CN107828062B - 水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂及其制备方法及其应用 - Google Patents
水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂及其制备方法及其应用 Download PDFInfo
- Publication number
- CN107828062B CN107828062B CN201711127103.4A CN201711127103A CN107828062B CN 107828062 B CN107828062 B CN 107828062B CN 201711127103 A CN201711127103 A CN 201711127103A CN 107828062 B CN107828062 B CN 107828062B
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- side chain
- settling agent
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂及其制备方法及其应用，特点是由聚合物主链聚羟乙基丙烯酰胺、阳离子型高分子侧链末端含羧基的聚甲基丙烯酰氧乙基三甲基氯化铵、功能高分子侧链前驱体聚合物末端含羧基的聚N‑乙烯基甲酰胺、水、催化剂即N‑羟基琥珀酰亚胺、1‑乙基‑3‑(3‑二甲胺基丙基)碳二亚胺碘甲烷盐、氢氧化钾及二硫化碳制备水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂，并将水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂用于处理染料合成或染整过程中排放出的染料废水及艺术涂料废水。其具有捕集能力强，沉降速度快，能处理重金属离子，能在数秒内捕获阴离子染料分子及重金属离子，快速生长成大的沉降颗粒，快速实现分离染料的目的，操作方便等优点。
Description
技术领域
本发明属于水处理技术及高分子功能材料领域，具体涉及水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂及其制备方法及其应用，其主要在染料合成或染整过程中排放出的染料废水及艺术涂料废水中应用，能实现同时除去染料废水的阴离子染料及重金属离子。
背景技术
近些年来，我国每年污水排放量达390多亿吨，其中工业污水占51% ，而染料废水又占总工业废水排放量的35%，而且还以1%的速度在逐年增加。染料废水主要来自于染料合成及染料使用企业，由合成或染整过程中排放出的染料、助剂等组成。随着印染工业的飞速发展，我国是纺织品生产和加工大国，纺织品出口额已多年来列居世界首位，每年的染料生产量达1.5×105吨，其中大约10%～15%的染料会直接随废水排入水体中，染料废水已成为水体重要污染源之一。为加强纺织染整工业水污染控制，2012年，环境保护部和国家质量监督检验检疫总局联合修订发布了《纺织染整工业水污染物排放标准》(GB 4287-2012)。根据新的排放标准，采用传统的处理技术，很多印染企业无法达到新的国家排放标准，出现很多偷排放现象，发生了严重的水体环境污染事件。总体来说，目前的染料废水处理技术还无法达到国家排放标准，急需新材料和新技术的研发解决目前企业排放问题。染料废水具有极强的污染感，且有色水体会影响日光照射，不利于水生生物的生长，一般的生化法很难对其进行处理。染料废水的排放量也很大，而且排放具有间歇性，水质也不稳定，属于难治理废水。
传统的废水处理方法有物化法、化学混凝法、物理吸附法、生化法、电化学法等。化学混凝法是在染料废水中加入混凝剂，使污染物形成胶粒，通过混凝沉淀或气浮，从而去除废水中的污染物。混凝沉淀法是实际应用中最广泛的。混凝法能同时去除染料污染物和其他的大分子悬浮污染物。对废水的处理效果主要取决于混凝剂的结构性质。目前使用的混凝剂主要有无机混凝剂和有机高分子混凝剂。无机混凝剂主要以铝盐和铁盐为主，对以胶体或悬浮态存在于废水中的染料有较好的混凝效果，但是对于水溶性染料中分子量较小的，混凝效果则比较差。有机高分子混凝剂分子量大，溶入水中后分散为巨大数量的线性分子，对水中的胶体悬浮粒子的吸附架桥能力强。有机高分子混凝剂性质稳定，残渣少，对pH值要求较宽，其中最有代表性的就是聚丙烯酰胺。但聚丙烯酰胺化学结构较为单一，存在着对染料分子捕捉能力较差，沉降速度较慢，无法处理重金属离子等问题。
