CN107556558A - 一种高弹性疏水混合物及其制备方法与应用 - Google Patents
一种高弹性疏水混合物及其制备方法与应用 Download PDFInfo
- Publication number
- CN107556558A CN107556558A CN201710727396.3A CN201710727396A CN107556558A CN 107556558 A CN107556558 A CN 107556558A CN 201710727396 A CN201710727396 A CN 201710727396A CN 107556558 A CN107556558 A CN 107556558A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixture
- high resiliency
- hydrophobic
- compound resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高弹性疏水混合物，主要由以下质量份的物料制成：复合树脂10‑20份、碳纤维0.5‑1份、活化橡胶80‑90份、有机硅乳液10‑15份、分散剂1‑2份和固化剂1‑2份；所述复合树脂主要由以下质量份的物料制成：聚酯树脂10‑20份、聚乙烯醇10‑20份、聚苯乙烯10‑20份和聚氨酯10‑20份；本发明还公开了该混合物的制备方法及应用；优点是：首先，本发明的混合物在保证高弹性的同时，保持着良好的疏水性能，可以有效的隔绝液体；其次，利用本发明的混合物制成的车载帐篷，不仅可以根据包裹的货物不规则的拉伸，而且可以起到有效的防水功能。
Description
技术领域
本发明涉及一种弹性材料，尤其涉及一种高弹性疏水混合物及其制备方法与应用。
背景技术
敞开式车厢货车送货时，为保持货物的清洁时常采用帐篷将车厢封闭，该帐篷需要具有弹性和隔水性，现有技术中往往采用一层涂有防水的材料的麻布，由此制作而成的帐篷在与货物的挤压时表面发生形变，其表面的防水涂层久而久之会产生裂纹并慢慢脱落，从而影响其防水效果。
发明内容
发明目的：本发明的第一目的是提供一种既有高弹性和疏水性以实现不规则的拉伸和防水功能的混合物，第二目的是提供该混合物的制备方法，第三目的是提供该混合物在货车敞开式车厢帐篷上的应用。
技术方案：本发明所述的高弹性疏水混合物，主要由以下质量份的物料制成：复合树脂10-20份、碳纤维0.5-1份、活化橡胶80-90份、有机硅乳液10-15份、分散剂1-2份和固化剂1-2份；
所述复合树脂主要由以下质量份的物料制成：聚酯树脂10-20份、聚乙烯醇10-20份、聚苯乙烯10-20份和聚氨酯10-20份；
其中，所述碳纤维为圆形管状或者多边形管状。
进一步，所述有机硅乳液的硅油含量为10-15％。
进一步，所述分散剂为聚羧酸钠盐。
所述的高弹性疏水混合物的制备方法，主要包括以下步骤：
(1)将聚酯树脂、聚乙烯醇、聚苯乙烯和聚氨酯混合在水中，并进行超声分散，除水后在100-120℃下放置1-2h，形成复合树脂；
(2)将复合树脂、碳纤维和分散剂混合，搅拌1-2h后，在NaOH溶液中浸泡0.5-0.75h，得到混合物A；
(3)将活化橡胶和有机硅乳液混合，在1000-1500r/min下离心1-2h得到混合物B；
(4)将混合物A和混合物B混合，发泡0.5-1h后静置1-2h，再加入固化剂，在200-300℃下搅拌2-3h即得。
