CN108351538A - 眼镜用光学膜、以及具有该眼镜用光学膜的眼镜用功能性膜、眼镜用光学层叠体和眼镜 - Google Patents
眼镜用光学膜、以及具有该眼镜用光学膜的眼镜用功能性膜、眼镜用光学层叠体和眼镜 Download PDFInfo
- Publication number
- CN108351538A CN108351538A CN201680065449.3A CN201680065449A CN108351538A CN 108351538 A CN108351538 A CN 108351538A CN 201680065449 A CN201680065449 A CN 201680065449A CN 108351538 A CN108351538 A CN 108351538A
- Authority
- CN
- China
- Prior art keywords
- glasses
- optical film
- optical
- light
- functional layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的目的在于提供一种眼镜用光学膜和使用了该眼镜用光学膜的眼镜用功能性膜、光学层叠体以及眼镜,通过感受到压力的人使用该眼镜用光学膜,能够容易地制作出呈现心理上感受到治愈的色调的空间。本发明提供一种眼镜用光学膜,其特征在于,具有光学功能层,以白色光为光源的透射光呈现淡色调。
Description
技术领域
本发明涉及例如适合构成眼镜或太阳镜等眼镜的光学膜、以及使用了该光学膜的眼镜用功能性膜、眼镜用光学层叠体和眼镜。
背景技术
近年来,如被称为压力社会这样,存在许多对各种事情承担压力的人。作为减轻压力的方法,例如可以举出引入对人给予治愈的颜色的方法。作为承担压力的人们感到治愈的颜色,有非专利文献1中记载的那样的淡色调的颜色。淡色调通常是指彩度比较低、明度高的色调,已知根据压力的原因或个人的颜色嗜好,感到治愈的色调有所不同。
作为在生活空间中引入给予治愈的颜色的方法,例如可以举出将房间的壁纸或家具、室内装饰、服装变更为淡色调的配色的方法。
现有技术文献
非专利文献
非专利文献1:物部宽太郎、高桥淳也、秋叶成美,“ストレス原因に適した癒しの色に関する研究(关于适合于压力原因的治愈色的研究)”、信息处理学会东北支部研究报告、Vol.2012-4
发明内容
发明所要解决的课题
但是,将空间整体变更为淡色调的配色并不容易,因此仅限于变更壁纸或改变服装这样的有限的变更。
另一方面,太阳镜是用色素等在透镜部着色,通过色素的吸收而降低入射至眼中的光量,减少眩光,能够提供良好的视野。此外,为了对太阳镜赋予设计性,有时在表面蒸镀多层膜。通过赋予多层膜,他人可看到太阳镜表面的蓝、绿、红之类的金属色调的色彩的反射光。
但是,对于透过太阳镜的光(透射光),重点主要放在调整成与裸眼相同的配色的方面。并未积极地进行利用透过太阳镜的光来改变生活空间中的明度或色调、赋予治愈的效果这样的研究。
因此,本发明的目的在于提供一种眼镜用光学膜以及具有该眼镜用光学膜的眼镜用功能性膜、眼镜用光学层叠体和眼镜,该眼镜用光学膜能够容易地制作出呈现使用者在心理上感受到治愈的色调的空间。
用于解决课题的手段
本发明人为了解决上述课题进行了深入研究,结果新发现了使用以透过光学膜的光(透射光)的色调为淡色调的方式设计的光学膜的眼镜能够解决上述课题,从而完成了本发明。即,本发明涉及以下的[1]~[9]。
[1]一种眼镜用光学膜,其特征在于,
具有光学功能层,
以白色光为光源的透射光呈现淡色调。
[2]如上述[1]所述的眼镜用光学膜,其中,以JIS Z 8781-4:2013中规定的L*a*b*色度系统将所述透射光的色调进行数值化时,表示明度的L*值为70以上100以下的范围。
