CN108384072A - 一种耐候性钢丝绳芯阻燃输送带覆盖胶及其制备方法 - Google Patents
一种耐候性钢丝绳芯阻燃输送带覆盖胶及其制备方法 Download PDFInfo
- Publication number
- CN108384072A CN108384072A CN201810262177.7A CN201810262177A CN108384072A CN 108384072 A CN108384072 A CN 108384072A CN 201810262177 A CN201810262177 A CN 201810262177A CN 108384072 A CN108384072 A CN 108384072A
- Authority
- CN
- China
- Prior art keywords
- agent
- parts
- conveyor belt
- steel core
- rubber cover
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐候性钢丝绳芯阻燃输送带覆盖胶，包括以下重量份配比的组分：改性氯磺化聚乙烯橡胶30～40份，氯丁橡胶35～52.5份，天然橡胶15～35份，炭黑50～60份，促进剂2～4份，防老剂1～3份，活性氧化镁2～5份，硫化剂0.5～1份，纳米氧化锌2～4份，硬脂酸1～2份，阻燃剂40～50份，软化剂4～7份，脱模剂2～3份。将氯磺化聚乙烯橡胶、氯丁橡胶、天然橡胶、防老剂、活性氧化镁、纳米氧化锌、硬脂酸、阻燃剂及促进剂加到密炼机，密炼1～3分钟，然后再加入炭黑、软化剂和脱模剂后密炼3～4分钟，最后加硫化剂密炼；后经过开炼机出的6～8mm胶片即可制成，本发明的有益效果是，耐候性能优异，适用于在臭氧、热和日光条件下的输送。
Description
技术领域
本发明涉及输送带技术领域，特别是一种耐候性钢丝绳芯阻燃输送带覆盖胶及其制备方法。
背景技术
由于输送带的使用寿命与覆盖胶密切相关，大型输送带大多在煤矿生产中使用，在运输过程中常常由于各种环境因素(如温度、湿度、拉伸应变)覆盖胶局部龟裂、磨损而整体报废造成客户投诉，影响企业声誉和生产成本。然而普通输送带不具备耐天候性，只能在较温和的条件下使用；因此研制耐候性阻燃钢丝绳芯输送带覆盖胶可以使覆盖胶与带芯具有相当长的使用寿命，充分发挥输送带的使用价值，减少资源浪费。
发明内容
本发明的目的是为了解决上述问题，设计了一种提高耐候性、阻燃性以及延长输送带使用寿命的钢丝绳芯输送带覆盖胶，
实现上述目的本发明的技术方案为，一种耐候性钢丝绳芯阻燃输送带覆盖胶，包括以下重量份配比的组分：改性氯磺化聚乙烯橡胶30～40份，氯丁橡胶35～52.5份，天然橡胶15～35份，炭黑50～60份，促进剂2～4份，防老剂1～3份，活性氧化镁2～5份，硫化剂0.5～1份，纳米氧化锌2～4份，硬脂酸1～2份，阻燃剂40～50份，软化剂4～7份，脱模剂2～3份。其中，改性氯磺化聚乙烯橡胶是以聚乙烯为主链的一种饱和型弹性体,其氯含量为35～42％，门尼粘度ML(1+4)100℃为31±5；氯丁橡胶是以硫磺和二硫化二异丙基黄原酸酯为混合调节剂的氯丁二烯聚合物，结晶速度中等，非污染型，具有抗撕裂强度高的特点。
进一步地，所述炭黑为炭黑N234、炭黑N330按照3:2组成的混合物。
进一步地，所述促进剂为促进剂TMTM、促进剂DOTG按照1：1～1:2组成的混合物。
进一步地，所述阻燃剂为IFR(膨胀型阻燃剂)、氯化石蜡(氯系阻燃剂)、三氧化二锑(无机阻燃剂)、硼酸锌(硼系阻燃剂)、三芳基磷酸酯(磷系阻燃剂)中的一种或几种。
