CN108486933B - 一种分散型阳离子染料喷墨墨水及其数码印花工艺 - Google Patents

一种分散型阳离子染料喷墨墨水及其数码印花工艺 Download PDF

Info

Publication number
CN108486933B
CN108486933B CN201810219022.5A CN201810219022A CN108486933B CN 108486933 B CN108486933 B CN 108486933B CN 201810219022 A CN201810219022 A CN 201810219022A CN 108486933 B CN108486933 B CN 108486933B
Authority
CN
China
Prior art keywords
parts
cationic dye
cation
ink
color paste
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201810219022.5A
Other languages
English (en)
Other versions
CN108486933A (zh
Inventor
秦国胜
孙志国
冒晓东
袁福顺
赵雪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hongsam Digital Science & Technology Co ltd
Original Assignee
Hongsam Digital Science & Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hongsam Digital Science & Technology Co ltd filed Critical Hongsam Digital Science & Technology Co ltd
Priority to CN201810219022.5A priority Critical patent/CN108486933B/zh
Publication of CN108486933A publication Critical patent/CN108486933A/zh
Application granted granted Critical
Publication of CN108486933B publication Critical patent/CN108486933B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种分散型阳离子染料喷墨墨水，重量份数组成为：分散型阳离子染料水性色浆15.00～30.00；粘度调节剂20.00～35.00；表面张力调节剂0.20～2.00；pH缓冲剂0.10～3.00；保湿剂12.00～20.00；杀菌剂0.10～2.00；去离子水8.00～52.6。其中所述色浆重量份数组成为：阳离子染料10.00～40.00；封闭剂5.00～25.00；分散剂5.00～27.00；pH缓冲剂0.50～2.50；杀菌剂0.10～1.00；去离子水4.5～79.40。其中色浆在研磨时添加封闭剂，确保了色浆的化学稳定性，色浆的pH值可以稳定地维持在中性或者弱碱性条件，从而保证了喷头的安全。本发明的墨水不仅具有打印流畅、储存稳定性高、精度高等特点，而且适用于腈纶、阳离子可染改性涤纶、锦纶、醋酯纤维和阴离子改性后的涤纶、真丝、棉、麻、丙纶及其混纺织物，颜色鲜艳，各项牢度优良。

Description

一种分散型阳离子染料喷墨墨水及其数码印花工艺
技术领域
