TW201728921A - 眼鏡用光學薄膜、以及具有此的眼鏡用機能性薄膜、眼鏡用光學層合體及眼鏡 - Google Patents
眼鏡用光學薄膜、以及具有此的眼鏡用機能性薄膜、眼鏡用光學層合體及眼鏡 Download PDFInfo
- Publication number
- TW201728921A TW201728921A TW105136678A TW105136678A TW201728921A TW 201728921 A TW201728921 A TW 201728921A TW 105136678 A TW105136678 A TW 105136678A TW 105136678 A TW105136678 A TW 105136678A TW 201728921 A TW201728921 A TW 201728921A
- Authority
- TW
- Taiwan
- Prior art keywords
- optical
- film
- color
- optical film
- light
- Prior art date
Abstract
本發明之目的在於提供眼鏡用光學薄膜及使用此的眼鏡用機能性薄膜、光學層合體以及眼鏡，其係經由感覺壓力的人使用，可容易作出呈現心理地感覺療癒之色調的空間。提供眼鏡用光學薄膜，其特徵為具有光學機能層，以白色光作為光源的透過光係呈現淡色調。
Description
本發明關於例如適合構成眼鏡或太陽眼鏡等之眼鏡的光學薄膜、以使用此之眼鏡用機能性薄膜、眼鏡用光學層合體及眼鏡。
近年來如被說是壓力社會般，對於各式各樣的事情抱持壓力的人係多數存在。作為減輕壓力之方法，例如可舉出引進給予療癒的顏色。抱持壓力的人們係有如非專利文獻1中記載之淡色調的色作為療癒感顏色。所謂的淡色調，就是一般而言彩度比較低、明度高之色調，已知取決於壓力的原因或個人的顏色之嗜好，療癒感色調係不同。
作為在生活空間之中引進給予療癒的顏色之方法，例如可舉出將房間的壁紙或家具、室內裝飾、服裝變更為淡色調的配色之方法。
先前技術文獻
非專利文獻
非專利文獻1：物部寬太郎、高橋淳也、秋葉成美，「關於適合壓力原因的療癒之顏色的研究」，資訊處理學會東北支部研究報告，Vol.2012-4
然而，由於將空間全體變更為淡色調的配色者係不容易，故限於變更壁紙或改變服裝等限定的變更。
另一方面，太陽眼鏡係以色素等著色於透鏡，藉由色素之吸收而減低入射至眼睛的光量，而減低眩光，可提供良好的視野。再者，為了對於太陽眼鏡賦予設計性，有在表面上蒸鍍多層膜之情況。藉由賦予多層膜，他人可見到太陽眼鏡表面之藍或綠、紅等的金屬調之色彩的反射光。
然而，對於穿透太陽眼鏡的光(透過光)，重點都放置在調整成與裸眼相同的配色。檢討藉由穿透太陽眼鏡的光而改變生活空間中的明度或色調，給予療癒的效果之檢討並沒有積極地進行。
因此，本發明之目的在於提供可容易作出呈現使用者心理地感覺療癒之色調的空間之眼鏡用光學薄膜、以及具有此的眼鏡用機能性薄膜、眼鏡用光學層合體及眼鏡。
本發明者們為了解決上述問題而進行專心致力的檢討，結果新穎地發現使用以穿透光學薄膜的光(透過光)之色調成為淡色調之方式所設計的光學薄膜之眼鏡係能解決上述問題，而達成本發明。即，本發明關於以下之[1]~[9]。
[1]一種眼鏡用光學薄膜，其特徵為：具有光學機能層，以白色光作為光源的透過光係呈現淡色調。
[2]如上述[1]記載之眼鏡用光學薄膜，其中以JIS Z 8781-4：2013中規定的L*a*b*表色系將前述透過光之色調予以數值化時，表示明度的L*值為70以上100以下之範圍。
[3]如上述[1]或[2]記載之眼鏡用光學薄膜，其中以JIS Z 8781-4：2013中規定的L*a*b*表色系將前述透過光之色調予以數值化時，藉由將表示色度的a*值及b*值代入下述式(1)而算出之表示彩度的C*值為1以上35以下之範圍；C*=[(a*)2+(b*)2]1/2 (1)。
