CN107935392A - A kind of celeste glaze with anti-pollution function - Google Patents
A kind of celeste glaze with anti-pollution function Download PDFInfo
- Publication number
- CN107935392A CN107935392A CN201711242815.0A CN201711242815A CN107935392A CN 107935392 A CN107935392 A CN 107935392A CN 201711242815 A CN201711242815 A CN 201711242815A CN 107935392 A CN107935392 A CN 107935392A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- pollution function
- raw material
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of celeste glaze with anti-pollution function, is made of potassium albite, melilite, boric acid powder, quartz, cupric oxide, alkaline earth, green glass, tin frit, cupric silicate barium.The present invention a kind of water resistance, the weatherability of the celeste glaze with anti-pollution function is good, and the cupric oxide and cupric silicate barium of addition have the antibacterial and effect of decomposing volatile organic matters, and anti-pollution function is strong;The celeste glaze of the present invention is applicable to outside construction sanitary ceramic, can be applied in the product surface such as concrete slab, plastic plate, plasterboard, paint, plastics, textile, applied widely, has good promotional value;The celeste glaze preparation process of the present invention is simple, and performance is stablized, and manufacturing cost is low.
Description
Technical field
The present invention relates to ceramic fabrication technique field, more particularly to a kind of celeste glaze with anti-pollution function.
Background technology
Glaze is a kind of silicate, and the glaze applied on ware is generally using quartz, feldspar, clay as raw material, ground plus water
After modulation, coated on billet surface, melted through the roasting of certain temperature, when the temperature drops, forming the nature of glass of ceramic surface
Thin layer.It makes ware increase mechanical strength, heat endurance, dielectric strength and the erosion for preventing liquid, gas.Glaze also has increase
Porcelain is beautiful and wipes easy to wash, the effect such as is not sticky with by dust.Substantially can be with according to the classification of product and purposes in ceramic industry
It is divided into following a few classes:Lead glaze and leadless glaze;Raw glaze and fritted glaze, ceramic tile, tableware, sanitary ceramics and electroceramics glaze.According to applying
The method of glaze can be divided into immersion oil, glaze spraying, pour glaze;High-temperature glaze, low temperature glaze;Highly expanded glaze, Low Thermal Expantion Glaze;It is coloured glaze, colourless
Glaze;Bright glaze, mat glaze.With the improvement of people's living standards, the species of ceramic glaze is more and more rich and varied, it is ceramic at present
Usually there are more gap, anti-pollution function be not strong for the glaze layer surface that glaze is formed.
The content of the invention
It is an object of the invention to:For above-mentioned problem, there is provided a kind of anti-pollution function is strong, preparation process is simple,
Manufacture the low celeste glaze with anti-pollution function of cost.
The present invention is achieved by the following technical solutions:
A kind of celeste glaze with anti-pollution function, is made of the component of following parts by weight:73~76 parts of potassium albite, melilite
10~15 parts, 20~25 parts of boric acid powder, quartz 20~25 parts, 15~20 parts of cupric oxide, 15~20 parts of alkaline earth, green glass 15~
20 parts, 3~4 parts of tin frit, 1~3 part of cupric silicate barium;Preparation process is as follows:A, raw material is measured according to parts by weight, by above-mentioned former material
Material adds pulverizer, is crushed to the mesh of 300 mesh~320, obtains hybrid particles;B, hybrid particles are stirred evenly, 1350 DEG C~
1500 DEG C of fusings, and keep the temperature 2h~4h;C, it is put into quench in the water that temperature is 15 DEG C~18 DEG C and frit is made, then vibration of ultrasonic wave
5min~8min, up to the celeste glaze with anti-pollution function.
Preferably, a kind of celeste glaze with anti-pollution function, is made of the component of following parts by weight:Potassium albite 73
Part, 10 parts of melilite, 20 parts of boric acid powder, quartz 20 parts, 15 parts of cupric oxide, 15 parts of alkaline earth, 15 parts of green glass, 3 parts of tin frit,
1 part of cupric silicate barium;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, are crushed to
300 mesh, obtain hybrid particles;B, hybrid particles are stirred evenly, in 1350 DEG C of fusings, and keeps the temperature 2h;C, temperature is put into as 15
DEG C water in quench frit be made, then vibration of ultrasonic wave 5min, up to the celeste glaze with anti-pollution function.