发明内容
本发明的目的是克服现有技术的不足而提供一种水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂及其制备方法及其应用，其捕集能力强，沉降速度快，能处理重金属离子，能在数秒内捕获阴离子染料分子及重金属离子，快速生长成大的沉降颗粒，快速实现分离染料的目的，操作方便。
为了达到上述目的，本发明的水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂的技术方案是这样实现的，其特征在于包括1～10份的聚合物主链聚羟乙基丙烯酰胺（PHEMAA）、20～100份的阳离子型高分子侧链末端含羧基的聚甲基丙烯酰氧乙基三甲基氯化铵（PDMC-COOH）、1～10份的功能高分子侧链前驱体聚合物末端含羧基的聚N-乙烯基甲酰胺（PNVF-COOH）、100～500份的水、1～5份的催化剂即N-羟基琥珀酰亚胺(NHS)、1～5份的1-乙基-3-(3-二甲胺基丙基)碳二亚胺碘甲烷盐(EDC·CH3I)、1～10份的氢氧化钾及1～10份的二硫化碳；以上均为质量份数。
在本技术方案中，所述聚合物主链聚羟乙基丙烯酰胺（PHEMAA）是通过普通自由基聚合或可控活性聚合法合成PHEMAA聚合物主链；所述阳离子型高分子侧链PDMC-COOH和功能高分子侧链前驱体聚合物PNVF-COOH主要采用偶氮二氰基戊酸为引发剂通过普通自由基聚合法合成末端含羧基的聚甲基丙烯酰氧乙基三甲基氯化铵（PDMC-COOH）聚合物；所述功能高分子侧链前驱体聚合物PNVF-COOH主要采用偶氮二氰基戊酸为引发剂通过普通自由基聚合合成末端含羧基的聚N-乙烯基甲酰胺（PNVF-COOH）聚合物。
为了达到上述目的，本发明的水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂的制备方法的技术方案是这样实现的，其特征在于将1～10份的聚合物主链聚羟乙基丙烯酰胺（PHEMAA）、20～100份的阳离子型高分子侧链末端含羧基的聚甲基丙烯酰氧乙基三甲基氯化铵（PDMC-COOH）和1～10份的功能高分子侧链前驱体聚合物末端含羧基的聚N-乙烯基甲酰胺（PNVF-COOH）混合溶于100～500份的水里，加入1～5份的催化剂即N-羟基琥珀酰亚胺(NHS)和1～5份的1-乙基-3-(3-二甲胺基丙基)碳二亚胺碘甲烷盐(EDC·CH3I)，控温于50～80℃，进行酯化反应10～70小时，获得聚羟乙基丙烯酰胺-接枝-（聚甲基丙烯酰氧乙基三甲基氯化铵-无规-聚N-乙烯基甲酰胺）(PHEMAA-g-(PDMC-r-PNVF))；再加入1～10份的氢氧化钾，控温于50～80℃，进行水解反应12～48小时，获得聚羟乙基丙烯酰胺-接枝-（聚甲基丙烯酰氧乙基三甲基氯化铵-无规-聚乙烯胺）（PHEMAA-g-(PDMC-r-PVA）)；再加入1～10份的二硫化碳，控温于20～40℃，进行加成反应1～3小时，最终获得聚羟乙基丙烯酰胺-接枝-（聚甲基丙烯酰氧乙基三甲基氯化铵-无规-聚乙烯胺基二硫代氨基甲酸钠）(PHEMAA-g-(PDMC-r-PVACS2Na))即水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂，以上均为质量份数。
在本技术方案中，所述聚羟乙基丙烯酰胺（PHEMAA）的聚合度为10～500，所述阳离子型高分子侧链PDMC-COOH及功能高分子侧链前驱体聚合物PNVF-COOH的聚合度均为10～200，阳离子型高分子侧链PDMC的接枝率为1～90%及螯合型侧链PVACS2Na的接枝率为1～5%。
