CN109130378A - Imitating crystal agate black jade decoration board - Google Patents

Imitating crystal agate black jade decoration board Download PDF

Info

Publication number
CN109130378A
CN109130378A CN201710509634.3A CN201710509634A CN109130378A CN 109130378 A CN109130378 A CN 109130378A CN 201710509634 A CN201710509634 A CN 201710509634A CN 109130378 A CN109130378 A CN 109130378A
Authority
CN
China
Prior art keywords
decoration board
black jade
glue
layer
solidification
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710509634.3A
Other languages
Chinese (zh)
Inventor
秦春玉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710509634.3A priority Critical patent/CN109130378A/en
Publication of CN109130378A publication Critical patent/CN109130378A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of imitating crystal agate black jade decoration boards, the decorative panel is multilayer composite sheet, surface layer is F-C paint, middle layer is calcium silicate board with microporous, inner layer is insulating layer, insulating layer is sandwiched between one piece of thin plate, it be it is a kind of there is high resistance to compression, do not absorb water, be moisture-proof, is airtight, the environment protecting thermal insulating decoration composite plate for the excellent properties such as lightweight, corrosion-resistant, long service life, thermal coefficient are low.It can solve ultraviolet light and solidify bleeding agent and fiber reinforced calcium silicate board or the strong infiltration of fiber cement board, rapid osmotic, percdation, deep cure film forming, and three-dimensional chemical network cross-linking reaction is formed with UV putty, UV seal coat, the adhesion problem of architectural surface and substrate can be solved.The present invention also provides a kind of fire proofings.The glue performance for the fire-resistant decoration plate being prepared using method of the invention meets requirements of the national standard, and assigns substrate flame retardant property；Moreover, will not influence the mechanical property of substrate, burst size of methanal is also at E1 grades or more, safety and environmental protection；Meanwhile maintaining the native texture of timber, good decorating effect.