[4]如上述[1]~[3]中任一項記載之眼鏡用光學薄膜，其中以JIS Z 8781-4：2013中規定的L*a*b*表色系將前述透過光之色調予以數值化時，表示色度的a*值為-15以上5以下之範圍，且b*值為-20以上0以下之範圍。
[5]一種眼鏡用機能性薄膜，其具備如上述[1]~[4]中
任一項記載之光學薄膜與偏光元件。
[6]一種眼鏡用光學層合體，其具備：如上述[1]~[4]中任一項記載之光學薄膜或如上述[5]中記載之機能性薄膜，與將前述光學薄膜或前述機能性薄膜以自其兩面側夾持之位置關係而配置的2個支持體。
[7]如上述[6]記載之眼鏡用光學層合體，其中前述2個支持體的至少一者係藉由選自由三乙醯基纖維素、聚碳酸酯、尼龍樹脂及環烯烴聚合物所成之群組的1種或2種以上之材料所形成。
[8]一種眼鏡，其包含如上述[6]或[7]記載之光學層合體。
[9]如上述[8]記載之眼鏡，其進一步包含透鏡，將前述光學層合體配置於前述透鏡的一面側或兩面側而成。
本發明可提供藉由以白色光作為光源的透過光呈現淡色調，可容易作出呈現使用者心理地感覺療癒之色調的空間之空間的眼鏡用光學薄膜、以及具有此的眼鏡用機能性薄膜、眼鏡用光學層合體及眼鏡。
1‧‧‧光學機能層
3‧‧‧黏著劑或接著劑
5‧‧‧偏光元件
7‧‧‧支持體
10‧‧‧眼鏡用光學薄膜
20‧‧‧眼鏡用機能性薄膜
30‧‧‧眼鏡用光學層合體
圖1係顯示具備本發明之眼鏡用光學薄膜的
眼鏡用光學層合體之一例的示意剖面圖。
實施發明的形態
[眼鏡用光學薄膜]
本發明之眼鏡用光學薄膜(以下僅稱「光學薄膜」)係特徵具有光學機能層，以白色光作為光源的透過光呈現淡色調。如此的光學薄膜當使用於太陽眼鏡或眼鏡等之眼鏡時，可容易作出對於使用者來說呈現心理地感覺療癒之色調的空間。
此處，所謂的白色光，一般而言就是意指可見光線的全部波長之光(色)均等地混合之光，不給予配色之感覺的光，但於本說明書中亦包含帶藍色調的白色光或帶黃色調的白色光，較佳為色溫度4000~7000凱氏溫度(K)之光。作為如此的光，例如可舉出太陽光(自然光)或以電燈泡、螢光燈及LED燈等作為光源之光、CIE規定的標準光C(所謂的C光源)等。又，所謂以白色光作為光源的透過光之色調(透過色)，就是意指以白色光作為光源，穿過光學薄膜的光之色澤。
又，淡色調(pale tone)係意指明度高、彩度低之色調。如此的色調係於PCCS(日本色研配色體系：Practical Color Co-ordinate System)之色調中，作為P(淡色)規定。作為本發明著眼之展現療癒效果的色調，較佳
可舉出PCCS色調之p3、p4、p5、p6、p7、p8、p9、p10、p11、p12、p13、p14、p15、p16、p19、p20、p21、p22、p23、p24，其中更佳為p6、p10、p11、p12、p14、p15、p16、p19、p20、p22、p24。
又，以JIS Z 8781-4：2013中規定的CIE(國際照明委員會)L*a*b*表色系將上述透過光之色調予以數值化時，如以下。再者，測定條件係C光源(CIE規定的標準光C)及2度視野。
表示明度的L*值較佳為70以上100以下之範圍，更佳為75以上98以下之範圍，尤佳為80以上95以下之範圍。
又，由表示色度的a*值及b*值，藉由下述式(1)算出之表示彩度的C*值較佳為1以上35以下之範圍，更佳為5以上30以下之範圍，尤佳為8以上25以下之範圍。
C*=[(a*)2+(b*)2]1/2 (1)。
另外，表示色度的a*值較佳為-15以上5以下之範圍，更佳為-12以上-5以下之範圍。
還有，表示色度的b*值較佳為-20以上0以下之範圍，更佳為-20以上-3以下之範圍。
特別地，表示色度的a*值較佳為-15以上5以下之範圍，且b*值較佳為-20以上0以下之範圍，可實現如此色調的透過光之本發明的光學薄膜，係藉由用於太陽眼鏡或眼鏡等之眼鏡而特別展現高的療癒的效果。