本发明涉及一种数码印花墨水及其数码印花方法，具体地说，是用分散型阳离子染料水性色浆，将其制成纺织品数码印花墨水，采用数码印花的方法对纺织品进行印花。
背景技术
随着数字化技术的发展与普及，纺织品数码印花技术已经成为21世纪最具发展潜力的生态纺织技术。2016年全球卷对卷数码印花布产量约为16亿m2，其中服装、家纺类纺织品占比54％，灯箱布、广告布等产品占比46％。WTiN预计未来几年全球数码印花市场将以17％的年复合增长率继续保持增长态势。
纺织品数码印花墨水主要分为：分散墨水、活性墨水、酸性墨水和涂料墨水等几类。目前市场上，分散墨水约占60％，活性约占30％，酸性约占7％，涂料约占2％左右。分散墨水目前主要用于热转印，主要成分为低温型分散染料，其数码印花工艺简单，无污水排放，但目前热转印市场正趋于饱和。活性数码印花工艺最为成熟，未来的发展方向是进一步提高印花速度。涂料印花具有诸多优点，工艺简单，印花后直接通过高温焙烘即可，通常无需水洗，是真正节能环保的纺织品印花方式。但涂料印花也存在一些问题，如印花织物色彩不够鲜艳，耐摩擦色牢度和耐水洗牢度较差，手感不够好等，目前仅在成衣数码印花领域使用量较大。伴随着市场上数码印花订单的快速增加及数码印花工艺的日益完善，客户需求日益提高。阳离子染料染色印花织物色泽浓艳，染色性能优良，各项牢度好，尤其是耐日晒牢度高，为其他类型染料墨水所不及。因此，开发专用于腈纶、酸改性涤纶等合成纤维的阳离子染料墨水迫在眉睫。
中国专利CN1276036提出了一种以阳离子染料为原料的数字印花墨水，引用该专利制作的阳离子染料数字印花墨水是阳离子染料的水溶液，根据阳离子染料在水中电离的机理，其水溶液呈强酸性，用该专利制得的强酸性的阳离子墨水对几乎所有打印机和喷头，特别是对金属合金部件、喷头以及喷头组件的胶黏剂有强烈的腐蚀作用，会造成胶黏剂脱胶、金属部件腐蚀、喷头堵塞、喷头损坏；并且，这种阳离子水溶液性质的墨水，即使添加了pH缓冲剂，也不能将pH值稳定在中性或者偏碱性，因为阳离子染料水溶液中有大量的阳离子基团而很快导致pH降低，墨水很快变质，并强烈腐蚀喷墨头以及喷墨组件，因而不具备实用价值。
中国专利CN102102303提出了一种阳离子型分散墨水，是将分散墨水用阳离子体系的分散剂制作，是打印涤纶织物的一种解决方案；该专利本质的着色剂是分散染料，应用方向为涤纶或者聚酯纤维纺织品的热熔式印花，而非本发明所用的阳离子染料，两类染料根本属于不同化学类型的染料，物理化学特性不同、上染机理不同，应用的纺织品纤维领域不同，不能解决腈纶和阳离子改性纤维的数码印花应用。两类染料特性不同、上染机理和应用的纺织品不同；该专利解决的是分散染料墨水组合物具有“阳离子性”从而具有某些功能，但是不能解决腈纶和阳离子改性纤维的数码印花应用。表1：阳离子染料和分散型阳离子染料上染腈纶的对比表
阳离子染料 分散型阳离子染料
染料索引名 C.I.Basic C.I.Basic
最适合的纤维 腈纶、改性涤纶 腈纶、改性涤纶
水溶性 可溶 不可溶
与水混合后的PH值 强酸性 中性
喷头腐蚀性 强烈腐蚀 无，喷头安全，可安全使用
墨水外观 透明溶液 悬浮液
化学稳定性 极不稳定，pH值持续变化 稳定，pH值等指标稳定
实用性 腐蚀喷头，不可持续打印 喷头安全，可持续使用
发明内容
本发明的目的是提供一种分散型阳离子染料喷墨墨水，其颜色鲜艳、得色深、流畅性好、贮藏稳定性好，各项色牢度优良，尤其耐日晒牢度高。可广泛用于腈纶、酸改性涤纶等合成纤维的数码印花等。
本发明的技术方案是：一种分散型阳离子染料喷墨墨水，按重量份数组成为：
分散型阳离子染料水性色浆15.00～30.00；
粘度调节剂20.00～35.00；
表面张力调节剂0.20～2.00；
pH缓冲剂0.10～3.00；
保湿剂12.00～20.00；
杀菌剂0.10～2.00；
去离子水8.00～52.6；