Description

Imitating crystal agate black jade decoration board
Technical field
The present invention relates to a kind of dalles, are exactly a kind of building inner and outer wall decorating plate methods.
Background technique
With the continuous improvement of the development of society and people's life taste, people are to building inner-outer wall color and decorative pattern More stringent requirements are proposed, it is desirable to which the pattern of exterior walls of buildings is more dazzled beautiful colorful.But there are following for decorative architecture beyond the region of objective existence wall Difficult: 1, the plate for constructing exterior walls of buildings decoration is mainly fiber reinforced calcium silicate board or fiber cement board, and is increased in fiber Gluing between coating interlayer poor adhesion, dope layer and plate easily occurs in the common coating of coating on strong calcium silicate board or fiber cement board The phenomenon that attached power is poor, plate boiling water resistance is poor and plate bursting；2, existing coating process be not suitable for mass production, production cost compared with Height, energy consumption are 5 times of UV fluorine carbon coating, are unfavorable for energy-saving and emission-reduction.The construction of heat preservation level water-proof decorative, needs glass fiber reticular cloth Or steel wire combination decorative mortar is levelling, then decorative layer of constructing, to achieve the purpose that anti-cracking waterproof and decoration.But cement mortar powder Brush layer and decorative mortar solidify the cracking generated and wall and precast concrete binding site because of construction factor and cement matrix Facing crack caused by sedimentation directly influences heat preservation surface layer waterproof and decorative effect.
Summary of the invention
The purpose of the present invention is to provide a kind of heat insulation effects, and a kind of good, appearance Integral decoration effect grace surface applies
Fill the decoration composite plate of F-C paint.
The purpose of the present invention is what is be achieved through the following technical solutions: a kind of imitating crystal agate black jade decoration board, feature Be: the decorative panel is multilayer composite sheet, and surface layer is F-C paint (1), and middle layer is calcium silicate board with microporous (2), and inner layer is insulating layer (3), Insulating layer (3) is sandwiched between one piece of thin plate (4)；Insulating layer (3) is using polystyrene resin as raw material；The thin plate (4) is Enhancement layer aluminium sheet, it is by using aluminium alloy panel of the surface through wire drawing process.
The production method of building inner and outer wall decorating plate, including following two big process flow, each process include specific following Step:
One, priming paint line processing process:
1. fixed thickness sanding and dedusting: smooth, positive sanding 120 mesh of abrasive band, back side sand is sanded in plate front and back sides with sander In favor of UV seal coat coating uniform later bottom drain phenomenon occurs for light 80 mesh of abrasive band when UV finishing coat being prevented to be sanded, from And guarantees finishing coat and do not continue to permeate to plate；Manually or dust removal machine removes plate surface floating dust, in case UV is greasy after influencing The attachment of son and UV seal coat；
2. roller coating back side seal coat is simultaneously solidified into the first UV closing paint layer: with single roller roller coating UV seal coat, solidification energy is 250-300 mj/cm2 ；
3. roller coating UV bleeding agent is twice: a stirs evenly whole bucket UV bleeding agent, after dispersing it 5-7 minutes, with sea and now There is technology to compare, the invention has the following advantages that
1. insulation and decoration is two-in-one to integrate the high-efficiency insulated performance of mineral wool and the decoration functions of decorative panel, one block of plate Two kinds of functions；
2. heat preservation, heat-proof quality are good
Heat insulating decorative board of the present invention is using industrialization Automatic Production Line, stable product quality, the high density of intermediate insulating layer Mineral wool has fabulous thermal insulation property, thermal coefficient λ≤0.035W/mK, the polyphenyl second generallyd use with the current country Alkene (thermal coefficient λ≤0.042W/mK), rock wool (thermal coefficient λ≤0.050W/mK) are compared, and heat insulation effect mentions After high 20% -25% by keel and wall connecting, the air layer between plate and wall can play double-layer heat insulation, be separated with Beneficial effect
The hollow pipe and accessory of uniform shapes improve the standardization and aesthetics of acoustic decoration board itself；Quickly connection and Connector system improves acoustic decoration board producing efficiency and technological level；Strong adsorption magnet arrangement and self-priming bayonet unit Application, can significantly improve the installation speed of acoustic decoration board, save project installation expense and time, dragon can be directly installed on On bone, the application of the levelling base's plate of building interior is saved, the overall cost and building weight bearing of engineering is significantly reduced, expands and inhale Cavity after soundboard significantly improves the sound absorption function of abatvoix；Flatness regulatory function device and all directions translational adjustment function dress The application set can significantly improve the flatness and aesthetics on acoustic decoration board surface, improve the decorative effect of sound-absorbing engineering；It is living The application of dynamic plug-in card, can radical change acoustic decoration board can not it is easy to disassemble, cannot replace and can not be used repeatedly Drawback improves the utilization efficiency and resource reutilization ability of product itself；Product does not have to gypsum, does not have to resin adhesive curing, no With timber, make product that there is the features such as intensity height, good environmental protection, fire-proof and water-proof, non-deformability is strong.
Thermal effect, thermal insulation property are much higher than the standard of national energy-saving 65%.
3. decorative effect is more
Appearance is rich and varied, and a variety of decorative forms such as imitation stone, imitative ceramic tile, imitation wood line and aluminum facade are able to satisfy different clients Individual demand.
4. security performance is high
Heat insulating decorative board avoids aging obscission caused by traditional chemistry is pasted, in addition using dry construction from heavy and light Mineral wool is A grades of incombustible materials, eliminates security risk.
5. construction efficiency is high
Traditional exterior-wall heat insulation Finish System construction, general on-site layering are gradually constructed, and the construction time is long, complex procedures, by day Gas factor influences big.The complete dry construction of heat insulating decorative board of the present invention is installed not by weather, seasonal effect, and mounting means is simple and direct, Construction efficiency is 2 times of traditional method or more.
Specific embodiment
The decoration composite plate is multilayer composite sheet, and surface layer is F-C paint 1, and middle layer is calcium silicate board with microporous 2, and inner layer is insulating layer 3, Insulating layer is sandwiched between one piece of thin plate 4, and insulating layer 3 is using polystyrene resin as raw material, and thin plate is enhancement layer aluminium sheet, it It is by using aluminium alloy panel of the surface through wire drawing process.
Insulating layer be using polystyrene resin as raw material, via the molding hard plate material of special process continuous extrusion foaming, Closed bubble structure is independent inside it, be it is a kind of there is high resistance to compression, do not absorb water, be moisture-proof, is airtight, lightweight, it is corrosion-resistant, The environment protecting thermal insulating material for the excellent properties such as long service life, thermal coefficient be low.

