CN108455945B - 一种质轻墙板及其制备方法 - Google Patents
一种质轻墙板及其制备方法 Download PDFInfo
- Publication number
- CN108455945B CN108455945B CN201810103724.7A CN201810103724A CN108455945B CN 108455945 B CN108455945 B CN 108455945B CN 201810103724 A CN201810103724 A CN 201810103724A CN 108455945 B CN108455945 B CN 108455945B
- Authority
- CN
- China
- Prior art keywords
- wallboard
- parts
- layer
- wall board
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及建筑材料技术领域，尤其是一种质轻墙板及其制备方法，包括墙板板层，所述墙板板层内部开设有空腔，所述空腔内固定连接有墙板空心支架，所述墙板板层外部设有墙板保护层，所述墙板板层的厚度为15‑35mm。本发明设计的质轻墙板的板层内设有空腔，且空腔内部固定安装墙板空心支架，对墙板具有支撑及固定作用，在减轻墙板重量的同时，延长墙板的使用寿命；在墙板的外部设置墙板保护层，能够对墙板起到保护作用，在保护层的物料内添加抗菌剂，在延长使用寿命墙体的同时具有抗菌作用，有利于保护环境。
Description
技术领域
本发明涉及建筑材料技术领域，尤其涉及一种质轻墙板及其制备方法。
背景技术
随着城市建筑的快速发展，建筑功能的不断完善，人们对墙体材料的环保、节能的要求越来越高，传统的墙体材料主要为实芯粘土砖，也就是人们常说的“红砖”，由于实芯粘土砖的生产要挖地取土，因此对土地，特别是对耕地造成了很大的破坏，烧制中需要大量的能源，并释放出大量的二氧化碳及二氧化硫，使大气污染，破坏生态环境，这种产品不但重，使用中需要大量的人工，占用空间大。据统计，目前国内墙体材料生产能耗和建筑采暖能耗煤，约占我国全年能耗总量15％左右。建材工业使用最多的资源是粘土、石灰石和砂石，目前的年均开采量超过50亿吨，破坏耕地近6700公顷。这将造成大量的植被破坏和水土流失。另外，粘土砖生产中还要排放大量的烟气和粉尘，每年仅C02排放量就达1.7亿吨。污染环境。
目前同类产品的墙体材料的夹芯层多为中空或中间有层苯板，虽然此类产品有许多优点，但夹芯层与面板黏结缝容易出现裂痕、脱落和豁口等现象，致使墙板的稳固性低，使用周期短，且传统材料制作的墙板重量太重，不利于使用；为此提出，一种质轻墙板及其制备方法。
发明内容
本发明的目的是为了解决现有技术中的缺点，而提出的一种质轻墙板及其制备方法。
为了实现上述目的，本发明采用了如下技术方案：
设计一种质轻墙板，包括墙板板层，所述墙板板层内部开设有空腔，所述空腔内固定连接有墙板空心支架，所述墙板板层外部设有墙板保护层，所述墙板板层的厚度为15-35mm。
优选的，所述墙板保护层的厚度为5-8mm。
优选的，所述墙板保护层的材料为改性膨胀型阻燃玻璃纤维增强聚丙烯复合材料。
优选的，所述改性膨胀型阻燃玻璃纤维增强聚丙烯复合材料，由以下重量配比的原料制成：阻燃聚丙烯50-60份、阻燃型玻璃纤维增强复合塑料50-60份、偶联剂6-8份、填充剂6-8份、改性剂0.5-1.2份、抗菌剂0.5-0.8份；所述偶联剂为锆类偶联剂，所述填充剂为二氧化硅：氧化铝以质量比为2:1的混合物，所述改性剂为氢氧化钾：氨水以体积比为3.5:1的混合溶液，所述抗菌剂为纳米银和石墨烯的混合物。
优选的，所述墙板板层由以下重量配比的原料制成：废弃秸秆15-25份、碎陶瓷粒15-25份、粉煤灰5-8份、氧化镁3-4份、乙烯基三胺1-3份、间苯二胺1-2份、凹凸棒土1-3份。
本发明还提供一种质轻墙板的制作方法，包括以下步骤：
1）取配方量的废弃秸秆、碎陶瓷粒、凹凸棒土粉碎至50-80目，加水，超声波处理3-5min；
2）向1）中加入配方量的粉煤灰、氧化镁、乙烯基三胺、间苯二胺，微波处理5-8min，在50-60℃条件下反应2-3h，得到墙板板层的物料；
