CN108070057B - 一种聚乙烯亚胺丙烯腈缩合物及改性水性粘合剂 - Google Patents
一种聚乙烯亚胺丙烯腈缩合物及改性水性粘合剂 Download PDFInfo
- Publication number
- CN108070057B CN108070057B CN201810038498.9A CN201810038498A CN108070057B CN 108070057 B CN108070057 B CN 108070057B CN 201810038498 A CN201810038498 A CN 201810038498A CN 108070057 B CN108070057 B CN 108070057B
- Authority
- CN
- China
- Prior art keywords
- polyethyleneimine
- acrylonitrile
- condensation product
- aqueous binder
- modified water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种聚乙烯亚胺丙烯腈缩合物及改性水性粘合剂，是将聚乙烯亚胺（PEI）与丙烯腈进行缩合反应得到一种聚乙烯亚胺丙烯腈缩合物。所述聚乙烯亚胺丙烯腈缩合物能以任意比例加入到含羧基（‑COOH）水性粘合剂体系中，从而极大地提高了改性水性粘合剂的粘接性能。
Description
技术领域
本发明涉及一种水性粘合剂，更特别地说，是指一种可稳定地应用于含羧基水性粘合剂的增粘树脂及改性的水性粘合剂。
背景技术
为了提高水性粘合剂对低表面张力物质的粘接能力，通常需要加入一种或几种增粘树脂，其中聚乙烯亚胺（PEI）是一种效果较好的增粘树脂，但由于聚乙烯亚胺（PEI）对羧基非常敏感，极大地限制了其在水性粘合剂领域的使用范围。
粘合剂是人们日常生活和工业生产中广泛使用的一类产品，但溶剂型粘合剂无论是生产过程还是使用过程都会有大量的有机挥发物排放到大气中，对环境造成破坏，使用水性粘合剂是最好的选择。
为了提高水性粘合剂对低表面张力物质如聚乙烯（PE）、聚丙烯（PP）、聚酯（PET）、尼龙（NY）等的粘接力，通常需要加入增粘树脂，聚乙烯亚胺（PEI）就是一种效果很好的增粘树脂，但由于聚乙烯亚胺（PEI）很容易与水性粘合剂中的羧基（-COOH）反应形成凝胶，破坏了水性粘合剂的使用性能。
发明内容
本发明的目的是提供一种聚乙烯亚胺丙烯腈缩合物，其既保持了聚乙烯亚胺（PEI）极佳的增粘性能，又能以任意比例加入到含羧基（-COOH）基团的水性粘合剂体系中。
本发明的技术方案是：将聚乙烯亚胺（PEI）与丙烯腈进行缩合反应得到一种聚乙烯亚胺丙烯腈缩合物。所述聚乙烯亚胺丙烯腈缩合物能以任意比例加入到水性粘合剂（特别是含羧基（-COOH））体系中，极大地提高粘接性能。
所述聚乙烯亚胺丙烯腈缩合物的化学结构式为：
本发明聚乙烯亚胺丙烯腈缩合物及改性水性粘合剂的优点在于：
①聚乙烯亚胺丙烯腈缩合物能以任意比例加入到水性粘合剂（特别是含羧基）体系，不会形成凝胶。
②改性水性粘合剂极大地提高粘接性能，特别是对低表面张力物质如聚乙烯（PE）、聚丙烯（PP）、聚酯（PET）、尼龙（NY）等的粘接力提升更加明显。
③改性水性粘合剂不含挥发性有机溶剂，更加绿色环保。
具体实施方式
下面将结合实施例对本发明做进一步的详细说明。
本发明的技术方案是：将聚乙烯亚胺（PEI）与丙烯腈进行缩合反应得到一种聚乙烯亚胺丙烯腈缩合物。所述聚乙烯亚胺丙烯腈缩合物能以任意比例加入到水性粘合剂（特别是含羧基（-COOH））体系中，极大地提高粘接性能。
所述聚乙烯亚胺丙烯腈缩合物的化学结构式为：
实施例 1
将1000克聚乙烯亚胺（PEI）投入反应釜中，升温至50℃，通氮气保护，开始滴加丙烯腈，控制反应温度在100℃以下，把177克丙烯腈滴加完后，升温至120℃，保温反应1.5小时，然后降温至50℃以下关氮气，出料，得到聚乙烯亚胺丙烯腈缩合物。
向反应釜中滴加丙烯腈使用恒压滴液漏斗，滴加时间为3～4小时。
将实施例1制得的聚乙烯亚胺丙烯腈缩合物加入到水性丙烯酸酯中经混合均匀，得到改性粘合剂。
将实施例1制得的改性粘合剂按照GB 8808-88的规定进行对比测定剥离力。按照QB/T 2358-98的规定方法进行对比测定热合强度。
表1
实施例2
将1000克聚乙烯亚胺（PEI）投入反应釜中，升温至50℃，通氮气保护，开始滴加丙烯腈，控制反应温度在100℃以下，把353克丙烯腈滴加完后，升温至120℃，保温反应1.5小时，然后降温至50℃以下关氮气，出料，得到聚乙烯亚胺丙烯腈缩合物。
向反应釜中滴加丙烯腈使用恒压滴液漏斗，滴加时间为3～4小时。
将实施例2制得的聚乙烯亚胺丙烯腈缩合物加入到水性丙烯酸酯中混合均匀，得到改性粘合剂。
将实施例2制得的改性粘合剂按照GB 8808-88的规定进行对比测定剥离力。按照QB/T 2358-98的规定方法进行对比测定热合强度。
表2
实施例3
将1000克聚乙烯亚胺（PEI）投入反应釜中，升温至50℃，通氮气保护，开始滴加丙烯腈，控制反应温度在100℃以下，把707克丙烯腈滴加完后，升温至120℃，保温反应1.5小时，然后降温至50℃以下关氮气，出料，得到聚乙烯亚胺丙烯腈缩合物。
向反应釜中滴加丙烯腈使用恒压滴液漏斗，滴加时间为3～4小时。
将实施例3制得的聚乙烯亚胺丙烯腈缩合物加入到水性丙烯酸酯中混合均匀，得到改性粘合剂。
将实施例3制得的改性粘合剂按照GB 8808-88的规定进行对比测定剥离力。按照QB/T 2358-98的规定方法进行对比测定热合强度。
表3
Claims (4)
1.一种聚乙烯亚胺丙烯腈缩合物的制备方法，其特征在于：是将聚乙烯亚胺与丙烯腈进行缩合反应得到一种聚乙烯亚胺丙烯腈缩合物；
所述聚乙烯亚胺丙烯腈缩合物的化学结构式为：
数，为小于等于17且大于等于1的自然数。
2.根据权利要求1所述的聚乙烯亚胺丙烯腈缩合物的制备方法，其特征在于：通过恒压滴液漏斗向装有聚乙烯亚胺反应釜中滴加丙烯腈，控制反应温度在100℃以下，滴加时间为3～4小时。
3.应用权利要求1所述的聚乙烯亚胺丙烯腈缩合物制得水性粘合剂的方法，其特征在于：是将聚乙烯亚胺丙烯腈缩合物以任意比例加入到水性粘合剂中，制得改性水性粘合剂。
4.根据权利要求3所述的制得水性粘合剂的方法，其特征在于：水性粘合剂是含羧基的水性粘合剂。