Preferably, a kind of celeste glaze with anti-pollution function, is made of the component of following parts by weight:Potassium albite 76
Part, 15 parts of melilite, 25 parts of boric acid powder, quartz 25 parts, 20 parts of cupric oxide, 20 parts of alkaline earth, 20 parts of green glass, 4 parts of tin frit,
3 parts of cupric silicate barium;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, are crushed to
320 mesh, obtain hybrid particles;B, hybrid particles are stirred evenly, in 1500 DEG C of fusings, and keeps the temperature 4h;C, temperature is put into as 18
DEG C water in quench frit be made, then vibration of ultrasonic wave 8min, up to the celeste glaze with anti-pollution function.
Preferably, a kind of celeste glaze with anti-pollution function, is made of the component of following parts by weight:Potassium albite 74
Part, 12 parts of melilite, 22 parts of boric acid powder, 23 parts of quartz, 18 parts of cupric oxide, 18 parts of alkaline earth, 17 parts of green glass, tin frit 3.5
Part, 2 parts of cupric silicate barium;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, are crushed
To 310 mesh, hybrid particles are obtained;B, hybrid particles are stirred evenly, in 1450 DEG C of fusings, and keeps the temperature 3h;C, being put into temperature is
Quench in 16 DEG C of water and frit is made, then vibration of ultrasonic wave 6min, up to the celeste glaze with anti-pollution function.
The raw material being related in this application can be obtained in buying on the market.
The beneficial effects of the invention are as follows:
1. the present invention a kind of water resistance, the weatherability of the celeste glaze with anti-pollution function is good, the cupric oxide and cupric silicate of addition
Barium has the antibacterial and effect of decomposing volatile organic matters, and anti-pollution function is strong.
2. a kind of celeste glaze with anti-pollution function of the present invention is applicable to outside construction sanitary ceramic, can be applied in mixed
The product surface such as concrete board, plastic plate, plasterboard, paint, plastics, textile, it is applied widely, there is good promotion price
Value.
3. a kind of celeste glaze preparation process with anti-pollution function of the present invention is simple, performance is stablized, and prepares and be somebody's turn to do with anti-
The cost of the celeste glaze of dirty function is low.
Embodiment
This specification(Including any accessory claim, summary)Disclosed in any feature, unless specifically stated,
Replaced by other equivalent or with similar purpose alternative features.I.e., unless specifically stated, each feature is a series of
An example in equivalent or similar characteristics.
Embodiment 1:
A kind of celeste glaze with anti-pollution function, is made of the component of following parts by weight:73 parts of potassium albite, melilite 10
Part, 20 parts of boric acid powder, 20 parts of quartz, 15 parts of cupric oxide, 15 parts of alkaline earth, 15 parts of green glass, 3 parts of tin frit, 1 part of cupric silicate barium;
Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, 300 mesh is crushed to, is mixed
Particle;B, hybrid particles are stirred evenly, in 1350 DEG C of fusings, and keeps the temperature 2h;C, it is put into quench in the water that temperature is 15 DEG C and is made
Frit, then vibration of ultrasonic wave 5min, up to the celeste glaze with anti-pollution function.
Embodiment 2:
A kind of celeste glaze with anti-pollution function, is made of the component of following parts by weight:76 parts of potassium albite, melilite 15
Part, 25 parts of boric acid powder, 25 parts of quartz, 20 parts of cupric oxide, 20 parts of alkaline earth, 20 parts of green glass, 4 parts of tin frit, 3 parts of cupric silicate barium;
Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, 320 mesh is crushed to, is mixed
Particle;B, hybrid particles are stirred evenly, in 1500 DEG C of fusings, and keeps the temperature 4h;C, it is put into quench in the water that temperature is 18 DEG C and is made
Frit, then vibration of ultrasonic wave 8min, up to the celeste glaze with anti-pollution function.