3）将2）中的物料加入模具中成型，在成型的墙板板层的空腔内固定安装墙板空心支架，在80-100℃条件下保温1.5-2h，然后以0.5℃/min的速度匀速降温至10-15℃，保温1.5-2h，得到质轻墙板预成品；
4）取配方量的阻燃聚丙烯、阻燃型玻璃纤维增强复合塑料、偶联剂、填充剂、改性剂、抗菌剂在超音速气流的作用下粉碎至纳米级，加入容器内，加入50wt%的水，超声波处理5min，40-60℃条件下保温反应45-60min，得到墙板保护层的物料；
5）将4）得到的物料均匀涂抹在质轻墙板预成品外部，在40-50℃条件下保温30-45min，得到质轻墙板。
本发明提出的一种质轻墙板及其制备方法，有益效果在于：本发明设计的质轻墙板的墙板板层内设有空腔，且空腔内部固定安装墙板空心支架，对墙板具有支撑及固定作用，在减轻墙板重量的同时，延长墙板的使用寿命；在墙板的外部设置墙板保护层，能够对墙板起到保护作用，在保护层的物料内添加抗菌剂，在延长使用寿命墙体的同时具有抗菌作用，有利于保护环境。
附图说明
图1为本发明的结构示意图。
图中：墙板空心支架1、墙板板层2、墙板保护层3。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。
实施例1
参照图1，一种质轻墙板，包括墙板板层2，墙板板层2内部开设有空腔，空腔内固定连接有墙板空心支架1，墙板板层2外部设有墙板保护层3，墙板板层2的厚度为15mm，墙板保护层3的厚度为5mm。
墙板保护层3的材料为改性膨胀型阻燃玻璃纤维增强聚丙烯复合材料。改性膨胀型阻燃玻璃纤维增强聚丙烯复合材料，由以下重量配比的原料制成：阻燃聚丙烯50份、阻燃型玻璃纤维增强复合塑料50份、偶联剂6份、填充剂6份、改性剂0.5份、抗菌剂0.5份；偶联剂为锆类偶联剂，填充剂为二氧化硅：氧化铝以质量比为2:1的混合物，改性剂为氢氧化钾：氨水以体积比为3.5:1的混合溶液，抗菌剂为纳米银和石墨烯的混合物。
墙板板层2由以下重量配比的原料制成：废弃秸秆15份、碎陶瓷粒15份、粉煤灰5份、氧化镁3份、乙烯基三胺1份、间苯二胺1份、凹凸棒土1份。
一种质轻墙板的制作方法，包括以下步骤：
1）取配方量的废弃秸秆、碎陶瓷粒、凹凸棒土粉碎至50目，加水，超声波处理5min；
2）向1）中加入配方量的粉煤灰、氧化镁、乙烯基三胺、间苯二胺，微波处理5min，在50℃条件下反应2h，得到墙板板层2的物料；
3）将2）中的物料加入模具中成型，在成型的墙板板层2的空腔内固定安装墙板空心支架1，在80℃条件下保温1.5h，然后以0.5℃/min的速度匀速降温至10-15℃，保温1.5h，得到质轻墙板预成品；
4）取配方量的阻燃聚丙烯、阻燃型玻璃纤维增强复合塑料、偶联剂、填充剂、改性剂、抗菌剂在超音速气流的作用下粉碎至纳米级，加入容器内，加入50wt%的水，超声波处理5min，40℃条件下保温反应45min，得到墙板保护层3的物料；
5）将4）得到的物料均匀涂抹在质轻墙板预成品外部，在40-50℃条件下保温30min，得到质轻墙板。
实施例2
参照图1，一种质轻墙板，包括墙板板层2，墙板板层2内部开设有空腔，空腔内固定连接有墙板空心支架1，墙板板层2外部设有墙板保护层3，墙板板层2的厚度为18mm，墙板保护层3的厚度为5mm。
墙板保护层3的材料为改性膨胀型阻燃玻璃纤维增强聚丙烯复合材料。改性膨胀型阻燃玻璃纤维增强聚丙烯复合材料，由以下重量配比的原料制成：阻燃聚丙烯60份、阻燃型玻璃纤维增强复合塑料60份、偶联剂8份、填充剂8份、改性剂1.2份、抗菌剂0.8份；偶联剂为锆类偶联剂，填充剂为二氧化硅：氧化铝以质量比为2:1的混合物，改性剂为氢氧化钾：氨水以体积比为3.5:1的混合溶液，抗菌剂为纳米银和石墨烯的混合物。
墙板板层2由以下重量配比的原料制成：废弃秸秆25份、碎陶瓷粒25份、粉煤灰8份、氧化镁4份、乙烯基三胺3份、间苯二胺2份、凹凸棒土3份。
一种质轻墙板的制作方法，包括以下步骤：
1）取配方量的废弃秸秆、碎陶瓷粒、凹凸棒土粉碎至80目，加水，超声波处理5min；
2）向1）中加入配方量的粉煤灰、氧化镁、乙烯基三胺、间苯二胺，微波处理7min，在60℃条件下反应3h，得到墙板板层2的物料；
3）将2）中的物料加入模具中成型，在成型的墙板板层2的空腔内固定安装墙板空心支架1，在100℃条件下保温2h，然后以0.5℃/min的速度匀速降温至15℃，保温2h，得到质轻墙板预成品；
