CN109054124A - 一种舒适乳胶垫片及女鞋 - Google Patents
一种舒适乳胶垫片及女鞋 Download PDFInfo
- Publication number
- CN109054124A CN109054124A CN201810637748.0A CN201810637748A CN109054124A CN 109054124 A CN109054124 A CN 109054124A CN 201810637748 A CN201810637748 A CN 201810637748A CN 109054124 A CN109054124 A CN 109054124A
- Authority
- CN
- China
- Prior art keywords
- comfortable
- natural emulsion
- latex gasket
- comfortable latex
- gasket
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种舒适乳胶垫片及女鞋。本发明通过在天然乳胶中添加石墨烯微片、微晶纤维素从而制备得到舒适、柔软、高耐磨性与抗菌性的舒适乳胶垫片。将该舒适乳胶垫片缝制在女鞋后跟围护鞋帮的内表面或者通过涂胶贴合于女鞋后跟围护鞋帮的内表面,使舒适乳胶垫片用于与脚后跟的接触,可有效减少脚后跟与鞋后跟之间的摩擦。与现有技术相比,本发明的舒适乳胶垫片不仅具有良好的抗菌性,还具有优异的韧性、耐磨性、柔软性。将舒适乳胶垫片应用于女鞋中可有效保护肌肤,提高了人体走动时的舒适性。
Description
技术领域
本发明涉及一种舒适乳胶垫片及女鞋,属于鞋类加工技术领域。
背景技术
追求时尚的女性大多喜欢穿高跟鞋,因为高跟鞋能够增加人的身高,使身材显得苗条、秀丽。高跟鞋渐渐成为每个女人的最爱,高跟鞋的性感、妩媚、淑女等百变形态是女性必备的武器。每年每季度,女性都会挑选出适合他们的高跟鞋,不管是什么样式和风格,都在细细的根上为女性带来自信与风韵。
但是高跟鞋后跟壁较硬,走路时间长了,脚就会有点酸痛,还会有些磨脚,或许刚买的新丝袜,因走了长时间的路,就有些磨损,给美丽的外表带来瑕疵。
天然乳胶(也称天然橡胶乳胶)是橡胶树割胶时流出的液体,呈乳白色,固含量为30%~40%,橡胶粒径平均为1.06微米。新鲜的天然乳胶含有橡胶成分、水、蛋白质、天然树脂、糖类、灰分等。天然乳胶主要用于制作海绵制品、压出制品和浸渍制品。
为了解决上述问题,本发明利用天然乳胶,制备了一种舒适乳胶鞋垫,将该舒适乳胶鞋垫缝制在女鞋后跟围护鞋帮的内表面,能很好的保护女性的脚跟,有效防止走路磨脚或磨损丝袜。
发明内容
本发明的目的之一在于提供一种舒适乳胶垫片,通过在天然乳胶中添加石墨烯微片、微晶纤维素以及能改善其在天然乳胶中分散性的分散剂,从而制备得到舒适、柔软、高耐磨性与抗菌性的舒适乳胶垫片。
本发明的另一目的在于提供一种女鞋,将舒适乳胶垫片缝制在女鞋后跟围护鞋帮的内表面,舒适乳胶垫片用于与脚后跟的接触,可有效减少后脚跟与鞋后跟之间的摩擦。
其技术解决方案包括:
一种舒适乳胶垫片,包括以下原料:天然乳胶、硫化剂、促进剂、稳定剂、抗菌剂、氧化锌、填料、分散剂、水。
