CN107573865A - 一种eva交联型防砸胶片的生产工艺 - Google Patents
一种eva交联型防砸胶片的生产工艺 Download PDFInfo
- Publication number
- CN107573865A CN107573865A CN201710854529.3A CN201710854529A CN107573865A CN 107573865 A CN107573865 A CN 107573865A CN 201710854529 A CN201710854529 A CN 201710854529A CN 107573865 A CN107573865 A CN 107573865A
- Authority
- CN
- China
- Prior art keywords
- eva
- film
- pounding
- films
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种EVA交联型防砸胶片的生产工艺。包括以下步骤,(1)制备母粒的步骤,母粒基材采用190℃时熔融指数为5‑15g/10min的EVA,采用高分子蜡作分散剂;(2)将母粒与EVA树脂和偶联剂混合均匀的步骤,EVA树脂在190℃时熔融指数为5‑15g/10min;(3)采用流延成膜工艺生成EVA玻璃胶片的步骤;(4)涂覆的步骤,将两层步骤(3)得到的EVA胶片涂覆在一层PET胶片的两侧,PET胶片的厚度为0.1‑0.15mm。本发明提供了一种EVA交联型防砸胶片的生产工艺,通过采用EVA材料代替传统的PVB材料、设计两侧EVA胶片与中部PET胶片的三层结构,提升了防砸胶片的结构强度,应用于玻璃时能够显著提升玻璃抵抗强烈冲击力的能力,同时提升了与玻璃之间的剥离强度和拉伸强度。
Description
技术领域
本发明涉及一种EVA交联型防砸胶片的生产工艺。
背景技术
在建筑装饰等领域,夹胶玻璃以其美观、坚固等优良特性得到了越来越广泛的应用,夹胶玻璃包括位于中心的玻璃胶片层和位于两侧的玻璃。防砸/防爆玻璃是一款将玻璃胶片复合进两层玻璃中间,经高温高压胶合后,一体成型的夹层结构的新型特种玻璃产品。现有的防砸胶片其结构强度低,与玻璃之间的剥离强度和拉伸强度低。
发明内容
本发明为解决公知技术中存在的技术问题而提供一种EVA交联型防砸胶片的生产工艺,解决背景技术中存在的问题。
本发明为解决公知技术中存在的技术问题所采取的技术方案是:一种EVA交联型防砸胶片的生产工艺包括以下步骤,(1)制备母粒的步骤,母粒基材采用190℃时熔融指数为5-15g/10min的EVA,采用高分子蜡作分散剂;(2)将母粒与EVA树脂和偶联剂混合均匀的步骤,EVA树脂在190℃时熔融指数为5-15g/10min;(3)采用流延成膜工艺生成EVA玻璃胶片的步骤;(4)涂覆的步骤,将两层步骤(3)得到的EVA胶片涂覆在一层PET胶片的两侧,PET胶片的厚度为0.1-0.15mm。
本发明的优点和积极效果是:本发明提供了一种EVA交联型防砸胶片的生产工艺,通过采用EVA材料代替传统的PVB材料、设计两侧EVA胶片与中部PET胶片的三层结构,提升了防砸胶片的结构强度,应用于玻璃时能够显著提升玻璃抵抗强烈冲击力的能力,同时提升了与玻璃之间的剥离强度和拉伸强度。
优选地:步骤(1)中所述的高分子蜡选取为聚乙烯蜡、EVA蜡、共聚酯蜡中的一种或多种。