为了达到上述目的，本发明的水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂的应用的技术方案是这样实现的，其特征在于0.1～1份的水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂加入到100～1000份的废水中，常温下搅拌1～5分钟，调节pH至2～5，废水中阴离子染料分子与水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂的阳离子型侧链PDMC发生静电吸附，废水中重金属离子与水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂的螯合型侧链PVACS2Na发生螯合吸附，再加入0.01～0.1份的助沉降剂，常温下搅拌1分钟，助沉降剂的金属离子将快速与水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂的螯合型侧链PVACS2Na发生化学沉淀反应，10秒内生成粒径大于100μm的絮体沉淀，可快速实现去除废水中的阴离子染料及重金属离子，以上均为质量份数。
在本技术方案中，所述助沉降剂为氯化钙、硫酸镁、氯化亚铁、三氯化铁、三氯化铝的一种或两种以上的任意组合。
本发明与现有技术相比，具有如下的优点及效果：
1、本发明解决了传统合成类高分子染料絮凝剂结构单一及捕捉性能差的缺陷，本发明含有二种不同功能的高分子侧链，阳离子型高分子侧链PDMC对阴离子型染料具有很好的静电吸附能力，在PVACS2Na功能高分子侧链的协同作用下，PVACS2Na高分子侧链与助沉降剂金属离子或重金属离子快速发生化学沉淀反应，达到高效捕捉及快速沉降功能具有高效捕捉阴离子型染料能力，出水基本无色，达到国家排放标准。
2、本发明的具有沉降速度的技术优势，能在少量助沉降剂下，发生螯合沉淀反应，数秒内快速生成大的聚集体，产生的污泥量少；
3、本发明具有双重功能，能同时捕捉阴离子型染料及重金属离子，解决了传统絮凝剂无法处理染料废水中重金属离子问题。
具体实施方式
下面结合实施例对本发明作进一步详细的描述，但本发明的实施方式不限于此。以下实施例中所涉及的份数均是质量份数。
实施例一
其是一种水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂，由以下步骤制备得到：
步骤一 合成PHEMAA聚合物主链
取3份的偶氮二异丁腈引发剂、100份的羟乙基丙烯酰胺（HEMAA）、400的份甲醇，在氮气保护下70℃进行聚合反应1小时，得到聚合度（DP）为35的聚羟乙基丙烯酰胺（PHEMAA）；
步骤二 合成阳离子型高分子侧链PDMC-COOH和功能高分子侧链前驱体聚合物PNVF-COOH
阳离子型高分子侧链PDMC-COOH的合成：取3份的偶氮二氰基戊酸引发剂、100份的甲基丙烯酰氧乙基三甲基氯化铵（DMC）和300份的水，在氮气保护下70℃进行自由基聚合反应3小时，得到聚合度（DP）为40的PDMC-COOH；
功能高分子侧链前驱体聚合物PNVF-COOH的合成：取2份的偶氮二氰基戊酸引发剂、100份的N-乙烯基甲酰胺（NVF）和300份的水，在氮气保护下70℃进行自由基聚合反应2小时，得到聚合度（DP）为50的PNVF-COOH；
步骤三 合成PHEMAA-g-(PDMC-r-PVACS2Na)
将步骤一中所得到的1份的聚羟乙基丙烯酰胺（PHEMAA）与步骤二中所得到的25份的阳离子型高分子侧链PDMC-COOH和2份的功能高分子侧链前驱体聚合物PNVF-COOH混合溶于100份的水里，加入1份的催化剂即N-羟基琥珀酰亚胺(NHS)和1份的1-乙基-3-(3-二甲胺基丙基)碳二亚胺碘甲烷盐(EDC·CH3I)，控温于55℃，进行酯化反应70小时，使聚合物主链的每个单元的羟基功能基团与末端含羧基的阳离子型高分子侧链PDMC-COOH和末端含羧基的功能高分子侧链前驱体聚合物PNVF无规地发生酯化反应，获得聚羟乙基丙烯酰胺-接枝-（聚甲基丙烯酰氧乙基三甲基氯化铵-无规-聚N-乙烯基甲酰胺）(PHEMAA-g-(PDMC-r-PNVF))；再加2份的氢氧化钾，控温于80℃，对接枝于聚合物主链功能高分子侧链前驱体聚合物PNVF进行水解反应12小时，获得聚羟乙基丙烯酰胺-接枝-（聚甲基丙烯酰氧乙基三甲基氯化铵-无规-聚乙烯胺）（PHEMAA-g-(PDMC-r-PVA）)；再加入2份的二硫化碳，控温于20℃，进行加成反应3小时，最终获得水溶性聚羟乙基丙烯酰胺-接枝-（聚甲基丙烯酰氧乙基三甲基氯化铵-无规-聚乙烯胺基二硫代氨基甲酸钠）(PHEMAA-g-(PDMC-r-PVACS2Na)) 即水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂。采用核磁共振仪测定PDMC和PVACS2Na侧链的接枝率分别为21%和1%。