Claims (8)

1. a kind of imitating crystal agate black jade decoration board, it is characterised in that: the decorative panel is multilayer composite sheet, and surface layer is F-C paint (1), middle layer is calcium silicate board with microporous (2), and inner layer is insulating layer (3), and insulating layer (3) is sandwiched between one piece of thin plate (4)；Insulating layer It (3) is using polystyrene resin as raw material；The thin plate (4) is enhancement layer aluminium sheet, it is by using surface through wire drawing process Aluminium alloy panel.
2. the imitating crystal agate black jade decoration board according to claim 1, it is characterised in that: the imitating crystal agate black jade Decorative panel handles the decorative panel for generating and having coating F-C paint according to the following steps:
1. dedusting: being dusted processing to the decorative plate of outer wall；
2. roller coating UV glue simultaneously solidifies the 2nd UV glue-line (7) of generation: with roll coater roller coating UV glue, UV semi-solid preparation: solidification energy For 50-80 mj/cm2, keep UV glue not fully cured；
3. paste have bionical effect UV transfer film constitute Biomimetic membranes (6): with UV transfer pasting membrane machine by UV transfer film gluing simultaneously It overlays on decorative plate of outer wall, UV solidification: ensures disposably to pass through energy 1200-2000mj/cm2；It will with automatic film rolling machine Basement membrane is rolled, that is, removes PET basement membrane；
4. infrared leveling；
5. roller coating UV glue generates the 3rd UV glue-line (10): using roll coater roller coating UV glue, UV solidification, solidification energy l00- 200mj/cm2 keeps UV glue not fully cured；
6. applying twice of UV finishing coat and solidifying and generate the 2nd UV in colored paint layer (11): a roll coater roller coating first pass UV finishing coat, UV solidification, solidification energy 180-240mj/cm2；B second time UV finishing coat of curtain coater showering, increases the full of finishing coat Degree, infrared leveling, UV solidification, solidification energy 1200-2000 mj/cm2；The decoration of exterior wall with bionical effect is made Plate.
3. the imitating crystal agate black jade decoration board according to claim 1, it is characterised in that: the plate (1) is fine Dimension enhancing calcium silicate board, specific gravity: interior wall 1.2-1.35g/cm3, exterior wall 1.5-1.9 g/cm3 and moisture content 8-10%.
4. according to claim 1 or imitating crystal agate black jade decoration board described in 2, it is characterised in that: the curing time is equal It is 3-10 seconds.
5. according to claim 1 or imitating crystal agate black jade decoration board described in 2, it is characterised in that: the UV is cured Device is high-pressure sodium lamp, iron lamp or Iodine gallium light.
6. according to claim 1 or imitating crystal agate black jade decoration board described in 2, it is characterised in that: the temperature of infrared leveling Degree: 50-60 DEG C, time 0.5-1 minute.
7. the imitating crystal agate black jade decoration board according to claim 7, wherein the blank assemblies include multilayer laminated , the Wooden veneer mutually to fit, this method further include between two layers adjacent of Wooden veneer coating contain flame-retarding adhesive Liquid mixture and hot pressing, solidification with curing agent.
8. imitating crystal agate black jade decoration board according to claim 7, wherein described to contain flame-retarding adhesive and curing agent The coating weight of liquid mixture is 50-500g/m2.
CN201710509634.3A 2017-06-28 2017-06-28 Imitating crystal agate black jade decoration board Pending CN109130378A (en)