CN108793735B - 一种玻璃组合物以及耐油污玻璃及其制备方法与应用 - Google Patents
一种玻璃组合物以及耐油污玻璃及其制备方法与应用 Download PDFInfo
- Publication number
- CN108793735B CN108793735B CN201810709640.8A CN201810709640A CN108793735B CN 108793735 B CN108793735 B CN 108793735B CN 201810709640 A CN201810709640 A CN 201810709640A CN 108793735 B CN108793735 B CN 108793735B
- Authority
- CN
- China
- Prior art keywords
- glass
- glass composition
- tio
- content
- caf
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
实施例1 | 擦拭3次后无指纹残留 |
实施例2 | 擦拭3次后无指纹残留 |
实施例3 | 擦拭2次后无指纹残留 |
实施例4 | 擦拭2次后无指纹残留 |
实施例5 | 擦拭3次后无指纹残留 |
实施例6 | 擦拭2次后无指纹残留 |
实施例7 | 擦拭1次后无指纹残留 |
实施例8 | 擦拭1次后无指纹残留 |
对比例1 | 擦拭7次后无指纹残留 |
对比例2 | 擦拭8次后无指纹残留 |
对比例3 | 擦拭8次后无指纹残留 |
Claims (10)