CN108252468A - The decoration composite plate of coated with fluoro-carbon paint - Google Patents
The decoration composite plate of coated with fluoro-carbon paint Download PDFInfo
- Publication number
- CN108252468A CN108252468A CN201611231637.7A CN201611231637A CN108252468A CN 108252468 A CN108252468 A CN 108252468A CN 201611231637 A CN201611231637 A CN 201611231637A CN 108252468 A CN108252468 A CN 108252468A
- Authority
- CN
- China
- Prior art keywords
- fluoro
- coated
- layer
- composite plate
- decoration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of decoration composite plates of coated with fluoro-carbon paint, the decorative panel is multilayer composite sheet, surface layer is F-C paint, middle layer is calcium silicate board with microporous, inner layer is insulating layer, insulating layer is sandwiched between one piece of thin plate, it be it is a kind of there is high resistance to compression, do not absorb water, be moisture-proof, is airtight, the environment protecting thermal insulating decoration composite plate of lightweight, the excellent properties such as corrosion-resistant, service life is long, thermal conductivity factor is low.It can solve ultraviolet light curing bleeding agent and fiber reinforced calcium silicate board or strong infiltration, rapid osmotic, the percdation of fiber cement board, deep cure forms a film, and three-dimensional chemical network cross-linking reaction is formed with UV putty, UV seal coats, the adhesion problem of architectural surface and substrate can be solved.The present invention also provides a kind of fire proofings.The glue performance for the fire-resistant decoration plate that method using the present invention is prepared meets requirements of the national standard, and assigns base material flame retardant property；Moreover, do not interfere with the mechanical property of base material, burst size of methanal is also at E1 grades or more, safety and environmental protection；Meanwhile maintain the native texture of timber, good decorating effect.
Description
Technical field
The present invention relates to a kind of dalles, are exactly a kind of building inner and outer wall decorating plates.
Background technology
With the development of society and the continuous improvement of people's life taste, people are to building inner-outer wall color and decorative pattern
Propose higher requirement, it is desirable to which the pattern of skin is more dazzled beautiful colorful.But there are following for decorative architecture beyond the region of objective existence wall
It is difficult：1st, the plank of structure skin decoration is mainly fiber reinforced calcium silicate board or fiber cement board, and is increased in fiber
Gluing between coating interlayer poor adhesion, dope layer and plank easily occurs in the common coating of application on strong calcium silicate board or fiber cement board
The phenomenon that attached force difference, plank boiling water resistance difference and plate bursting；2nd, existing coating process is not suitable for mass production, production cost compared with
Height, energy consumption are 5 times of UV fluorine carbon applications, are unfavorable for energy-saving and emission-reduction.Heat preservation level water-proof decorative is constructed, and needs glass fiber reticular cloth
Or steel wire combination decorative mortar is levelling, then decorative layer of constructing, to achieve the purpose that anti-cracking waterproof and decoration.But cement mortar powder
Brush layer and decorative mortar are because of the cracking and wall of construction factor and cement matrix curing generation and precast concrete binding site
Facing crack caused by sedimentation directly influences heat preservation face layer waterproof and decorative effect.
Invention content
The purpose of the present invention is to provide a kind of heat insulation effect is good, a kind of surface of appearance Integral decoration effect grace applies
Fill the decoration composite plate of F-C paint.
The purpose of the present invention is what is be achieved through the following technical solutions：A kind of decoration composite plate of coated with fluoro-carbon paint,
It is characterized in that：The decorative panel is multilayer composite sheet, and surface layer is F-C paint (1), and middle layer is calcium silicate board with microporous (2), and inner layer is heat preservation
Layer (3), insulating layer (3) are sandwiched between one piece of thin plate (4)；Insulating layer (3) is using polystyrene resin as raw material；The thin plate
(4) it is enhancement layer aluminium sheet, it is by using aluminium alloy panel of the surface through wire drawing process.
