CN107825086A - 一种贵金属物品的加工方法 - Google Patents
一种贵金属物品的加工方法 Download PDFInfo
- Publication number
- CN107825086A CN107825086A CN201711301105.0A CN201711301105A CN107825086A CN 107825086 A CN107825086 A CN 107825086A CN 201711301105 A CN201711301105 A CN 201711301105A CN 107825086 A CN107825086 A CN 107825086A
- Authority
- CN
- China
- Prior art keywords
- noble metal
- processing method
- finished product
- metal article
- titanizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种贵金属物品的加工方法,包括将贵金属坯料制成板条的过程,其特征在于,包括镀钛步骤,镀钛步骤包括:在贵金属板条的表面上通过磁控溅射法镀上一层钛膜,然后再进行后续加工。本发明的贵金属物品的加工方法,通过优化轧制工艺,利用镀钛工艺与冲压工艺相结合的方式来生产贵金属纪念币,在保证成型质量和加工精度的情况下,提高了贵金属纪念币的耐磨性、抗腐蚀性和硬度,使贵金属纪念币得以长久保质。
Description
本申请是名称为:一种贵金属纪念币的加工方法,申请号为:201610275402.1的发明专利的分案申请,母案申请日为2016年04月29日。
技术领域
本发明属于贵金属加工成形技术领域,特别是涉及一种贵金属物品的加工方法。
背景技术
贵金属一般常用的有:金、银、铂、钯及其合金,制造饰品和工业用部件一般采用以下工艺方法制造:手工打造,精密铸造,压力加工,机械加工,电铸,焊接等方法。在贵金属珠类装饰品中,各种款式和造型的珠类和链类贵金属首饰,使得贵金属饰品的种类繁复,但也因此挑战着生产企业的工艺能力和技术水平,因此,贵金属首饰加工厂一般都设有备料部,以实现将贵金属锭在各种机械设备上进行拉伸、冲压、缠绕、剪切等操作,为其他部门的进一步加工准备初步毛坯件,因此,在贵金属加工上开发的机械设备有拉板、拉线机、压片机、油压模冲压机、冲减模冲压机、扭片机等。
目前,现有的贵金属纪念币在质量上还存在着一个较重要的问题,即纪念币耐腐蚀和耐磨的问题。在贵金属纪念币收藏中,纪念币往往会受外部环境而被腐蚀和氧化,例如人们在收藏黄金纪念币时,黄金纪念币跟人皮肤接触后,会吸收人皮肤的毒素和汗液而发黑发黄,同时,黄金纪念币还会与人们的生活用品(如化妆品中的汞)和空气中的硫发生反应而发黑,当黄金纪念币与铂金戒指或铂金项链相互摩擦时,黄金纪念币的表面上还会因蹭上铂金而发白,这些问题都会损害收藏者的利益;由于纯度越高的黄金和银,它们的柔软度就越高,耐磨性就越低,当人们在收藏金银纪念币时,在长期的刮蹭中,黄金和银的质量会慢慢减少,影响纪念币的重量和尺寸精度,这些问题都会导致纪念币的收藏价值的降低。
发明内容
本发明的发明目的在于:针对上述存在的问题,提供一种贵金属物品的加工方法,通过优化轧制工艺,利用镀钛工艺与冲压工艺相结合的方式来生产贵金属纪念币,在保证成型质量和加工精度的情况下,提高贵金属纪念币的耐磨性、抗腐蚀性和硬度,使贵金属纪念币得以长久保质。
为达到上述目的,本发明采用的技术方案如下:一种贵金属物品的加工方法,包括将贵金属坯料制成板条的过程,其特征在于,包括镀钛步骤,镀钛步骤包括:在贵金属板条的表面上通过磁控溅射法镀上一层钛膜,然后再进行后续加工。
进一步,钛膜的厚度为60-100μm,以保证得到合乎要求的钛层。
进一步,对镀钛后的贵金属板条进行初轧和精轧后,得到半成品,然后对半成品进行光饰处理后得到成品。
进一步,对成品进行检测验收,对于尺寸不足的成品通过镀钛的方式补足尺寸。
进一步,在进行光饰处理时,先将得到的半成品进行表面清洗,然后放入离心光饰机的小桶内,启动电机,调节离心光饰机的主要参数,使离心光饰机的转速为300-500rad/min进行光饰处理,光饰处理完后,再放入无水乙醇中浸泡3-5h,最后取出烘干即可。