一种舒适乳胶垫片,由以下重量份计的原料制备而成:天然乳胶200~350份、硫化剂0.8~2.4份、促进剂0.4~3份、稳定剂1~3份、抗菌剂0.8~2.4份、氧化锌0.8~1.4份、填料1~3份、分散剂0.3~1.5份、水30~40份。
可选的,所述硫化剂为硫磺。
可选的,所述促进剂为促进剂PX、促进剂ZDC、2-巯基苯并噻唑、二乙基二硫代氨基甲酸锌中的一种或者多种的混合;此外优选所述促进剂2-巯基苯并噻唑。
可选的,所述稳定剂为氢氧化钾、去甲二氢愈创木酸、酪素中的一种或者多种的混合。此外优选,所述稳定剂为去甲二氢愈创木酸。
优选的,所述抗菌剂为纳米银和/或茶树油β-环糊精包合物。此外优选,所述抗菌剂为茶树油β-环糊精包合物。
茶树油又称为澳大利亚黄金,是澳洲土著传说中著名的神奇肌肤治疗用品,是一种强有力的天然抗菌剂。但茶树油不稳定易挥发,其中的成分在光或氧作用下,生成具有皮肤刺激性的p-异丙基苯。本发明添加的茶树油β-环糊精包合物安全稳定,无刺激性气味,能相容于本发明的天然乳胶中,最终得到具备良好抗菌性的舒适乳胶垫片。
优选的,所述填料为石墨烯微片和/或微晶纤维素。
进一步优选的,所述填料为石墨烯微片和微晶纤维素按质量比(1.5~3.2):1混合而成。
石墨烯微片具备优良的物理性能,添加一定量的石墨烯微片至天然乳胶中能够显著改善天然乳胶的耐磨性、舒适型。
本发明的微晶纤维素有助于改善天然乳胶的粘度,在天然乳胶硫化过程中能起到一定的制孔作用,丰富的多孔结构能够有利于抗菌效果的进一步提升。
优选的,所述微晶纤维素的制备方法如下:
a)将干玉米棒粉碎至10~20目,得到玉米棒粉末;取70~80g玉米棒粉末加入到玻璃烧杯中,加入0.8~1.2L浓度为3.5wt%硝酸水溶液、8~12mg亚硝酸钠,在100~300转/分、75~95℃条件下搅拌加热1.5~3小时,500目网纱过滤,得到的滤饼用蒸馏水洗涤至滤液呈中性;接着,将洗涤后的滤饼加入到700~800mL碱性水溶液中(其中氢氧化钠的浓度为2wt%,亚硫酸钠的浓度为2wt%)在45~55℃保温0.8~1.5h,500目网纱过滤,得到的滤饼用蒸馏水洗涤至滤液呈中性;接着加入到200~300mL浓度为1.75wt%NaOCl水溶液中,煮沸25~40min,500目网纱过滤,得到的滤饼用蒸馏水洗涤至滤液呈中性;接着加入到400~600mL浓度为17.5wt%NaOH水溶液中,在75~90℃保温20~35min,500目网纱过滤,得到的滤饼用蒸馏水洗涤至滤液呈中性;接着到180~220mL浓度为10wt%H2O2水溶液中在55~70℃下保温0.8~1.5h,500目网纱过滤,得到的滤饼用蒸馏水洗涤至滤液呈中性,得到的滤饼在绝对压强为0.08MPa、温度为60℃的条件下干燥8~20h,即得α-纤维素;
b)取0.8~1.2gα-纤维素加入到20~30mL浓度为45wt%硫酸水溶液中在100~300转/分、40~50℃下保温40~50min,接着冷却至室温(25℃),加入20~30mL蒸馏水,静置10~15h,在8000~12000转/分的条件下离心20~30min,得到的沉淀洗涤至上清液呈中性,得到的沉淀洗涤加入到8~15mL蒸馏水中在超声功率为135W、超声频率为42KHz的条件下超声分散5~15min,得到分散液,将分散液装入截留分子量为5000的透析袋中,浸没在100mL蒸馏水中透析3~4天中,每8h更换一次蒸馏水,得到的透析液(透析袋中的液体为透析液)喷雾干燥,得到微晶纤维素。所述喷雾干燥的进风温度为170~185℃,出风温度为80~92℃,热风风速为3~5m3/min,供料速度为35~50mL/min,雾化机转速为200~350r/min。