进一步地，所述防老剂为防老剂4010NA、防老剂RD、微晶石蜡中的一种或几种。
进一步地，所述硫化剂为S-80。
进一步地，所述软化剂为C5石油树脂、芳烃油、聚乙烯蜡的一种或几种。
一种耐候性钢丝绳芯阻燃输送带覆盖胶的制备方法，包括以下制备步骤：
a、按照上述重量份配比原料，将改性氯磺化聚乙烯橡胶、氯丁橡胶、天然橡胶、防老剂、活性氧化镁、纳米氧化锌、硬脂酸、阻燃剂及促进剂加到密炼机，密炼1～3分钟；
b、向密炼机中依次加入炭黑、软化剂、脱模剂后密炼3～4分钟；
c、向密炼机中加入硫化剂后密炼1～2分钟得到胶体，排料温度控制在100～110℃，将胶体排出；
d、胶体排出后进入开炼机，经过开炼机后得到6～8mm厚的胶片，将胶片表面涂覆隔离剂后，叠好入库存放。
利用本发明的技术方案制作的一种耐候性钢丝绳芯阻燃输送带覆盖胶，其有益效果在于，1、原材料性能优异；选用的改性氯磺化聚乙烯橡胶是聚乙烯经氯化和磺化处理后得到的具有饱和主链的弹性体，加工性能优异，具有优良的耐天候性、耐臭氧性的特点；氯丁橡胶是以硫磺和二硫化二异丙基黄原酸酯为混合调节剂的氯丁二烯聚合物，具有结晶速度中等，非污染型和抗撕裂强度高等特点；选用以上两种材料并用天然橡胶改善输送带覆盖胶加工性及阻燃性能，减少覆盖胶老化龟裂等现象，提高耐磨性能，以延长输送带使用寿命，耐候性能优异，适用于在臭氧、热和日光条件下的输送；2、生产设备简单，生产成本低：改性氯磺化聚乙烯橡胶可以用普通的橡胶设备加工，不需要额外增加设备投资，降低生产成本。
具体实施方式
实施例1
一种耐候性钢丝绳芯阻燃输送带覆盖胶，包括以下重量份配比的组分：改性氯磺化聚乙烯橡胶30份，氯丁橡胶35份，天然橡胶37份，炭黑50份，促进剂1.2份，防老剂1份，活性氧化镁5份，硫化剂0.5份，纳米氧化锌4份，硬脂酸1份，阻燃剂40份，软化剂4份，脱模剂2份。
优选地，所述炭黑为炭黑N234、炭黑N330按照3:2组成的混合物。
优选地，所述促进剂为促进剂TMTM、促进剂DOTG按照1：1组成的混合物。
优选地，所述阻燃剂为IFR(膨胀型阻燃剂)、氯化石蜡(氯系阻燃剂)按1:1混合。
优选地，所述防老剂为防老剂4010NA。
优选地，所述硫化剂为S-80。
优选地，所述软化剂为C5石油树脂。
一种耐候性钢丝绳芯阻燃输送带覆盖胶的制备方法，包括以下制备步骤：
a、按照上述重量份配比原料，将改性氯磺化聚乙烯橡胶、氯丁橡胶、天然橡胶、防老剂、活性氧化镁、纳米氧化锌、硬脂酸、阻燃剂及促进剂加到密炼机，密炼1分钟；
b、向密炼机中依次加入炭黑、软化剂、脱模剂后密炼3分钟；
c、向密炼机中加入硫化剂后密炼1分钟得到胶体，排料温度控制在100℃，将胶体排出；
d、胶体排出后进入开炼机，经过开炼机后得到6～8mm厚的胶片，将胶片表面涂覆隔离剂后，叠好入库存放。
实施例2：
一种耐候性钢丝绳芯阻燃输送带覆盖胶，包括以下重量份配比的组分：改性氯磺化聚乙烯橡胶33份，氯丁橡胶40份，天然橡胶20份，炭黑55份，促进剂3份，防老剂2份，活性氧化镁4份，硫化剂0.7份，纳米氧化锌3份，硬脂酸1.5份，阻燃剂45份，软化剂5份，脱模剂2.5份。进一步地，所述炭黑为炭黑N234、炭黑N330按照3:2组成的混合物。
优选地，所述促进剂为促进剂TMTM、促进剂DOTG按照1：1组成的混合物。
优选地，所述阻燃剂为三氧化二锑(无机阻燃剂)、硼酸锌(硼系阻燃剂)、氯化石蜡(氯系阻燃剂)按照1：1：2组成的混合物。
优选地，所述防老剂为防老剂RD。
优选地，所述硫化剂为S-80。
优选地，所述软化剂为C5石油树脂、芳烃油、聚乙烯蜡按照5：2：3组成的混合物。
一种耐候性钢丝绳芯阻燃输送带覆盖胶的制备方法，包括以下制备步骤：
