CN108221033A - 一种遮挡尖端效应的电镀夹具 - Google Patents

一种遮挡尖端效应的电镀夹具 Download PDF

Info

Publication number
CN108221033A
CN108221033A CN201611140229.0A CN201611140229A CN108221033A CN 108221033 A CN108221033 A CN 108221033A CN 201611140229 A CN201611140229 A CN 201611140229A CN 108221033 A CN108221033 A CN 108221033A
Authority
CN
China
Prior art keywords
conductive material
outer ring
electrically non
inner ring
insulation inner
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201611140229.0A
Other languages
English (en)
Other versions
CN108221033B (zh
Inventor
刘洪�
郭群
徐春红
肖文英
陈文超
王红秀
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Aviation Industry Standard Parts Manufacturing Co Ltd
Original Assignee
China Aviation Industry Standard Parts Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China Aviation Industry Standard Parts Manufacturing Co Ltd filed Critical China Aviation Industry Standard Parts Manufacturing Co Ltd
Priority to CN201611140229.0A priority Critical patent/CN108221033B/zh
Publication of CN108221033A publication Critical patent/CN108221033A/zh
Application granted granted Critical
Publication of CN108221033B publication Critical patent/CN108221033B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明是一种适用于紧固件局部电镀时，避免尖端效应产生的电镀夹具。该电镀夹具主要由不导电材料制外圈、塑料制绝缘内圈、及铜制挂钩组成。其中铜制挂钩整个结构表面用绝缘漆涂刷，进行绝缘；不导电材料制外圈的外圆直径大于零件电镀部位的直径0.5～MM；不导电材料制外圈的长度小于等于塑料绝缘内圈的长度。使用过程中，将塑料绝缘内圈套在零件不需要电镀的部位外部，再将不导电材料制外圈套在塑料绝缘内圈外部，最后将零件两端装夹于铜制挂钩处，这样即方便操作，又通过不导电材料制外圈遮挡住零件的尖端部位，使得电镀过程中，不再产生尖端效应，尖端也不会再抢电流，避免现有技术的缺点。