优选的,所述分散剂为十二烷基硫酸钠、十二烷基苯磺酸钠、N-乙基-N-(2-羟基-3-磺丙基)-3-甲基苯胺钠、聚乙烯吡咯烷酮中的一种或者多种。
进一步优选的,所述分散剂为N-乙基-N-(2-羟基-3-磺丙基)-3-甲基苯胺钠和聚乙烯吡咯烷酮按质量比(1~3):1混合而成。
N-乙基-N-(2-羟基-3-磺丙基)-3-甲基苯胺钠:简称TOOS,CAS号:82692-93-1,能够显著的改善石墨烯微片在天然乳胶中的分散性。
上述舒适乳胶垫片的制备方法,包括以下步骤:
S1按配比称取原料,将天然乳胶、稳定剂、硫化剂、促进剂在30~40℃的条件下搅拌6~10h,得到预硫化天然乳胶;
S2将预硫化天然乳胶进行发泡,在发泡后的硫化天然乳胶中依次添加抗菌剂、氧化锌、填料、分散剂、水,搅拌均匀,置于模具中,在95~105℃下热烘45~60分钟,接着在70~75℃下恒温3~5h,得到固化后的天然乳胶;
S3将固化后的天然乳胶通风、按生产尺寸剪切,即得所述舒适乳胶垫片。
本发明还公开了上述舒适乳胶垫片在制备女鞋上的应用。
具体应用如下:将舒适乳胶垫片缝制在女鞋后跟围护鞋帮的内表面,使舒适乳胶垫片用于与脚后跟的接触,可有效减少后脚跟与鞋后跟之间的摩擦,提高舒适性。
本发明的舒适乳胶垫片也可通过涂胶贴合于女鞋后跟围护鞋帮的内表面,使舒适乳胶垫片用于与脚后跟的接触,可有效减少后脚跟与鞋后跟之间的摩擦。
所述女鞋后跟围护鞋帮的内表面也称作女鞋后跟内衬。
本发明带来的技术效果有:
(1)本发明舒适乳胶垫片不仅具有良好抑菌性,还具有优异的韧性、耐磨性、柔软性;将舒适乳胶垫片应用于女鞋中可有效减少后脚跟与鞋后跟之间的摩擦,有效保护肌肤,提高了人体走动时的舒适性。
(2)本发明制得的舒适乳胶垫片具有良好的耐磨性能与柔软性,在用作鞋后跟垫片时不仅具有良好的缓冲耐磨作用,还具有良好的舒适性。不仅如此,本发明所得舒适乳胶垫片具有良好的抑菌性,对大金黄色葡萄球菌具备良好的抑制作用。
(3)本发明添加的微晶纤维素是通过废弃玉米棒制备得到的,有效的利用废弃物,合理利用资源,对环境保护作出了一定的贡献。
具体实施方式
实施例中各原料来源:
若非特指,本发明中所述的化学物质,均为分析纯的市售商品。
天然乳胶:平均总固形物约为36%,干胶含量34.5%,氨含量≤0.72%,碱度≤0.65,机械稳定度≥650,挥发脂肪酸≤0.05,产地:泰国。
硫磺:CAS号7704-34-9,含量99%。
2-巯基苯并噻唑:CAS号149-30-4。
去甲二氢愈创木酸:CAS号500-38-9。
茶树油β-环糊精包合物:按照周衡刚等“茶树油β-环糊精包合物的制备工艺研究”广东化工,2010年第2期第37卷总第202一文中规定的方法制备得到。
石墨烯微片:平均厚度0.98~3.54nm,使用前在70℃下烘6h。
N-乙基-N-(2-羟基-3-磺丙基)-3-甲基苯胺钠:简称TOOS,CAS号:82692-93-1。