[3]如上述[1]或[2]所述的眼镜用光学膜,其中,以JIS Z 8781-4:2013中规定的L*a*b*色度系统将所述透射光的色调进行数值化时,通过将表示色度的a*值和b*值代入下述式(1)中而算出的表示彩度的C*值为1以上35以下的范围。
C*=[(a*)2+(b*)2]1/2 (1)
[4]如上述[1]~[3]中任一项所述的眼镜用光学膜,其中,以JIS Z 8781-4:2013中规定的L*a*b*色度系统将所述透射光的色调进行数值化时,表示色度的a*值为-15以上5以下的范围,并且b*值为-20以上0以下的范围。
[5]一种眼镜用功能性膜,其具备上述[1]~[4]中任一项所述的光学膜和偏振元件。
[6]一种眼镜用光学层叠体,其具备:
上述[1]~[4]中任一项所述的光学膜或上述[5]所述的功能性膜;和
以将所述光学膜或所述功能性膜从其两面侧进行夹持的位置关系配置的两个支撑体。
[7]如上述[6]所述的眼镜用光学层叠体,其中,所述两个支撑体中的至少一者由选自由三乙酰纤维素、聚碳酸酯、尼龙树脂和环烯烃聚合物组成的组中的1种或2种以上的材料形成。
[8]一种眼镜,其包含上述[6]或[7]所述的光学层叠体。
[9]如上述[8]所述的眼镜,其进一步包含透镜,
其是将所述光学层叠体配置于所述透镜的一面侧或两面侧而成的。
发明的效果
本发明可以提供一种眼镜用光学膜、以及具有该眼镜用光学膜的眼镜用功能性膜、眼镜用光学层叠体和眼镜,该眼镜用光学膜通过使以白色光为光源的透射光呈现淡色调,能够容易地制作出呈现使用者在心理上感受到治愈的色调的空间。
附图说明
图1是示出具备本发明的眼镜用光学膜的眼镜用光学层叠体的一例的示意性截面图。
具体实施方式
[眼镜用光学膜]
本发明的眼镜用光学膜(以下简称为“光学膜”)的特征在于,具有光学功能层,以白色光为光源的透射光呈现淡色调。这样的光学膜在用于太阳镜或眼镜等眼镜的情况下,能够容易地制作出呈现对使用者而言在心理上感受到治愈的色调的空间。
此处,白色光通常是指可见光线的所有波长的光(颜色)均等地混杂的光,是不给予配色的感觉的光,但在本说明书中还包括带蓝色调的白色光、带黄色调的白色光,优选色温为4000~7000开尔文(K)的光。作为这样的光,可以举出例如太阳光(自然光)、或以电灯泡、荧光灯和LED灯等为光源的光、CIE规定的标准光C(所谓的C光源)等。另外,以白色光为光源的透射光的色调(透射色)是指以白色光为光源从光学膜中透射的光的配色。
另外,淡色调(pale tone)是指明度高、彩度低的色调。这样的色调在PCCS(日本色研配色体系:Practical Color Co-ordinate System)的色调中被规定为p(pale,淡)。作为表现出本发明所着眼的治愈效果的淡色调,优选可以举出PCCS色调的p3、p4、p5、p6、p7、p8、p9、p10、p11、p12、p13、p14、p15、p16、p19、p20、p21、p22、p23、p24,其中更优选p6、p10、p11、p12、p14、p15、p16、p19、p20、p22、p24。
另外,在以JIS Z 8781-4:2013中规定的CIE(国际照明委员会)L*a*b*色度系统将上述透射光的色调进行数值化的情况下,如下所述。需要说明的是,测定条件为C光源(CIE规定的标准光C)和2度视野。
表示明度的L*值优选为70以上100以下的范围,更优选为75以上98以下的范围,进一步优选为80以上95以下的范围。
另外,由表示色度的a*值和b*值通过下述式(1)算出的表示彩度的C*值优选为1以上35以下的范围,更优选为5以上30以下的范围,进一步优选为8以上25以下的范围。
C*=[(a*)2+(b*)2]1/2 (1)
另外,表示色度的a*值优选为-15以上5以下的范围,更优选为-12以上-5以下的范围。
另外,表示色度的b*值优选为-20以上0以下的范围,更优选为-20以上-3以下的范围。
特别优选的是,表示色度的a*值为-15以上5以下的范围、并且b*值为-20以上0以下的范围,能够实现这种色调的透射光的本发明的光学膜通过用于太阳镜或眼镜等眼镜,表现出特别高的治愈效果。