其中，所述的活化橡胶的制备方法为：将天然橡胶粉碎过200-300目筛，加入浓度为5-15％的NaCl溶液中，同时加入油类软化剂，浸泡10-15h后取出，重新放置于沸水中持续0.5-1h，取出静置冷却即得。
所述的高弹性疏水混合物的应用，将该高弹性疏水混合物直接压卷制成薄膜状用于作为货车敞开式车厢的帐篷。
有益效果：与现有技术相比，本发明的显著的优点为：(1)本发明的混合物在保证高弹性的同时，保持着良好的疏水性能，可以有效的隔绝液体；(2)利用本发明的混合物制成的车载帐篷，不仅可以根据包裹的货物不规则的拉伸，而且可以起到有效的防水功能。
具体实施方式
实施例1
一种高弹性疏水混合物，主要由以下质量份的物料制成：复合树脂10份、碳纤维0.5份、活化橡胶80份、有机硅乳液10份、分散剂1份和固化剂1份；
所述复合树脂主要由以下质量份的物料制成：聚酯树脂10份、聚乙烯醇10份、聚苯乙烯10份和聚氨酯10份；
其中，所述碳纤维为圆形管状，所述有机硅乳液的硅油含量为10％，所述分散剂为聚羧酸钠盐。
所述高弹性疏水混合物的制备方法，主要包括以下步骤：
(1)将聚酯树脂、聚乙烯醇、聚苯乙烯和聚氨酯混合在水中，并进行超声分散，除水后在100℃下放置1h，形成复合树脂；
(2)将复合树脂、碳纤维和分散剂混合，搅拌1h后，在NaOH溶液中浸泡0.5h，得到混合物A；
(3)将活化橡胶和有机硅乳液混合，在1000r/min下离心1h得到混合物B；
(4)将混合物A和混合物B混合，发泡0.5h后静置1h，再加入固化剂，在200℃下搅拌2h即得。
其中，所述的活化橡胶的制备方法为：将天然橡胶粉碎过200目筛，加入浓度为5％的NaCl溶液中，同时加入油类软化剂，浸泡10h后取出，重新放置于沸水中持续0.5h，取出静置冷却即得。
实施例2
一种高弹性疏水混合物，主要由以下质量份的物料制成：复合树脂15份、碳纤维0.75份、活化橡胶85份、有机硅乳液12份、分散剂1.5份和固化剂1.5份；
所述复合树脂主要由以下质量份的物料制成：聚酯树脂15份、聚乙烯醇15份、聚苯乙烯15份和聚氨酯15份；
其中，所述碳纤维为多边形管状，所述有机硅乳液的硅油含量为12％，所述分散剂为聚羧酸钠盐。
所述的高弹性疏水混合物的制备方法，主要包括以下步骤：
(1)将聚酯树脂、聚乙烯醇、聚苯乙烯和聚氨酯混合在水中，并进行超声分散，除水后在110℃下放置1.5h，形成复合树脂；
(2)将复合树脂、碳纤维和分散剂混合，搅拌1.5h后，在NaOH溶液中浸泡0.6h，得到混合物A；
(3)将活化橡胶和有机硅乳液混合，在1250r/min下离心1.5h得到混合物B；
(4)将混合物A和混合物B混合，发泡0.75h后静置1.5h，再加入固化剂，在250℃下搅拌2.5h即得。
其中，所述的活化橡胶的制备方法为：将天然橡胶粉碎过250目筛，加入浓度为10％的NaCl溶液中，同时加入油类软化剂，浸泡12h后取出，重新放置于沸水中持续0.75h，取出静置冷却即得。
实施例3
一种高弹性疏水混合物，主要由以下质量份的物料制成：复合树脂20份、碳纤维1份、活化橡胶90份、有机硅乳液15份、分散剂2份和固化剂2份；
所述复合树脂主要由以下质量份的物料制成：聚酯树脂20份、聚乙烯醇20份、聚苯乙烯20份和聚氨酯20份；
其中，所述碳纤维为圆形管状，所述有机硅乳液的硅油含量为15％，所述分散剂为聚羧酸钠盐。
所述的高弹性疏水混合物的制备方法，主要包括以下步骤：
(1)将聚酯树脂、聚乙烯醇、聚苯乙烯和聚氨酯混合在水中，并进行超声分散，除水后在120℃下放置2h，形成复合树脂；
(2)将复合树脂、碳纤维和分散剂混合，搅拌2h后，在NaOH溶液中浸泡0.75h，得到混合物A；