聚乙烯吡咯烷酮:简称PVP,CAS号9003-39-8,能显著改善微晶纤维素在天然乳胶中的分散性,本发明采用型号K90,山东佰鸿新材料有限公司。
十二烷基苯磺酸钠:简称SDS,CAS号25155-30-0。
实施例1
一种女鞋,将舒适乳胶垫片缝制在女鞋后跟内衬上。使得舒适乳胶垫片用于与脚后跟的接触,极大的减少后脚跟与鞋后跟之间的摩擦。
所述舒适乳胶垫片为实施例3中制备得到的舒适乳胶垫片。
实施例2
微晶纤维素的制备方法:
a)将干玉米棒粉碎至10目,得到玉米棒粉末;取75g玉米棒粉末加入到玻璃烧杯中,加入1L浓度为3.5wt%硝酸水溶液、10mg亚硝酸钠,在200转/分、90℃条件下搅拌加热2小时,500目网纱过滤,得到的滤饼用蒸馏水洗涤至滤液呈中性;接着,将洗涤后的滤饼加入到750mL碱性水溶液中(其中氢氧化钠的浓度为2wt%,亚硫酸钠的浓度为2wt%)在50℃保温1h,500目网纱过滤,得到的滤饼用蒸馏水洗涤至滤液呈中性;接着加入到250mL浓度为1.75wt%NaOCl水溶液中,煮沸30min,500目网纱过滤,得到的滤饼用蒸馏水洗涤至滤液呈中性;接着加入到500mL浓度为17.5wt%NaOH水溶液中,在80℃保温30min,500目网纱过滤,得到的滤饼用蒸馏水洗涤至滤液呈中性;接着到200mL浓度为10wt%H2O2水溶液中在60℃下保温1h,500目网纱过滤,得到的滤饼用蒸馏水洗涤至滤液呈中性,得到的纤维在绝对压强为0.08MPa、温度为60℃的条件下干燥12h,即得α-纤维素;
b)取1gα-纤维素加入到25mL浓度为45wt%硫酸水溶液中在200转/分、45℃下保温45min,接着冷却至室温(25℃),加入25mL蒸馏水,静置12h,在10000转/分的条件下离心25min,得到的沉淀洗涤至上清液呈中性,得到的沉淀洗涤加入到10mL蒸馏水中在超声功率为135W、超声频率为42KHz的条件下超声分散10min,得到分散液,将分散液装入截留分子量为5000的透析袋中,浸没在100mL蒸馏水中透析4天中,每8h更换一次蒸馏水,得到的透析液(透析袋中的液体为透析液)喷雾干燥,得到微晶纤维素。所述喷雾干燥的进风温度为180℃,出风温度为85℃,热风风速为4m3/min,供料速度为40mL/min,雾化机转速为300r/min。
实施例3
一种舒适乳胶垫片,由以下重量份计的原料制备而成:天然乳胶280份、硫化剂1.1份、促进剂0.7份、稳定剂0.8份、抗菌剂1.5份、氧化锌0.8份、填料1.5份、分散剂0.8份、水40份。
所述硫化剂为硫磺。
所述促进剂2-巯基苯并噻唑。
所述稳定剂为去甲二氢愈创木酸。
所述抗菌剂为茶树油β-环糊精包合物。
所述填料为石墨烯微片。
所述分散剂为十二烷基苯磺酸钠。
上述舒适乳胶垫片的制备方法,包括以下步骤:
S1按配比称取原料,将天然乳胶、稳定剂、硫化剂、促进剂在200转/分、35℃的条件下搅拌8h,得到预硫化天然乳胶;
S2将预硫化天然乳胶加入到PLC控制全自动CJ-30型乳胶发泡机(青岛程进机械制造有限公司)进行发泡,控制发泡倍率为15倍,在发泡后的硫化天然乳胶中依次添加抗菌剂、氧化锌、填料、分散剂、水,300转/分的条件下搅拌10min,置于模具中,在70℃下烘烤定型,接着在70℃下恒温4h,脱模,得到固化后的天然乳胶;