另外,本发明的光学膜只要至少具有光学功能层即可,可以仅由1层光学功能层构成,也可以是2层以上的光学功能层层叠而成。在2层以上的光学功能层层叠的情况下,各层可以为相同种类的光学功能层,也可以为种类互相不同的光学功能层。各光学功能层的层叠数取决于光学功能层的种类,可以按照以光学功能层的层叠物整体来看透射光呈现淡色调的方式适当决定。另外,本发明的光学膜可以在不损害透射光的色调的范围内进一步具有光学功能层以外的层,作为光学功能层以外的层,例如可以举出粘接剂层、粘合剂层、硬涂层等。
光学功能层只要能够使透射光的色调(以下简称为“透射色”)为淡色调就没有特别限制。作为光学功能层,例如可以举出利用色素、金属蒸镀得到的多层膜、折射率不同的树脂多层膜、选择性地对可见光区域的光进行反射的胆甾型液晶层等,这些光学功能层可以为单独一种或者两种以上的组合。其中,从仅通过改变材料的配比就能够容易地调整透射色、并且能够以较少的层数实现目标透射色的方面出发,优选使用胆甾型液晶层。
胆甾型液晶层可以通过将液晶组合物中的向列型液晶化合物的胆甾型取向固定而形成。液晶组合物至少包含具有手性的向列型液晶化合物、或者向列型液晶化合物和手性剂。制作胆甾型液晶层的方法例如优选至少包括:制备液晶组合物的工序;涂布液晶组合物而形成涂布膜的工序;使涂布膜干燥的工序;和使干燥的涂布膜固化的工序。
在制备液晶组合物的工序中,优选在向列型液晶化合物中添加必要量的右旋或左旋的手性剂以对所期望的波长进行反射。通过手性剂的种类或量,可以任意地设计液晶分子的螺旋方向和反射波长。接着,将它们溶解于溶剂中,根据需要添加光聚合引发剂和助剂。
与所谓的利用电场进行操作的液晶不同,向列型液晶是将螺旋取向状态固定化来使用的,因此优选使用具有聚合性基团的向列型液晶单体作为向列型液晶化合物。具有聚合性基团的向列型液晶单体是在分子内具有聚合性基团、在某一温度范围或浓度范围内显示出液晶性的化合物。作为聚合性基团,例如可以举出(甲基)丙烯酰基、乙烯基、查耳酮基、肉桂酰基和环氧基等。另外,为了显示出液晶性,优选在分子内具有介晶基元(mesogen)基团。介晶基元基团是具有诱导液晶相行为的能力的基团,例如为联苯基、三联苯基、(聚)苯甲酸苯酯基、(聚)醚基、亚苄基苯胺基和苊并喹喔啉基等棒状或板状的取代基、或者苯并[9,10]菲基、酞菁基和氮杂冠醚基等圆盘状的取代基。具有棒状或板状基的液晶化合物作为棒状液晶在该技术领域中是已知的。具有这种聚合性基团的向列型液晶单体具体可以举出日本特开2003-315556号公报和日本特开2004-29824号公报中记载的聚合性液晶、Paliocolor(注册商标、以下相同)系列(BASF Japan株式会社制造)和RMM系列(默克株式会社制造)等。这些具有聚合性基团的向列型液晶单体可以单独使用,或者也可以使用2种以上的混合物。
作为手性剂,优选能够使具有上述聚合性基团的向列型液晶单体右旋或左旋螺旋取向、与具有聚合性基团的向列型液晶单体同样地具有聚合性基团的化合物。作为这样的手性剂,例如可以举出PaliocolorLC756(BASF Japan株式会社制造)等。手性剂的添加量还根据手性剂的种类和所反射的波长而不同,相对于具有聚合性基团的向列型液晶单体100质量份,优选为0.5质量份~30质量份左右,更优选为1质量份~20质量份左右。
此外,还可以在液晶组合物中添加能够与具有聚合性基团的向列型液晶单体反应的不具有液晶性的聚合性化合物。作为这样的化合物,例如可以举出紫外线固化型树脂等。