又，本發明之光學薄膜只要至少具有光學機
能層即可，也可僅由1層的光學機能層所構成，亦可層合2層以上的光學機能層所成。層合2層以上的光學機能層時，各層可為相同種類的光學機能層，也可為互相不同種類的光學機能層。各光學機能層之層合數係可按照光學機能層之種類，作為光學機能層之層合物全體，以透過光呈現淡色調之方式適宜決定。又，本發明之光學薄膜係在不損害透過光的色調之範圍內，亦可進一步具有光學機能層以外之層，作為光學機能層以外之層，例如可舉出接著劑層或黏著劑層、硬塗層等。
光學機能層只要是能使透過光之色調(以下僅稱「透過色」)成為淡色調，則沒有特別的限制。作為光學機能層，例如可舉出經由色素、金屬蒸鍍的多層膜、折射率不同的樹脂多層膜、選擇反射可見光區域的光之膽固醇液晶層等，此等係可單獨或複數組合。其中，基於僅改變材料之配合比而能容易地調整透過色且以少的層數能實現目的之透過色，較佳為使用膽固醇液晶層。
膽固醇液晶層係藉由將液晶組成物中的向列液晶化合物之膽固醇配向予以固定而形成。液晶組成物至少包含具有手性的向列液晶化合物、或向列液晶化合物及對掌劑。製作膽固醇液晶層之方法，例如較佳為至少包含調製液晶組成物之步驟、塗佈液晶組成物而形成塗佈膜之步驟、使塗佈膜乾燥之步驟、與使經乾燥的塗佈膜硬化之步驟。
於調製液晶組成物之步驟中，較佳為於向列
液晶化合物中添加必要量的右旋或左旋之對掌劑而反射所欲的波長。取決於對掌劑之種類或量，可任意地設計液晶分子的螺旋方向或反射波長。接著，將此等溶解於溶劑中，按照需要添加光聚合起始劑及助劑。
向列液晶係與所謂的以電場操作之液晶不同，由於將螺旋配向狀態固定化而使用，作為向列液晶化合物，較佳為具有聚合性基的向列液晶單體。具有聚合性基的向列液晶單體係在分子內具有聚合性基，在某溫度範圍或濃度範圍中顯示液晶性之化合物。作為聚合性基，例如可舉出(甲基)丙烯醯基、乙烯基、查耳酮基、桂皮醯基及環氧基等。又，為了顯示液晶性，較佳為在分子內具有介晶基。介晶(mesogen)基係具有誘導液晶相行為的能力之基，例如聯苯基、聯三苯基、(聚)苯甲酸苯酯基、(聚)醚基、亞苄基苯胺基及苊并喹喔啉基等之棒狀或板狀的取代基、或聯三伸苯基、酞菁基及氮雜王冠基等之圓盤狀的取代基。具有棒狀或板狀基的液晶化合物係作為桿狀(calamitic)液晶，為該技術領域中已知。具有如此之聚合性基的向列液晶單體，具體而言可舉出日本特開2003-315556號公報及日本特開2004-29824號公報中記載之聚合性液晶或Paliocolor(註冊商標，以下相同)系列(BASF日本股份有限公司製)及RMM係列(Merck股份有限公司製)等。此等具有聚合性基的向列液晶單體係可單獨使用，或也可使用2種以上的混合物。
作為對掌劑，較佳為可使具有上述聚合性基
的向列液晶單體右旋或左旋螺旋配向，具有與具有聚合性基的向列液晶單體同樣之聚合性基的化合物。作為如此的對掌劑，例如可舉出Paliocolor LC756(BASF日本股份有限公司製)等。對掌劑之添加量亦隨著對掌劑的種類或所反射的波長而不同，但相對於具有聚合性基的向列液晶單體100質量份，較佳可為0.5~30質量份左右，更佳可為1~20質量份左右。
再者，亦可將與具有聚合性基的向列液晶單體能反應之不具有液晶性的聚合性化合物加到液晶組成物中。作為如此的化合物，例如可舉出紫外線硬化型樹脂等。作為紫外線硬化型樹脂，例如可舉出二季戊四醇六(甲基)丙烯酸酯、二季戊四醇五(甲基)丙烯酸酯與1,6-六亞甲基二異氰酸酯之反應生成物、具有異三聚氰酸環的三聚氰酸酯與季戊四醇三(甲基)丙烯酸酯之反應生成物、季戊四醇三(甲基)丙烯酸酯與異佛爾酮二異氰酸酯之反應生成物、二季戊四醇五(甲基)丙烯酸酯、二季戊四醇四(甲基)丙烯酸酯、季戊四醇四(甲基)丙烯酸酯、季戊四醇三(甲基)丙烯酸酯、三羥甲基丙烷三(甲基)丙烯酸酯、二個三羥甲基丙烷四(甲基)丙烯酸酯、三(丙烯醯氧基乙基)異三聚氰酸酯、三(甲基丙烯醯氧基乙基)異三聚氰酸酯、甘油三環氧丙基醚與(甲基)丙烯酸之反應生成物、己內酯改性三(丙烯醯氧基乙基)異三聚氰酸酯、三羥甲基丙烷三環氧丙基醚與(甲基)丙烯酸之反應生成物、三甘油二(甲基)丙烯酸酯、丙二醇二環氧丙基醚與(甲基)丙烯酸之反應生