S3将固化后的天然乳胶通风、按生产尺寸剪切,即得所述舒适乳胶垫片。
实施例4
一种舒适乳胶垫片,由以下重量份计的原料制备而成:天然乳胶280份、硫化剂1.1份、促进剂0.7份、稳定剂0.8份、抗菌剂1.5份、氧化锌0.8份、填料1.5份、分散剂0.8份、水40份。
所述硫化剂为硫磺。
所述促进剂2-巯基苯并噻唑。
所述稳定剂为去甲二氢愈创木酸。
所述抗菌剂为茶树油β-环糊精包合物。
所述填料为微晶纤维素。
所述微晶纤维素的制备方法同实施例2一致,此处不再赘述。
所述分散剂为十二烷基苯磺酸钠。
上述舒适乳胶垫片的制备方法,包括以下步骤:
S1按配比称取原料,将天然乳胶、稳定剂、硫化剂、促进剂在200转/分、35℃的条件下搅拌8h,得到预硫化天然乳胶;
S2将预硫化天然乳胶加入到PLC控制全自动CJ-30型乳胶发泡机(青岛程进机械制造有限公司)进行发泡,控制发泡倍率为15倍,在发泡后的硫化天然乳胶中依次添加抗菌剂、氧化锌、填料、分散剂、水,300转/分的条件下搅拌10min,置于模具中,在70℃下烘烤定型,接着在70℃下恒温4h,脱模,得到固化后的天然乳胶;
S3将固化后的天然乳胶通风、按生产尺寸剪切,即得所述舒适乳胶垫片。
实施例5
一种舒适乳胶垫片,由以下重量份计的原料制备而成:天然乳胶280份、硫化剂1.1份、促进剂0.7份、稳定剂0.8份、抗菌剂1.5份、氧化锌0.8份、填料1.5份、分散剂0.8份、水40份。
所述硫化剂为硫磺。
所述促进剂2-巯基苯并噻唑。
所述稳定剂为去甲二氢愈创木酸。
所述抗菌剂为茶树油β-环糊精包合物。
所述填料为石墨烯微片和微晶纤维素按质量比2.5:1混合而成。
所述微晶纤维素的制备方法同实施例2一致,此处不再赘述。
所述分散剂为十二烷基苯磺酸钠。
上述舒适乳胶垫片的制备方法,包括以下步骤:
S1按配比称取原料,将天然乳胶、稳定剂、硫化剂、促进剂在200转/分、35℃的条件下搅拌8h,得到预硫化天然乳胶;
S2将预硫化天然乳胶加入到PLC控制全自动CJ-30型乳胶发泡机(青岛程进机械制造有限公司)进行发泡,控制发泡倍率为15倍,在发泡后的硫化天然乳胶中依次添加抗菌剂、氧化锌、填料、分散剂、水,300转/分的条件下搅拌10min,置于模具中,在70℃下烘烤定型,接着在70℃下恒温4h,脱模,得到固化后的天然乳胶;
S3将固化后的天然乳胶通风、按生产尺寸剪切,即得所述舒适乳胶垫片。
实施例6
一种舒适乳胶垫片,由以下重量份计的原料制备而成:天然乳胶280份、硫化剂1.1份、促进剂0.7份、稳定剂0.8份、抗菌剂1.5份、氧化锌0.8份、填料1.5份、分散剂0.8份、水40份。
所述硫化剂为硫磺。
所述促进剂2-巯基苯并噻唑。
所述稳定剂为去甲二氢愈创木酸。
所述抗菌剂为茶树油β-环糊精包合物。
所述填料为石墨烯微片和微晶纤维素按质量比2.5:1混合而成。
所述微晶纤维素的制备方法同实施例2一致,此处不再赘述。
所述分散剂为N-乙基-N-(2-羟基-3-磺丙基)-3-甲基苯胺钠。
上述舒适乳胶垫片的制备方法,包括以下步骤:
S1按配比称取原料,将天然乳胶、稳定剂、硫化剂、促进剂在200转/分、35℃的条件下搅拌8h,得到预硫化天然乳胶;