The production method of building inner and outer wall decorating plate, including following two big technological processes, each flow includes specific following
Step：
First, priming paint line processing process：
1. fixed thickness sanding and dedusting：Smooth, positive sanding 120 mesh of abrasive band, back side sand is sanded in plank positive and negative with sander
Light 80 mesh of abrasive band in favor of UV seal coat coating uniforms later, prevents UV finishing coats from bottom drain phenomenon occurs when being sanded, from
And ensure finishing coat and do not continue to permeate to plank；Manually or dust removal machine removes plate surface floating dust, in case UV is greasy after influencing
The attachment of son and UV seal coats；
2. roller coating back side seal coat is simultaneously solidified into the first UV closing enamelled coatings：With single roller roller coating UV seal coats, solidification energy is
250-300 mj/cm2 ；
3. roller coating UV bleeding agents are twice：A stirs evenly whole bucket UV bleeding agents, after making its dispersion 5-7 minutes, with sea and now
There is technology to compare, the present invention has the following advantages：
1. insulation and decoration is two-in-one to integrate the high-efficiency insulated performance of mineral wool and the decoration functions of decorative panel, one block of plank
Two kinds of functions；
2. heat preservation, heat-proof quality are good
Heat insulating decorative board of the present invention is stablized using industrialization Automatic Production Line, product quality, the high density of intermediate insulating layer
Mineral wool has fabulous heat-insulating property, thermal conductivity factor λ≤0.035W/mK, the polyphenyl second generally used with the current country
Alkene (thermal conductivity factor λ≤0.042W/mK), rock wool (thermal conductivity factor λ≤0.050W/mK) are compared, and heat insulation effect carries
After high 20% -25% by keel and wall connecting, the air layer between plank and wall can play double-layer heat insulation, be separated with
Beneficial effect
The hollow pipe and accessory of uniform shapes improve acoustic decoration board standardization in itself and aesthetics；Quickly connection and
Connector system improves acoustic decoration board producing efficiency and technological level；Strong adsorption magnet arrangement and self-priming bayonet unit
Application, the installation speed of acoustic decoration board can be significantly improved, project installation expense and time is saved, dragon can be directly installed on
On bone, the application of the levelling base's plank of building interior is saved, the synthesis cost and building for significantly reducing engineering are born a heavy burden, and are expanded and are inhaled
Cavity after soundboard significantly improves the sound absorption function of abatvoix；Flatness regulatory function device and all directions translational adjustment function dress
The application put can significantly improve the flatness and aesthetics on acoustic decoration board surface, improve the decorative effect of sound-absorbing engineering；It is living
The application of dynamic plug-in card, can radical change acoustic decoration board can not it is easy to disassemble, cannot replace and can not be used repeatedly
Drawback improves the utilization ratio of product itself and resource reutilization ability；Product does not have to gypsum, without resin adhesive curing, no
With timber, make product that there is the features such as intensity height, good environmental protection, fire-proof and water-proof, non-deformability is strong.
Thermal effect, heat-insulating property are far above the standard of national energy-saving 65%.
3. decorative effect is more
Appearance is rich and varied, imitates a variety of decorative forms such as stone material, imitative ceramic tile, imitation wood line and aluminum facade, can meet different clients
Individual demand.
4. security performance is high
Heat insulating decorative board, using dry construction, avoids aging obscission caused by traditional chemistry is pasted, in addition from heavy and light
Mineral wool is A grades of incombustible materials, eliminates security risk.
5. construction efficiency is high
Traditional exterior-wall heat insulation Finish System construction, general on-site layering are gradually constructed, and the construction time is long, complex procedures, by day
Gas factor influences big.The complete dry construction of heat insulating decorative board of the present invention is installed not by weather, seasonal effect, and mounting means is simple and direct,
Construction efficiency is 2 times of traditional method or more.
Description of the drawings
Fig. 1 is the schematic cross-sectional view of building inner and outer wall decorating plate of the present invention.
Specific embodiment
The decoration composite plate is multilayer composite sheet, and surface layer is F-C paint 1, and middle layer is calcium silicate board with microporous 2, and inner layer is insulating layer 3,
Insulating layer is sandwiched between one piece of thin plate 4, and insulating layer 3 is using polystyrene resin as raw material, and thin plate is enhancement layer aluminium sheet, it
It is by using aluminium alloy panel of the surface through wire drawing process.