在本实施例中，水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂的应用
取本实施例的水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂做染料废水测试，取100份的含甲基红50 mg/L的废水，添加到0.1份的水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂中，常温下搅拌1分钟，采用0.1 mol/L盐酸调节废水pH值到2.0，再加入0.01份的助沉降剂氯化钙，常温下搅拌1分钟，10秒内生成粒径大于130 μm的絮体沉淀，过滤，采用紫外吸收分光光度计测定滤液中甲基红浓度为0.03mg/L，脱除效率>99.9%。
实施例二
其是一种水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂，由以下步骤制备得到：
步骤一 合成PHEMAA聚合物主链
取2份的2-溴异丁酸乙酯引发剂2份的CuBr及2份的4,4-联吡啶（BPy）、100份的羟乙基丙烯酰胺（HEMAA）、20的份甲醇，在氮气保护下55℃进行聚合反应10小时，得到聚合度（DP）为490的聚羟乙基丙烯酰胺（PHEMAA）；
步骤二 合成阳离子型高分子侧链PDMC-COOH和功能高分子侧链前驱体聚合物PNVF-COOH
阳离子型高分子侧链PDMC-COOH的合成：取1份的偶氮二氰基戊酸引发剂、200份的甲基丙烯酰氧乙基三甲基氯化铵（DMC）和50份的水，在氮气保护下75℃进行自由基聚合反应5小时，得到聚合度（DP）为130的PDMC-COOH；
功能高分子侧链前驱体聚合物PNVF-COOH的合成：取1份的偶氮二氰基戊酸引发剂、200份的N-乙烯基甲酰胺（NVF）和60份的水，在氮气保护下75℃进行自由基聚合反应6小时，得到聚合度（DP）为110的PNVF-COOH；
步骤三 合成PHEMAA-g-(PDMC-r-PVACS2Na)
将步骤一中所得到的4份的聚羟乙基丙烯酰胺（PHEMAA）与步骤二中所得到的60份的阳离子型高分子侧链PDMC-COOH和6份的功能高分子侧链前驱体聚合物PNVF-COOH混合溶于300份的水里，加入3份的催化剂即N-羟基琥珀酰亚胺(NHS)和3份的1-乙基-3-(3-二甲胺基丙基)碳二亚胺碘甲烷盐(EDC·CH3I)，控温于60℃，进行酯化反应50小时，使聚合物主链的每个单元的羟基功能基团与末端含羧基的阳离子型高分子侧链PDMC-COOH和末端含羧基的功能高分子侧链前驱体聚合物PNVF无规地发生酯化反应，获得聚羟乙基丙烯酰胺-接枝-（聚甲基丙烯酰氧乙基三甲基氯化铵-无规-聚N-乙烯基甲酰胺）(PHEMAA-g-(PDMC-r-PNVF))；再加5份的氢氧化钾，控温于60℃，对接枝于聚合物主链功能高分子侧链前驱体聚合物PNVF进行水解反应24小时，获得聚羟乙基丙烯酰胺-接枝-（聚甲基丙烯酰氧乙基三甲基氯化铵-无规-聚乙烯胺）（PHEMAA-g-(PDMC-r-PVA）)；再加入5份 二硫化碳，控温于30℃，进行加成反应2小时，最终获得水溶性聚羟乙基丙烯酰胺-接枝-（聚甲基丙烯酰氧乙基三甲基氯化铵-无规-聚乙烯胺基二硫代氨基甲酸钠）(PHEMAA-g-(PDMC-r-PVACS2Na)) 即水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂。采用核磁共振仪测定PDMC和PVACS2Na侧链的接枝率分别为32%和3%。
在本实施例中，水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂的应用
取本实施例的水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂做染料废水测试，取500份刚果红40 mg/L和镉离子2mg/L的废水，添加到0.5份的水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂中，常温下搅拌3分钟，采用0.1 mol/L盐酸调节废水pH值到4.0，再加入0.05份的助沉降剂二氯化亚铁，常温下搅拌1分钟，6秒内生成粒径大于390 μm的絮体沉淀，过滤，采用紫外吸收分光光度计及原子吸收分光光度计分别测定滤液中刚果红浓度为0.04mg/L及Cd2+离子浓度为0.02mg/L，脱除效率>99.9%。
