CN107827360A - A kind of marbling ceramic glaze - Google Patents

A kind of marbling ceramic glaze Download PDF

Info

Publication number
CN107827360A
CN107827360A CN201711242802.3A CN201711242802A CN107827360A CN 107827360 A CN107827360 A CN 107827360A CN 201711242802 A CN201711242802 A CN 201711242802A CN 107827360 A CN107827360 A CN 107827360A
Authority
CN
China
Prior art keywords
parts
marbling
glaze
ceramic glaze
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711242802.3A
Other languages
Chinese (zh)
Inventor
符绩承
吴锡银
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanning Shengrun Technology Co Ltd
Original Assignee
Nanning Shengrun Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanning Shengrun Technology Co Ltd filed Critical Nanning Shengrun Technology Co Ltd
Priority to CN201711242802.3A priority Critical patent/CN107827360A/en
Publication of CN107827360A publication Critical patent/CN107827360A/en
Withdrawn legal-status Critical Current

Abstract

The present invention relates to a kind of marbling ceramic glaze, is made up of potassium albite, white glass, bryozoatum, Chi Yutu, vermiculite power, glaze fruit, green glass, tin frit, salt.The present invention a kind of water resistance, the weatherability of marbling ceramic glaze is good, and compactness is good, sustainable muchly to suppress bacterium;A kind of marbling ceramic glaze of the present invention is applicable to outside construction sanitary ceramic, can be applied in the product surface such as concrete slab, plastic plate, plasterboard, paint, plastics, textile, applied widely, has good promotional value;A kind of marbling ceramic glaze preparation technology of the present invention is simple, stable performance, and it is low to prepare cost.