作为紫外线固化型树脂,例如可以举出二季戊四醇六(甲基)丙烯酸酯、二季戊四醇五(甲基)丙烯酸酯与1,6-六亚甲基二异氰酸酯的反应产物、具有异氰脲酸环的三异氰酸酯与季戊四醇三(甲基)丙烯酸酯的反应产物、季戊四醇三(甲基)丙烯酸酯与异佛尔酮二异氰酸酯的反应产物、二季戊四醇五(甲基)丙烯酸酯、二季戊四醇四(甲基)丙烯酸酯、季戊四醇四(甲基)丙烯酸酯、季戊四醇三(甲基)丙烯酸酯、三羟甲基丙烷三(甲基)丙烯酸酯、双(三羟甲基丙烷)四(甲基)丙烯酸酯、三(丙烯酰氧基乙基)异氰脲酸酯、三(甲基丙烯酰氧基乙基)异氰脲酸酯、甘油三缩水甘油醚与(甲基)丙烯酸的反应产物、己内酯改性三(丙烯酰氧基乙基)异氰脲酸酯、三羟甲基丙烷三缩水甘油醚与(甲基)丙烯酸的反应产物、三甘油二(甲基)丙烯酸酯、丙二醇二缩水甘油醚与(甲基)丙烯酸的反应产物、聚丙二醇二(甲基)丙烯酸酯、三丙二醇二(甲基)丙烯酸酯、聚乙二醇二(甲基)丙烯酸酯、四乙二醇二(甲基)丙烯酸酯、三乙二醇二(甲基)丙烯酸酯、季戊四醇二(甲基)丙烯酸酯、1,6-己二醇二缩水甘油醚与(甲基)丙烯酸的反应产物、1,6-己二醇二(甲基)丙烯酸酯、甘油二(甲基)丙烯酸酯、乙二醇二缩水甘油醚与(甲基)丙烯酸的反应产物、二乙二醇二缩水甘油醚与(甲基)丙烯酸的反应产物、双(丙烯酰氧基乙基)羟乙基异氰脲酸酯、双(甲基丙烯酰氧基乙基)羟乙基异氰脲酸酯、双酚A二缩水甘油醚与(甲基)丙烯酸的反应产物、(甲基)丙烯酸四氢糠酯、己内酯改性(甲基)丙烯酸四氢糠酯、(甲基)丙烯酸-2-羟基乙酯、(甲基)丙烯酸-2-羟基丙酯、聚丙二醇(甲基)丙烯酸酯、聚乙二醇(甲基)丙烯酸酯、(甲基)丙烯酸苯氧基羟丙酯、丙烯酰吗啉、甲氧基聚乙二醇(甲基)丙烯酸酯、甲氧基四乙二醇(甲基)丙烯酸酯、甲氧基三乙二醇(甲基)丙烯酸酯、甲氧基乙二醇(甲基)丙烯酸酯、(甲基)丙烯酸甲氧基乙酯、(甲基)丙烯酸缩水甘油酯、甘油(甲基)丙烯酸酯、乙基卡必醇(甲基)丙烯酸酯、(甲基)丙烯酸-2-乙氧基乙酯、(甲基)丙烯酸-N,N-二甲氨基乙酯、(甲基)丙烯酸-2-氰基乙酯、丁基缩水甘油醚与(甲基)丙烯酸的反应产物、丁氧基三乙二醇(甲基)丙烯酸酯和丁二醇单(甲基)丙烯酸酯等,它们可以单独使用或者将两种以上混合使用。这些不具有液晶性的紫外线固化型树脂必须以不使液晶性丧失的程度添加到具有聚合性基团的向列型液晶单体中,相对于具有聚合性基团的向列型液晶单体100质量份,优选为0.1质量份~20质量份、更优选为1.0质量份~10质量份左右的添加量。
在具有聚合性基团的向列型液晶单体或其他聚合性化合物为紫外线固化型的情况下,为了利用紫外线进行固化,优选在液晶组合物中进一步添加光聚合引发剂。作为光聚合引发剂,例如可以举出2-甲基-1-[4-(甲硫基)苯基]-2-吗啉代丙烷-1-酮(BASF Japan株式会社制造Irgacure(注册商标、以下相同)907)、1-羟基环己基苯基酮(BASF Japan株式会社制造Irgacure 184)、4-(2-羟基乙氧基)苯基(2-羟基-2-丙基)酮(BASF Japan株式会社制造Irgacure 2959)、1-(4-十二烷基苯基)-2-羟基-2-甲基丙烷-1-酮(默克株式会社制造Darocure(注册商标、以下相同)953)、1-(4-异丙基苯基)-2-羟基-2-甲基丙烷-1-酮(默克株式会社制造Darocure 1116)、2-羟基-2-甲基-1-苯基丙烷-1-酮(BASF Japan株式会社制造Irgacure 1173)、二乙氧基苯乙酮等苯乙酮系化合物、苯偶姻、苯偶姻甲醚、苯偶姻乙醚、苯偶姻异丙醚、苯偶姻异丁醚、2,2-二甲氧基-2-苯基苯乙酮(BASF Japan株式会社制造Irgacure 651)等苯偶姻系化合物、苯甲酰苯甲酸、苯甲酰苯甲酸甲酯、4-苯基二苯甲酮、羟基二苯甲酮、4-苯甲酰基-4’-甲基二苯基硫醚、3,3’-二甲基-4-甲氧基二苯甲酮(日本化药株式会社制造Kayacure MBP)等二苯甲酮系化合物、噻吨酮、2-氯噻吨酮(日本化药株式会社制造Kayacure CTX)、2-甲基噻吨酮、2,4-二甲基噻吨酮(日本化药株式会社制造Kayacure RTX)、异丙基噻吨酮、2,4-二氯噻吨酮(日本化药株式会社制造Kayacure CTX)、2,4-二乙基噻吨酮(日本化药株式会社制造Kayacure DETX)、或2,4-二异丙基噻吨酮(日本化药株式会社制造Kayacure DITX)等噻吨酮系化合物等。