其中所述分散型阳离子染料水性色浆的重量份数组成为：
阳离子染料10.00～40.00；
封闭剂5.00～25.00；
分散剂5.00～27.00；
pH缓冲剂0.50～2.50；
杀菌剂0.10～1.00；
去离子水4.5～79.40。
优选的是：所述的粘度调节剂为丙三醇、二乙二醇、聚乙烯吡咯烷酮、聚乙二醇、1,5-戊二醇中的一种或多种。
优选的是：所述的表面张力调节剂为炔二醇类表面活性剂、烷基酚类表面活性剂、有机硅类表面活性剂中的一种或多种。
优选的是：所述的pH缓冲剂为有机碱性物质一乙醇胺、二乙醇胺、三乙醇胺、异丙醇胺、2-氨基乙醇中的一种或多种；或无机碱性物质氢氧化钠、碳酸钠、碳酸氢钠、磷酸钠中的一种或多种。
优选的是：所述的保湿剂为乙二醇、二乙二醇、三乙二醇、三缩四乙二醇、1,2-丙二醇、1,3-丙二醇、1,4-丁二醇、丙三醇、1,5-戊二醇、乙醇、异丙醇中的一种或多种。
优选的是：所述的杀菌剂为异噻唑啉酮类杀菌剂，如杀菌剂Preventol D7、杀菌剂Proxel GXL、杀菌剂BIT等广谱杀菌剂中的一种。
优选的是，所述封闭剂为有机磺酸化合物，包括苯系萘磺酸衍生物、萘系磺酸衍生物、脂肪族磺酸衍生物中的一种或多种。
优选的是，所述苯系萘磺酸衍生物包括二硝基苯磺酸，4,4’-联苯二磺酸钠，4-硝基-2-磺酸甲苯衍生物，对硝基甲苯磺酸钠，对硝基苯磺酸钠和对氯苯磺酸钠；所述萘系磺酸衍生物包括1-萘磺酸，1,3,6-萘三磺酸钠，1,5-萘二磺酸钠，木质素磺酸钠，α-萘磺酸钠，β-萘磺酸钠；所述脂肪族磺酸衍生物包括脂肪醇硫酸钠。
优选的是，所述分散剂为无机分散剂、有机小分子分散剂和超分散剂中的一种或多种。
优选的是，所述的无机分散剂包括聚磷酸盐、碳酸盐、硅酸盐；所述有机小分子分散剂包括月桂酰二乙醇胺、失水山梨醇单月桂酸酯非离子型表面活性剂；所述阴离子型表面活性剂包括苄基萘磺酸甲醛缩合物、β-萘磺酸甲醛缩合物、甲基萘磺酸钠的甲醛缩合物、磺化木质素类、亚甲基萘磺酸类、木质素磺酸盐类。所述超分散剂包括聚羧酸盐、聚丙烯酸衍生物、聚甲基丙烯酸衍生物、水性聚氨酯型类分散剂。
所述分散型阳离子染料水性色浆的制备方法为，按重量组成称取去离子水、pH缓冲剂、杀菌剂、封闭剂、分散剂，混合并搅拌均匀后加入阳离子染料，再添加0.3mm锆珠，在卧式砂磨机中研磨1-10小时，调整转速为600-2000r/min，直到粒径＜250nm，待色浆降至室温后先后经5.0μm和1.0μm的过滤芯过滤得到分散型阳离子染料水性色浆。
优选的是，研磨方式还包括高压均质机研磨、超声波分散、摇摆机研磨。
本发明还提供了所述分散型阳离子染料喷墨墨水的制备包括：按所述的重量份数计加入去离子水、粘度调节剂、表面张力调节剂、pH缓冲剂、保湿剂、杀菌剂，搅拌混合均匀后向溶液中加入规定量的分散型阳离子染料水性色浆，搅拌混合均匀混合后经0.8μm的混纤膜过滤后即得所述的分散型阳离子染料墨水。其中所述分散型阳离子染料水性色浆的制备方法为，按重量组成称取去离子水、pH缓冲剂、杀菌剂、封闭剂、分散剂，混合并搅拌均匀后加入阳离子染料，再添加0.3mm锆珠，在卧式砂磨机中研磨1-10小时，调整转速为600-2000r/min，直到粒径＜250nm，待色浆降至室温后先后经5.0μm和1.0μm的过滤芯过滤得到分散型阳离子染料水性色浆。
本发明还提供了一种分散型阳离子染料喷墨墨水的数码印花方法，其步骤包括：第一步，对纺织品进行预处理；第二步，用数码印花机印花；第三步，对纺织品进行后处理，印花织物可以是腈纶、阳离子可染改性涤纶、锦纶、醋酯纤维和阴离子改性后的涤纶、真丝、棉、麻、丙纶及其混纺织物。