成物、聚丙二醇二(甲基)丙烯酸酯、三丙二醇二(甲基)丙烯酸酯、聚乙二醇二(甲基)丙烯酸酯、四乙二醇二(甲基)丙烯酸酯、三乙二醇二(甲基)丙烯酸酯、季戊四醇二(甲基)丙烯酸酯、1,6-己二醇二環氧丙基醚與(甲基)丙烯酸之反應生成物、1,6-己二醇二(甲基)丙烯酸酯、甘油二(甲基)丙烯酸酯、乙二醇二環氧丙基醚與(甲基)丙烯酸之反應生成物、二乙二醇二環氧丙基醚與(甲基)丙烯酸之反應生成物、雙(丙烯醯氧基乙基)羥基乙基異三聚氰酸酯、雙(甲基丙烯醯氧基乙基)羥基乙基異三聚氰酸酯、雙酚A二環氧丙基醚與(甲基)丙烯酸之反應生成物、(甲基)丙烯酸四氫糠酯、己內酯改性(甲基)丙烯酸四氫糠酯、(甲基)丙烯酸2-羥基乙酯、(甲基)丙烯酸2-羥基丙酯、聚丙二醇(甲基)丙烯酸酯、聚乙二醇(甲基)丙烯酸酯、(甲基)丙烯酸苯氧基羥基丙酯、丙烯醯基嗎啉、甲氧基聚乙二醇(甲基)丙烯酸酯、甲氧基四乙二醇(甲基)丙烯酸酯、甲氧基三乙二醇(甲基)丙烯酸酯、甲氧基乙二醇(甲基)丙烯酸酯、(甲基)丙烯酸甲氧基乙酯、(甲基)丙烯環氧丙酸酯、甘油(甲基)丙烯酸酯、乙基卡必醇(甲基)丙烯酸酯、(甲基)丙烯酸2-乙氧基乙酯、(甲基)丙烯酸N,N-二甲基胺基乙酯、(甲基)丙烯酸2-氰基乙酯、丁基環氧丙基醚與(甲基)丙烯酸之反應生成物、丁氧基三乙二醇(甲基)丙烯酸酯、及丁二醇單(甲基)丙烯酸酯等，此等係可單獨或複數混合使用。此等之不具有液晶性的紫外線硬化型樹脂，必須在具有聚合性基的向列液晶單體中以不喪失液晶性之程度添加，相對於
具有聚合性基的向列液晶單體100質量份，可為0.1~20質量份，較佳可為1.0~10質量份左右之添加量。
當具有聚合性基的向列液晶單體或其他的聚合性化合物為紫外線硬化型時，為了藉由紫外線硬化，較佳為更將光聚合起始劑加到液晶組成物中。作為光聚合起始劑，例如可舉出2-甲基-1-[4-(甲硫基)苯基]-2-嗎啉代丙烷-1(BASF日本股份有限公司製Irgacure(註冊商標，以下相同)907)、1-羥基環己基苯基酮(BASF日本股份有限公司製Irgacure 184)、4-(2-羥基乙氧基)-苯基(2-羥基-2-丙基)酮(BASF日本股份有限公司製Irgacure 2959)、1-(4-十二基苯基)-2-羥基-2-甲基丙-1-酮(Merck股份有限公司製Darocure(註冊商標，以下相同)953)、1-(4-異丙基苯基)-2-羥基-2-甲基丙-1-酮(Merck股份有限公司製Darocure 1116)、2-羥基-2-甲基-1-苯基丙-1-酮(BASF日本股份有限公司製Irgacure 1173)、二乙氧基苯乙酮等之苯乙酮系化合物、苯偶姻、苯偶姻甲基醚、苯偶姻乙基醚、苯偶姻異丙基醚、苯偶姻異丁基醚、2,2-二甲氧基-2-苯基苯乙酮(BASF日本股份有限公司製Irgacure 651)等之苯偶姻系化合物、苯甲醯基苯甲酸、苯甲醯基苯甲酸甲酯、4-苯基二苯基酮、羥基二苯基酮、4-苯甲醯基-4’-甲基二苯基硫化物、3,3’-二甲基-4-甲氧基二苯基酮(日本化藥股份有限公司製Kayacure MBP)等之二苯基酮系化合物、噻噸酮、2-氯噻噸酮(日本化藥股份有限公司製Kayacure CTX)、2-甲基噻噸酮、2,4-二甲基噻噸酮(日本化藥股份有限公司製