作为光聚合引发剂,优选可以举出例如Irgacure TPO、Irgacure TPO-L、Irgacure OXE01、Irgacure OXE02、Irgacure1300、Irgacure 184、Irgacure 369、Irgacure 379、Irgacure 819、Irgacure 127、Irgacure 907或Irgacure 1173(均为BASF Japan株式会社制造),特别优选可以举出Irgacure TPO、Irgacure TPO-L、Irgacure OXE01、Irgacure OXE02、Irgacure 1300或Irgacure 907。这些光聚合引发剂可以单独使用一种,也可以将两种以上以任意的比例混合使用。
在使用二苯甲酮系化合物或噻吨酮系化合物作为光聚合引发剂的情况下,为了促进光聚合反应,还可以合用助剂。作为这样的助剂,例如可以举出三乙醇胺、甲基二乙醇胺、三异丙醇胺、正丁胺、N-甲基二乙醇胺、甲基丙烯酸二乙基氨基乙酯、米希勒酮、4,4’-二乙基氨基苯酮、4-二甲氨基苯甲酸乙酯、4-二甲氨基苯甲酸(正丁氧基)乙酯或4-二甲氨基苯甲酸异戊酯等胺系化合物。
光聚合引发剂和助剂的添加量优选设定为不对液晶组合物的液晶性产生影响的范围。相对于液晶组合物中的利用紫外线进行固化的化合物100质量份,光聚合引发剂的添加量优选为0.5质量份~10质量份、更优选为2质量份~8质量份左右。另外,相对于光聚合引发剂的质量,助剂向液晶组合物中的添加量可以为0.5倍至2倍量左右。
在液晶组合物中,可以进一步添加用于溶解液晶化合物的溶剂。溶剂例如为环戊酮、甲苯和甲基乙基酮等,本领域技术人员可以适当决定。相对于液晶组合物的总固体成分100质量份,溶剂的添加量优选为300质量份~1000质量份。
接着,在涂布液晶组合物而形成涂布膜的工序中,优选将如此制备的液晶组合物以厚度尽可能均匀的方式涂布到PET膜等塑料基板上,形成涂布膜。
在使液晶组合物的涂布膜干燥的工序中,优选一边加热液晶组合物的涂布膜而除去溶剂,一边以在基板上形成胆甾型液晶且以所期望的螺旋间距取向的温度条件放置一定时间。加热温度优选设定为40℃~200℃的范围,加热时间优选设定为1分钟~7分钟,但加热的温度和时间可以由本领域技术人员适当调整。此时,通过在涂布前预先对塑料膜基板表面进行摩擦或拉伸等取向处理,能够使胆甾型液晶的取向更均匀,能够降低作为膜的雾度值。
接着,在使干燥的涂布膜固化的工序中,在保持液晶化合物的取向状态的情况下,利用高压汞灯等照射紫外线,使取向固定化,由此可得到胆甾型液晶层。此处,在选择成为右旋螺旋取向的手性剂的情况下,所得到的是反射右圆偏振光的胆甾型液晶层,在选择成为左旋螺旋取向的手性剂的情况下,所得到的是反射左圆偏振光的胆甾型液晶层。
胆甾型液晶层的透射色根据反射波段而不同。反射波段使用作为该反射波段的中心值的中心反射波长来表现。为了使透射色为淡色调,优选使中心反射波长为可见光区域,中心反射波长根据所要求的色调在400nm~800nm、更优选410nm~780nm、进一步优选430nm~700nm的范围进行适当选择。例如,中心反射波长为450nm的情况下透射色为黄色,550nm的情况下透射色为紫红色,650nm的情况下透射色为淡蓝色。
为了使用胆甾型液晶层实现淡色调的透射色,调整胆甾型液晶层的透射率和反射波段以达到所期望的明度和彩度即可。具体而言,胆甾型液晶层的透射率可以通过改变该液晶层的厚度来调整。为了实现淡色调的透射色,使胆甾型液晶层的厚度例如为0.3μm~7μm、优选为0.5μm~5μm以下左右为宜。
在所期望的反射波段宽的情况下,可以通过将具有不同反射波段的胆甾型液晶层层叠两层以上来进行反射波段的调整。例如,通过将中心反射波长为450nm的胆甾型液晶层与中心反射波长为650nm的胆甾型液晶层层叠,能够表现出黄绿色的透射色。因此,眼镜用光学膜可以包含单独1层的胆甾型液晶层,也可以组合包含具有不同透射色的2个以上的胆甾型液晶层。该组合没有特别限制,通过该组合能够得到复杂多样的透射色。胆甾型液晶层的层数可根据所期望的透射色而适当调整,例如为1~5、优选为1或2。