优选地:步骤(2)中所述的偶联剂选取为氨丙基三甲氧基硅烷、氨丙基甲基二甲氧基硅烷、氨丙基三乙氧基硅烷、氨乙基氨丙基三甲氧基硅烷、氨乙基氨丙基三乙氧基硅烷、氨乙基氨丙基甲基二甲氧基硅烷、乙烯基三甲氧基硅烷、乙烯基三乙氧基硅烷、甲基丙烯酰氧基三甲氧基硅烷中的一种或多种。
优选地:步骤(3)中流延成膜工艺采用单螺杆挤出机,挤出温度为80-100℃。
具体实施方式
为能进一步了解本发明的发明内容、特点及功效,兹举以下实施例详细说明如下:
实施例1
(1)制备母粒的步骤,母粒基材采用190℃时熔融指数在5g/10min的EVA,采用高分子蜡作分散剂;(2)将母粒与EVA树脂和偶联剂混合均匀的步骤,EVA树脂在190℃时熔融指数在8g/10min;(3)采用流延成膜工艺生成EVA玻璃胶片的步骤;(4)涂覆的步骤,将两层步骤(3)得到的EVA胶片涂覆在一层PET胶片的两侧,PET胶片的厚度为0.1mm。
其中,步骤(1)中所述的高分子蜡选取为聚乙烯蜡;步骤(2)中所述的偶联剂选取为氨乙基氨丙基三甲氧基硅烷;步骤(3)中流延成膜工艺采用单螺杆挤出机,挤出温度为80℃。
实施例2
(1)制备母粒的步骤,母粒基材采用190℃时熔融指数在10g/10min的EVA,采用高分子蜡作分散剂;(2)将母粒与EVA树脂和偶联剂混合均匀的步骤,EVA树脂在190℃时熔融指数在10g/10min;(3)采用流延成膜工艺生成EVA玻璃胶片的步骤;(4)涂覆的步骤,将两层步骤(3)得到的EVA胶片涂覆在一层PET胶片的两侧,PET胶片的厚度为0.12mm。
其中,步骤(1)中所述的高分子蜡选取为EVA蜡;步骤(2)中所述的偶联剂选取为氨乙基氨丙基三甲氧基硅烷;步骤(3)中流延成膜工艺采用单螺杆挤出机,挤出温度为90℃。
实施例3
(1)制备母粒的步骤,母粒基材采用190℃时熔融指数在15g/10min的EVA,采用高分子蜡作分散剂;(2)将母粒与EVA树脂和偶联剂混合均匀的步骤,EVA树脂在190℃时熔融指数在14g/10min;(3)采用流延成膜工艺生成EVA玻璃胶片的步骤;(4)涂覆的步骤,将两层步骤(3)得到的EVA胶片涂覆在一层PET胶片的两侧,PET胶片的厚度为0.15mm。
其中,步骤(1)中所述的高分子蜡选取为共聚酯蜡;步骤(2)中所述的偶联剂选取为乙烯基三甲氧基硅烷;步骤(3)中流延成膜工艺采用单螺杆挤出机,挤出温度为100℃。
Claims (4)
1.一种EVA交联型防砸胶片的生产工艺,其特征是:包括以下步骤,
(1)制备母粒的步骤,母粒基材采用190℃时熔融指数为5-15g/10min的EVA,采用高分子蜡作分散剂;
(2)将母粒与EVA树脂和偶联剂混合均匀的步骤,EVA树脂在190℃时熔融指数为5-15g/10min;
(3)采用流延成膜工艺生成EVA玻璃胶片的步骤;
(4)涂覆的步骤,将两层步骤(3)得到的EVA胶片涂覆在一层PET胶片的两侧,PET胶片的厚度为0.1-0.15mm。
2.如权利要求1所述的EVA交联型防砸胶片的生产工艺,其特征在于:步骤(1)中所述的高分子蜡选取为聚乙烯蜡、EVA蜡、共聚酯蜡中的一种或多种。
3.如权利要求1所述的EVA交联型防砸胶片的生产工艺,其特征在于:步骤(2)中所述的偶联剂选取为氨丙基三甲氧基硅烷、氨丙基甲基二甲氧基硅烷、氨丙基三乙氧基硅烷、氨乙基氨丙基三甲氧基硅烷、氨乙基氨丙基三乙氧基硅烷、氨乙基氨丙基甲基二甲氧基硅烷、乙烯基三甲氧基硅烷、乙烯基三乙氧基硅烷、甲基丙烯酰氧基三甲氧基硅烷中的一种或多种。
4.如权利要求1所述的EVA交联型防砸胶片的生产工艺,其特征在于:步骤(3)中流延成膜工艺采用单螺杆挤出机,挤出温度为80-100℃。