Kayacure RTX)、異丙基噻噸酮、2,4-二氯噻噸酮(日本化藥股份有限公司製Kayacure CTX)、2,4-二乙基噻噸酮(日本化藥股份有限公司製Kayacure DETX)或2,4-二異丙基噻噸酮(日本化藥股份有限公司製Kayacure DITX)等之噻噸酮系化合物。作為光聚合起始劑，較佳為例如可舉出Irgacure TPO、Irgacure TPO-L、Irgacure OXE01、Irgacure OXE02、Irgacure 1300、Irgacure 184、Irgacure 369、Irgacure 379、Irgacure 819、Irgacure 127、Irgacure 907或Irgacure 1173(皆BASF日本股份有限公司製)，特佳為Irgacure TPO、Irgacure TPO-L、Irgacure OXE01、Irgacure OXE02、Irgacure 1300或Irgacure 907。此等之光聚合起始劑係可為單獨1種類，也可以任意的比例混合複數而使用。
使用二苯基酮系化合物或噻噸酮系化合物作為光聚合起始劑時，為了促進光聚合反應，亦可併用助劑。作為如此的助劑，例如可舉出三乙醇胺、甲基二乙醇胺、三異丙醇胺、正丁胺、N-甲基二乙醇胺、甲基丙烯酸二乙基胺基乙酯、米蚩酮、4,4’-二乙基胺基苯酮、4-二甲基胺基苯甲酸乙酯、4-二甲基胺基苯甲酸(正丁氧基)乙酯、或4-二甲基胺基苯甲酸異戊酯等之胺系化合物。
光聚合起始劑及助劑之添加量較佳為不對於液晶組成物的液晶性造成影響之範圍。相對於液晶組成物中之以紫外線硬化的化合物100質量份，光聚合起始劑之添加量較佳可為0.5~10質量份，更佳可為2~8質量份
左右。又，相對於光聚合起始劑之質量，助劑對於液晶組成物的添加量可為0.5倍至2倍量左右。
於液晶組成物中，可進一步添加用於溶解液晶化合物的溶劑。溶劑例如為環戊酮、甲苯及甲基乙基酮等，本業者可適宜決定。相對於液晶組成物的全部固體成分100質量份，溶劑之添加量較佳為300~1000質量份。
接著，於塗佈液晶組成物而形成塗佈膜之步驟中，較佳為將如此所調製的液晶組成物以厚度儘可能成為均勻之方式塗佈於PET薄膜等之塑膠基板上，而形成塗佈膜。
於使液晶組成物之塗佈膜乾燥的步驟中，較佳為一邊加熱液晶組成物的塗佈膜而去除溶劑，一邊於基板上於以成為膽固醇液晶且以所欲螺旋間距配向之溫度條件下放置一定時間。加熱溫度較佳為40~200℃之範圍，加熱時間較佳為1~7分鐘，但加熱之溫度及時間係本業者可適宜調整。此時，於塗佈前預先對於塑膠薄膜基板表面進行摩擦或延伸等之配向處理，膽固醇液晶之配向可更均勻，可減低作為薄膜的霧值。
其次，於使經乾燥的塗佈膜硬化之步驟中，藉由保持著液晶化合物的配向狀態，以高壓水銀燈等照射紫外線，使配向固定化而得到膽固醇液晶層。此處，選擇成為右旋螺旋配向的對掌劑時，所得者為反射右圓偏光的膽固醇液晶層，選擇成為左旋螺旋配向的對掌劑時，所得者為反射左圓偏光的膽固醇液晶層。
膽固醇液晶層之透過色係隨著反射波長區域而不同。反射波長區域係使用該反射波長區域之中心值的中心反射波長來表現。為了透過色成為淡色調，較佳為使中心反射波長在可見光區域中，中心反射波長為400nm~800nm，較佳為410~780nm，更佳為430~700nm之範圍，按照所要求的色調來適宜選擇。例如，中心反射波長為450nm時的透過色係成為黃色，550nm時係成為紅紫色，650nm時係成為水色。
為了於使用膽固醇液晶層來實現淡色調的透過色，可以成為所欲的明度與彩度之方式，調整膽固醇液晶層之透過率與反射波長區域。具體而言，膽固醇液晶層之透過率係可藉由改變該液晶層的厚度而調整。為了實現淡色調的透過色，可使膽固醇液晶層的厚度例如成為0.3~7μm，較佳成為0.5~5μm以下左右。
反射波長區域之調整，當所欲的反射波長區域為寬時，可藉由層合複數層的具有不同的反射波長區域之膽固醇液晶層而進行。例如，藉由層合中心反射波長為450nm的膽固醇液晶層與中心反射波長為650nm的膽固醇液晶層，可表現黃綠色的透過色。因此，於眼鏡用光學薄膜中，膽固醇液晶層可包含單獨1層，也可組合具有不同透過色的複數之膽固醇液晶層而包含。此組合係沒有特別的限制，藉由此組合而得到複雜且多樣的透過色。膽固醇液晶層之層數係按照所欲的透過色而適宜調整，例如為1~5，較佳為1或2。