4）取配方量的阻燃聚丙烯、阻燃型玻璃纤维增强复合塑料、偶联剂、填充剂、改性剂、抗菌剂在超音速气流的作用下粉碎至纳米级，加入容器内，加入50wt%的水，超声波处理5min，60℃条件下保温反应60min，得到墙板保护层3的物料；
5）将4）得到的物料均匀涂抹在质轻墙板预成品外部，在50℃条件下保温45min，得到质轻墙板。
实施例3
参照图1，一种质轻墙板，包括墙板板层2，墙板板层2内部开设有空腔，空腔内固定连接有墙板空心支架1，墙板板层2外部设有墙板保护层3，墙板板层2的厚度为20mm，墙板保护层3的厚度为5mm。
墙板保护层3的材料为改性膨胀型阻燃玻璃纤维增强聚丙烯复合材料。改性膨胀型阻燃玻璃纤维增强聚丙烯复合材料，由以下重量配比的原料制成：阻燃聚丙烯55份、阻燃型玻璃纤维增强复合塑料55份、偶联剂7份、填充剂7份、改性剂1份、抗菌剂0.5份；偶联剂为锆类偶联剂，填充剂为二氧化硅：氧化铝以质量比为2:1的混合物，改性剂为氢氧化钾：氨水以体积比为3.5:1的混合溶液，抗菌剂为纳米银和石墨烯的混合物。
墙板板层2由以下重量配比的原料制成：废弃秸秆15-25份、碎陶瓷粒20份、粉煤灰5份、氧化镁3份、乙烯基三胺2份、间苯二胺2份、凹凸棒土2份。
一种质轻墙板的制作方法，包括以下步骤：
1）取配方量的废弃秸秆、碎陶瓷粒、凹凸棒土粉碎至80目，加水，超声波处理3min；
2）向1）中加入配方量的粉煤灰、氧化镁、乙烯基三胺、间苯二胺，微波处理5min，在50℃条件下反应2h，得到墙板板层2的物料；
3）将2）中的物料加入模具中成型，在成型的墙板板层2的空腔内固定安装墙板空心支架1，在100℃条件下保温2h，然后以0.5℃/min的速度匀速降温至10℃，保温1.8h，得到质轻墙板预成品；
4）取配方量的阻燃聚丙烯、阻燃型玻璃纤维增强复合塑料、偶联剂、填充剂、改性剂、抗菌剂在超音速气流的作用下粉碎至纳米级，加入容器内，加入50wt%的水，超声波处理5min，60℃条件下保温反应60min，得到墙板保护层3的物料；
5）将4）得到的物料均匀涂抹在质轻墙板预成品外部，在50℃条件下保温45min，得到质轻墙板。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (2)
1.一种质轻墙板，包括墙板板层（2），其特征在于：所述墙板板层（2）内部开设有空腔，所述空腔内固定连接有墙板空心支架（1），所述墙板板层（2）外部设有墙板保护层（3），所述墙板板层（2）的厚度为15-35mm；所述墙板保护层（3）的厚度为5-8mm；所述墙板保护层（3）的材料为改性膨胀型阻燃玻璃纤维增强聚丙烯复合材料；所述改性膨胀型阻燃玻璃纤维增强聚丙烯复合材料，由以下重量配比的原料制成：阻燃聚丙烯50-60份、阻燃型玻璃纤维增强复合塑料50-60份、偶联剂6-8份、填充剂6-8份、改性剂0.5-1.2份、抗菌剂0.5-0.8份；所述偶联剂为锆类偶联剂，所述填充剂为二氧化硅：氧化铝以质量比为2:1的混合物，所述改性剂为氢氧化钾：氨水以体积比为3.5:1的混合溶液，所述抗菌剂为纳米银和石墨烯的混合物；所述墙板板层（2）由以下重量配比的原料制成：废弃秸秆15-25份、碎陶瓷粒15-25份、粉煤灰5-8份、氧化镁3-4份、乙烯基三胺1-3份、间苯二胺1-2份、凹凸棒土1-3份。
2.一种权利要求1所述质轻墙板的制作方法，其特征在于：包括以下步骤：
1）取配方量的废弃秸秆、碎陶瓷粒、凹凸棒土粉碎至50-80目，加水，超声波处理3-5min；
2）向1）中加入配方量的粉煤灰、氧化镁、乙烯基三胺、间苯二胺，微波处理5-8min，在50-60℃条件下反应2-3h，得到墙板板层（2）的物料；
3）将2）中的物料加入模具中成型，在成型的墙板板层（2）的空腔内固定安装墙板空心支架（1），在80-100℃条件下保温1.5-2h，然后以0.5℃/min的速度匀速降温至10-15℃，保温1.5-2h，得到质轻墙板预成品；
4）取配方量的阻燃聚丙烯、阻燃型玻璃纤维增强复合塑料、偶联剂、填充剂、改性剂、抗菌剂在超音速气流的作用下粉碎至纳米级，加入容器内，加入50wt%的水，超声波处理5min，40-60℃条件下保温反应45-60min，得到墙板保护层（3）的物料；
5）将4）得到的物料均匀涂抹在质轻墙板预成品外部，在40-50℃条件下保温30-45min，得到质轻墙板。