a、按照上述重量份配比原料，将改性氯磺化聚乙烯橡胶、氯丁橡胶、天然橡胶、防老剂、活性氧化镁、纳米氧化锌、硬脂酸、阻燃剂及促进剂加到密炼机，密炼2分钟；
b、向密炼机中依次加入炭黑、软化剂、脱模剂后密炼3分钟；
c、向密炼机中加入硫化剂后密炼1分钟得到胶体，排料温度控制在110℃，将胶体排出；
d、胶体排出后进入开炼机，经过开炼机后得到6～8mm厚的胶片，将胶片表面涂覆隔离剂后，叠好入库存放。
实施例3：
一种耐候性钢丝绳芯阻燃输送带覆盖胶，包括以下重量份配比的组分：改性氯磺化聚乙烯橡胶39份，氯丁橡胶52.5份，天然橡胶17.5份，炭黑60份，促进剂4份，防老剂3份，活性氧化镁5份，硫化剂1份，纳米氧化锌4份，硬脂酸2份，阻燃剂50份，软化剂7份，脱模剂3份。
优选地，所述炭黑为炭黑N234、炭黑N330按照3:2组成的混合物。
优选地，所述促进剂为促进剂TMTM、促进剂DOTG按照1:2组成的混合物。
优选地，所述阻燃剂为IFR(膨胀型阻燃剂)、硼酸锌(硼系阻燃剂)、三芳基磷酸酯(磷系阻燃剂)按照3:1:1组成的混合物。
优选地，所述防老剂为微晶石蜡。
优选地，所述硫化剂为S-80。
优选地，所述软化剂为聚乙烯蜡。
一种耐候性钢丝绳芯阻燃输送带覆盖胶的制备方法，包括以下制备步骤：
a、按照上述重量份配比原料，将改性氯磺化聚乙烯橡胶、氯丁橡胶、天然橡胶、防老剂、活性氧化镁、纳米氧化锌、硬脂酸、阻燃剂及促进剂加到密炼机，密炼3分钟；
b、向密炼机中依次加入炭黑、软化剂、脱模剂后密炼4分钟；
c、向密炼机中加入硫化剂后密炼2分钟得到胶体，排料温度控制在110℃，将胶体排出；
d、胶体排出后进入开炼机，经过开炼机后得到6～8mm厚的胶片，将胶片表面涂覆隔离剂后，叠好入库存放。
下表为各实施例产品指标检测表：
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种耐候性钢丝绳芯阻燃输送带覆盖胶，其特征在于，包括以下重量份配比的组分：改性氯磺化聚乙烯橡胶30～40份，氯丁橡胶35～52.5份，天然橡胶15～35份，炭黑50～60份，促进剂2～4份，防老剂1～3份，活性氧化镁2～5份，硫化剂0.5～1份，纳米氧化锌2～4份，硬脂酸1～2份，阻燃剂40～50份，软化剂4～7份，脱模剂2～3份。
2.根据权利要求1所述的一种耐候性钢丝绳芯阻燃输送带覆盖胶，其特征在于，所述炭黑为炭黑N234、炭黑N330按照3:2组成的混合物。
3.根据权利要求1所述的一种耐候性钢丝绳芯阻燃输送带覆盖胶，其特征在于，所述促进剂为促进剂TMTM、促进剂DOTG按照1：1～1:2组成的混合物。
4.根据权利要求1所述的一种耐候性钢丝绳芯阻燃输送带覆盖胶，其特征在于，所述阻燃剂为IFR、氯化石蜡、三氧化二锑、硼酸锌、三芳基磷酸酯中的一种或几种。
5.根据权利要求1所述的一种耐候性钢丝绳芯阻燃输送带覆盖胶，其特征在于，所述防老剂为防老剂4010NA、防老剂RD、微晶石蜡中的一种或几种。
6.根据权利要求1所述的一种耐候性钢丝绳芯阻燃输送带覆盖胶，其特征在于，所述硫化剂为S-80。
7.根据权利要求1所述的一种耐候性钢丝绳芯阻燃输送带覆盖胶，其特征在于，所述软化剂为C5石油树脂、芳烃油、聚乙烯蜡的一种或几种。
8.一种耐候性钢丝绳芯阻燃输送带覆盖胶的制备方法，其特征在于，包括以下制备步骤：
a、按照上述重量份配比原料，将改性氯磺化聚乙烯橡胶、氯丁橡胶、天然橡胶、防老剂、活性氧化镁、纳米氧化锌、硬脂酸、阻燃剂及促进剂加到密炼机，密炼1～3分钟；
b、向密炼机中依次加入炭黑、软化剂、脱模剂后密炼3～4分钟；
c、向密炼机中加入硫化剂后密炼1～2分钟得到胶体，排料温度控制在100～110℃，将胶体排出；
d、胶体排出后进入开炼机，经过开炼机后得到6～8mm厚的胶片。