实施例三
其是一种水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂，由以下步骤制备得到：
步骤一 合成PHEMAA聚合物主链
取2份的2-溴异丁酸乙酯引发剂、2份的CuBr及2份的4,4-联吡啶（BPy）、100份的羟乙基丙烯酰胺（HEMAA）、50的份甲醇，在氮气保护下70℃进行聚合反应15小时，得到聚合度（DP）为350的聚羟乙基丙烯酰胺（PHEMAA）；
步骤二 合成阳离子型高分子侧链PDMC-COOH和功能高分子侧链前驱体聚合物PNVF-COOH
阳离子型高分子侧链PDMC-COOH的合成：取1份的偶氮二氰基戊酸引发剂、300份的甲基丙烯酰氧乙基三甲基氯化铵（DMC）和50份的水，在氮气保护下85℃进行自由基聚合反应6小时，得到聚合度（DP）为180的PDMC-COOH；
功能高分子侧链前驱体聚合物PNVF-COOH的合成：取1份的偶氮二氰基戊酸引发剂、400份的N-乙烯基甲酰胺（NVF）和100份的水，在氮气保护下85℃进行自由基聚合反应6小时，得到聚合度（DP）为170的PNVF-COOH；
步骤三 合成PHEMAA-g-(PDMC-r-PVACS2Na)
将步骤一中所得到的3份的聚羟乙基丙烯酰胺（PHEMAA）与步骤二中所得到的95份的阳离子型高分子侧链PDMC-COOH、和10份的功能高分子侧链前驱体聚合物PNVF-COOH混合溶于500份的水里，加入5份的催化剂即N-羟基琥珀酰亚胺(NHS)和5份的1-乙基-3-(3-二甲胺基丙基)碳二亚胺碘甲烷盐(EDC·CH3I)，控温于80℃，进行酯化反应12小时，使聚合物主链的每个单元的羟基功能基团与末端含羧基的阳离子型高分子侧链PDMC-COOH和末端含羧基的功能高分子侧链前驱体聚合物PNVF无规地发生酯化反应，获得聚羟乙基丙烯酰胺-接枝-（聚甲基丙烯酰氧乙基三甲基氯化铵-无规-聚N-乙烯基甲酰胺）(PHEMAA-g-(PDMC-r-PNVF))；再加10份的氢氧化钾，控温于50℃，对接枝于聚合物主链功能高分子侧链前驱体聚合物PNVF进行水解反应12小时，获得聚羟乙基丙烯酰胺-接枝-（聚甲基丙烯酰氧乙基三甲基氯化铵-无规-聚乙烯胺）（PHEMAA-g-(PDMC-r-PVA）)；再加入10份的二硫化碳，控温于20℃，进行加成反应3小时，最终获得水溶性聚羟乙基丙烯酰胺-接枝-（聚甲基丙烯酰氧乙基三甲基氯化铵-无规-聚乙烯胺基二硫代氨基甲酸钠）(PHEMAA-g-(PDMC-r-PVACS2Na)) 水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂。采用核磁共振仪测定PDMC和PVACS2Na侧链的接枝率分别为85%和5%。
在本实施例中，水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂的应用
取本实施例的水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂做染料废水测试，取1000份的含甲基橙30 mg/L和铅离子2mg/L的废水，添加到1.0份的水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂中，常温下搅拌5分钟，采用0.1 mol/L盐酸调节废水pH值到5.0，再加入0.1份的助沉降剂三氯化铝，常温下搅拌1分钟，4秒内生成粒径大于600μm的絮体沉淀，过滤，采用紫外吸收分光光度计及原子吸收分光光度计分别测定滤液中甲基橙浓度为0.06 mg/L及Pb2+离子浓度为0.04 mg/L，脱除效率>99.9%。
上述实施例为本发明较佳的实施方式，但本发明的实施方式并不受上述实施例的限制，其他的任何未背离本发明的精神实质与原理下所作的改变、修饰、替代、组合、简化，均应为等效的置换方式，都包含在本发明的保护范围之内。
Claims (4)
