CN107674530A - A kind of colorful imitative exterior wall tile coating containing anion powder and preparation method thereof - Google Patents
A kind of colorful imitative exterior wall tile coating containing anion powder and preparation method thereof Download PDFInfo
- Publication number
- CN107674530A CN107674530A CN201710968499.9A CN201710968499A CN107674530A CN 107674530 A CN107674530 A CN 107674530A CN 201710968499 A CN201710968499 A CN 201710968499A CN 107674530 A CN107674530 A CN 107674530A
- Authority
- CN
- China
- Prior art keywords
- parts
- exterior wall
- containing anion
- wall tile
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of colorful imitative exterior wall tile coating containing anion powder, and its raw material includes following components by weight：60 90 parts of organosilicon-modified acrylate emulsion, 180 210 parts of quartz sand, 15 30 parts of negative ion powder, 18 30 parts of cellulose solution, 9 30 parts of colored paint, 0.1 0.3 parts of bactericide, 0.1 0.3 parts of defoamer, 0.1 0.3 parts of multifunctional assistant, 25 parts of coalescents, 0.2 0.5 parts of thickener, 10 20 parts of deionized water.The present invention also provides its preparation method, the present invention the colorful imitative exterior wall tile coating containing anion powder have good dicoration, the feature of environmental protection, water resistance, alkali resistance, temperature-change resistance and weatherability are nonpoisonous and tasteless, green, security is good, containing anion, can antibacterial taste removal the characteristics of, it can effectively improve IAQ, dispel formaldehyde in indoor air, toluene, the harmful pollutants such as ammonia, meet people to environmental protection and the double requirements of health.
Description
Technical field
The present invention relates to a kind of exterior wall tile coating, relates in particular to a kind of colorful imitative exterior wall tile containing anion powder
Coating and preparation method thereof.
Background technology
Early in the 70's of 20th century, European Section scholar influences to have carried out comprehensive system research finger afterwards on room air
Go out：
From 500 gas chromatographies of room air detection, there is more than 20 kinds of carcinogenic substance.The World Health Organization《World health report
Accuse》In statistics, the nearly half people in the whole world is in indoor pollution, the patient that breathing problem is suffered from because of indoor environmental pollution
Account for generation
The 36% of boundary's population, chronic account for 23%, and tracheitis, bronchitis and patients with lung cancer account for 17/1000ths.Chinese room
Interior trim association indoor pollution detection observation center understands, and in numerous ornament materials, toxic material accounts for 68%, can produce 300
A variety of VOCs（VOC）, and triggering more than 30 kinds of disease, induction property cancer is the most prominent.
Most of interior/exterior decoration material on the market is organic material or organic/inorganic composite material, and they contain greatly
Measure VOC, such as formaldehyde, benzene noxious material, after making moist easily colours fading, yellowing, it is mouldy, come off, and exist the problem of easy to aging with
Inflammable potential safety hazard.Therefore research safety, nontoxic, good weatherability, the colorful imitative exterior wall tile coating containing anion, which turn into, grinds
Study carefully focus, greatly develop demand and real needs that such building and ornament materials are the epoch.
The content of the invention
For above-mentioned deficiency of the prior art, the technical problem to be solved in the present invention is to provide one kind to contain negative ion powder
The colorful imitative exterior wall tile coating of body, colorful imitative exterior wall tile coating of this kind containing anion powder have it is good it is ornamental,
The feature of environmental protection, water resistance, alkali resistance, temperature-change resistance and weatherability are nonpoisonous and tasteless, green, security is good, contain anion, energy
The characteristics of enough antibacterial taste removals, another object of the present invention is to provide colorful imitative exterior wall tile coating of this kind containing anion powder
Preparation method.
To achieve these goals, the present invention adopts the technical scheme that：It is a kind of colorful imitative outer containing anion powder
Wall brick coating, its raw material include following components by weight：Organosilicon-modified acrylate emulsion 60-90 parts, quartz sand 180-
210 parts, negative ion powder 15-30 parts, cellulose solution 18-30 parts, colored paint 9-30 parts, bactericide 0.1-0.3 parts, defoamer 0.1-
0.3 part, multifunctional assistant 0.1-0.3 parts, coalescents 2-5 parts, thickener 0.2-0.5 parts, deionized water 10-20 parts.
Further, a kind of described colorful imitative exterior wall tile coating containing anion powder, its raw material wrap by weight
Include following components：60 parts of organosilicon-modified acrylate emulsion, 180 parts of quartz sand, 15 parts of negative ion powder, 18 parts of cellulose solution,
9 parts of colored paint, 0.1 part of bactericide, 0.1 part of defoamer, 0.1 part of multifunctional assistant, 2 parts of coalescents, 0.2 part of thickener, go from
Sub- 10 parts of water.