将胆甾型液晶层层叠的手段没有特别限制,优选使用粘合剂或粘接剂进行层叠。作为粘合剂,可以举出丙烯酸系或橡胶系的粘合剂,优选容易调整粘接性和保持力等的丙烯酸系粘合剂。另外,作为粘接剂,可以举出紫外线固化型树脂组合物或热固化型树脂组合物。在紫外线固化型树脂的情况下,可以在光聚合引发剂的存在下对将两种以上具有丙烯酰基或环氧基的单体混合而成的组合物照射紫外线,由此使其固化而粘接。在热固化型树脂组合物的情况下,可以在酸催化剂的存在下对将两种以上具有环氧基的单体混合而成的组合物进行加热,由此使其固化而粘接。或者,可以在具有异氰酸酯基或三聚氰胺的化合物的存在下对包含具有氨基、羧基或羟基的2种以上的单体或聚合物的组合物进行加热,由此使其固化而粘接。
另外,作为将胆甾型液晶层层叠的粘合剂或粘接剂,也可以使用溶解有色素的粘合剂或粘接剂。由此,能够得到具有更复杂的透射色的眼镜用光学膜。
[眼镜用功能性膜]
眼镜用功能性膜(以下有时简称为“功能性膜”)具备上述光学膜和偏振元件。通过在上述光学膜上层叠偏振元件,能够抑制透射率,进一步调整明度。
作为偏振元件,典型地可以举出PVA偏振膜,制作方法没有特别限定,使碘或二色性染料等色素吸附到由聚乙烯醇(PVA)或其衍生物形成的高分子膜上并使该膜进行单向拉伸取向而制造。作为色素,从耐热性的方面考虑,优选二色性染料,特别优选由具有磺酸基的偶氮色素构成的直接染料。
作为将上述光学膜与偏振元件层叠的方法,没有特别限定,从得到高粘接力的方面考虑,优选藉由上述的粘合剂或粘接剂之类的粘接层来贴合。作为粘接层,热熔型粘接剂和固化型粘接剂均可使用。粘接上述光学膜和偏振元件的粘接剂也可以使用溶解有调光染料的粘接剂。
[眼镜用光学层叠体]
眼镜用光学层叠体(以下有时简称为“光学层叠体”)具备上述光学膜或上述功能性膜、和以将上述光学膜或上述功能性膜从其两面侧进行夹持的位置关系配置的两个支撑体。
作为支撑体,例如可以使用聚碳酸酯(PC)、三乙酰纤维素(TAC)、尼龙树脂、环烯烃聚合物等透明性高的树脂。两个支撑体可以由相同材料形成,也可以由不同材料形成。优选的是,两个支撑体中的至少一者由选自由三乙酰纤维素、聚碳酸酯、尼龙树脂和环烯烃聚合物组成的组中的1种或2种以上的材料形成。
另外,优选两个支撑体各自与上述光学膜或上述功能性膜藉由粘接剂层而贴合。粘接剂层没有特别限定,为了得到高粘接力,眼镜用功能性膜优选利用上述的粘合剂或粘接剂形成。作为粘接层,热熔型粘接剂和固化型粘接剂均可使用。
另外,这样的光学层叠体在作为眼镜使用时,优选成型为所期望的形状并固定于框架中来使用。
此处,图1中,作为本发明的光学层叠体的构成的一例示出示意性截面图。如图1所示,本发明的光学层叠体30具备本发明的功能性膜20和以将功能性膜20从其两面侧进行夹持的位置关系配置的两个支撑体7,各层利用粘合剂层或粘接剂层3进行层叠。此处,功能性膜20具备本发明的光学膜10和偏振元件5,各层藉由粘合剂层或粘接剂层3进行层叠。另外,光学膜10具有光学功能层1,此处,特别是2层光学功能层1藉由粘合剂层或粘接剂层3进行层叠。
图1中,2层光学功能层1可以为种类相同的光学功能层,也可以为种类相互不同的光学功能层。作为为种类相互不同的光学功能层的情况,例如可以举出一者为反射右圆偏振光的胆甾型液晶层(R)、另一者为反射左圆偏振光的胆甾型液晶层(L)的情况等。
[眼镜]
眼镜包含上述光学层叠体,根据需要可以进一步包含固定光学层叠体的框架、透镜。
特别是在眼镜包含具备功能性膜的光学层叠体的情况下,光学膜优选按照比偏振元件更靠外侧的方式固定于框架中。
另外,在眼镜包含透镜的情况下,优选将上述光学层叠体配置于透镜的一面侧或两面侧。
在这样的眼镜中,可以进一步对光学层叠体的外侧表面适当进行用于硬涂或防反射、防雾的表面处理等。
眼镜适宜为太阳镜或护目镜等形态,只要覆盖视野的一部分或全部就没有特别限定。在室内或室外均可使用。使用者特别是在感到压力时等,通过佩戴本发明的眼镜,能够容易地制作出呈现心理上感到治愈的色调的空间,通过视觉能够感受到治愈,能够缓解压力。