进一步地，当印花织物为腈纶、阳离子可染改性涤纶等时，所述第一步纺织品预处理工艺为：(1)将待印花织物于45℃下在0.5g/L净洗剂Ju溶液中处理15min后取出，流水洗净，晾干或烘干；(2)按如下重量份数配制浆料：尿素4.00～12.00、酸剂5.00～15.00、糊料2.00～6.00、去离子水67.00～89.00，先将尿素、酸剂溶于去离子水，再加入糊料搅拌混合均匀；(3)将待印花织物浸轧浆料后，晾干或烘干待印花织物。对于喷墨印花精度要求较低的诸如毛毯、地毯等毛绒织物可省略上述工艺(2)和(3)。
更进一步地：所述第一步浆料中的酸剂主要包括有机酸如甲酸、柠檬酸、酒石酸、马来酸，或释酸剂如氯化铵、硫酸铵中的一种或多种。糊料主要包括龙胶、白糊精、瓜尔豆胶中的一种。
进一步地：所述第二步数码印花机为惠普热发泡式数码印花机或EPSON、MUTOH、ROLAND、SPECTRA、精工SPT、京瓷KYOCERA等压电式数码印花机。
进一步地：所述第三步纺织品后处理是(1)将印花后的织物晾干；(2)印花织物在饱和蒸汽汽蒸下汽蒸20～40min；(3)水洗；(4)晾干或烘干。
本发明提供的分散型阳离子染料喷墨墨水及其数码印花工艺，采用申请人自主研发的分散型阳离子染料水性色浆，不依赖于市售分散阳离子染料的封端，而是不论采用水溶性阳离子染料或者市售分散型阳离子染料，在研磨时继续添加封闭剂，防止封闭基团发生解封，从而进一步巩固分散型阳离子染料水性色浆的化学稳定性。因而用该色浆制备的分散型阳离子染料喷墨墨水的pH值能很好地控制在中性和偏碱性条件，能很好地应用在压电式、热发泡等打印机。墨水得以长期稳定地储存和应用，完全不同于现有技术的路线和应用。
本发明的有益效果在于墨水的颜色鲜艳、得色深、流畅性好、贮藏稳定性好，各项色牢度优良，尤其耐日晒牢度高。可广泛用于腈纶、酸改性涤纶等合成纤维的数码印花等。
具体实施方式
下面结合具体实施方式对本发明做进一步的阐述说明。应理解，这些实施例仅用于说明本发明而不用于限制本发明所要保护的范围。此外应理解，在阅读了本发明讲授的内容之后，本领域技术人员可以对本发明作各种改动或修改，这些等价形式同样落于本申请所附权利要求书所限定的范围。
一、制备所述分散型阳离子染料水性色浆(以下简称色浆)
所述色浆按重量份数由以下组分组成：
阳离子染料10.00～40.00；
封闭剂5.00～25.00；
分散剂5.00～27.00；
pH缓冲剂0.50～2.50；
杀菌剂0.10～1.00；
去离子水4.5～79.40。
其中所述分散阳离子染料选自水溶性阳离子染料和分散型阳离子染料中的一种或多种。其中，水溶性阳离子染料为C.I.Basic Orange 21、C.I.Basic Orange 22、C.I.Basic Orange 30、C.I.Basic Yellow 11、C.I.Basic Yellow 13、C.I.Basic Yellow19、C.I.Basic Yellow 21、C.I.Basic Yellow 24、C.I.Basic Yellow 28、C.I.BasicYellow 29、C.I.Basic Yellow 40、C.I.Basic Yellow 49、C.I.Basic Yellow 51、C.I.Basic Yellow 62、C.I.Basic Yellow 87、C.I.Basic Red 12、C.I.Basic Red 13、C.I.Basic Red 14、C.I.Basic Red 15、C.I.Basic Red 18、C.I.Basic Red 18:1、C.I.Basic Red 22、C.I.Basic Red 29、C.I.Basic Red 46、C.I.Basic Red 49、C.I.BasicRed 51、C.I.Basic Red 54、C.I.Basic Violet 7、C.I.Basic Violet 16、C.I.Basic Blue3、C.I.Basic Blue 41、C.I.Basic Blue 41:1、C.I.Basic