CN107474925A - 一种防锈润滑油 - Google Patents
一种防锈润滑油 Download PDFInfo
- Publication number
- CN107474925A CN107474925A CN201710779235.9A CN201710779235A CN107474925A CN 107474925 A CN107474925 A CN 107474925A CN 201710779235 A CN201710779235 A CN 201710779235A CN 107474925 A CN107474925 A CN 107474925A
- Authority
- CN
- China
- Prior art keywords
- parts
- rust preventive
- lubricating oil
- preventive lubricating
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种防锈润滑油,其特征在于:所述防锈润滑油由以下质量份数的各组分组成 :基础油 60‑65 份、柠檬酸钠 2‑3 份、聚氨酯 2‑3 份、烷基磷酸酯 5‑8 份、二氯甲烷 0.2‑0.3 份、苯并三氮唑 0.2‑0.3 份、二异辛基二苯胺 0.5‑0.8 份;亚磷酸脂 5‑9 份,增粘剂 2‑3 份,滑石粉 4‑7 份,磷酸 10‑13 份,抗氧抗腐剂 0.2‑0.8 份;本发明的防锈润滑油可以解决现有防锈润滑油粘度指数低的问题,本发明的防锈润滑油对机器设备具有良好的冷却、密封、防腐、防锈、绝缘作用。冷却、润滑效果好,使用时摩擦力小。
Description
技术领域
本发明涉及机械润滑领域,尤其涉及一种防锈润滑油。
背景技术
防锈润滑油是用在汽车、机械设备上以减少摩擦、保护机械及加工件的液体或半固体润滑剂,主要起润滑、冷却、防锈、清洁、密封和缓冲等作用。防锈润滑油由基础油和添加剂两部分组成,基础油是防锈润滑油的主要成分,决定着防锈润滑油的基本性质,添加剂则可弥补和改善基础油性能方面的不足,赋予某些新的性能,是防锈润滑油的重要组成部分。
粘度指数是指油品粘度随温度变化的程度,粘度指数越高,表示油品粘度受温度的影响越小,其粘温性能越好,反之越差;粘度指数是防锈润滑油性能的重要指标,因此,如何提 高防锈润滑油的粘度指数成为目前防锈润滑油研究领域的热点。
防锈润滑油一般由基础油和添加剂两部分组成。基础油是防锈润滑油的主要成分,决定着防锈润滑油的基本性质,添加剂则可弥补和改善基础油性能方面的不足,赋予某些新的性能,是防锈润滑油的重要组成部分。防锈润滑油是用在各种类型汽车、机械设备上以减少摩擦,保护机械及加工件的液体或半固体润滑剂,主要起润滑、冷却、防锈、清洁、密封和缓冲等作用。
发明内容
本发明要解决的技术问题是提供一种防锈润滑油,解决现有防锈润滑油粘度指数低的问题,冷却、润滑效果好,使用时摩擦力小。
为解决上述技术问题,本发明的技术方案为:一种防锈润滑油,其创新点在于:所述防锈润滑油由以下质量份数的各组分组成 :基础油 60-65 份、柠檬酸钠 2-3 份、聚氨酯 2-3 份、烷基磷酸酯 5-8 份、二氯甲烷 0.2-0.3 份、苯并三氮唑 0.2-0.3 份、二异辛基二苯胺 0.5-0.8 份;亚磷酸脂 5-9 份,增粘剂 2-3 份,滑石粉 4-7 份,磷酸 10-13份,抗氧抗腐剂 0.2-0.8 份。
进一步的,所述基础油是粘度指数为 90以上的高粘度指 数的Ⅰ、Ⅱ、Ⅲ类基础油。
进一步的,所述增粘剂是聚甲基丙烯酸酯、聚丙烯酸酯、 无规聚丙烯、乙丙共聚物中的一种或混合物。
进一步的,该防锈润滑油的制作方法具体如下:
(1)将配方量的基础油、柠檬酸钠、聚氨酯、烷基磷酸酯、二氯甲烷混合,加热至 45-55℃,搅拌 30-35min ;
