CN109174462A - 一种方铅矿的选择性抑制剂及其应用 - Google Patents
一种方铅矿的选择性抑制剂及其应用 Download PDFInfo
- Publication number
- CN109174462A CN109174462A CN201811254407.1A CN201811254407A CN109174462A CN 109174462 A CN109174462 A CN 109174462A CN 201811254407 A CN201811254407 A CN 201811254407A CN 109174462 A CN109174462 A CN 109174462A
- Authority
- CN
- China
- Prior art keywords
- galena
- phosphate
- selective depressant
- sodium
- carboxymethyl cellulose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种方铅矿的选择性抑制剂，由磷酸盐类化合物30‑50%、硫化钠30‑50%和羧甲基纤维素5‑20%制成。磷酸盐类化合物为含有‑PO4基团的磷酸盐或磷酸盐多聚物。采用上述技术方案的方铅矿选择性抑制剂，其作用原理在于磷酸盐的选择性使方铅矿表面的铅离子溶出，减少其表面的活性质点；硫化钠一方面具有脱药作用，一方面水解产生的HS‑与捕收剂阴离子在矿物表面发生竞争吸附；而羧甲基纤维素本身对方铅矿具有抑制作用，几种药剂配伍强化了对方铅矿的抑制作用。
Description
技术领域
本发明属于多金属硫化矿的浮选回收与分离技术领域，具体涉及一种方铅矿的选择性抑制剂及其应用。
背景技术
多金属硫化矿是提取有色金属的最主要的矿产资源，多金属硫化矿指的是铜、铅、锌、铁等硫化物在矿石中至少两种或两种以上致密共生的矿石。目前，多金属硫化矿选别分离绝大多数采用浮选方法，它利用硫化矿物间表面润湿性差异，采取人工添加浮选药剂的方式来进行浮选分离。在多金属硫化矿中，由于某些矿物浮游性质十分接近，矿物嵌布极细，结构复杂，氧化严重，含泥量多等，造成回收利用困难。
铜铅硫化矿的分离是矿物分选中的一大难题，因为铜与铅矿物的天然可浮性相似，所以铜铅分离成为铜铅多金属硫化矿浮选分离中的关键性问题。用于抑制方铅矿的常见选择性抑制剂主要有：重铬酸盐、羧甲基纤维素、水玻璃、亚硫酸及其盐类等，这些选择性抑制剂或者用量大、选择性抑制效果不强，或者如重铬酸盐对方铅矿抑制效果好，但是污染较严重，对环境的危害巨大。
发明内容
基于现有技术所存在的问题，本发明所要解决的第一个技术问题是提供一种选择性抑制能力强且环保的方铅矿选择性抑制剂。
本发明所要解决的第二个技术问题是提供该选择性选择性抑制剂的应用方法。
本发明的目的是以下述方式实现的：
一种方铅矿的选择性抑制剂，由磷酸盐类化合物30-50%、硫化钠30-50%和羧甲基纤维素5-20%制成。
所述磷酸盐类化合物为含有-PO4基团的磷酸盐或磷酸盐多聚物。
所述磷酸盐为磷酸三钠、磷酸三钾、磷酸氢二钠、磷酸氢二钾、磷酸二氢钠和磷酸二氢钾，磷酸盐多聚物为焦磷酸钠、焦磷酸钾、三聚磷酸钠、三聚磷酸钾和六偏磷酸钠。
如上述的方铅矿的选择性抑制剂的制备方法，室温下，按比例称取磷酸盐类化合物、硫化钠和羧甲基纤维素，混合搅拌，加水配制成质量百分比为5-10%的选择性抑制剂水溶液。