Blue 53、C.I.Basic Blue 54、C.I.Basic Blue 54:1、C.I.Basic Blue 159、C.I.Basic Blue 162以及俗称的阳离子橙GL、阳离子橙G、阳离子橙R、阳离子橙3RN、阳离子橙GLH、阳离子荧光黄X-10GFF、阳离子荧光黄4GL、阳离子艳黄E-4GL、阳离子黄X-GRL、阳离子黄X-2RL、阳离子金黄X-GL、阳离子黄X-4GL、阳离子黄X-5GL、阳离子黄X-7GL、阳离子黄X-8GL、阳离子黄X-8GLL、阳离子金黄M-4GL、阳离子金黄M-RL、阳离子艳红X-5GN、阳离子艳红E-4BL、阳离子艳红G、阳离子桃红X-FG、阳离子红FF、阳离子红AFF、阳离子红X-GRL、阳离子红X-2BL、阳离子红2GL、阳离子红2GLN、阳离子红GTL、阳离子红GTLP、阳离子红GTLN、阳离子红3R、阳离子红M-RL、阳离子红X-B、阳离子红X-6B、阳离子紫3BL、阳离子艳紫X-5BLH、阳离子蓝GSL、阳离子艳蓝RL、阳离子艳蓝2RL、阳离子蓝M-RL、阳离子蓝X-FRL、阳离子蓝X-BL、阳离子蓝X-BBL、阳离子蓝X-BLL、阳离子蓝X-GRL、阳离子蓝X-GRRL、阳离子翠蓝GB、阳离子藏青X-BRL、阳离子深蓝2RM、阳离子深蓝RB、阳离子深蓝2RN、阳离子深棕X-3RL、阳离子蓝E-3RL、阳离子黑X-RL、阳离子黑X-2RL、阳离子黑X-3RL、阳离子黑X-5RL、阳离子黑X-6RL、阳离子黑X-2G、阳离子黑X-O、阳离子黑X-O-A、阳离子黑HS、阳离子黑FBL、阳离子黑FDL、阳离子黑OB、阳离子黑X-TRL、阳离子黑M、阳离子黑GLL、阳离子黑SL、阳离子黑NH、阳离子黑GW、阳离子黑VS-N、阳离子黑LB、阳离子黑LIN、阳离子黑ON、阳离子黑3GRL、阳离子黑FRH等中的一种或多种。其中，分散型阳离子染料为C.I.Basic Orange 21、C.I.Basic Orange 22、C.I.Basic Yellow 19、C.I.Basic Yellow24、C.I.Basic Yellow 28、C.I.Basic Yellow 29、C.I.Basic Yellow 40、C.I.BasicYellow 51、C.I.Basic Yellow 67、C.I.Basic Yellow 71、C.I.Basic Red 13、C.I.BasicRed 14、C.I.Basic Red 27、C.I.Basic Red 29、C.I.Basic Red 46、C.I.Basic Blue 3、C.I.Basic Blue 41、C.I.Basic Blue 54、C.I.Basic Blue 54:1、C.I.Basic Blue 57、C.I.Basic Blue 75、C.I.Basic Blue 116、C.I.Basic Blue 159以及俗称的：分散阳离子橙SD-G、分散阳离子黄SD-10GFF、分散阳离子黄SD-GL、分散阳离子黄SD-5GL、分散阳离子黄SD-7GL、分散阳离子黄SD-GRL、分散阳离子黄SD-2RL、分散阳离子黄SD-3RL、分散阳离子艳黄5GL-ED、分散阳离子黄7GL-ED、分散阳离子黄GSL-ED、分散阳离子黄3RL-ED、分散阳离子黄GL-ED、分散阳离子艳红SD-5GN、分散阳离子红SD-2GL、分散阳离子红SD-GRL、分散阳离子桃红SD-FG、分散阳离子红GL-ED、分散阳离子红BSL-ED、分散阳离子红GRL-ED、分散阳离子艳桃红B-ED、分散阳离子蓝SD-GSL、分散阳离子蓝SD-BL、分散阳离子蓝SD-RL、分散阳离子蓝SD-FRR、分散阳离子翠蓝SD-GB、分散阳离子蓝2RL-ED、分散阳离子蓝3RL-ED、分散阳离子蓝BGL-ED、分散阳离子蓝GSL