Further, a kind of described colorful imitative exterior wall tile coating containing anion powder, its raw material wrap by weight
Include following components：90 parts of organosilicon-modified acrylate emulsion, 210 parts of quartz sand, 30 parts of negative ion powder, 30 parts of cellulose solution,
30 parts of colored paint, 0.3 part of bactericide, 0.3 part of defoamer, 0.3 part of multifunctional assistant, 5 parts of coalescents, 0.5 part of thickener, go from
Sub- 20 parts of water.
Further, a kind of described colorful imitative exterior wall tile coating containing anion powder, its raw material wrap by weight
Include following components：80 parts of organosilicon-modified acrylate emulsion, 200 parts of quartz sand, 25 parts of negative ion powder, 22 parts of cellulose solution,
22 parts of colored paint, 0.2 part of bactericide, 0.2 part of defoamer, 0.2 part of multifunctional assistant, 3 parts of coalescents, 0.3 part of thickener, go from
Sub- 16 parts of water.
Further, a kind of described colorful imitative exterior wall tile coating containing anion powder, described cellulose solution are
Gained is prepared by the fine micro- element of ethoxy and deionized water, its optimum weight part proportioning is deionized water：The fine micro- element of ethoxy is
（90-100）：（0.5-0.8）.
Further, described a kind of colorful imitative exterior wall tile coating containing anion powder, its preparation method include with
Lower step：
It is prepared by S10, cellulose solution：The accurate deionized water that weighs is added in agitator tank, and ethoxy is slowly added under stirring at low speed
Fine micro- element, is stirred while adding, until system is uniform, moderate viscosity, it is stand-by；
S11, emulsion allotment：By deionized water, bactericide, defoamer, multifunctional assistant, organosilicon-modified acrylate breast
Liquid, coalescents are added in agitator tank, are stirred, and dispersing speed 300-500r/min, add thickener, adjust body
It is moderate viscosity, filtering is stand-by；
S12, coating preparation：The emulsion that precise step S11 is first allocated to gained is added in agitator tank, in stirring at low speed
Lower addition colored paint, adds quartz sand, negative ion powder, stirs while adding, the fiber being eventually adding obtained by prepared by step S10
Plain liquid, until system is uniform, moderate viscosity, packs and produce colorful imitative exterior wall tile coating of this required kind containing anion.
Further, described described negative ion powder is ultra-fine negative ion powder, nanometer anion powder or its combination.
Further, described described defoamer is organic silicon defoamer, mineral oil defoaming agent or its group
Close.
The beneficial effects of the present invention are：A kind of colorful imitative exterior wall tile coating containing anion powder of the present invention is not
Only there is good dicoration, the feature of environmental protection, water resistance, alkali resistance, temperature-change resistance and weatherability, and per minute can also persistently release
Anion is put, can effectively improve IAQ, dispels the harmful pollutants such as formaldehyde in indoor air, toluene, ammonia；The painting
Material can also cigarette in decontamination chamber, oil fume, air pollution and electronic pollution caused by household electrical appliance rapidly；Substantially reduce electromagnetism
Radiation intensity etc. is multi-functional in one, and up to more than 90%, its health shows as passing through improvement for its 24 hours sterilizations, sterilization rates
Air quality, reach enhancing body immunity, the booster action of prevention of various diseases, meet people to the double of environmental protection and health
It is important to ask.Space using coating as carrier periphery indoors construct one it is pure natural, be not required to any energy just can forever discharge it is negative
The vert space of ion, this practical coating turn into people and improve environment, focus on the decoration preferred product of health.This kind containing negative
The invention of the colorful imitative exterior wall tile coating of ion powder allows indoor wall to discharge natural negative ion, and cost is low, easy to process, can
Using spraying, roller coating, brushing, blade coating etc..Its application surface is extensive.With the continuous improvement of living standards of the people, health perception
Constantly strengthen, the application of colorful imitative exterior wall tile coating of this kind containing anion powder will be increasing.
Embodiment
In order that present disclosure is more likely to be clearly understood, below according to the specific embodiment of the present invention, to this
Invention is described in further detail.
Embodiment 1
A kind of colorful imitative exterior wall tile coating containing anion powder, its raw material include following components by weight：Organosilicon changes
60 parts of acrylic acid ester emulsion of property, 180 parts of quartz sand, 15 parts of negative ion powder, 18 parts of cellulose solution, 9 parts of colored paint, 0.1 part of bactericide,
0.1 part of defoamer, 0.1 part of multifunctional assistant, 2 parts of coalescents, 0.2 part of thickener, 10 parts of deionized water.