1.一种水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂，其特征在于包括1～10份的聚合物主链聚羟乙基丙烯酰胺（PHEMAA）、20～100份的阳离子型高分子侧链末端含羧基的聚甲基丙烯酰氧乙基三甲基氯化铵（PDMC-COOH）、1～10份的功能高分子侧链前驱体聚合物末端含羧基的聚N-乙烯基甲酰胺（PNVF-COOH）、100～500份的水、1～5份的催化剂即N-羟基琥珀酰亚胺(NHS)、1～5份的1-乙基-3-(3-二甲胺基丙基)碳二亚胺碘甲烷盐(EDC·CH3I)、1～10份的氢氧化钾及1～10份的二硫化碳；
所述聚合物主链聚羟乙基丙烯酰胺（PHEMAA）是通过普通自由基聚合或可控活性聚合法合成PHEMAA聚合物主链；所述阳离子型高分子侧链PDMC-COOH和功能高分子侧链前驱体聚合物PNVF-COOH主要采用偶氮二氰基戊酸为引发剂通过普通自由基聚合法合成末端含羧基的聚甲基丙烯酰氧乙基三甲基氯化铵（PDMC-COOH）聚合物；所述功能高分子侧链前驱体聚合物PNVF-COOH主要采用偶氮二氰基戊酸为引发剂通过普通自由基聚合合成末端含羧基的聚N-乙烯基甲酰胺（PNVF-COOH）聚合物；
水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂的制备方法，将1～10份的聚合物主链聚羟乙基丙烯酰胺（PHEMAA）、20～100份的阳离子型高分子侧链末端含羧基的聚甲基丙烯酰氧乙基三甲基氯化铵（PDMC-COOH）和1～10份的功能高分子侧链前驱体聚合物末端含羧基的聚N-乙烯基甲酰胺（PNVF-COOH）混合溶于100～500份的水里，加入1～5份的催化剂即N-羟基琥珀酰亚胺(NHS)和1～5份的1-乙基-3-(3-二甲胺基丙基)碳二亚胺碘甲烷盐(EDC·CH3I)，控温于50～80℃，进行酯化反应10～70小时，获得聚羟乙基丙烯酰胺-接枝-（聚甲基丙烯酰氧乙基三甲基氯化铵-无规-聚N-乙烯基甲酰胺）(PHEMAA-g-(PDMC-r-PNVF))；再加入1～10份的氢氧化钾，控温于50～80℃，进行水解反应12～48小时，获得聚羟乙基丙烯酰胺-接枝-（聚甲基丙烯酰氧乙基三甲基氯化铵-无规-聚乙烯胺）（PHEMAA-g-(PDMC-r-PVA）)；再加入1～10份的二硫化碳，控温于20～40℃，进行加成反应1～3小时，最终获得聚羟乙基丙烯酰胺-接枝-（聚甲基丙烯酰氧乙基三甲基氯化铵-无规-聚乙烯胺基二硫代氨基甲酸钠）(PHEMAA-g-(PDMC-r-PVACS2Na))即水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂；
以上均为质量份数。
2.根据权利要求1所述的水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂，其特征在于所述聚羟乙基丙烯酰胺（PHEMAA）的聚合度为10～500，所述阳离子型高分子侧链PDMC-COOH及功能高分子侧链前驱体聚合物PNVF-COOH的聚合度均为10～200，阳离子型高分子侧链PDMC的接枝率为1～90%及螯合型侧链PVACS2Na的接枝率为1～5%。
3.根据权利要求1所述的水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂的应用，其特征在于0.1～1份的水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂加入到100～1000份的废水中，常温下搅拌1～5分钟，调节pH至2～5，废水中阴离子染料分子与水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂的阳离子型侧链PDMC发生静电吸附，废水中重金属离子与水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂的螯合型侧链PVACS2Na发生螯合吸附，再加入0.01～0.1份的助沉降剂，常温下搅拌1分钟，助沉降剂的金属离子将快速与水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂的螯合型侧链PVACS2Na发生化学沉淀反应，10秒内生成粒径大于100μ m的絮体沉淀，可快速实现去除废水中的阴离子染料及重金属离子，以上均为质量份数。
4.根据权利要求3所述水溶性三元阳离子型聚合物分子刷染料捕捉沉降剂的应用，其特征在于所述助沉降剂为氯化钙、硫酸镁、氯化亚铁、三氯化铁、三氯化铝的一种或两种以上的任意组合。