-ED、分散阳离子蓝BG-ED、分散阳离子蓝4GSL-ED、分散阳离子蓝FP-ED、分散阳离子蓝TL-ED、分散阳离子蓝GTL-ED、分散阳离子藏青SD-BRL、分散阳离子蓝5G-ED、分散阳离子藏青A-ED、分散阳离子藏青RP-ED、分散阳离子深棕SD-3RL、分散阳离子灰SD-FL、分散阳离子黑SD-O、分散阳离子黑SD-MG、分散阳离子黑SD-FBL、分散阳离子黑SD-RL、分散阳离子黑R-ED、分散阳离子黑MR-ED、分散阳离子黑BS-ED、分散阳离子黑MG-ED的一种或多种。
在本发明的色浆实施例中，所述封闭剂可选择克拉玛尔公司生产的1,3,6-萘三磺酸钠、对硝基苯磺酸钠，加拿大天柏公司生产的ARBO N22；所述分散剂可选择英国路博润公司生产的SOLSPERSE 44000、美德维实伟克公司生产的Reax 85A、英国迪高公司生产的TEGODispers 760W；所述pH缓冲剂可选择德国巴斯夫公司生产的三乙醇胺、北京伊诺凯科技有限公司生产的磷酸一氢钠；所述杀菌剂可选择瑞士龙沙公司生产的Proxel GXL、德国朗盛化学公司生产的Preventol D7。
色浆实施例1：
一种分散型阳离子染料红水性色浆，其按重量份数包括以下组分：分散阳离子红SD-FG 20.00、1,3,6-萘三磺酸钠9.00、SOLSPERSE 44000 19.50、三乙醇胺0.90、ProxelGXL 0.20、去离子水50.40。将上述组分按比例混合均匀后加入0.3mm锆珠，在卧式砂磨机中研磨8小时，调整转速为1700r/min，待色浆降至室温后先后经5.0μm和1.0μm的过滤芯过滤得到分散型阳离子染料红水性色浆DM-001S。
色浆实施例2：
一种分散型阳离子染料黄水性色浆，其按重量份数包括以下组分：分散阳离子黄SD-3RL 12.00、对硝基苯磺酸钠6.50、Reax 85A 12.00、三乙醇胺1.00、Preventol D70.20、去离子水68.30。将上述组分按比例混合均匀后加入0.3mm锆珠，在卧式砂磨机中研磨6小时，调整转速为950r/min，待色浆降至室温后先后经5.0μm和1.0μm的过滤芯过滤得到分散型阳离子染料黄水性色浆DY-001S。
色浆实施例3：
一种分散型阳离子染料蓝水性色浆，其按重量份数包括以下组分：分散阳离子蓝GSL-ED 15.00、ARBO N22 8.00、TEGO Dispers 760W 17.50、磷酸一氢钠1.25、Proxel GXL0.20、去离子水58.05。将上述组分按比例混合均匀后加入0.3mm锆珠，在卧式砂磨机中研磨9小时，调整转速为1900r/min，待色浆降至室温后先后经5.0μm和1.0μm的过滤芯过滤得到分散型阳离子染料蓝水性色浆DC-001S。
色浆实施例4：
一种分散型阳离子染料黑水性色浆，其按重量份数包括以下组分：分散阳离子黑SD-FBL 32.00、1,3,6-萘三磺酸钠14.50、Reax 85A 24.00、三乙醇胺1.85、Preventol D70.20、去离子水27.45。将上述组分按比例混合均匀后加入0.3mm锆珠，在卧式砂磨机中研磨10小时，调整转速为2000r/min，待色浆降至室温后先后经5.0μm和1.0μm的过滤芯过滤得到分散型阳离子染料黑水性色浆DK-001S。
色浆实施例5：
一种分散型阳离子染料黄水性色浆，其按重量份数包括以下组分：阳离子黄X-5GL12.00、ARBO N22 24.50、Reax 85A 21.00、磷酸一氢钠1.5、Proxel GXL 0.20、去离子水40.8。将上述组分按比例混合均匀后加入0.3mm锆珠，在卧式砂磨机中研磨10小时，调整转速为1750r/min，待色浆降至室温后先后经5.0μm和1.0μm的过滤芯过滤得到分散型阳离子染料黄水性色浆DY-002S。
色浆的实施效果：