Description

A kind of marbling ceramic glaze
Technical field
The present invention relates to ceramic fabrication technique field, more particularly to a kind of marbling ceramic glaze.
Background technology
Glaze is a kind of silicate, and the glaze applied on ware is typically using quartz, feldspar, clay as raw material, ground plus water After modulation, coated on billet surface, melted through the roasting of certain temperature, when the temperature drops, forming the nature of glass of ceramic surface Thin layer.It makes ware increase mechanical strength, heat endurance, dielectric strength and the erosion for preventing liquid, gas.Glaze also has increase Porcelain is attractive in appearance and is easy to wash and wipes, the effect such as is not sticky with by dust.Substantially can be with according to the classification of product and purposes in ceramic industry It is divided into following a few classes:Lead glaze and leadless glaze;Raw glaze and fritted glaze, ceramic tile, tableware, sanitary ceramics and electroceramics glaze.According to applying The method of glaze can be divided into immersion oil, glaze spraying, pour glaze;High-temperature glaze, low temperature glaze;Highly expanded glaze, Low Thermal Expantion Glaze;It is coloured glaze, colourless Glaze;Bright glaze, mat glaze.With the improvement of people's living standards, the species of ceramic glaze is more and more rich and varied, Dali at present Shell stone patterns ceramic glaze has porous, and easy dyeing, is easily stained with spot.
The content of the invention
It is an object of the invention to:For above-mentioned problem, there is provided a kind of antifouling property is strong, preparation technology is simple, The low marbling ceramic glaze of manufacturing cost.
The present invention is achieved by the following technical solutions:
A kind of marbling ceramic glaze, is made up of the component of following parts by weight:50~55 parts of potassium albite, white glass 10 ~15 parts, 20~25 parts of bryozoatum, red beautiful 20~25 parts of soil, 15~20 parts of vermiculite power, 15~20 parts of glaze fruit, green glass 15~ 20 parts, 3~4 parts of tin frit, 1~3 part of salt;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added Enter pulverizer, be crushed to the mesh of 300 mesh~320, obtain hybrid particles;B, hybrid particles are stirred, 1350 DEG C~1500 DEG C fusing, and is incubated 2h~4h;C, it is put into quench in the water that temperature is 15 DEG C~18 DEG C and frit is made, then vibration of ultrasonic wave 5min~ 8min, produce the marbling ceramic glaze.
Preferably, a kind of marbling ceramic glaze, is made up of the component of following parts by weight:50 parts of potassium albite, 10 parts of white glass, 20 parts of bryozoatum, red beautiful 20 parts of soil, 15 parts of vermiculite power, 15 parts of glaze fruit, 15 parts of green glass, 3 parts of tin frit, food 1 part of salt;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, 300 mesh is crushed to, obtains To hybrid particles;B, hybrid particles are stirred, in 1350 DEG C of fusings, and is incubated 2h;C, it is put into the water that temperature is 15 DEG C Quench and frit is made, then vibration of ultrasonic wave 5min, produce the marbling ceramic glaze.
Preferably, a kind of marbling ceramic glaze, is made up of the component of following parts by weight:55 parts of potassium albite, 15 parts of white glass, 25 parts of bryozoatum, red beautiful 25 parts of soil, 20 parts of vermiculite power, 20 parts of glaze fruit, 20 parts of green glass, 4 parts of tin frit, food 3 parts of salt;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, 320 mesh is crushed to, obtains To hybrid particles;B, hybrid particles are stirred, in 1500 DEG C of fusings, and is incubated 4h;C, it is put into the water that temperature is 18 DEG C Quench and frit is made, then vibration of ultrasonic wave 8min, produce the marbling ceramic glaze.
Preferably, a kind of marbling ceramic glaze, is made up of the component of following parts by weight:52 parts of potassium albite, 12 parts of white glass, 22 parts of bryozoatum, red beautiful 23 parts of soil, 18 parts of vermiculite power, 18 parts of glaze fruit, 17 parts of green glass, 3.5 parts of tin frit, 2 parts of salt;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, are crushed to 310 mesh, Obtain hybrid particles;B, hybrid particles are stirred, in 1450 DEG C of fusings, and is incubated 3h;C, it is put into the water that temperature is 16 DEG C In quench frit be made, then vibration of ultrasonic wave 6min produces the marbling ceramic glaze.
The raw material being related in this application can obtain in buying on the market.
The beneficial effects of the invention are as follows:
1. the present invention a kind of water resistance, the weatherability of marbling ceramic glaze is good, compactness is good, it is sustainable muchly Suppress bacterium.
2. a kind of marbling ceramic glaze of the present invention is applicable to outside construction sanitary ceramic, coagulation can be applied in The product surface such as native plate, plastic plate, plasterboard, paint, plastics, textile, it is applied widely, there is good promotional value.
3. a kind of marbling ceramic glaze preparation technology of the present invention is simple, stable performance, and it is low to prepare cost.
Embodiment
This specification(Including any accessory claim, summary)Disclosed in any feature, unless specifically stated otherwise, Replaced by other equivalent or with similar purpose alternative features.I.e., unless specifically stated otherwise, each feature is a series of An example in equivalent or similar characteristics.
Embodiment 1:
A kind of marbling ceramic glaze, is made up of the component of following parts by weight:50 parts of potassium albite, 10 parts of white glass, 20 parts of bryozoatum, red beautiful 20 parts of soil, 15 parts of vermiculite power, 15 parts of glaze fruit, 15 parts of green glass, 3 parts of tin frit, 1 part of salt;Prepare Step is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, are crushed to 300 mesh, obtain mixing Grain;B, hybrid particles are stirred, in 1350 DEG C of fusings, and is incubated 2h;C, be put into temperature be quenched in 15 DEG C of water be made it is molten Block, then vibration of ultrasonic wave 5min, produce the marbling ceramic glaze.
Embodiment 2:
A kind of marbling ceramic glaze, is made up of the component of following parts by weight:55 parts of potassium albite, 15 parts of white glass, 25 parts of bryozoatum, red beautiful 25 parts of soil, 20 parts of vermiculite power, 20 parts of glaze fruit, 20 parts of green glass, 4 parts of tin frit, 3 parts of salt;Prepare Step is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, are crushed to 320 mesh, obtain mixing Grain;B, hybrid particles are stirred, in 1500 DEG C of fusings, and is incubated 4h;C, be put into temperature be quenched in 18 DEG C of water be made it is molten Block, then vibration of ultrasonic wave 8min, produce the marbling ceramic glaze.
Embodiment 3:
A kind of marbling ceramic glaze, is made up of the component of following parts by weight:52 parts of potassium albite, 12 parts of white glass, 22 parts of bryozoatum, red beautiful 23 parts of soil, 18 parts of vermiculite power, 18 parts of glaze fruit, 17 parts of green glass, 3.5 parts of tin frit, 2 parts of salt;System Standby step is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into pulverizer, are crushed to 310 mesh, obtain mixing Grain;B, hybrid particles are stirred, in 1450 DEG C of fusings, and is incubated 3h;C, be put into temperature be quenched in 16 DEG C of water be made it is molten Block, then vibration of ultrasonic wave 6min, produce the marbling ceramic glaze.
Although above the present invention is described in detail with a general description of the specific embodiments, On the basis of the present invention, it can be made some modifications or improvements, this will be apparent to those skilled in the art.Cause This, these modifications or improvements, belong to the scope of protection of present invention without departing from theon the basis of the spirit of the present invention.