实施例
下面,通过实施例详细例示本发明。实施例中,份是指质量份。
<涂布液(液晶组合物)的制备>
按照下述表1和2所示的组成,使聚合性液晶单体、手性剂和聚合引发剂溶解于溶剂中,分别制备出涂布液(R剂)和(L剂)。
【表1】
涂布液(R剂)的组成表
【表2】
涂布液(L剂)的组成表
手性剂:化合物1(日本特开2002-179668号公报中记载的例示化合物2-1)
【化1】
<光学功能层的制作>
使用按照上述表1和2的组成制备的涂布液(R1~4和L1~4),按照下述步骤制作出光学功能层(R1~4和L1~4)。下面,以使用涂布液(R1)的情况为例进行说明。
首先,使用线棒在室温下将涂布液(R1)涂布至PET膜(东洋纺绩株式会社制造、无底涂层)上,使干燥后的膜的厚度为4μm。
接着,将涂布至PET膜上的涂布液(R1)在150℃加热5分钟,除去溶剂,制成胆甾型液晶层。接着,对于该胆甾型液晶层,利用高压汞灯(哈利盛东芝照明株式会社(现东芝照明技术株式会社)制造),以120W输出功率、5秒~10秒的条件进行UV照射,将胆甾型液晶层固定,得到光学功能层(R1)。
需要说明的是,在使用涂布液(R2~4和L1~4)的情况下,也同样地按照上述步骤得到光学功能层(R2~4和L1~4)。
[实施例1]
将通过上述步骤制作的光学功能层(R1)从PET膜剥离,得到由光学功能层(R1)构成的实施例1的眼镜用光学膜。
[实施例2]
将通过上述步骤制作的光学功能层(R2)从PET膜剥离,得到由光学功能层(R2)构成的实施例2的眼镜用光学膜。
[实施例3]
将通过上述步骤制作的光学功能层(R3)从PET膜剥离,得到由光学功能层(R3)构成的实施例3的眼镜用光学膜。
[实施例4]
将通过上述步骤制作的光学功能层(R4)从PET膜剥离,得到由光学功能层(R4)构成的实施例4的眼镜用光学膜。
[实施例5]
将通过上述步骤制作的光学功能层(R1)和光学功能层(L1)按照光学功能层侧彼此相向的方式藉由丙烯酸系粘合剂进行层叠。之后,将位于两面的PET膜剥离,得到具有光学功能层(R1)和光学功能层(L1)的实施例5的眼镜用光学膜。
[实施例6]
代替光学功能层(R1)和(L1)而使用通过上述步骤制作的光学功能层(R2)和(L2),除此以外通过与实施例5同样的操作得到具有光学功能层(R2)和光学功能层(L2)的实施例6的眼镜用光学膜。
[实施例7]
代替光学功能层(R1)和(L1)而使用通过上述步骤制作的光学功能层(R2)和(R3),除此以外通过与实施例5同样的操作得到具有光学功能层(R2)和光学功能层(R3)的实施例7的眼镜用光学膜。
[实施例8]
代替光学功能层(R1)和(L1)而使用通过上述步骤制作的光学功能层(R3)和(R4),除此以外通过与实施例5同样的操作得到具有光学功能层(R3)和光学功能层(R4)的实施例8的眼镜用光学膜。
[实施例9]
代替光学功能层(R1)和(L1)而使用通过上述步骤制作的光学功能层(R2)和(R4),除此以外通过与实施例5同样的操作得到具有光学功能层(R2)和光学功能层(R4)的实施例9的眼镜用光学膜。
[比较例1]
代替光学功能层(R1)和(L1)而使用通过上述步骤制作的光学功能层(R3)和(L3),除此以外通过与实施例5同样的操作得到具有光学功能层(R3)和光学功能层(L3)的比较例1的眼镜用光学膜。
[比较例2]
代替光学功能层(R1)和(L1)而使用通过上述步骤制作的光学功能层(R4)和(L4),除此以外通过与实施例5同样的操作得到具有光学功能层(R4)和光学功能层(L4)的比较例2的眼镜用光学膜。
[透射光的色调的观察]
对实施例1~9以及比较例1和2中制作的眼镜用光学膜的透射光的色调(透射色)进行观察。具体而言,在荧光灯(三菱电机株式会社制造ルピカラインEX-N色温5000K)下,将眼镜用光学膜配置于距离眼为1cm~3cm左右的位置,隔着眼镜用光学膜观察白色的屏幕,对其色调进行评价。需要说明的是,在本实施例中,透射光的色调的判断依照PCCS的比色图表(日本色研PCCS调和色图表201-L)的颜色样本来进行。将所观察到的透射光的色调(透射色)记载于下述表3中。