S2将预硫化天然乳胶加入到PLC控制全自动CJ-30型乳胶发泡机(青岛程进机械制造有限公司)进行发泡,控制发泡倍率为15倍,在发泡后的硫化天然乳胶中依次添加抗菌剂、氧化锌、填料、分散剂、水,300转/分的条件下搅拌10min,置于模具中,在70℃下烘烤定型,接着在70℃下恒温4h,脱模,得到固化后的天然乳胶;
S3将固化后的天然乳胶通风、按生产尺寸剪切,即得所述舒适乳胶垫片。
实施例7
一种舒适乳胶垫片,由以下重量份计的原料制备而成:天然乳胶280份、硫化剂1.1份、促进剂0.7份、稳定剂0.8份、抗菌剂1.5份、氧化锌0.8份、填料1.5份、分散剂0.8份、水40份。
所述硫化剂为硫磺。
所述促进剂2-巯基苯并噻唑。
所述稳定剂为去甲二氢愈创木酸。
所述抗菌剂为茶树油β-环糊精包合物。
所述填料为石墨烯微片和微晶纤维素按质量比2.5:1混合而成。
所述微晶纤维素的制备方法同实施例2一致,此处不再赘述。
所述分散剂为聚乙烯吡咯烷酮。
上述舒适乳胶垫片的制备方法,包括以下步骤:
S1按配比称取原料,将天然乳胶、稳定剂、硫化剂、促进剂在200转/分、35℃的条件下搅拌8h,得到预硫化天然乳胶;
S2将预硫化天然乳胶加入到PLC控制全自动CJ-30型乳胶发泡机(青岛程进机械制造有限公司)进行发泡,控制发泡倍率为15倍,在发泡后的硫化天然乳胶中依次添加抗菌剂、氧化锌、填料、分散剂、水,300转/分的条件下搅拌10min,置于模具中,在70℃下烘烤定型,接着在70℃下恒温4h,脱模,得到固化后的天然乳胶;
S3将固化后的天然乳胶通风、按生产尺寸剪切,即得所述舒适乳胶垫片。
实施例8
一种舒适乳胶垫片,由以下重量份计的原料制备而成:天然乳胶280份、硫化剂1.1份、促进剂0.7份、稳定剂0.8份、抗菌剂1.5份、氧化锌0.8份、填料1.5份、分散剂0.8份、水40份。
所述硫化剂为硫磺。
所述促进剂2-巯基苯并噻唑。
所述稳定剂为去甲二氢愈创木酸。
所述抗菌剂为茶树油β-环糊精包合物。
所述填料为石墨烯微片和微晶纤维素按质量比2.5:1混合而成。
所述微晶纤维素的制备方法同实施例2一致,此处不再赘述。
所述分散剂为N-乙基-N-(2-羟基-3-磺丙基)-3-甲基苯胺钠和聚乙烯吡咯烷酮按质量比2.5:1混合而成。
上述舒适乳胶垫片的制备方法,包括以下步骤:
S1按配比称取原料,将天然乳胶、稳定剂、硫化剂、促进剂在200转/分、35℃的条件下搅拌8h,得到预硫化天然乳胶;
S2将预硫化天然乳胶加入到PLC控制全自动CJ-30型乳胶发泡机(青岛程进机械制造有限公司)进行发泡,控制发泡倍率为15倍,在发泡后的硫化天然乳胶中依次添加抗菌剂、氧化锌、填料、分散剂、水,300转/分的条件下搅拌10min,置于模具中,在70℃下烘烤定型,接着在70℃下恒温4h,脱模,得到固化后的天然乳胶;
S3将固化后的天然乳胶通风、按生产尺寸剪切,即得所述舒适乳胶垫片。
测试例1
实施例制备的舒适乳胶垫片的耐磨性能、硬度分别参考标准“GB/T 3903.1-2008鞋类通用试验方法耐折性能”和“HG/T2489-2007鞋用微孔材料硬度试验方法”进行检测。
表1:耐磨性能、硬度测试结果
耐磨性能(磨痕长度,mm) | 硬度 | |
实施例3 | 16.8 | 13 |
实施例4 | 16.2 | 13 |
实施例5 | 18.6 | 11 |
实施例6 | 17.5 | 10 |
实施例7 | 18.2 | 10 |