如上述的方铅矿的选择性抑制剂在多金属硫化矿浮选过程中的应用，选择性抑制剂的用量为500-2000g/t。
采用上述技术方案的方铅矿选择性抑制剂，其作用原理在于磷酸盐的选择性使方铅矿表面的铅离子溶出，减少其表面的活性质点；硫化钠一方面具有脱药作用，一方面水解产生的HS-与捕收剂阴离子在矿物表面发生竞争吸附；而羧甲基纤维素本身对方铅矿具有抑制作用，几种药剂配伍强化了对方铅矿的抑制作用。
附图说明
图1是铜铅混合精矿浮选分离试验流程。
具体实施方式
为了使本领域技术人员更好地理解本发明的技术方案，下面结合具体实施例对本发明进行详细描述，本部分的描述仅是示范性和解释性，不应对本发明的保护范围有任何的限制作用。
所述磷酸盐为磷酸三钠、磷酸三钾、磷酸氢二钠、磷酸氢二钾、磷酸二氢钠和磷酸二氢钾，磷酸盐多聚物为焦磷酸钠、焦磷酸钾、三聚磷酸钠、三聚磷酸钾和六偏磷酸钠。
实施例1：
一种方铅矿的选择性抑制剂，由磷酸盐类化合物30-50%、硫化钠30-50%和羧甲基纤维素5-20%制成。
磷酸盐类化合物为含有-PO4基团的磷酸盐或磷酸盐多聚物。
如上述的方铅矿的选择性抑制剂的制备方法，室温下，称取磷酸盐类化合物、硫化钠和羧甲基纤维素，混合搅拌，加水配制成质量百分比为5-10%的选择性抑制剂水溶液。
如上述的方铅矿的选择性抑制剂在多金属硫化矿浮选过程中的应用，选择性抑制剂的用量为500-2000g/t，此处的用量是选择性抑制剂的用量，不含水。
实施例2：
一种方铅矿的选择性抑制剂，由磷酸盐类化合物30%、硫化钠50%和羧甲基纤维素20%制成。
如上述的方铅矿的选择性抑制剂的制备方法，室温下，称取磷酸盐类化合物、硫化钠和羧甲基纤维素，混合搅拌，加水配制成质量百分比为5%的选择性抑制剂水溶液。
如上述的方铅矿的选择性抑制剂在多金属硫化矿浮选过程中的应用，选择性抑制剂的用量为500g/t。
实施例3：
一种方铅矿的选择性抑制剂，由磷酸盐类化合物35%、硫化钠45%和羧甲基纤维素20%制成。
如上述的方铅矿的选择性抑制剂的制备方法，室温下，称取磷酸盐类化合物、硫化钠和羧甲基纤维素，混合搅拌，加水配制成质量百分比为6%的选择性抑制剂水溶液。
如上述的方铅矿的选择性抑制剂在多金属硫化矿浮选过程中的应用，选择性抑制剂的用量为600g/t。
实施例4：
一种方铅矿的选择性抑制剂，由磷酸盐类化合物40%、硫化钠40%和羧甲基纤维素20%制成。
如上述的方铅矿的选择性抑制剂的制备方法，室温下，称取磷酸盐类化合物、硫化钠和羧甲基纤维素，混合搅拌，加水配制成质量百分比为7%的选择性抑制剂水溶液。
如上述的方铅矿的选择性抑制剂在多金属硫化矿浮选过程中的应用，选择性抑制剂的用量为800g/t。
如上述的方铅矿的选择性抑制剂在多金属硫化矿浮选过程中的应用，选择性抑制剂的用量为600g/t。
实施例5：
一种方铅矿的选择性抑制剂，由磷酸盐类化合物45%、硫化钠35%和羧甲基纤维素20%制成。
如上述的方铅矿的选择性抑制剂的制备方法，室温下，称取磷酸盐类化合物、硫化钠和羧甲基纤维素，混合搅拌，加水配制成质量百分比为8%的选择性抑制剂水溶液。
如上述的方铅矿的选择性抑制剂在多金属硫化矿浮选过程中的应用，选择性抑制剂的用量为1000g/t。
实施例6：
一种方铅矿的选择性抑制剂，由磷酸盐类化合物50%、硫化钠30%和羧甲基纤维素20%制成。
如上述的方铅矿的选择性抑制剂的制备方法，室温下，称取磷酸盐类化合物、硫化钠和羧甲基纤维素，混合搅拌，加水配制成质量百分比为9%的选择性抑制剂水溶液。
如上述的方铅矿的选择性抑制剂在多金属硫化矿浮选过程中的应用，选择性抑制剂的用量为1200g/t。