(2)加入配方量的其余组分,搅拌 15-20min,冷却至室温,过滤即得。
本发明的优点在于:
1)本发明的防锈润滑油可以解决现有防锈润滑油粘度指数低的问题,本发明的防锈润滑油对机器设备具有良好的冷却、密封、防腐、防锈、绝缘作用。冷却、润滑效果好,使用时摩擦力小。
具体实施方式
下面的实施例可以使本专业的技术人员更全面地理解本发明,但并不因此将本发明限制在所述的实施例范围之中。
实施例1:
基础油 60kg、柠檬酸钠 2kg、聚氨酯 2 kg、烷基磷酸酯 5 kg、二氯甲烷 0.2 kg、苯并三氮唑 0.2 kg、二异辛基二苯胺 0.5 kg;亚磷酸脂 5 kg,增粘剂 2 kg,滑石粉 4 kg,磷酸 10 kg,抗氧抗腐剂 0.2 kg;
本发明的防锈润滑油制备方法如下:
将基础油 60kg、柠檬酸钠 2kg、聚氨酯 2 kg、烷基磷酸酯 5 kg、二氯甲烷 0.2 kg混合,加热至45℃;搅拌30min;
加入苯并三氮唑 0.2 kg、二异辛基二苯胺 0.5 kg;亚磷酸脂 5 kg,增粘剂 2 kg,滑石粉 4 kg,磷酸 10 kg,抗氧抗腐剂 0.2 kg;搅拌15min,冷却至室温,过滤即得。
实施例2:
基础油 62kg、柠檬酸钠 2.5kg、聚氨酯 2.5kg、烷基磷酸酯 7kg、二氯甲烷 0.25kg、苯并三氮唑 0.25kg、二异辛基二苯胺 0.7kg;亚磷酸脂 7kg,增粘剂2.5kg,滑石粉6kg,磷酸12kg,抗氧抗腐剂 0.5kg。
本发明的防锈润滑油制备方法如下:
将基础油 62kg、柠檬酸钠 2.5kg、聚氨酯 2.5kg、烷基磷酸酯 7kg、二氯甲烷 0.25kg混合,加热至45℃;搅拌30min;
加入苯并三氮唑 0.25kg、二异辛基二苯胺 0.7kg;亚磷酸脂 7kg,增粘剂2.5kg,滑石粉6kg,磷酸 12kg,抗氧抗腐剂 0.5kg;搅拌15min,冷却至室温,过滤即得。
实施例3:
基础油 65kg、柠檬酸钠 3kg、聚氨酯 3kg、烷基磷酸酯 8kg、二氯甲烷 0.3kg、苯并三氮唑 0.3kg、二异辛基二苯胺 0.8kg;亚磷酸脂 9kg,增粘剂3kg,滑石粉7kg,磷酸 13kg,抗氧抗腐剂 0.8kg。
本发明的防锈润滑油制备方法如下:
基础油 65kg、柠檬酸钠 3kg、聚氨酯 3kg、烷基磷酸酯 8kg、二氯甲烷 0.3kg混合,加热至55℃;搅拌35min;
加入苯并三氮唑 0.3kg、二异辛基二苯胺 0.8kg;亚磷酸脂 9kg,增粘剂3kg,滑石粉7kg,磷酸 13kg,抗氧抗腐剂 0.8kg;搅拌20min,冷却至室温,过滤即得。
本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (4)
1.一种防锈润滑油,其特征在于:所述防锈润滑油由以下质量份数的各组分组成 :基础油 60-65 份、柠檬酸钠 2-3 份、聚氨酯 2-3 份、烷基磷酸酯 5-8 份、二氯甲烷 0.2-0.3 份、苯并三氮唑 0.2-0.3 份、二异辛基二苯胺 0.5-0.8 份;亚磷酸脂 5-9 份,增粘剂2-3 份,滑石粉 4-7 份,磷酸 10-13 份,抗氧抗腐剂 0.2-0.8 份。
2.根据权利要求1所述的一种防锈润滑油,其特征在于:所述基础油是粘度指数为 90以上的高粘度指 数的Ⅰ、Ⅱ、Ⅲ类基础油。
3.根据权利要求1所述的一种防锈润滑油,其特征在于:所述增粘剂是聚甲基丙烯酸酯、聚丙烯酸酯、 无规聚丙烯、乙丙共聚物中的一种或混合物。
4.根据权利要求1所述的一种防锈润滑油,其特征在于:该防锈润滑油的制作方法具体如下:
(1)将配方量的基础油、柠檬酸钠、聚氨酯、烷基磷酸酯、二氯甲烷混合,加热至 45-55℃,搅拌 30-35min ;
(2)加入配方量的其余组分,搅拌 15-20min,冷却至室温,过滤即得。