Described cellulose solution is to prepare gained by the fine micro- plain and deionized water of ethoxy, and its optimum weight part proportioning is to go
Ionized water：The fine micro- element of ethoxy is 90：0.5.
Its preparation method comprises the following steps：
It is prepared by S10, cellulose solution：The accurate deionized water that weighs is added in agitator tank, and ethoxy is slowly added under stirring at low speed
Fine micro- element, is stirred while adding, until system is uniform, moderate viscosity, it is stand-by；
S11, emulsion allotment：By deionized water, bactericide, defoamer, multifunctional assistant, organosilicon-modified acrylate breast
Liquid, coalescents are added in agitator tank, are stirred, dispersing speed 300r/min adds thickener, and regulation system sticks
Spend it is moderate, filtering it is stand-by；
S12, coating preparation：The emulsion that precise step S11 is first allocated to gained is added in agitator tank, in stirring at low speed
Lower addition colored paint, adds quartz sand, negative ion powder, stirs while adding, the fiber being eventually adding obtained by prepared by step S10
Plain liquid, until system is uniform, moderate viscosity, packs and produce colorful imitative exterior wall tile coating of this required kind containing anion.
Described described negative ion powder is ultra-fine negative ion powder.
Described described defoamer is organic silicon defoamer.
Embodiment 2
A kind of colorful imitative exterior wall tile coating containing anion powder, its raw material include following components by weight：Organosilicon changes
90 parts of acrylic acid ester emulsion of property, 210 parts of quartz sand, 30 parts of negative ion powder, 30 parts of cellulose solution, 30 parts of colored paint, bactericide 0.3
Part, 0.3 part of defoamer, 0.3 part of multifunctional assistant, 5 parts of coalescents, 0.5 part of thickener, 20 parts of deionized water.
Described cellulose solution is to prepare gained by the fine micro- plain and deionized water of ethoxy, and its optimum weight part proportioning is to go
Ionized water：The fine micro- element of ethoxy is 90：0.8.
Its preparation method comprises the following steps：
It is prepared by S10, cellulose solution：The accurate deionized water that weighs is added in agitator tank, and ethoxy is slowly added under stirring at low speed
Fine micro- element, is stirred while adding, until system is uniform, moderate viscosity, it is stand-by；
S11, emulsion allotment：By deionized water, bactericide, defoamer, multifunctional assistant, organosilicon-modified acrylate breast
Liquid, coalescents are added in agitator tank, are stirred, dispersing speed 500r/min adds thickener, and regulation system sticks
Spend it is moderate, filtering it is stand-by；
S12, coating preparation：The emulsion that precise step S11 is first allocated to gained is added in agitator tank, in stirring at low speed
Lower addition colored paint, adds quartz sand, negative ion powder, stirs while adding, the fiber being eventually adding obtained by prepared by step S10
Plain liquid, until system is uniform, moderate viscosity, packs and produce colorful imitative exterior wall tile coating of this required kind containing anion.
Described described negative ion powder is nanometer anion powder.
Described described defoamer is mineral oil defoaming agent.
Embodiment 3
A kind of colorful imitative exterior wall tile coating containing anion powder, its raw material include following components by weight：Organosilicon changes
80 parts of acrylic acid ester emulsion of property, 200 parts of quartz sand, 25 parts of negative ion powder, 22 parts of cellulose solution, 22 parts of colored paint, bactericide 0.2
Part, 0.2 part of defoamer, 0.2 part of multifunctional assistant, 3 parts of coalescents, 0.3 part of thickener, 16 parts of deionized water.
Described cellulose solution is to prepare gained by the fine micro- plain and deionized water of ethoxy, and its optimum weight part proportioning is to go
Ionized water：The fine micro- element of ethoxy is 100：0.5.
Its preparation method comprises the following steps：
It is prepared by S10, cellulose solution：The accurate deionized water that weighs is added in agitator tank, and ethoxy is slowly added under stirring at low speed
Fine micro- element, is stirred while adding, until system is uniform, moderate viscosity, it is stand-by；
S11, emulsion allotment：By deionized water, bactericide, defoamer, multifunctional assistant, organosilicon-modified acrylate breast
Liquid, coalescents are added in agitator tank, are stirred, dispersing speed 400r/min adds thickener, and regulation system sticks
Spend it is moderate, filtering it is stand-by；
S12, coating preparation：The emulsion that precise step S11 is first allocated to gained is added in agitator tank, in stirring at low speed
Lower addition colored paint, adds quartz sand, negative ion powder, stirs while adding, the fiber being eventually adding obtained by prepared by step S10
Plain liquid, until system is uniform, moderate viscosity, packs and produce colorful imitative exterior wall tile coating of this required kind containing anion.