实施例7：
一种方铅矿的选择性抑制剂，由磷酸盐类化合物40%、硫化钠50%和羧甲基纤维素10%制成。
如上述的方铅矿的选择性抑制剂的制备方法，室温下，称取磷酸盐类化合物、硫化钠和羧甲基纤维素，混合搅拌，加水配制成质量百分比为10%的选择性抑制剂水溶液。
如上述的方铅矿的选择性抑制剂在多金属硫化矿浮选过程中的应用，选择性抑制剂的用量为1500g/t。
实施例8：
一种方铅矿的选择性抑制剂，由磷酸盐类化合物45%、硫化钠40%和羧甲基纤维素15%制成。
如上述的方铅矿的选择性抑制剂的制备方法，室温下，称取磷酸盐类化合物、硫化钠和羧甲基纤维素，混合搅拌，加水配制成质量百分比为10%的选择性抑制剂水溶液。
如上述的方铅矿的选择性抑制剂在多金属硫化矿浮选过程中的应用，选择性抑制剂的用量为1800g/t。
实施例9：
一种方铅矿的选择性抑制剂，由磷酸盐类化合物50%、硫化钠45%和羧甲基纤维素5%制成。
如上述的方铅矿的选择性抑制剂的制备方法，室温下，称取磷酸盐类化合物、硫化钠和羧甲基纤维素，混合搅拌，加水配制成质量百分比为10%的选择性抑制剂水溶液。
如上述的方铅矿的选择性抑制剂在多金属硫化矿浮选过程中的应用，选择性抑制剂的用量为2000g/t。
实施例10：
方铅矿的选择性抑制，由磷酸盐类化合物、硫化钠和羧甲基纤维素，按质量比分别为45%、50%、5%的比例配制而成，此处的磷酸盐类化合物为焦磷酸钠。
某多金属硫化矿，铜铅混浮作业，铜铅混合精矿Cu品位为5.62%，Pb品位为44.08%，添加本发明的抑制剂2000g/t，在20℃的矿浆温度下使用，按照图1的浮选流程进行选别，可得到表1的分离结果。
由表1结果可知，通过一粗一精一扫，可得到Cu品位为27.35%，回收率为52.09%的铜精矿和Pb品位为55.62%，回收率为85.39%的铅精矿，实现了铜和铅的分离与回收。
需要说明的是，在本文中，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。
本文中应用了具体个例对本发明的原理及实施方式进行了阐述，以上实例的说明只是用于帮助理解本发明的方法及其核心思想。以上所述仅是本发明的优选实施方式，应当指出，由于文字表达的有限性，而客观上存在无限的具体结构，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进、润饰或变化，也可以将上述技术特征以适当的方式进行组合；这些改进润饰、变化或组合，或未经改进将发明的构思和技术方案直接应用于其它场合的，均应视为本发明的保护范围。
Claims (5)
1.一种方铅矿的选择性抑制剂，其特征在于：由磷酸盐类化合物30-50%、硫化钠30-50%和羧甲基纤维素5-20%制成。
2.根据权利要求1所述的方铅矿的选择性抑制剂，其特征在于：所述磷酸盐类化合物为含有-PO4基团的磷酸盐或磷酸盐多聚物。
3.根据权利要求2所述的方铅矿的选择性抑制剂，其特征在于：所述磷酸盐为磷酸三钠、磷酸三钾、磷酸氢二钠、磷酸氢二钾、磷酸二氢钠和磷酸二氢钾，磷酸盐多聚物为焦磷酸钠、焦磷酸钾、三聚磷酸钠、三聚磷酸钾和六偏磷酸钠。
4.如权利要求1-3任一所述的方铅矿的选择性抑制剂的制备方法，其特征在于：室温下，按比例称取磷酸盐类化合物、硫化钠和羧甲基纤维素，混合搅拌，加水配制成质量百分比为5-10%的选择性抑制剂水溶液。
5.如权利要求1-3任一所述的方铅矿的选择性抑制剂在多金属硫化矿浮选过程中的应用，选择性抑制剂的用量为500-2000g/t。