CN109158525A - 一种铸造用型砂配方 - Google Patents

一种铸造用型砂配方 Download PDF

Info

Publication number
CN109158525A
CN109158525A CN201811221023.XA CN201811221023A CN109158525A CN 109158525 A CN109158525 A CN 109158525A CN 201811221023 A CN201811221023 A CN 201811221023A CN 109158525 A CN109158525 A CN 109158525A
Authority
CN
China
Prior art keywords
parts
casting
sand
chrysotile
flyash
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201811221023.XA
Other languages
English (en)
Inventor
张福新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Spheroidal Graphite Cast-Iron Factory Of Hanshan County Xingda
Original Assignee
Spheroidal Graphite Cast-Iron Factory Of Hanshan County Xingda
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Spheroidal Graphite Cast-Iron Factory Of Hanshan County Xingda filed Critical Spheroidal Graphite Cast-Iron Factory Of Hanshan County Xingda
Priority to CN201811221023.XA priority Critical patent/CN109158525A/zh
Publication of CN109158525A publication Critical patent/CN109158525A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种铸造用型砂配方，包括石英砂、铬矿砂、刚玉砂、松香、酚醛树脂、碳酸钠、玻璃纤维、粉煤灰、蛇纹石石棉、石膏粉、呋喃树脂，氢氧化镁。本发明制成的型砂能有效的减少铸造过程中产生的缺陷，减少铸造次品率，提高铸造品质。

Description

一种铸造用型砂配方
技术领域
本发明涉及一种铸造用型砂配方，属于铸造技术领域。
背景技术
铸造是将金属熔炼成符合一定要求的液体并浇进铸型里，经冷却凝固、清整处理后得到有预定形状、尺寸和性能的铸件的工艺过程。铸造毛坯因近乎成形，而达到免机械加或少量加工的目的降低了成本并在一定程度上减少了制作时间。
而在铸造中型砂是非常重要的一环，型砂在铸造生产中的作用极为重要，因型砂的质量不好而造成的铸件废品约占铸件总废品的30~50%。铸件在生产过程中经常会发生各种不同的铸造缺陷，如裂纹、气孔、砂眼、缩孔等，这些缺陷很大一部分是因为型砂的质量不好而造成的。
发明内容
为克服上述不足，本发明目的提供一种铸造用型砂配方。
本发明的方案如下：一种铸造用型砂配方，按照重量份数由以下原料组成：石英砂70~90份、铬矿砂30~40份、刚玉砂30~40份、松香20~30份、酚醛树脂40~60份、碳酸钠6~15份、玻璃纤维5~9份、粉煤灰40~60份、蛇纹石石棉8~13份、石膏粉20~30份、呋喃树脂6~9份，氢氧化镁11~21份。
优选的，按照重量份数由以下原料组成：石英砂70份、铬矿砂30份、刚玉砂30份、松香20份、酚醛树脂40份、碳酸钠6份、玻璃纤维5份、粉煤灰40份、蛇纹石石棉8份、石膏粉20份、呋喃树脂6份，氢氧化镁11份。
优选的，按照重量份数由以下原料组成：石英砂90份、铬矿砂40份、刚玉砂40份、松香30份、酚醛树脂60份、碳酸钠15份、玻璃纤维9份、粉煤灰60份、蛇纹石石棉13份、石膏粉30份、呋喃树脂9份，氢氧化镁21份。
优选的，按照重量份数由以下原料组成：石英砂80份、铬矿砂35份、刚玉砂35份、松香25份、酚醛树脂50份、碳酸钠10份、玻璃纤维7份、粉煤灰50份、蛇纹石石棉9份、石膏粉25份、呋喃树脂7份，氢氧化镁16份。
本发明的有益效果：本发明制成的型砂能有效的减少铸造过程中产生的缺陷，减少铸造次品率，提高铸造品质。
具体实施方式
实施列1
一种铸造用型砂配方，按照重量份数由以下原料组成：石英砂70份、铬矿砂30份、刚玉砂30份、松香20份、酚醛树脂40份、碳酸钠6份、玻璃纤维5份、粉煤灰40份、蛇纹石石棉8份、石膏粉20份、呋喃树脂6份，氢氧化镁11份。
实施列2
一种铸造用型砂配方，按照重量份数由以下原料组成：石英砂90份、铬矿砂40份、刚玉砂40份、松香30份、酚醛树脂60份、碳酸钠15份、玻璃纤维9份、粉煤灰60份、蛇纹石石棉13份、石膏粉30份、呋喃树脂9份，氢氧化镁21份。
实施列3
一种铸造用型砂配方，按照重量份数由以下原料组成：石英砂80份、铬矿砂35份、刚玉砂35份、松香25份、酚醛树脂50份、碳酸钠10份、玻璃纤维7份、粉煤灰50份、蛇纹石石棉9份、石膏粉25份、呋喃树脂7份，氢氧化镁16份。
尽管上文对本发明的具体实施方式给予了详细描述和说明，但是应该指明的是，我们可以依据本发明的构想对上述实施方式进行各种等效改变和修改，其所产生的功能作用仍未超出说明书所涵盖的精神时，均应在本发明的保护范围之内。

Claims (4)

1.一种铸造用型砂配方，其特征在于，按照重量份数由以下原料组成：石英砂70~90份、铬矿砂30~40份、刚玉砂30~40份、松香20~30份、酚醛树脂40~60份、碳酸钠6~15份、玻璃纤维5~9份、粉煤灰40~60份、蛇纹石石棉8~13份、石膏粉20~30份、呋喃树脂6~9份，氢氧化镁11~21份。
2.根据权利要求1所述一种铸造用型砂配方，其特征在于，按照重量份数由以下原料组成：石英砂70份、铬矿砂30份、刚玉砂30份、松香20份、酚醛树脂40份、碳酸钠6份、玻璃纤维5份、粉煤灰40份、蛇纹石石棉8份、石膏粉20份、呋喃树脂6份，氢氧化镁11份。
3.根据权利要求1所述一种铸造用型砂配方，其特征在于，按照重量份数由以下原料组成：石英砂90份、铬矿砂40份、刚玉砂40份、松香30份、酚醛树脂60份、碳酸钠15份、玻璃纤维9份、粉煤灰60份、蛇纹石石棉13份、石膏粉30份、呋喃树脂9份，氢氧化镁21份。
4.根据权利要求1所述一种铸造用型砂配方，其特征在于，按照重量份数由以下原料组成：石英砂80份、铬矿砂35份、刚玉砂35份、松香25份、酚醛树脂50份、碳酸钠10份、玻璃纤维7份、粉煤灰50份、蛇纹石石棉9份、石膏粉25份、呋喃树脂7份，氢氧化镁16份。
CN201811221023.XA 2018-10-19 2018-10-19 一种铸造用型砂配方 Withdrawn CN109158525A (zh)