CN109252250A - 聚丙烯腈基碳纤维的碳化处理方法 - Google Patents
聚丙烯腈基碳纤维的碳化处理方法 Download PDFInfo
- Publication number
- CN109252250A CN109252250A CN201810883266.3A CN201810883266A CN109252250A CN 109252250 A CN109252250 A CN 109252250A CN 201810883266 A CN201810883266 A CN 201810883266A CN 109252250 A CN109252250 A CN 109252250A
- Authority
- CN
- China
- Prior art keywords
- polyacrylonitrile
- carbon fiber
- based carbon
- carbonization treatment
- carbon fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (5)