層合膽固醇液晶層之手段係沒有特別的限制，但較佳為使用黏著劑或接著劑進行層合。作為黏著劑，可舉出丙烯酸系或橡膠系的黏著劑，但較佳為容易調整接著性或保持力等的丙烯酸系黏著劑。又，作為接著劑，可舉出紫外線硬化型樹脂組成物或熱硬化型樹脂組成物。於紫外線硬化型樹脂時，可將混合有複數的具有丙烯醯基或環氧基之單體的組成物在光聚合起始劑之存在下，照射紫外線而使硬化及接著。於熱硬化型樹脂組成物時，可將混合有複數的具有環氧基之單體的組成物在酸觸媒之存在下加熱，而使硬化及接著。或者，可將包含具有胺基、羧基或羥基的複數之單體或聚合物的組成物在具有異氰酸酯基或三聚氰胺的化合物之存在下加熱，而使硬化及接著。
又，作為層合膽固醇液晶層的黏著劑或接著劑，亦可使用溶解有色素的黏著劑或接著劑。藉此，可更得到具有複雜的透過色之眼鏡用光學薄膜。
[眼鏡用機能性薄膜]
眼鏡用機能性薄膜(以下亦僅稱「機能性薄膜」)具備上述光學薄膜與偏光元件。藉由在上述光學薄膜上層合偏光元件，可抑制透過率，更可調整明度。
作為偏光元件，典型上可舉出PVA偏光薄膜，製作方法係沒有特別的限定，可於由聚乙烯醇(PVA)或其衍生物所形成的高分子薄膜上吸附碘或二色性染料等
之色素，使該薄膜單軸地延伸配向而製造。作為色素，從耐熱性之點來看，較佳為二色性染料，特佳為由具有磺酸基的偶氮色素所構成之直接染料。
作為層合上述光學薄膜與偏光元件之方法，並沒有特別的限定，但從得到高的接著力來看，宜經由上述之黏著劑或接著劑等的接著層而貼合。作為接著層，熱熔型接著劑與硬化型接著劑皆可使用。於接著上述光學薄膜與偏光元件之接著劑中，亦可使用溶解有調光染料之接著劑。
[眼鏡用光學層合體]
眼鏡用光學層合體(以下亦僅稱「光學層合體」)具備：上述光學薄膜或上述機能性薄膜，與將上述光學薄膜或前述機能性薄膜以自其兩面側夾持之位置關係而配置的2個支持體。
作為支持體，例如可使用聚碳酸酯(PC)、三乙醯基纖維素(TAC)、尼龍樹脂、環烯烴聚合物等之透明性高的樹脂。2個支持體係可由相同的材料所形成，也可由不同的材料所形成。較佳為2個支持體的至少一者係由選自由三乙醯基纖維素、聚碳酸酯、尼龍樹脂及環烯烴聚合物所成之群組的1種或2種以上之材料所形成。
又，2個支持體各自與上述光學薄膜或上述機能性薄膜，較佳為經由接著劑層貼合。接著劑層係沒有特別的限定，但為了得到高的接著力，眼鏡用機能性薄膜宜
藉由上述之黏著劑或接著劑而形成。作為接著層，熱熔型接著劑與硬化型接著劑皆可使用。
另外，如此的光學層合體在作為眼鏡用時，較佳為成形為所欲的形狀，固定在框架中而使用。
此處，圖1中係作為本發明之光學層合體的構成之一例，顯示示意剖面圖。如圖1中所示，本發明之光學層合體30具備本發明之機能性薄膜20與將機能性薄膜20以自其兩面側夾持之位置關係而配置的2個支持體7，各層係藉由黏著劑層或接著劑層3進行層合。此處，機能性薄膜20具備本發明之光學薄膜10與偏光元件5，各層係經由黏著劑層或接著劑層3而層合。又，光學薄膜10具有光學機能層1，此處尤其2層的光學機能層1係經由黏著劑層或接著劑層3而層合。
圖1中，2層的光學機能層1可為相同種類的光學機能層，也可為互相不同種類的光學機能層。於互相不同種類的光學機能層時，例如可舉出一方係反射右圓偏光之膽固醇液晶層(R)，另一方為反射左圓偏光之膽固醇液晶層(L)的情況等。
[眼鏡]
眼鏡包含上述光學層合體，視需要亦可進一步包含將光學層合體固定的框架或透鏡。
特別地，當眼鏡包含具備機能性薄膜的光學層合體時，光學薄膜較佳以成為比偏光元件更外側之方式固定在
框架。
又，當眼鏡包含透鏡時，較佳為將上述光學層合體配置在透鏡的一面側或兩面側。
於如此的眼鏡中，對於光學層合體之外側表面，較佳為進一步適宜地進行硬塗或防反射、防霧用的表面處理等。