实施例8 | 20.7 | 8 |
从上表可以看出,实施例8制备得到的舒适乳胶垫片的耐磨性、硬度均较实施例5~7制备得到的舒适乳胶垫片更加优良。其原因可能在于,石墨烯微片与微晶纤维素片不同结构使其需要不同的表面活性剂改善其在天然乳胶中的分散性;N-乙基-N-(2-羟基-3-磺丙基)-3-甲基苯胺钠有助于石墨烯微片的分散,聚乙烯吡咯烷酮有助于微晶纤维素的分散,当两种分散剂同时存在其协同作用使得石墨烯微片与微晶纤维素片良好的分散在天然乳胶中,使得制备得到的舒适乳胶垫片的耐磨性更好,硬度更低,手感更加舒适。
测试例2
实施例制备得到的舒适乳胶垫片的抗菌性能参考国家标准GB/T20944.3-2008《纺织品抗菌性能的评价第3部分:振荡法》进行测试,以金黄色葡萄球菌ATCC No.6538(革兰氏阳性菌)为试验菌种。
表2:舒适乳胶垫片的抗菌性
抑菌率 | |
实施例5 | 90.2% |
实施例6 | 91.3% |
实施例7 | 93.6% |
实施例8 | 99.7% |
以上对本发明进行了详细介绍,本文中应用了具体个例对本发明的原理及实施方式进行了阐述,以上实施例的说明只是用于帮助理解本发明的方法及其核心思想;同时,对于本领域的一般技术人员,依据本发明的思想,在具体实施方式及应用范围上均会有改变之处,综上所述,本说明书内容不应理解为对本发明的限制。
Claims (10)
1.一种舒适乳胶垫片,其特征在于,包括以下原料:天然乳胶、硫化剂、促进剂、稳定剂、抗菌剂、氧化锌、填料、分散剂、水。
2.一种舒适乳胶垫片,其特征在于,由以下重量份计的原料制备而成:天然乳胶200~350份、硫化剂0.8~2.4份、促进剂0.4~3份、稳定剂1~3份、抗菌剂0.8~2.4份、氧化锌0.8~1.4份、填料1~3份、分散剂0.3~1.5份、水30~40份。
3.如权利要求2所述的舒适乳胶垫片,其特征在于:所述硫化剂为硫磺。
4.如权利要求2所述的舒适乳胶垫片,其特征在于:所述促进剂为促进剂PX、促进剂ZDC、2-巯基苯并噻唑、二乙基二硫代氨基甲酸锌中的一种或者多种的混合。
5.如权利要求2所述的舒适乳胶垫片,其特征在于:所述稳定剂为氢氧化钾、去甲二氢愈创木酸、酪素中的一种或者多种的混合。
6.如权利要求2所述的舒适乳胶垫片,其特征在于:所述抗菌剂为纳米银和/或茶树油β-环糊精包合物。
7.如权利要求2所述的舒适乳胶垫片,其特征在于:所述填料为石墨烯微片和/或微晶纤维素。
8.如权利要求2所述的舒适乳胶垫片,其特征在于:所述分散剂为十二烷基硫酸钠、十二烷基苯磺酸钠、N-乙基-N-(2-羟基-3-磺丙基)-3-甲基苯胺钠、聚乙烯吡咯烷酮中的一种或者多种的混合。
9.如权利要求1~8任一项所述的舒适乳胶垫片的制备方法,其特征在于,包括以下步骤:
S1按配比称取原料,将天然乳胶、稳定剂、硫化剂、促进剂在30~40℃的条件下搅拌6~10h,得到预硫化天然乳胶;
S2将预硫化天然乳胶进行发泡,在发泡后的硫化天然乳胶中依次添加抗菌剂、氧化锌、填料、分散剂、水,搅拌均匀,置于模具中,在95~105℃下热烘45~60分钟,接着在70~75℃下恒温3~5h,得到固化后的天然乳胶;
S3将固化后的天然乳胶通风、按生产尺寸剪切,即得所述舒适乳胶垫片。
10.如权利要求1~8任一项所述的舒适乳胶垫片在制备女鞋上的应用。