(3)将活化橡胶和有机硅乳液混合，在1500r/min下离心2h得到混合物B；
(4)将混合物A和混合物B混合，发泡1h后静置2h，再加入固化剂，在300℃下搅拌3h即得。
其中，所述的活化橡胶的制备方法为：将天然橡胶粉碎过300目筛，加入浓度为15％的NaCl溶液中，同时加入油类软化剂，浸泡15h后取出，重新放置于沸水中持续1h，取出静置冷却即得。
试验例1
选取市面较为普遍的汽车车厢帐篷(即一层麻布表面涂有防水涂料)作为对比例1，将实施例1、实施例2和实施例3所制成的混合料压卷制成与对比例1的麻布一样的厚度帐篷，并对对比例1、实施例1、实施例2和实施例3所制成的帐篷的两侧施加拉力直至帐篷发生损坏，测量对比例1、实施例1、实施例2和实施例3所制成的帐篷的损坏临界长度，见表1：
表1 对比例1、实施例1、实施例2和实施例3所制成的帐篷的拉伸性能
| 拉伸前长度/m | 拉伸断裂时的临界长度/m | |
| 对比例1 | 2 | 2.5 |
| 实施例1 | 2 | 4 |
| 实施例2 | 2 | 4.2 |
| 实施例3 | 2 | 4.1 |
表1可以看出本发明实施例1、实施例2和实施例3所制成的帐篷拉伸性能远优于对比例1中普通帐篷的拉伸性能。
试验例2
选取市面较为普遍的汽车车厢帐篷(即一层麻布表面涂有防水涂料)作为对比例1，将实施例1、实施例2和实施例3所制成的混合料压卷制成与对比例1的麻布一样的厚度帐篷，将对比例1、实施例1、实施例2和实施例3所制成的帐篷弯卷成凹槽状，在凹槽内盛一定量水，间隔时间测量所剩水量，见表2：
表2 对比例1、实施例1、实施例2和实施例3所制成的帐篷的防水性能
表2可以看出，本发明实施例1、实施例2和实施例3所制成的帐篷的防水性能远优于对比例1中普通帐篷的防水性能。
Claims (7)
1.一种高弹性疏水混合物，其特征在于：主要由以下质量份的物料制成：复合树脂10-20份、碳纤维0.5-1份、活化橡胶80-90份、有机硅乳液10-15份、分散剂1-2份和固化剂1-2份；
所述复合树脂主要由以下质量份的物料制成：聚酯树脂10-20份、聚乙烯醇10-20份、聚苯乙烯10-20份和聚氨酯10-20份。
2.根据权利要求1所述的高弹性疏水混合物，其特征在于：所述碳纤维为圆形管状或者多边形管状。
3.根据权利要求1所述的高弹性疏水混合物，其特征在于：所述有机硅乳液的硅油含量为10-15％。
4.根据权利要求1所述的高弹性疏水混合物，其特征在于：所述分散剂为聚羧酸钠盐。
5.权利要求1所述的高弹性疏水混合物的制备方法，其特征在于：主要包括以下步骤：
(1)将聚酯树脂、聚乙烯醇、聚苯乙烯和聚氨酯混合在水中，并进行超声分散，除水后在100-120℃下放置1-2h，形成复合树脂；
(2)将复合树脂、碳纤维和分散剂混合，搅拌1-2h后，在NaOH溶液中浸泡0.5-0.75h，得到混合物A；
(3)将活化橡胶和有机硅乳液混合，在1000-1500r/min下离心1-2h得到混合物B；
(4)将混合物A和混合物B混合，发泡0.5-1h后静置1-2h，再加入固化剂，在200-300℃下搅拌2-3h即得。
6.根据权利要求1或者5所述的活化橡胶的制备方法，其特征在于：将天然橡胶粉碎过200-300目筛，加入浓度为5-15％的NaCl溶液中，同时加入油类软化剂，浸泡10-15h后取出，重新放置于沸水中持续0.5-1h，取出静置冷却即得。
7.权利要求1所述的高弹性疏水混合物的应用，其特征在于：将该高弹性疏水混合物直接压卷制成薄膜状用于作为货车敞开式车厢的帐篷。