate is natural sand or artificial sand.
The hardening agent is one of following material: epoxy resin, unsaturated polyester (UP), the third cream it is polymer-bonded Agent.
The water-reducing agent is polycarboxylate water-reducer.
Second object of the present invention is achieved in that
A kind of preparation method of the grass planting concrete construction based on draft root system configuration, be characterized in: specific step is as follows:
(1), same gradation coarse aggregate, the fine aggregate of lower layer are added to blender, stirred evenly;
(2), cement is added and continues dry mixing 30s, material is made to be evenly distributed;
(3), it is eventually adding water, hardening agent, water-reducing agent stirring 120s, amounts to stirring 3.5min;
(4), the surface that will be close to the lower-layer concrete of ground is flattened using template or short time vibration flattens;
(5), by upper one layer of repetition (1)-(4) of lower layer the step of, cross construction are successively laid with, until upper layer;
(6), natural soil, plant ash, durable composite fertilizer and water are mixed in 1000:30:0.5:600 ratio, stirs evenly, matches It is set to the suitable nutrient soil of paste, mobility, water pump is reused and is filled into liquid/paste in the hole of grass planting concrete;And Perfusion;
(7), sow and be laid with plant;
(8), sprinkling maintenance early period finally obtains grass planting concrete construction.
Grass planting concrete construction of the invention is to infuse nutrient soil using the grass planting concrete of random macroporosity as skeleton In the hole for entering grass planting concrete, draft root system is grown in the hole of grass planting concrete, and it is one that plant is melted with grass planting concrete Body forms the environmentally friendly eco-concrete with some strength and vegetative coverage.Preparation method of the invention is from coagulation The microscopical structures features such as native pore structure, porosity, the quantity in hole, dispersion degree and vegetation physiological growth characteristic parameter angle are comprehensive Consider, helps to provide the good growing space of science and growth conditions for plant root growth, improve herbaceous plant in coagulation Growth vigor and coverage rate in soil promote resistance to compression, anti-folding, bending resistance and the anti-filter performance of concrete, are formed and adapt to plant nature " draft-concrete-soil " complex of growth rhythm.
Compared with prior art, the remarkable result that the present invention has is:
1, multilayer grass planting concrete construction of the invention has the natural characteristic for complying with plant growth, the more life of suitable for plant Long, the combination of draft root system and grass planting concrete in grass planting concrete can be improved in it, makes the entirety of grass planting concrete Mechanical property and intensity greatly improve, and take into account plant life and security function, while also acting as certain anti-filter effect, increase bank slope Soil conservation.It is difficult to the technology of base that the intensity for solving current grass planting concrete is not high, bad, draft of planting fruit of coming into force is difficult to penetrate Topic breaches the technology for reducing growth resistant, while can also increase the thickness of grass planting concrete, and how structurally reasonable preparation is to increase The performances such as strong resistance to compression, tension and anti-filter;
2, the structure of grass planting concrete of the present invention follows the pore property of draft root system nature growth rhythm, significantly improves plant The physiological environment of object growth, improves the growth vigor of plant, finally improves the survival rate of grass planting in grass planting concrete, covering Rate and growing way maintain the Nature Link of water and bank, maintain bio-diversity;
3, structure of the invention is simple, and cast-in-place or preformed patterns can be used, and is easy to construct, and is conducive to produce streamlined and scale Change, can be widely applied to the improvement of the Ecological Slopes such as water conservancy, traffic, ground mine, territory and municipal administration.
Detailed description of the invention
Fig. 1 is the cross-sectional view of the structure for being suitable for the grass planting concrete of longer fibrous root type;
Fig. 2 is the cross-sectional view of the structure for being suitable for the grass planting concrete compared with short hairs root type;
Fig. 3 is the cross-sectional view of the structure for being suitable for the grass planting concrete of taproot type.
Specific embodiment
In order to make content of the present invention easily facilitate understanding, below with reference to embodiment, for the specific of different draft Embodiment is described in further detail technical solutions according to the invention, but the present invention is not limited only to this.
Embodiment 1:
For longer fibrous root type herbaceous plant, such as vetiver, herba eleusines indicae, without obvious main root type, the radical density of root system is concentrated Within 40cm, the fibrous root distribution within the scope of the grass planting concrete thickness in addition to upper layer is more uniform.
The overall thickness of grass planting concrete is 12cm, is divided into 2 levels, upper layer 4cm, and lower layer is 8 cm.
In Fig. 1, upper layer 1 is the grass planting concrete layer of big partial size coarse aggregate, and lower layer 4 is that the grass planting of middle small particle coarse aggregate is mixed Solidifying soil layer is planted by cursive script 7 in grass planting concrete eight, and long root system 10 passes through the hole 9 of grass planting concrete, penetrates grass planting concrete Lower layer enters soil layer 11.