Description

一种遮挡尖端效应的电镀夹具
技术领域：
本发明涉及一种夹具，主要是一种适用于紧固件局部电镀时，避免尖端效应产生的电镀夹具。
背景技术：
紧固件的生产特点是零件小、数量大。特别还有一些产品需要局部电镀。长期以来，对于只要求杆部电镀的产品，我们采用绝缘胶带和热塑管的方法对头部进行绝缘，以防止松动脱落。而非电镀部位则采用特制的钢制内圈管套进行绝缘。由于管套与零件杆部接触处形成了一个尖端面，从而产生了尖端负效应。在电镀过程中，由于尖端效应的作用，电镀时间只有两三个小时时，尖端面就已经迅速生长铬层，并形成树枝状生长在端面周围，而且随着电镀时间的延长，树枝越长越大，疯狂抢夺电流，致使本来只有17％的镀铬电流效率降到更低，不仅使电镀时间延长，而且导致零件本身得不到均匀的镀层。如果将零件提出槽液面，敲掉树枝状铬层，放回去继续电镀，零件表面本来完好的铬层又会因此起泡或生长麻点。通常在电镀这类产品时，都是按照工艺规定时间的最大范围24小时进行电镀，但由于尖端效应抢电流，最终还是得不到满意的镀层和厚度，合格率也仅为50％左右。
发明内容：
本发明的目的是提供一种简单、使用方便、高效的电镀夹具，在电镀过程中可以遮挡尖端效应的电镀夹具，以克服现有技术的不足。
本发明采取的技术方案是：提供一种局部电镀导电夹具，该电镀夹具主要由不导电材料制外圈(3)、塑料制绝缘内圈(2)、及铜制挂钩(1)组成。其中铜制挂钩(1)整个结构表面用绝缘漆涂刷，进行绝缘；不导电材料制外圈(3)的外圆直径大于零件电镀部位的直径0.5～2MM；不导电材料制外圈(3)的长度小于等于塑料绝缘内圈(2)的长度。在使用过程中，先将塑料绝缘内圈(2)套在零件不需要电镀的部位外部，再将不导电材料制外圈(3)套在塑料绝缘内圈(2)外部，最后将零件两端装夹于铜制挂钩(1)处。这样即方便操作，又通过使用不导电材料制外圈(3)遮挡住零件(4)的尖端部位，使得电镀过程中，不再产生尖端效应，尖端也不会再抢电流，从而避免了现有技术的缺点。
本发明与现有技术比较有下列优点：
(1)节约电镀时间，提高了生产效率，每槽所用的时间比原来缩短了2/3；
(2)避免了树枝状镀层的生长，零件受镀均匀，产品合格率由原来的50％提高到了90％。
附图说明：
图1为本发明装夹零件示意图；
图2为零件示意图；
图3为不导电材料制外圈3与塑料绝缘内圈2装配示意图；
图4为不导电材料制外圈3、塑料绝缘内圈2与零件装配示意图；其中铜制挂钩1外表面用绝缘漆进行绝缘。
具体实施方式：
实施例1:
对规格为M5×30的螺栓进行局部电镀，使用本发明对其进行电镀。其中螺栓需要电镀的杆部直径为12MM，不需电镀的的杆部直径为6.5MM，长度为15MM。
使用的电镀夹具由PP材料制外圈(3)、热塑管制绝缘内圈(2)、铜制挂钩(1)组成。其中铜制挂钩(1)整个结构表面用绝缘漆涂刷，进行绝缘；热塑管制绝缘内圈的(2)内圆直径为6MM,PP材料制外圈(3)的内圆直径为10MM，他们的壁厚均为2MM，长度为16～18MM。在使用过程中，先将塑料绝缘内圈(2)套在零件非电镀杆部处，再将不导电材料制外圈(3)套在塑料绝缘内圈(2)外，最后将零件两端装夹于铜制挂钩(1)处,每个挂钩上装夹2个零件后进行电镀。
实施例2:
对规格为M12×60的螺栓进行局部电镀，其中螺栓需要电镀的杆部直径为23MM，不需电镀的的杆部直径为17.5MM，长度为15MM。
使用的电镀夹具由PVC材料制外圈(3)、热塑管制绝缘内圈(2)、铜制挂钩(1)组成。其中铜制挂钩(1)整个结构表面用绝缘漆涂刷，进行绝缘；热塑管制绝缘内圈(2)的内圆直径为18MM,PP材料制外圈(3)的内圆直径为22MM，他们的壁厚均为2MM，长度为16～18MM。在使用过程中，先将塑料绝缘内圈(2)套在零件非电镀杆部处，再将不导电材料制外圈(3)套在塑料绝缘内圈(2)外，最后将零件两端装夹于铜制挂钩(1)处,每个挂钩上装夹2个零件后进行电镀。

Claims (5)

1.一种遮挡尖端效应的电镀夹具，由不导电材料制外圈(3)、塑料制绝缘内圈(2)、及铜制挂钩(1)组成；其特征在于：塑料制绝缘内圈(2)套在零件不需要电镀的部位外部，再将不导电材料制外圈(3)套在塑料绝缘内圈(2)外部，最后将零件两端装夹于铜制挂钩(1)处。
2.根据权利要求1所述的一种遮挡尖端效应的电镀夹具，其特征在于：所述不导电材料制外圈(3)的外圆直径大于零件电镀部位的直径0.5～2MM。
3.根据权利要求1所述的一种遮挡尖端效应的电镀夹具，其特征在于：所述不导电材料制外圈(3)的长度小于等于塑料绝缘内圈(2)的长度。
4.根据权利要求1所述的一种遮挡尖端效应的电镀夹具，其特征在于：所述不导电材料制外圈(3)采用PVC材料或PP材料制作。
5.根据权利要求1所述的一种遮挡尖端效应的电镀夹具，其特征在于：所述塑料制绝缘内圈(2)采用热塑管制作。
CN201611140229.0A 2016-12-12 2016-12-12 一种遮挡尖端效应的电镀夹具 Active CN108221033B (zh)