Insulating layer be using polystyrene resin as raw material, via the molding hard plate material of special process continuous extrusion foaming,
Closed bubble structure is independent inside it, be it is a kind of there is high resistance to compression, do not absorb water, be moisture-proof, is airtight, lightweight, it is corrosion-resistant,
The environment protecting thermal insulating material for the excellent properties such as service life is long, thermal conductivity factor is low.
Claims (8)
1. a kind of decoration composite plate of coated with fluoro-carbon paint, it is characterised in that：The decorative panel is multilayer composite sheet, and surface layer is fluorine
Carbon paint (1), middle layer are calcium silicate board with microporous (2), and inner layer is insulating layer (3), and insulating layer (3) is sandwiched between one piece of thin plate (4)；It protects
Warm layer (3) is using polystyrene resin as raw material；The thin plate (4) is enhancement layer aluminium sheet, it is by using surface through wire drawing
The aluminium alloy panel of reason.
2. the decoration composite plate of the coated with fluoro-carbon paint according to claim 1, it is characterised in that：The external coating
The decoration composite plate of F-C paint handles decorative panel of the generation with application F-C paint according to the following steps：
1. dedusting：Processing is dusted to the decorative plate of outer wall；
2. roller coating UV glue simultaneously cures the 2nd UV glue-lines of generation（7）：With roll coater roller coating UV glue, UV semi-solid preparations：Solidification energy
For 50-80 mj/cm2, make UV glue not fully cured；
3. UV transfer film of the patch with bionical effect forms Biomimetic membranes（6）：With UV transfer pasting membranes machine by UV transfer films gluing simultaneously
It overlays on decorative plate of outer wall, UV cures：Ensure disposably through energy 1200-2000mj/cm2；It will with automatic film rolling machine
Basement membrane is rolled, i.e., except PET basement membranes；
4. infrared leveling；
5. roller coating UV glue generates the 3rd UV glue-lines（10）：With roll coater roller coating UV glue, UV curings, solidification energy l00-
200mj/cm2 makes UV glue not fully cured；
6. it applies twice of UV finishing coat and cures the 2nd UV of generation in colored paint layer（11）：A roll coater roller coating first pass UV finishing coats,
UV cures, solidification energy 180-240mj/cm2；B second time UV finishing coat of curtain coater showering, increases the full of finishing coat
Degree, infrared leveling, UV curings, solidification energy 1200-2000 mj/cm2；The decoration of exterior wall with bionical effect is made
Plate.
3. the decoration composite plate of the coated with fluoro-carbon paint according to claim 1, it is characterised in that：The plank（1）
It is fiber reinforced calcium silicate board, proportion：Interior wall 1.2-1.35g/cm3, exterior wall 1.5-1.9 g/cm3 and moisture content 8-10%.
4. the decoration composite plate of the coated with fluoro-carbon paint according to claim 1 or 2, it is characterised in that：The curing
Time is 3-10 seconds.
5. the decoration composite plate of the coated with fluoro-carbon paint according to claim 1 or 2, it is characterised in that：The UV consolidates
The device of change is high-pressure sodium lamp, iron lamp or Iodine gallium light.
6. the decoration composite plate of the coated with fluoro-carbon paint according to claim 1 or 2, it is characterised in that：Infrared ray stream
Flat temperature：50-60 DEG C, time 0.5-1 minute.
7. the decoration composite plate of the coated with fluoro-carbon paint according to claim 7, wherein, the blank assemblies include more
Layer stackup, the Wooden veneer that mutually fits, coating is containing fire-retardant between this method is additionally included in two layers adjacent of Wooden veneer
The liquid mixture of adhesive and curing agent and hot pressing, curing.
8. the decoration composite plate of coated with fluoro-carbon paint according to claim 7, wherein, it is described containing flame-retarding adhesive and
The coating weight of curing agent liquid mixture is 50-500g/m2.