The porosity of the grass planting concrete on upper layer 1 is controlled 35%, using the big partial size coarse aggregate of 30mm~40mm, lower layer 4 Grass planting concrete porosity control 10~15%, using the middle small particle coarse aggregate of the mm of 10mm~20.
Upper layer grass planting concrete is prepared by raw material as follows in parts by weight: 113 parts of cement, 1568 parts of coarse aggregate, 113 parts of fine aggregate, 10 parts of hardening agent, 0.23 part of water-reducing agent, 29 parts of water.Lower layer's grass planting concrete is by original as follows in parts by weight Material is prepared: 262--313 parts of cement, 1450 parts of coarse aggregate, 262--313 parts of fine aggregate, 2--4 parts of hardening agent, and water-reducing agent 0.52-0.63 part, 80--95 parts of water.
Embodiment 2
It is concentrated within the scope of 2-6cm for compared with short hairs root type herbaceous plant, such as the radical density of Bermuda grass, Festuca Arundinacea, root system.
The overall thickness of grass planting concrete is 13cm, is divided into 3 levels, and lift height is respectively upper layer 4cm, middle layer 6cm, under Layer 3cm.
In Fig. 2, upper layer 1 is the grass planting concrete layer of big partial size coarse aggregate, and middle layer 2 is the grass planting coagulation of middle partial size coarse aggregate Soil layer, lower layer 3 are the grass planting concrete layer of small particle coarse aggregate, are planted by cursive script 7 in grass planting concrete eight, the short root system 10 of draft is logical The hole 9 of grass planting concrete is crossed, the lower layer of partial penetration grass planting concrete enters soil layer 11.
By the control of the porosity of the grass planting concrete on upper layer 1 30%, using the big partial size coarse aggregate of 30mm~35mm, in The porosity control of the grass planting concrete of layer 2 is 15~20%, using the middle small particle coarse aggregate of the mm of 10mm~20, lower layer 3 The porosity of grass planting concrete is controlled 10~15%, using the small particle coarse aggregate of 10mm.
Upper layer grass planting concrete is prepared by raw material as follows in parts by weight: 117 parts of cement, 1568 parts of coarse aggregate, 117 parts of fine aggregate, 10 parts of hardening agent, 0.23 part of water-reducing agent, 36 parts of water.Middle layer grass planting concrete is by original as follows in parts by weight Material is prepared: 211--262 parts of cement, 1450 parts of coarse aggregate, 211--262 parts of fine aggregate, 4--6 parts of hardening agent, and water-reducing agent 0.42-0.52 part, 64--80 parts of water.Lower layer's grass planting concrete is prepared by raw material as follows in parts by weight: cement 262--313 parts, 1421 parts of coarse aggregate, 262--313 parts of fine aggregate, 2--3 parts of hardening agent, 0.52-0.63 part of water-reducing agent, water 80--95 parts.
Embodiment 3:
For taproot type herbaceous plant, such as alfalfa.The radical density of root system concentrates within the scope of 0-10cm.
The overall thickness of grass planting concrete is 15cm, is divided into 4 levels, and lift height is respectively upper layer 5cm, at the middle and upper levels 4cm, Middle lower layer 4cm, bottom 2cm.
In Fig. 3, upper layer 1 is the grass planting concrete layer of big partial size coarse aggregate, and 5 is mixed for the grass planting of middle partial size coarse aggregate at the middle and upper levels Solidifying soil layer, at the middle and upper levels 6 be middle partial size coarse aggregate grass planting concrete layer, lower layer 3 is the grass planting concrete layer of small particle coarse aggregate, It is planted by cursive script 7 in grass planting concrete eight, the short root system 10 of draft passes through the hole 9 of grass planting concrete, partial penetration grass planting concrete Lower layer enters soil layer 11.
The porosity of the grass planting concrete on upper layer 1 is controlled 30%, using the big partial size coarse aggregate of 30mm~35mm;In The porosity of the grass planting concrete on upper layer 5 is controlled 25%, using the middle small particle coarse aggregate of the mm of 15mm~25;Middle lower layer 6 The porosity of grass planting concrete is controlled 20%, using the middle small particle coarse aggregate of the mm of 10mm~20;The grass planting concrete of lower layer 3 Porosity control 10~15%, using the coarse aggregate of 10mm small particle.