Described described negative ion powder is the combination of ultra-fine negative ion powder, any ratio of nanometer anion powder.
Described described defoamer is the combination of organic silicon defoamer, any ratio of mineral oil defoaming agent.
Following table is a kind of colorful imitative exterior wall tile coating technology index containing anion powder of the present invention
Above said content is only the basic explanation under present inventive concept, and is made according to technical scheme any etc.
Effect conversion, all should belong to protection scope of the present invention.
Claims (8)
1. a kind of colorful imitative exterior wall tile coating containing anion powder, it is characterised in that its raw material includes following by weight
Component：Organosilicon-modified acrylate emulsion 60-90 parts, quartz sand 180-210 parts, negative ion powder 15-30 parts, cellulose solution
18-30 parts, colored paint 9-30 parts, bactericide 0.1-0.3 parts, defoamer 0.1-0.3 parts, multifunctional assistant 0.1-0.3 parts, film forming help
Agent 2-5 parts, thickener 0.2-0.5 parts, deionized water 10-20 parts.
2. a kind of colorful imitative exterior wall tile coating containing anion powder according to claim 1, it is characterised in that it is former
Material includes following components by weight：60 parts of organosilicon-modified acrylate emulsion, 180 parts of quartz sand, 15 parts of negative ion powder, fibre
Tie up plain 18 parts of liquid, 9 parts of colored paint, 0.1 part of bactericide, 0.1 part of defoamer, 0.1 part of multifunctional assistant, 2 parts of coalescents, thickener
0.2 part, 10 parts of deionized water.
3. a kind of colorful imitative exterior wall tile coating containing anion powder according to claim 1, it is characterised in that it is former
Material includes following components by weight：90 parts of organosilicon-modified acrylate emulsion, 210 parts of quartz sand, 30 parts of negative ion powder,
30 parts of cellulose solution, 30 parts of colored paint, 0.3 part of bactericide, 0.3 part of defoamer, 0.3 part of multifunctional assistant, 5 parts of coalescents, increasing
Thick dose 0.5 part, 20 parts of deionized water.
4. a kind of colorful imitative exterior wall tile coating containing anion powder according to claim 1, it is characterised in that it is former
Material includes following components by weight：80 parts of organosilicon-modified acrylate emulsion, 200 parts of quartz sand, 25 parts of negative ion powder, fibre
Tie up plain 22 parts of liquid, 22 parts of colored paint, 0.2 part of bactericide, 0.2 part of defoamer, 0.2 part of multifunctional assistant, 3 parts of coalescents, thickening
0.3 part of agent, 16 parts of deionized water.
5. according to a kind of any described colorful imitative exterior wall tile coating containing anion powder of claim 1-4, its feature exists
In described cellulose solution is to prepare gained by the fine micro- element of ethoxy and deionized water, and its optimum weight part proportioning is deionization
Water：The fine micro- element of ethoxy is（90-100）：（0.5-0.8）.
6. according to a kind of any described colorful imitative exterior wall tile coating containing anion powder of claim 1-4, its feature exists
In its preparation method comprises the following steps：
It is prepared by S10, cellulose solution：The accurate deionized water that weighs is added in agitator tank, and ethoxy is slowly added under stirring at low speed
Fine micro- element, is stirred while adding, until system is uniform, moderate viscosity, it is stand-by；
S11, emulsion allotment：By deionized water, bactericide, defoamer, multifunctional assistant, organosilicon-modified acrylate breast
Liquid, coalescents are added in agitator tank, are stirred, and dispersing speed 300-500r/min, add thickener, adjust body
It is moderate viscosity, filtering is stand-by；
S12, coating preparation：The emulsion that precise step S11 is first allocated to gained is added in agitator tank, in stirring at low speed
Lower addition colored paint, adds quartz sand, negative ion powder, stirs while adding, the fiber being eventually adding obtained by prepared by step S10
Plain liquid, until system is uniform, moderate viscosity, packs and produce colorful imitative exterior wall tile coating of this required kind containing anion.
7. according to a kind of any described colorful imitative exterior wall tile coating containing anion powder of claim 1-4, its feature exists
In described described negative ion powder is ultra-fine negative ion powder, nanometer anion powder or its combination.
8. according to a kind of any described colorful imitative exterior wall tile coating containing anion powder of claim 1-4, its feature exists
In described described defoamer is organic silicon defoamer, mineral oil defoaming agent or its combination.