眼鏡係適合太陽眼鏡或護目鏡等之形態，只要是覆蓋視野的一部分或全體者，則沒有特別的限定。室內或野外皆可使用。使用者特別是當感到壓力時等，藉由戴用本發明之眼鏡，可容易作出呈現心理地感覺療癒之色調的空間，可通過視覺而感到療癒，可緩和壓力。
實施例
以下，藉由實施例詳細地例示本發明。實施例中的份係意指質量份。
<塗佈液(液晶組成物)之調製>
以下述表1及2中所示的組成，使聚合性液晶單體、對掌劑及聚合起始劑溶解於溶劑中，分別調製塗佈液(R劑)及(L劑)。
對掌劑：化合物1(日本特開2002-179668號公報中記載的例示化合物2-1)
<光學機能層之製作>
使用以上述表1及2之組成所調製的塗佈液(R1~4及L1~4)，以下述之程序，製作光學機能層(R1~4及L1~4)。以下以使用塗佈液(R1)之情況為例而說明。
首先，使用刮棒，以乾燥後的膜之厚度成為4μm方式，在室溫將塗佈液(R1)塗佈於PET薄膜(東洋紡績股份有限公司製，無底塗層)上。
其次，將在PET薄膜上所塗佈的塗佈液(R1)於150℃加熱5分鐘而去除溶劑，成為膽固醇液晶層。接著，對於此膽固醇液晶層，藉由高壓水銀燈(HARISON TOSHIBA LIGHTING股份有限公司(現TOSHIBA LIGHTING股份有限公司)製)，於120W輸出、5~10秒之條件下進行UV照射，而固定膽固醇液晶層，得到光學機能層(R1)。
再者，對於使用塗佈液(R2~4及L1~4)之情況，亦同樣地以上述程序得到光學機能層(R2~4及L1~4)。
[實施例1]
將經由上述程序所製作的光學機能層(R1)從PET薄膜剝離，得到由光學機能層(R1)所成的實施例1之眼鏡用光學薄膜。
[實施例2]
將經由上述程序所製作的光學機能層(R2)從PET薄膜
剝離，得到由光學機能層(R2)所成的實施例2之眼鏡用光學薄膜。
[實施例3]
將經由上述程序所製作的光學機能層(R3)從PET薄膜剝離，得到由光學機能層(R3)所成的實施例3之眼鏡用光學薄膜。
[實施例4]
將經由上述程序所製作的光學機能層(R4)從PET薄膜剝離，得到由光學機能層(R4)所成的實施例4之眼鏡用光學薄膜。
[實施例5]
將經由上述程序所製作的光學機能層(R1)與光學機能層(L1)，以光學機能層側彼此相對之方式，經由丙烯酸系黏著劑層合。然後，剝離兩面的PET薄膜，得到具有光學機能層(R1)與光學機能層(L1)之實施例5的眼鏡用光學薄膜。
[實施例6]
除了代替光學機能層(R1)及(L1)，使用經由上述程序所製作的光學機能層(R2)及(L2)之點以外，藉由與實施例5同樣之操作，得到具有光學機能層(R2)與光學機能層
(L2)之實施例6的眼鏡用光學薄膜。
[實施例7]
除了代替光學機能層(R1)及(L1)，使用經由上述程序所製作的光學機能層(R2)及(R3)之點以外，藉由與實施例5同樣之操作，得到具有光學機能層(R2)與光學機能層(R3)之實施例7的眼鏡用光學薄膜。
[實施例8]
除了代替光學機能層(R1)及(L1)，使用經由上述程序所製作的光學機能層(R3)及(R4)之點以外，藉由與實施例5同樣之操作，得到具有光學機能層(R3)與光學機能層(R4)之實施例8的眼鏡用光學薄膜。
[實施例9]
除了代替光學機能層(R1)及(L1)，使用經由上述程序所製作的光學機能層(R2)及(R4)之點以外，藉由與實施例5同樣之操作，得到具有光學機能層(R2)與光學機能層(R4)之實施例9的眼鏡用光學薄膜。
[比較例1]
除了代替光學機能層(R1)及(L1)，使用經由上述程序所製作的光學機能層(R3)及(L3)之點以外，藉由與實施例5同樣之操作，得到具有光學機能層(R3)與光學機能層
(L3)之比較例1的眼鏡用光學薄膜。
[比較例2]
除了代替光學機能層(R1)及(L1)，使用經由上述程序所製作的光學機能層(R4)及(L4)之點以外，藉由與實施例5同樣之操作，得到具有光學機能層(R4)與光學機能層(L4)之比較例2的眼鏡用光學薄膜。
[透過光的色調之觀察]