Embodiment 3:
A kind of celeste glaze with anti-pollution function, is made of the component of following parts by weight:74 parts of potassium albite, melilite 12
Part, 22 parts of boric acid powder, 23 parts of quartz, 18 parts of cupric oxide, 18 parts of alkaline earth, 17 parts of green glass, 3.5 parts of tin frit, cupric silicate barium 2
Part;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, 310 mesh is crushed to, obtains
Hybrid particles;B, hybrid particles are stirred evenly, in 1450 DEG C of fusings, and keeps the temperature 3h;C, it is put into the water that temperature is 16 DEG C and quenches
Frit, then vibration of ultrasonic wave 6min is made, up to the celeste glaze with anti-pollution function.
Although above the present invention is described in detail with a general description of the specific embodiments,
On the basis of the present invention, it can be made some modifications or improvements, this will be apparent to those skilled in the art.Cause
This, these modifications or improvements, belong to the scope of protection of present invention without departing from theon the basis of the spirit of the present invention.
Claims (4)
- A kind of 1. celeste glaze with anti-pollution function, it is characterised in that:It is made of the component of following parts by weight:Potassium albite 73 ~76 parts, 10~15 parts of melilite, 20~25 parts of boric acid powder, quartz 20~25 parts, 15~20 parts of cupric oxide, alkaline earth 15~20 Part, 15~20 parts of green glass, 3~4 parts of tin frit, 1~3 part of cupric silicate barium;Preparation process is as follows:A, measured according to parts by weight Above-mentioned raw material are added pulverizer, are crushed to the mesh of 300 mesh~320, obtain hybrid particles by raw material;B, hybrid particles are stirred Uniformly, in 1350 DEG C~1500 DEG C fusings, and 2h~4h is kept the temperature;C, be put into temperature be quench in 15 DEG C~18 DEG C of water be made it is molten Block, then vibration of ultrasonic wave 5min~8min, up to the celeste glaze with anti-pollution function.
- A kind of 2. celeste glaze with anti-pollution function according to claim 1, it is characterised in that:It is by the group of following parts by weight It is grouped into:73 parts of potassium albite, 10 parts of melilite, 20 parts of boric acid powder, 20 parts of quartz, 15 parts of cupric oxide, 15 parts of alkaline earth, green glass 15 parts of glass, 3 parts of tin frit, 1 part of cupric silicate barium;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added Enter pulverizer, be crushed to 300 mesh, obtain hybrid particles;B, hybrid particles are stirred evenly, in 1350 DEG C of fusings, and keeps the temperature 2h; C, it is put into quench in the water that temperature is 15 DEG C and frit is made, then vibration of ultrasonic wave 5min, up to described reddish black with anti-pollution function Glaze.
- A kind of 3. celeste glaze with anti-pollution function according to claim 1, it is characterised in that:It is by the group of following parts by weight It is grouped into:76 parts of potassium albite, 15 parts of melilite, 25 parts of boric acid powder, 25 parts of quartz, 20 parts of cupric oxide, 20 parts of alkaline earth, green glass 20 parts of glass, 4 parts of tin frit, 3 parts of cupric silicate barium;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added Enter pulverizer, be crushed to 320 mesh, obtain hybrid particles;B, hybrid particles are stirred evenly, in 1500 DEG C of fusings, and keeps the temperature 4h; C, it is put into quench in the water that temperature is 18 DEG C and frit is made, then vibration of ultrasonic wave 8min, up to described reddish black with anti-pollution function Glaze.
- A kind of 4. celeste glaze with anti-pollution function according to claim 1, it is characterised in that:It is by the group of following parts by weight It is grouped into:74 parts of potassium albite, 12 parts of melilite, 22 parts of boric acid powder, 23 parts of quartz, 18 parts of cupric oxide, 18 parts of alkaline earth, green glass 17 parts of glass, 3.5 parts of tin frit, 2 parts of cupric silicate barium;Preparation process is as follows:A, raw material is measured according to parts by weight, by above-mentioned raw material Pulverizer is added, 310 mesh is crushed to, obtains hybrid particles;B, hybrid particles are stirred evenly, in 1450 DEG C of fusings, and kept the temperature 3h;C, it is put into quench in the water that temperature is 16 DEG C and frit is made, then vibration of ultrasonic wave 6min, up to the day with anti-pollution function Blue or green glaze.