Claims (4)

  1. A kind of 1. marbling ceramic glaze, it is characterised in that:It is made up of the component of following parts by weight:Potassium albite 50~ 55 parts, 10~15 parts of white glass, 20~25 parts of bryozoatum, red beautiful 20~25 parts of soil, 15~20 parts of vermiculite power, glaze fruit 15~20 Part, 15~20 parts of green glass, 3~4 parts of tin frit, 1~3 part of salt;Preparation process is as follows:A, raw material is measured according to parts by weight, Above-mentioned raw material are added into pulverizer, the mesh of 300 mesh~320 is crushed to, obtains hybrid particles;B, hybrid particles are stirred, In 1350 DEG C~1500 DEG C fusings, and it is incubated 2h~4h;C, it is put into quench in the water that temperature is 15 DEG C~18 DEG C and frit is made, then surpasses Acoustic wave vibrations 5min~8min, produce the marbling ceramic glaze.
  2. A kind of 2. marbling ceramic glaze according to claim 1, it is characterised in that:It is by the component of following parts by weight Composition:50 parts of potassium albite, 10 parts of white glass, 20 parts of bryozoatum, red beautiful 20 parts of soil, 15 parts of vermiculite power, 15 parts of glaze fruit, green glass 15 parts of glass, 3 parts of tin frit, 1 part of salt;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into powder Broken machine, 300 mesh are crushed to, obtain hybrid particles;B, hybrid particles are stirred, in 1350 DEG C of fusings, and is incubated 2h;C, put Enter to quench in the water that temperature is 15 DEG C and frit is made, then vibration of ultrasonic wave 5min, produce the marbling ceramic glaze.
  3. A kind of 3. marbling ceramic glaze according to claim 1, it is characterised in that:It is by the component of following parts by weight Composition:55 parts of potassium albite, 15 parts of white glass, 25 parts of bryozoatum, red beautiful 25 parts of soil, 20 parts of vermiculite power, 20 parts of glaze fruit, green glass 20 parts of glass, 4 parts of tin frit, 3 parts of salt;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added into powder Broken machine, 320 mesh are crushed to, obtain hybrid particles;B, hybrid particles are stirred, in 1500 DEG C of fusings, and is incubated 4h;C, put Enter to quench in the water that temperature is 18 DEG C and frit is made, then vibration of ultrasonic wave 8min, produce the marbling ceramic glaze.
  4. A kind of 4. marbling ceramic glaze according to claim 1, it is characterised in that:It is by the component of following parts by weight Composition:52 parts of potassium albite, 12 parts of white glass, 22 parts of bryozoatum, red beautiful 23 parts of soil, 18 parts of vermiculite power, 18 parts of glaze fruit, green glass 17 parts of glass, 3.5 parts of tin frit, 2 parts of salt;Preparation process is as follows:A, raw material is measured according to parts by weight, above-mentioned raw material is added Pulverizer, 310 mesh are crushed to, obtain hybrid particles;B, hybrid particles are stirred, in 1450 DEG C of fusings, and is incubated 3h;C、 It is put into quench in the water that temperature is 16 DEG C and frit is made, then vibration of ultrasonic wave 6min, produce the marbling ceramic glaze.
CN201711242802.3A 2017-11-30 2017-11-30 A kind of marbling ceramic glaze Withdrawn CN107827360A (en)