[L*值、a*值和b*值的测定以及C*值的计算]
使用分光光度计MPC-3100(株式会社岛津制作所制造),测定实施例1~9以及比较例1和2中制作的眼镜用光学膜的透射光谱。使用所得到的光谱进行色彩计算,分别求出JISZ 8781-4:2013中规定的L*a*b*色度系统(C光源、2度视野)中的L*值、a*值和b*值。关于表示彩度的C*,通过将表示色度的a*值和b*值代入下述式(1)中而算出。将所得到的结果记载于下述表3中。
C*=[(a*)2+(b*)2]1/2 (1)
[治愈效果的评价]
对实施例1~9以及比较例1和2的眼镜用光学膜所给予的治愈效果进行了试验。具体而言,请20几岁~40几岁的男女共9名评委观察眼镜用光学膜的透射光的色调(透射色),对于其色调,就是否感受到治愈效果实施问卷调查。眼镜用光学膜的透射色的观察通过在荧光灯(同上)下将眼镜用光学膜配置于距离眼为1cm~3cm左右的位置,隔着眼镜用光学膜观察景向10秒~20秒左右来实施。计算出回答“感受到”治愈效果的评委的比例,将其结果记载于下述表3中。在本实施例中,将33%以上(9人中3人以上)回答感受到治愈效果的情况作为合格线。
【表3】
(注)表中的下划线粗字表示本发明的适当范围外的情况和评价结果未达到本实施例中的合格水平的情况。
如表3所示,比较例1和2的眼镜用光学膜由于透射光未呈现淡色调,因此对使用者无法给予治愈效果。与此相对,本发明的实施例1~9的眼镜用光学膜由于透射光均呈现淡色调,因此确认到对使用者能够给予治愈效果。
此外可知,实施例1、2、5和7的眼镜用光学膜通过a*值为-15以上5以下的范围且b*值为-20以上0以下的范围,对70%以上的使用者给予高的治愈效果。
根据本发明的眼镜用光学膜,通过透射光呈现淡色调,能够容易地制作出呈现使用者在心理上感受到治愈的色调的空间。因此,根据使用了这种本发明的眼镜用光学膜的眼镜用功能性膜、光学层叠体和眼镜,能够通过视觉给予使用者治愈效果,能够缓解使用者的压力。
符号说明
1 光学功能层
3 粘合剂或粘接剂
5 偏振元件
7 支撑体
10 眼镜用光学膜
20 眼镜用功能性膜
30 眼镜用光学层叠体
Claims (9)
1.一种眼镜用光学膜,其特征在于,
具有光学功能层,
以白色光为光源的透射光呈现淡色调。
2.如权利要求1所述的眼镜用光学膜,其中,以JIS Z 8781-4:2013中规定的L*a*b*色度系统将所述透射光的色调进行数值化时,表示明度的L*值为70以上100以下的范围。
3.如权利要求1或2所述的眼镜用光学膜,其中,以JIS Z 8781-4:2013中规定的L*a*b*色度系统将所述透射光的色调进行数值化时,通过将表示色度的a*值和b*值代入下述式(1)中而算出的表示彩度的C*值为1以上35以下的范围,
C*=[(a*)2+(b*)2]1/2 (1)。
4.如权利要求1~3中任一项所述的眼镜用光学膜,其中,以JIS Z 8781-4:2013中规定的L*a*b*色度系统将所述透射光的色调进行数值化时,表示色度的a*值为-15以上5以下的范围,并且b*值为-20以上0以下的范围。
5.一种眼镜用功能性膜,其具备权利要求1~4中任一项所述的光学膜和偏振元件。
6.一种眼镜用光学层叠体,其具备:
权利要求1~4中任一项所述的光学膜或权利要求5所述的功能性膜;和
以将所述光学膜或所述功能性膜从其两面侧进行夹持的位置关系配置的两个支撑体。
7.如权利要求6所述的眼镜用光学层叠体,其中,所述两个支撑体中的至少一者由选自由三乙酰纤维素、聚碳酸酯、尼龙树脂和环烯烃聚合物组成的组中的1种或2种以上的材料形成。
8.一种眼镜,其包含权利要求6或7所述的光学层叠体。
9.如权利要求8所述的眼镜,其进一步包含透镜,
其是将所述光学层叠体配置于所述透镜的一面侧或两面侧而成的。