Upper layer grass planting concrete is prepared by raw material as follows in parts by weight: 117 parts of cement, 1568 parts of coarse aggregate, 117 parts of fine aggregate, 10 parts of hardening agent, 0.23 part of water-reducing agent, 36 parts of water.Grass planting concrete is by as follows in parts by weight at the middle and upper levels Raw material is prepared: 170 parts of cement, 1480 parts of coarse aggregate, 170 parts of fine aggregate, 5 parts of hardening agent, and 0.34 part of water-reducing agent, water 52 Part.Middle lower layer's grass planting concrete is prepared by raw material as follows in parts by weight: 211 parts of cement, 1450 parts of coarse aggregate, thin bone 211 parts, 5 parts of hardening agent, 0.42 part of water-reducing agent, 64 parts of water of material.Lower layer's grass planting concrete is by raw material system as follows in parts by weight It is standby to form: 262--313 parts of cement, 1421 parts of coarse aggregate, 262--313 parts of fine aggregate, 2--3 parts of hardening agent, water-reducing agent 0.52- 0.63 part, 80--95 parts of water.

Claims (10)

1. a kind of grass planting concrete construction based on draft root system configuration, it is characterised in that: grass planting concrete is random by multilayer Hole contexture, the coarse aggregate size from upper layer to lower layer are gradually reduced, while the porosity of grass planting concrete is reduced to by 35% 10%, form the multilayered structure grass planting concrete for adapting to herbaceous plant nature growth rhythm.
2. the grass planting concrete construction according to claim 1 based on draft root system configuration, it is characterised in that: according to root system The natural growth rhythm of density and root diameter, the overall thickness of grass planting concrete are 10~15cm, by grass planting concrete from longitudinal cross-section Be divided into 2-4 level: when dividing 2 layers, the thickness ratio of upper layer and lower layer is 1:2-1:1;When dividing 3 layers, upper layer, middle layer and lower layer Thickness ratio be 1.5:2:1;At points 4 layers, upper layer, at the middle and upper levels, the thickness ratio of middle lower layer and lower layer be 2.5:2:2:1;It plants The porosity of careless concrete is 10-35%.
3. the grass planting concrete construction according to claim 1 based on draft root system configuration, it is characterised in that: according to root diameter The herbaceous plant of size is prepared from growth rhythm, the partial size of coarse aggregate along depth direction from large to small, the hole of grass planting concrete For rate according to the draft natural law, the partial size of upper layer coarse aggregate is larger, and more concentrates, and is prepared using large-sized coarse aggregate porous The porosity control of concrete, the grass planting concrete on upper layer is adjusted in 30-35%, middle layer or lower layer according to the variation of root quantity The porosity of the size of coarse aggregate size, the grass planting concrete in middle layer is 15~30%, and the porosity of the grass planting concrete of lower layer is 10%~15%.
4. the grass planting concrete construction according to claim 1 based on draft root system configuration, it is characterised in that: grass planting coagulation Soil is made of following raw material in parts by weight: 113--313 parts of cement, 1421--1568 parts of coarse aggregate, fine aggregate 113--313 Part, 2--10 parts of hardening agent, 0.23-0.63 part of water-reducing agent, 29--95 parts of water.
5. the grass planting concrete construction according to claim 4 based on draft root system configuration, it is characterised in that: the water Mud is R42.5 ordinary portland cement.
6. the grass planting concrete construction according to claim 4 based on draft root system configuration, it is characterised in that: described is thick Aggregate is artificial rubble and natural pebble, and partial size is 10~40mm, and large-sized coarse aggregate is 30mm~40mm.
7. the grass planting concrete construction according to claim 4 based on draft root system configuration, it is characterised in that: described is thin Aggregate is natural sand or artificial sand.
8. the grass planting concrete construction according to claim 4 based on draft root system configuration, it is characterised in that: described is strong Agent is one of following material: epoxy resin, unsaturated polyester (UP), the third newborn polymer adhesive.
9. the grass planting concrete construction according to claim 4 based on draft root system configuration, it is characterised in that: water-reducing agent is Polycarboxylate water-reducer.
10. a kind of preparation method of the grass planting concrete construction based on draft root system configuration, be characterized in: specific step is as follows:
(1), same gradation coarse aggregate, the fine aggregate of lower layer are added to blender, stirred evenly;
(2), cement is added and continues dry mixing 30s, material is made to be evenly distributed;
(3), it is eventually adding water, hardening agent, water-reducing agent stirring 120s, amounts to stirring 3.5min;
(4), the surface that will be close to the lower-layer concrete of ground is flattened using template or short time vibration flattens;
(5), by upper one layer of repetition (1)-(4) of lower layer the step of, cross construction are successively laid with, until upper layer;
(6), natural soil, plant ash, durable composite fertilizer and water are mixed in 1000:30:0.5:600 ratio, stirs evenly, matches It is set to the suitable nutrient soil of paste, mobility, water pump is reused and is filled into liquid/paste in the hole of grass planting concrete;And Perfusion;
(7), sow and be laid with plant;
(8), sprinkling maintenance early period finally obtains grass planting concrete construction.
CN201811529421.8A 2018-12-14 2018-12-14 Grass planting concrete structure based on herbaceous root system configuration and preparation method thereof Active CN109369112B (en)