按照国家相关标准，分别对本发明的分散型阳离子染料水性色浆的性能进行检测，老化条件为60℃烘箱中老化4周，测试结果如表2所示。
表2分散型阳离子染料水性色浆基本性能测试结果
Figure BDA0001599614160000091
二、制备分散型阳离子染料喷墨墨水(以下简称墨水)
本发明的墨水，按其重量百分比由以下组分组成：
前述色浆15.00～30.00；
粘度调节剂20.00～35.00；
表面张力调节剂0.20～2.00；
pH缓冲剂0.10～3.00；
保湿剂12.00～20.00；
杀菌剂0.10～2.00；
去离子水8.00～52.6；
在墨水的实施例中，所述炔二醇类表面活性剂可选择美国气体公司生产的Surfynol 465；所述杀菌剂可选择瑞士龙沙公司生产的Proxel GXL。
墨水实施例1：
一种分散型阳离子染料红喷墨墨水，其按重量份数包括以下组分：DM-001S(色浆实施例1的红色色浆)20.00、乙二醇12.50、Surfynol 465 0.20、三乙醇胺0.50、Proxel GXL0.20、去离子水49.38。将上述组分混合均匀后经0.8μm的混纤膜过滤后即得分散型阳离子染料红DM-001墨水。
墨水实施例2：
一种分散型阳离子染料黄喷墨墨水，其按重量份数包括以下组分：DY-001S(色浆实施例2的黄色色色浆)18.00、乙二醇15.00、Surfynol 465 0.40、三乙醇胺0.30、ProxelGXL 0.30、去离子水41.58。将上述组分混合均匀后经0.8μm的混纤膜过滤后即得分散型阳离子染料黄DY-001墨水。
墨水实施例3：
一种分散型阳离子染料蓝喷墨墨水，其按重量份数包括以下组分：DC-001S(色浆实施例3的蓝色色浆)25.00、乙二醇17.50、Surfynol 465 0.50、三乙醇胺0.70、Proxel GXL0.30、去离子水27.58。将上述组分混合均匀后经0.8μm的混纤膜过滤后即得分散型阳离子染料蓝DC-001墨水。
墨水实施例4：
一种分散型阳离子染料黑喷墨墨水，其按重量份数包括以下组分：DK-001S(色浆实施例4的黑色色浆)30.00、乙二醇20.00、Surfynol 465 1.00、三乙醇胺0.50、Proxel GXL0.40、去离子水23.18。将上述组分混合均匀后经0.8μm的混纤膜过滤后即得分散型阳离子染料黑DK-001墨水。
实施例5：腈纶、阳离子可染改性涤纶织物的数码印花
取上述墨水实施例1、2、3、4的分散型阳离子染料喷墨墨水，装入数码印花机的四色墨囊中待用。第一步：对腈纶、阳离子可染改性涤纶织物进行预处理：(1)将待印花织物于45℃下在0.5g/L净洗剂Ju溶液中处理15min后取出，流水洗净，晾干或烘干；(2)按如下重量份数配制浆料：尿素6.00、柠檬酸6.00、龙胶5.00、去离子水83.00，先将尿素、柠檬酸溶于去离子水，再加入龙胶搅拌混合均匀；(3)将待印花织物浸轧浆料后，晾干待印花织物。
第二步数码印花机选用压电式星光LA喷头数码印花机，通过光栅图像处理软件(RIP)进行数码印花，其操作为本行业技术人员所掌握，不再赘述。
第三步纺织品后处理是(1)将印花后的织物晾干；(2)印花织物在饱和蒸汽汽蒸下汽蒸40min；(3)水洗；(4)烘干。
本发明的实施效果：
按照国家相关标准，对本发明的分散型阳离子染料喷墨墨水的性能进行检测，测试结果如表3所示。
表3分散型阳离子染料喷墨墨水的基本性能测试结果
Figure BDA0001599614160000111
Figure BDA0001599614160000121
所用的一种分散型阳离子数码印花墨水在富士星光1024LA压电式打印机上打印，打印在腈纶和阳离子可染改性涤纶织物上各项色牢度均符合国家生态纺织品技术要求标准GB/T 18885-2009，测试结果见表4。
