CN108862386A - 一种钼酸钠的制备方法 - Google Patents
一种钼酸钠的制备方法 Download PDFInfo
- Publication number
- CN108862386A CN108862386A CN201810655493.0A CN201810655493A CN108862386A CN 108862386 A CN108862386 A CN 108862386A CN 201810655493 A CN201810655493 A CN 201810655493A CN 108862386 A CN108862386 A CN 108862386A
- Authority
- CN
- China
- Prior art keywords
- sodium
- molybdate
- molybdenum
- ammonium molybdate
- sodium nitrite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种钼酸钠的制备方法,其特征在于:在常温下,把浓度为1.0g/L‑50g/L的亚硝酸钠溶液逐滴加入到浓度为1.0g/L‑50g/L的钼酸铵溶液中,控制钠与钼的原子摩尔比为2:1,不断搅拌,随即产生白色沉淀,陈化12h后,分别用蒸馏水和无水乙醇洗涤3次,过滤、干燥后,即制得白色片状的钼酸钠成品。本发明的有益效果:以钼酸铵和亚硝酸钠为原料制备出钼酸钠,过滤后的亚硝酸母液可作制备亚硝酸钠的原料,具有成本低,反应条件温和,操作方便、易控制、重复性好的特点,制备出的样品颗粒均匀。
Description
技术领域
本发明属化学制剂制备领域,涉及一种钼酸钠的制备方法。
背景技术
随着社会的进步以及飞速发展,钼获得了很广泛的利用,尤其是钼酸盐在抑制剂和缓蚀剂方面有着很大的应用价值。目前,我国钼工业的消费及加工有几个方面。第一,是将钼精矿加工成冶金炉料成品后应用于钢铁行业、有色金属行业;第二,防腐是属于化工行业一类,首先是将钼加工成钼酸盐或氧化钼,并进一步加工成钼催化剂、颜料等;第三,是以钼金属或钼基合金的形式用于高温环境下使用的机械或设施、器具的结构部件或功能性部件。不锈钢和特种钢是钼的主要应用领域,以及催化剂和化工类的用钼量逐渐增加。
钼酸钠(Na2MoO4·2H2O)是一种重要的无机钼酸盐,为白色菱形结晶,微溶于水,它的产量和销量仅次于钼酸铵物质。钼酸钠主要用于化工、催化剂、搪瓷、染料、颜料、钼盐、缓蚀剂、清洗剂、润滑剂、微量元素肥料等领域。钼酸钠是一种无公害型冷却水系统的金属缓蚀剂,可以作为缓蚀剂代替有毒的铬酸盐等物质,成为环保的首选物质。
目前,钼酸钠的生产方法主要有两种:(1) 钼酸铵液碱(纯碱)法,即以钼酸铵为原材料,让其溶解于氢氧化钠或碳酸钠溶液中,制备得钼酸钠晶体;(2) 氧化钼液碱(纯碱)法,即以氧化钼为原材料,让其溶解于氢氧化钠或碳酸钠溶液中,制备得钼酸钠晶体。此外,还有焙烧液碱(纯碱)法、纯碱硝石烧结法、碱湿法、酸湿法、水热法等。这些方法存在合成过程复杂、原料价格高,产生有毒气体,产品颗粒比较大等一些缺点。随着社会的发展,钼酸钠因成本较低,缓蚀性良好,在缓蚀剂方面的需求量是越来越大,质量要求越来越高,因此开展钼酸钠的实验研究具有十分重要的意义。
发明内容
本发明的目的在于解决现有钼酸钠生产成本高、合成过程复杂的问题,提供一种钼酸钠的制备方法。
为实现上述目的,本发明采用的技术方案如下:
一种钼酸钠的制备方法,其特征在于:
a.在常温下(20-25℃),把浓度为1.0 g/L - 50 g/L的亚硝酸钠溶液逐滴加入到浓度为1.0 g/L -50 g/L的钼酸铵溶液中,控制钠与钼的原子摩尔比为2:1,不断搅拌,随即产生白色沉淀,陈化12 h使沉淀聚沉后,分别用蒸馏水和无水乙醇洗涤3次,过滤、干燥后,即制得白色片状的钼酸钠成品。
进一步,所述亚硝酸钠包括工业亚硝酸钠,或由钠盐(硝酸钠、碳酸钠)制备出的亚硝酸钠。
进一步,所述钼酸铵包括工业钼酸铵,或由钼盐(二硫化钼、三氧化钼)制备出的钼酸铵。
以钼酸铵和亚硝酸钠为原料,在常温下采用化学液相反应生成钼酸钠和亚硝酸铵。由于亚硝酸铵不稳定,常温时即逐渐分解为氮气和水,所以促使钼酸钠有序生成,防止产物颗粒过大,可以控制产品粒径大小。过滤后的亚硝酸母液可作制备亚硝酸钠的原料,具有成本低廉、反应条件温和、操作方便、易控制、重复性好等特点,制备出的样品颗粒均匀。
本发明的有益效果:以钼酸铵和亚硝酸钠为原料制备出钼酸钠,过滤后的亚硝酸母液可作制备亚硝酸钠的原料,具有成本低,反应条件温和,操作方便、易控制、重复性好的特点,制备出的样品颗粒均匀。
附图说明
图1是采用本方法制备的钼酸钠产品。
具体实施方式
实施例一
准确称取1.7111克工业亚硝酸钠,溶于100 mL蒸馏水中,制得亚硝酸钠溶液,准确称取2.1891克工业钼酸铵,溶于100 mL蒸馏水中,制得钼酸铵溶液;在20℃条件下,把亚硝酸钠溶液逐滴加入到钼酸铵溶液中,并不断搅拌,随即产生白色沉淀,陈化12 h后,分别用蒸馏水和无水乙醇洗涤3次,用滤纸过滤过滤、在70 ℃烘箱里干燥12 h后,即制得2.9057克白色片状的钼酸钠产品。
实施例二
准确称取1.7111克工业亚硝酸钠,溶于50 mL蒸馏水中,制得亚硝酸钠溶液,准确称取2.1891克工业钼酸铵,溶于50 mL蒸馏水中,制得钼酸铵溶液;在25℃条件下,把亚硝酸钠溶液逐滴加入到钼酸铵溶液中,并不断搅拌,随即产生白色沉淀,陈化12 h后,分别用蒸馏水和无水乙醇洗涤3次,用滤纸过滤过滤、在70 ℃烘箱里干燥12 h后,即制得2.9586克白色片状的钼酸钠产品。
以上所述仅为本发明的优选实施方式,应当指出,对于本领域的普通技术人员来说,在不脱离本发明创造构思的前提下,做出若干改进和变换,这些都属于本发明的保护范围。
Claims (3)
1.一种钼酸钠的制备方法,其特征在于采用以下步骤:
在常温下,把浓度为1.0 g/L - 50 g/L的亚硝酸钠溶液逐滴加入到浓度为1.0 g/L -50 g/L的钼酸铵溶液中,控制钠与钼的原子摩尔比为2:1,不断搅拌,随即产生白色沉淀,陈化12 h后,分别用蒸馏水和无水乙醇洗涤3次,过滤、干燥后,即制得白色片状的钼酸钠成品。
2.根据权利要求1所述一种钼酸钠的制备方法,其特征在于亚硝酸钠包括工业亚硝酸钠,或由钠盐制备出的亚硝酸钠。
3.根据权利要求1所述一种钼酸钠的制备方法,其特征在于钼酸铵包括工业钼酸铵,或由钼盐制备出的钼酸铵。