在上述工艺步骤中,贵金属板条的表面镀上一层钛膜,可以防止贵金属板条在热处理时形成氧化层,减小贵金属的加工损耗,若贵金属板条的尺寸过小,则可通过镀钛的方式来满足设计的尺寸精度要求。贵金属板条镀钛后,经过轧制冲裁得到半成品坯饼,由于钛膜具有良好的可塑性,在此过程中,钛膜在轧制过程会发生挤压和延伸变形,会使钛膜由表面镀层向贵金属内部渗透,进而在贵金属表面上形成一层钛-贵金属过渡层,达到类似“渗钛”的效果,在热处理时,会加速这种过渡层的形成。形成的过渡层一方面能使钛膜结合牢固,几乎不会发生脱皮、剥落等现象,另一方面,钛在贵金属中形成的化合物能大幅提高贵金属表面的耐磨性、硬度和耐空蚀性能,虽然这种效果不如渗钛工艺所带来的效果,但这种方式较渗钛工艺成本低很多,得到的贵金属表面的性能也足以满足现实需求。
在最终得到的贵金属纪念币中,由于钛膜具有高硬度、防摩擦、不剥落、不易划伤等特点,在紫外线下不会脱皮,这些性能使贵金属纪念币在刮蹭摩擦过程中不会被磨损,贵金属纪念币的重量几乎能保持恒重;在耐腐蚀性上,钛膜具有高度防腐性,钛膜表面无论是氮化钛、碳化钛或碳氮化钛,都具有很强的化学稳定性,不与一般性酸碱反应,不易被电化学腐蚀,不会与汞之类的化工元素反应,能保护贵金属纪念币的表面,使贵金属表面不会发生发黑发白的现象,也不会附着其他金属成分;在耐久性上,形成的钛膜的颜色在长期使用时也不会掉色,抗破坏性较强,表面易清洗,在经过光饰后,钛膜的表面成色可保持长期不变,使贵金属纪念币长久保质。
综上所述,由于采用了上述技术方案,本发明的有益效果是:本发明的贵金属物品的加工方法,通过优化轧制工艺,利用镀钛工艺与冲压工艺相结合的方式来生产贵金属纪念币,在保证成型质量和加工精度的情况下,提高了贵金属纪念币的耐磨性、抗腐蚀性和硬度,使贵金属纪念币得以长久保质。
具体实施方式
下面结合实施例,对本发明作详细的说明。
为了使本发明的目的、技术方案及优点更加清楚明白,以下结合实施例,对本发明进行进一步详细说明。应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。
一种贵金属纪念币的加工方法,包括以下步骤:
步骤一、根据所需加工的贵金属的产品设计图,制作压制机的冲压模具;
步骤二、将贵金属的坯料经过辊压机压制成符合设计要求的板条;
步骤三、步骤二完成后,在贵金属板条的表面上通过磁控溅射法,镀上一层钛膜,钛膜的厚度为60-100μm(具体厚度根据贵金属的种类和纪念币的规格确定);
步骤四、将步骤三中得到的板条进行退火处理,然后对贵金属坯料进行初轧,初轧后得到贵金属坯料,对贵金属坯料进行退火处理,退火后进行精轧,其中,最后三次的精轧道次的轧制压力恒定或者减小;精轧完成后,对贵金属坯料进行冲裁,得到符合设计形状、尺寸和性能的半成品坯饼,然后再对得到的半成品坯饼的进行尺寸检测验收,对于尺寸不足的半成品坯饼,通过镀钛的方式补足尺寸,以减少废品率的产生;
步骤五、将得到的坯饼进行表面清洗,然后放入离心光饰机的小桶内,启动电机,调节离心光饰机的主要参数,使离心光饰机的转速为300-500rad/min进行光饰处理,光饰处理完后,再放入无水乙醇中浸泡3-5h,最后取出烘干,得到成品坯饼;
步骤六、将得到的成品坯饼用已设计制作好的冲压模具的压制机压制,得到所需表面形状的纪念币。
本发明的贵金属纪念币的加工方法,通过优化轧制工艺,利用镀钛工艺与冲压工艺相结合的方式来生产贵金属纪念币,在保证成型质量和加工精度的情况下,提高了贵金属纪念币的耐磨性、抗腐蚀性和硬度,使贵金属纪念币得以长久保质。
通过上述加工方法得到的贵金属纪念币,其耐磨性、抗腐蚀性和硬度大大提高,贵金属纪念币可长久保质,同时,在外观质量上,由于钛膜具有多种不同的颜色,可根据贵金属纪念币的颜色选择与之配对的颜色,然后经光饰处理后,纪念币表面光滑硬度高,颜色几乎未变,不影响纪念币的美观价值。
以上所述仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等,均应包含在本发明的保护范围之内。
Claims (5)
1.一种贵金属物品的加工方法,包括将贵金属坯料制成板条的过程,其特征在于,包括镀钛步骤,镀钛步骤包括:在贵金属板条的表面上通过磁控溅射法镀上一层钛膜,然后再进行后续加工。
2.如权利要求1所述的贵金属物品的加工方法,其特征在于,钛膜的厚度为60-100μm。
3.如权利要求1所述的贵金属物品的加工方法,其特征在于,对镀钛后的贵金属板条进行初轧和精轧后,得到半成品,然后对半成品进行光饰处理后得到成品。
4.如权利要求3所述的贵金属物品的加工方法,其特征在于,对成品进行检测验收,对于尺寸不足的成品通过镀钛的方式补足尺寸。
5.如权利要求4所述的贵金属物品的加工方法,其特征在于,在进行光饰处理时,先将得到的半成品进行表面清洗,然后放入离心光饰机的小桶内,启动电机,调节离心光饰机的主要参数,使离心光饰机的转速为300-500rad/min进行光饰处理,光饰处理完后,再放入无水乙醇中浸泡3-5h,最后取出烘干即可。