表4分散型阳离子染料喷墨墨水的基本性能测试结果
Figure BDA0001599614160000122

Claims (3)

1.一种分散型阳离子染料喷墨墨水，其特征是：其重量份数组成为：
分散型阳离子染料水性色浆15.00～30.00；
粘度调节剂20.00～35.00；
表面张力调节剂0.20～2.00；
pH缓冲剂0.10～3.00；
保湿剂12.00～20.00；
杀菌剂0.10～2.00；
去离子水8.00～52.6；
其中所述分散型阳离子染料水性色浆的重量份数组成为：
阳离子染料10.00～40.00；
封闭剂5.00～25.00；
分散剂5.00～27.00；
pH缓冲剂0.50～2.50；
杀菌剂0.10～1.00；
去离子水4.5～79.40；
所述分散型阳离子染料水性色浆的制备方法为：按配方称取去离子水、pH缓冲剂、杀菌剂、封闭剂、分散剂，混合并搅拌均匀后加入阳离子染料，再添加0.3mm锆珠，在卧式砂磨机中研磨1-10小时，调整转速为600-2000r/min，直到粒径＜250nm，待色浆降至室温后先后经5.0μm和1.0μm的过滤芯过滤得到分散型阳离子染料水性色浆；
其中：所述阳离子染料为水溶性阳离子染料和分散型阳离子染料中的一种或多种；
所述的pH缓冲剂为一乙醇胺、二乙醇胺、三乙醇胺、异丙醇胺、2-氨基乙醇中的一种或多种；或氢氧化钠、碳酸钠、碳酸氢钠、磷酸钠中的一种或多种；
所述的粘度调节剂为丙三醇、二乙二醇、聚乙烯吡咯烷酮、聚乙二醇、1,5-戊二醇中的一种或多种；
所述的表面张力调节剂为炔二醇类表面活性剂、烷基酚类表面活性剂、有机硅类表面活性剂中的一种或多种；
所述的保湿剂为乙二醇、二乙二醇、三乙二醇、三缩四乙二醇、1,2-丙二醇、1,3-丙二醇、1,4-丁二醇、丙三醇、1,5-戊二醇、乙醇、异丙醇中的一种或多种；
所述的杀菌剂为异噻唑啉酮类杀菌剂，选自杀菌剂Preventol D7、杀菌剂Proxel GXL、杀菌剂BIT中的一种。
2.如权利要求1所述的一种分散型阳离子染料喷墨墨水的制备方法，其特征在于：按重量份数计加入去离子水、粘度调节剂、表面张力调节剂、pH缓冲剂、保湿剂、杀菌剂，搅拌混合均匀后向溶液中加入规定量的分散型阳离子染料水性色浆，搅拌混合均匀后经0.8μm的混纤膜过滤后即得所述的分散型阳离子染料喷墨墨水。
3.如权利要求1所述的一种分散型阳离子染料喷墨墨水的数码印花方法, 其特征在于：第一步，对织物进行预处理；第二步，用数码印花机印花；第三步，对织物进行后处理，印花织物选自腈纶、阳离子可染改性涤纶织物；
其中，所述第一步织物预处理工艺为：(1)将待印花织物于45℃下在0.5g/L净洗剂Ju溶液中处理15min后取出，流水洗净，晾干或烘干；(2)按如下重量份数配制浆料：尿素4.00～12.00、酸剂5.00～15.00、糊料2.00～6.00、去离子水67.00～89.00，先将尿素、酸剂溶于去离子水，再加入糊料搅拌混合均匀；(3)将待印花织物浸轧浆料后，晾干或烘干待印花织物；对于喷墨印花精度要求较低的毛绒织物可省略上述工艺(2)和(3)；
所述的第一步浆料中的酸剂选自甲酸、柠檬酸、酒石酸、马来酸、氯化铵、硫酸铵中的一种或多种，所述糊料选自龙胶、白糊精、瓜尔豆胶中的一种；
所述第二步中的数码印花机为惠普热发泡式数码印花机或EPSON、MUTOH、ROLAND、SPECTRA、精工SPT、京瓷KYOCERA压电式数码印花机；
所述的第三步织物后处理是(1)将印花后的织物晾干；(2)印花织物在饱和蒸汽下汽蒸20～40min；(3)水洗；(4)晾干或烘干。
CN201810219022.5A 2018-03-16 2018-03-16 一种分散型阳离子染料喷墨墨水及其数码印花工艺 Active CN108486933B (zh)