觀察實施例1~9以及比較例1及2所製作的眼鏡用光學薄膜之透過光的色調(透過色)。具體而言，於螢光燈(三菱電機股份有限公司製Rupiklan EX-N色溫度5000K)之下，在與眼睛1~3cm左右的距離配置眼鏡用光學薄膜，通過眼鏡用光學薄膜觀察白底的螢幕，評價其色調。再者，於實施例中，透過光的色調之判斷係對照PCCS的色圖(日本色研PCCS調和色圖201-L)之色樣品而進行。下述表3中記載所觀察之透過光的色調(透過色)。
[L*值、a*值及b*值之測定以及C*值之算出]
使用分光光度計MPC-3100(股份有限公司島津製作所製)，測定實施例1~9以及比較例1及2所製作的眼鏡用光學薄膜之透過光譜。使用所得之光譜，進行色彩計算，求得JIS Z 8781-4：2013所規定的L*a*b*表色系(C光源、2度視野)中之L*值、a*值及b*值之各自。表示彩度
的C*係藉由將表示色度的a*值及b*值代入下述式(1)而算出。下述表3中記載所得之結果。
C*=[(a*)2+(b*)2]1/2 (1)。
[療癒效果之評價]
試驗實施例1~9以及比較例1及2之眼鏡用光學薄膜所給予的療癒效果。具體而言，請20~40歲世代之男女計9名的評審員觀察眼鏡用光學薄膜之透過光的色調(透過色)，實施對於該色調是否感覺療癒效果之問卷調查。眼鏡用光學薄膜的透過色之觀察係藉由於螢光燈(同上)之下，在與眼睛1~3cm左右之距離配置眼鏡用光學薄膜，通過眼鏡用光學薄膜觀察光景10~20秒左右而實施。算出回答「感覺療癒效果」的評審員之比率，下述表3中記載其結果。於本實施例中，將33%以上(9人中3人以上)回答感覺療癒效果的情況當作合格線。
如表3中所示，比較例1及2之眼鏡用光學薄膜由於透過光不呈現淡色調，而無法對於使用者給予療癒效果。相對於其，本發明的實施例1~9之眼鏡用光學薄膜由於皆透過光呈現淡色調，故確認可對於使用者給予療癒效果。
再者，實施例1、2、5及7之眼鏡用光學薄膜，可知由於a*值為-15以上5以下之範圍，且b*值為-20
以上0以下之範圍，而在使用者之70%以上給予高的療癒效果。
藉由本發明之眼鏡用光學薄膜，由於透過光呈現淡色調，而可容易作出呈現使用者心理地感覺療癒之色調的空間。因此，藉由使用如此的本發明之眼鏡用光學薄膜的眼鏡用機能性薄膜、光學層合體及眼鏡，可給予使用者通過視覺的療癒效果，可緩和使用者的壓力。
Claims (9)
- 一種眼鏡用光學薄膜，其特徵為：具有光學機能層，以白色光作為光源的透過光係呈現淡色調。
- 如請求項1之眼鏡用光學薄膜，其中以JIS Z 8781-4：2013中規定的L*a*b*表色系將前述透過光之色調予以數值化時，表示明度的L*值為70以上100以下之範圍。
- 如請求項1或2之眼鏡用光學薄膜，其中以JIS Z 8781-4：2013中規定的L*a*b*表色系將前述透過光之色調予以數值化時，藉由將表示色度的a*值及b*值代入下述式(1)而算出之表示彩度的C*值為1以上35以下之範圍；C*=[(a*)2+(b*)2]1/2 (1)。
- 如請求項1~3中任一項之眼鏡用光學薄膜，其中以JIS Z 8781-4：2013中規定的L*a*b*表色系將前述透過光之色調予以數值化時，表示色度的a*值為-15以上5以下之範圍，且b*值為-20以上0以下之範圍。
- 一種眼鏡用機能性薄膜，其具備如請求項1~4中任一項之光學薄膜與偏光元件。
- 一種眼鏡用光學層合體，其具備：如請求項1~4中任一項之光學薄膜或如請求項5之機能性薄膜，與將前述光學薄膜或前述機能性薄膜以自其兩面側夾持 之位置關係而配置的2個支持體。
- 如請求項6之眼鏡用光學層合體，其中前述2個支持體的至少一者係藉由選自由三乙醯基纖維素、聚碳酸酯、尼龍樹脂及環烯烴聚合物所成之群組的1種或2種以上之材料所形成。
- 一種眼鏡，其包含如請求項6或7之光學層合體。
- 如請求項8之眼鏡，其進一步包含透鏡，將前述光學層合體配置於前述透鏡的一面側或兩面側而成。